Super-ductile PBT alloy with excellent heat resistance

Thermal Treatment Effects on Structure and Mechanical Properties of Polybutylene Terephthalate and Epoxy Resin Composites Reinforced with Glass Fiber

In this study, two types of composites, polybutylene terephthalate (PBT) and epoxy resin (ER), reinforced with 20% of glass fiber (GF) are used as the comparative research objects. Their mechanical properties after thermal aging at 85~145 °C are evaluated by tensile strength and fracture morphology analysis. The results show that the composites have similar aging laws. The tensile strength of GF/PBT and GF/ER decrease gradually with the increase of aging temperature, while their elastic moduli are independent of the thermal treatment temperature. Scanning electron microscopy study of the fracture surface shows that separation of glass fiber from PBT and ER matrix becomes more obvious at higher aging temperature. The fibers on the matrix surface appear clear and smooth, and the whole pulled out GFs can be observed. As a main mechanical strength degradation mechanism, the deterioration of interface adhesion between the matrix and GF is discussed. A large difference in coefficients of thermal expansion of the matrix and GF is a main factor of the mechanical degradation.

Effect of Thermal Aging on Mechanical Properties and Morphology of GF/PBT Composites

The effects of thermal aging at 85~145 °C in air on the tensile and flexural mechanical properties of 20% glass fiber (GF)-reinforced commercial grade polybutylene terephthalate (PBT) composites were studied. The results showed that as the aging temperature increased, the tensile and flexural strength of the GF/PBT composites significantly decreased. However, the elastic modulus of the composites was almost independent of aging. As the aging temperature increased, the separation between GF and the PBT matrix became more pronounced, and the fibers exposed on the surface of the matrix became clearer and smoother, indicating a decrease in interfacial adhesion between the PBT matrix and GF. The reason for this decrease in strength and brittle fracture of composites is the interface damage between the GF and PBT matrix caused by the difference in their thermal expansion coefficients during thermal aging.