Enhancing the mechanical, morphological, and rheological behavior of polyethylene/polypropylene blends with maleic anhydride‐grafted polyethylene

Composition Dependence of Flow-Induced Crystallization in High-Density Polyethylene/Isotactic Polypropylene Blends

Polyolefins, including high-density polyethylene (HDPE) and isotactic polypropylene (iPP), account for over half of the worldwide plastics market and have wide-ranging applications. Recycling of these materials is hindered due to separation difficulties as co-mingled blends of HDPE and iPP often exhibit brittle mechanical behavior because phase separated domains detach under stress due to low interfacial adhesion. Motivated to improve mechanical properties of mixed recyclates during processing, this work examines the effect of shear on the crystallization kinetics and rheological properties of HDPE-iPP blends utilizing a combination of differential scanning calorimetry (DSC), rheo-Raman spectroscopy, polarized optical microscopy, and scanning electron microscopy (SEM). In the quiescent experiments, the crystallization temperature as a function of blend composition exhibits a distinct decrease when the iPP forms the droplet phase, as expected, due to fractionated crystallization. In the presence of shear, we find elongated domains due to high capillary number. Unexpectedly, we find a compositional dependence to the flow-induced crystallization (FIC) of iPP: stronger FIC is observed in all blends compared to the pure iPP. Moreover, the flow completely counteracts the reduced crystallization arising from fractionated crystallization, indicating that the flow is able to induce nucleation in droplets to an extent such that it offsets the reduction in active nucleating agents in finite size droplets. We attribute these effects to differing microflow fields in the various morphologies as the iPP domains deform under shear.

The Effect of Coupling Agents and Graphene on the Mechanical Properties of Film-Based Post-Consumer Recycled Plastic

This study aims to improve the mechanical properties of post-consumer recycled (PCR) plastic composed primarily of polypropylene (PP) and polyethylene (PE), which generally exhibit poor miscibility, by applying coupling agents and graphene. Here, we compare a commercially available coupling agent with a directly synthesized maleic anhydride (MA) coupling agent. When applied to a 5:5 blend of recycled PP and PE, an optimum tensile strength was achieved at a 3 wt% coupling agent concentration, with the MA coupling agent outperforming the commercial one. Characterization through Fourier transform infrared spectroscopy (FT-IR) and thermogravimetry analysis (TGA) revealed a PP:PE ratio of approximately 3:7 in the PCR plastics, with 4.86% heterogeneous materials present. Applying 3 wt% of the commercial and MA coupling agents to the PCR plastics resulted in a significant 53.9% increase in the tensile strength, reaching 11.25 MPa, and a remarkable 421.54% increase in the melt flow index (MFI), reaching 25.66 g/10 min. Furthermore, incorporating 5 wt% graphene led to a notable 64.84% increase in the tensile strength. In addition, the application of MA coupling agents and graphene improved the thermal stability of the PCR plastics. These findings show significant promise for addressing environmental concerns associated with plastic waste by facilitating the recycling of PCR plastics into new products. The utilization of coupling agents and graphene offers a viable approach to enhance the mechanical properties of PCR plastics, paving the way for sustainable and environmentally friendly solutions.

On the Mechanical, Thermal, and Rheological Properties of Polyethylene/Ultra-High Molecular Weight Polypropylene Blends

The novel ultra-high molecular weight polypropylene (UHMWPP) as a dispersed component was melt blended with conventional high-density polyethylene (PE) and maleic anhydride grafted-polyethylene (mPE) in different proportions through a kneader. Ultra-high molecular weight polypropylene is a high-performance polymer material that has excellent mechanical properties and toughness compared to other polymers. Mechanical, thermal, and rheological properties were presented for various UHMWPP loadings, and correlations between mechanical and rheological properties were examined. Optimal comprehensive mechanical properties are achieved when the UHMWPP content reaches approximately 50 wt%, although the elongation properties do not match those of pure PE or mPE. However, it is worth noting that the elongation properties of these blends did not match those of PE or mPE. Particularly, for the PE/UHMWPP blends, a significant drop in tensile strength was observed as the UHMWPP content decreased (from 30.24 MPa for P50U50 to 13.12 MPa for P90U10). In contrast, the mPE/UHMWPP blends demonstrated only minimal changes in tensile strength (ranging from 29 MPa for mP50U50 to 24.64 MPa for mP90U10) as UHMWPP content varied. The storage modulus of the PE/UHMWPP blends increased drastically with the UHMWPP content due to the UHMWPP chain entanglements and rigidity. Additionally, we noted a substantial reduction in the melt index of the blend system when the UHMWPP content exceeded 10% by weight.