Curing behavior and thermal and mechanical properties enhancement of tetraglycidyl-4,4′-diaminodiphenylmethane/4,4′-diaminodiphenylsulfone using a liquid crystalline epoxy

Improved thermal and mechanical properties of bismaleimide nanocomposites via incorporation of a new allylated siloxane graphene oxide

A thermosetting resin system based on bismaleimide (BMI) has been developed via copolymerization with 4,4′-diaminodiphenylsulfone in the presence of a newly synthesized graphene oxide, modified using allylated siloxane (AS-GO). The curing behavior of the AS-GO-containing resin system was evaluated using curing kinetics. The dispersibility of AS-GO in the resin was observed through polarizing optical microscopy (POM), which indicates that AS-GO has good dispersibility in the resin due to GO modified with allylated siloxane which has a good phase compatibility with BMI. The effect of AS-GO on the thermomechanical and mechanical properties of the cured modified resin was also studied. Results of thermogravimetric analysis indicated that the cured sample systems display a high char yield at lower concentrations of AS-GO (≤0.5 wt%) with an improved thermal stability. Using dynamic mechanical analysis, a marked increase in glass transition temperature (T_g) with increasing AS-GO content was observed. Mechanical property analyses revealed a possible effect of AS-GO as a toughener, and the results showed that an addition of 0.3% AS-GO maximized the toughness of the modified resin systems, which was confirmed by analysis of fracture surfaces.

A thermosetting resin system based on bismaleimide has been developed via copolymerization of a new allylated siloxane graphene oxide.

Enhancement of Thermal and Mechanical Properties of Bismaleimide Using a Graphene Oxide Modified by Epoxy Silane

A thermosetting resin system, based on bismaleimide (BMI), has been developed via copolymerization of 4,4′-diaminodiphenylsulfone with a newly synthesized graphene oxide modified using epoxy silane (ES-GO). The effect of ES-GO on the thermomechanical and mechanical properties of cured modified resin was studied. To evaluate the efficiency of the modified BMI systems, the composite samples using glass fiber cloth were molded and tested. Thermogravimetric analysis indicates that the cured sample systems displays a high char yield at lower concentrations of ES-GO (≤0.5 wt.%), suggesting an improved thermal stability. Using dynamic mechanical analysis, a marked increase in glass transition temperature (Tg) with increasing ES-GO content was observed. Analysis of mechanical properties reveals a possible effect of ES-GO as a toughener. The results also showed that the addition of 0.3 wt.% ES-GO maximizes the toughness of the modified resin systems, which was further confirmed by the result of analysis of fracture surfaces. At the same time, a molded composite with ES-GO showed improved mechanical properties and retention rate at 150 °C as compared to that made with neat resin.

Synthesis of multifunctional liquid crystalline epoxy resin embedded cyclic-siloxane chain with Tg-less behavior and enhanced toughness

A novel tetrafunctional mesogenic epoxy monomer with a cyclic-siloxane chain as a central part was successfully synthesized and characterized by proton nuclear magnetic resonance, Fourier transform infrared spectroscopy, differential scanning calorimetry, and polarized optical microscopy. The transition temperature and liquid crystallinity of cyclic-siloxane type mesogenic epoxy were compared with those of linear-siloxane type mesogenic epoxy. Moreover, epoxy thermosets were prepared based on the cyclic- and linear-siloxane type mesogenic epoxy monomers and 4,4′-diaminodiphenylethane. The effects of epoxy backbone moiety on thermal and mechanical properties were investigated in detail. As a result, the cyclic-siloxane type mesogenic epoxy thermoset shows glass transition temperature-less behavior and low coefficient of linear thermal expansion without a decrease in toughness.