Double network structure via ionic bond and covalent bond of carboxymethyl chitosan and poly(ethylene glycol): Factors affecting hydrogel formation

The factors were studied that affect the formation of DN hydrogel, which was prepared using a water-based, environmental-friendly system. The DN hydrogel was designed and prepared based on a cross-linked, polysaccharide-based, polymer carboxymethyl chitosan (CMCS) via an ionic crosslinking reaction for the first network structure. UV irradiation created a radical crosslinking reaction of poly(ethylene glycol) from a double bond at the chain end for the second network structure. It was found that the optimum hydrogel was produced using 9.5 %v/v of 1000PEGGMA, CMCS 5%w/v, and CaCl₂ 3%w/v. The results showed the highest percentage of the gel fraction was 87.84 % and the hydrogel was stable based on its rheological properties. Factors affecting the hydrogel formation were the concentration and molecular weight of PEGGMA and the concentrations of CMCS and calcium chloride (CaCl₂). The DN hydrogel had bioactivity due to its octacalcium phosphate (OCP) hydroxyapatite crystal form. In addition, the composite DN scaffold with a conductive polymer of chitosan-grafted-polyaniline (CS-g-PANI) had conduction of 2.33 × 10^-5 S/cm when the concentration of CS-g-PANI was 3 mg/ml, confirming the semi-conductive nature of the material. All the results indicated that DN hydrogel could be a candidate to apply in tissue-engineering applications.

Microgel-integrated, high-strength in-situ formed hydrogel enables timely emergency trauma treatment

High-strength hydrogels formed in situ through a convenient gel transition process are highly desirable for emergency treatment due to their ability to quickly respond to accidents. However, current in-situ formed hydrogels require a laborious precursor preparation process or lack sufficient mechanical strength. Herein, we reported a series of microgels that were capable of convenient in-situ transition to high-strength hydrogels from their easily portable form, thereby facilitating emergency treatment. Three kinds of microgels were derived from two types of hydrogen bonds (H-bonds; OH⋯OC, NH⋯OC) crosslinked preformed hydrogels, and all exhibited excellent stability when stored at room temperature. After mixing with water, all these microgels could undergo a quick hydration process and then transform into high-strength hydrogels in situ through H-bonds. Specifically, stronger H-bond crosslinked microgels could build hydrogels with higher mechanical strength, albeit at the cost of longer hydration and operation time. Nevertheless, the whole operation process could be finished within several minutes, and the resultant hydrogels could exhibit maximally megapascal-level compressive strength and tens of kilopascal storage modulus. In the comparison of emergency application performance with commercial chitosan hemostatic powder (CHP), we found that the microgels could stop accidental bleeding almost immediately, and the whole process from taking out the stored microgels to hemostasis could be completed within 15 s, which was superior to CHP. Overall, the results indicated that the in-situ formed microgel-based hydrogels with convenient gel-transition ability and high strength showed great potential in emergency treatments.

Bioactivity of star-shaped polycaprolactone/chitosan composite hydrogels for biomaterials

Recently, our group reported the synthesis and fabrication of composite hydrogels of chitosan (CS) and star-shaped polycaprolactone (stPCL). The co-crosslink of modified stPCL with carboxyl at the end chain (stPCL-COOH) provided good mechanical properties and stability to the composite hydrogels. This research presents the bioactivities of composite hydrogels showing a potential candidate to develop biomaterials such as wound dressing and bone tissue engineering. The bioactivities were the antibacterial activity, cell viability, skin irritation, decomposability, and ability to attach ions for apatite nucleation. The results showed that all the composite hydrogels were completely decomposed within 2 days. The composite hydrogels had better antibacterial activity and higher efficiency to Gram-negative (Escherichia coli) than to Gram-positive (Staphylococcus epidermidis) bacteria. The composite hydrogels were studied for cell viability based on MTT assay and skin irritation on rabbit skin. The results indicated high cell survival more than 80% and no skin irritation. In addition, the results showed that calcium and phosphorous were preferentially attached to the composite hydrogel surface to grow apatite crystal (Ca/P ratio 1.86) compared to attaching to the chitosan hydrogel (Ca/P ratio 1.48) in 21 days of testing.