Miscibility and surface segregation in PVC/polyester blends—The influence of chain architecture and composition

Synthesis of azelaic acid copolyester plasticizers and their application in PVC

A series of 2-methyl-1,3-propanediol (MPO) modified azelaic acid and hexylene glycol copolyester (PHMAZ) plasticizers with varying contents were synthesized using a direct esterification melt polycondensation method, and their structures were characterized systematically. Analysis using infrared spectroscopy and nuclear magnetic resonance spectroscopy confirmed the synthesis of the designed copolyester structure. Gel permeation chromatography (GPC) tests indicated that the number average molecular weight of each copolyester sample ranged between 2000 and 3000. These copolyesters were used to plasticize polyvinyl chloride (PVC) resin, and the glass transition temperature of the plasticized PVC samples was tested using a differential scanning calorimeter (DSC). Further characterization of the plasticizing effects was conducted using an electronic universal testing machine. The research results showed that as the content of MPO increased, the plasticizing effect of the copolyester initially increased and then decreased. Specifically, the copolyester containing 45% MPO, PHMAZ-45, demonstrated the best plasticizing effect on PVC, with the glass transition temperature of the plasticized PVC system around -35 °C, elongation at break at 908.4%, and a plasticizing efficiency of 254.5%. Additionally, this new type of copolyester plasticizer uses bio-based raw materials, exhibits excellent plasticizing effects, and the preparation process is stable and controllable. It holds promising potential to replace traditional volatile and toxic phthalate esters, presenting significant industrial application value.

Isosorbide as Core Component for Tailoring Biobased Unsaturated Polyester Thermosets for a Wide Structure-Property Window

Biobased unsaturated polyester thermosets as potential replacements for petroleum-based thermosets were designed. The target of incorporating rigid units, to yield thermosets with high thermal and mechanical performance, both in the biobased unsaturated polyester (UP) and reactive diluent (RD) while retaining miscibility was successfully achieved. The biobased unsaturated polyester thermosets were prepared by varying the content of isosorbide, 1,4-butanediol, maleic anhydride, and succinic anhydride in combination with the reactive diluent isosorbide-methacrylate (IM). Isosorbide was chosen as the main component in both the UP and the RD to enhance the rigidity of the formed thermosets, to overcome solubility issues commonly associated with biobased UPs and RDs and volatility and toxicity associated with styrene as RD. All UPs had good solubility in the RD and the viscosity of the mixtures was primarily tuned by the feed ratio of isosorbide but also by the amount of maleic anhydride. The flexural modulus and storage modulus were tailorable by altering the monomer composition The fabricated thermosets had superior thermal and mechanical properties compared to most biobased UP thermosets with thermal stability up to about 250 °C and a storage modulus at 25 °C varying between 0.5 and 3.0 GPa. These values are close to commercial petroleum-based UP thermosets. The designed tailorable biobased thermosets are, thus, promising candidates to replace their petroleum analogs.