Nonisothermal crystallization kinetics of poly(ε-caprolactone) blocks in double crystalline triblock copolymers containing poly(3-hydroxybutyrate-co-3-hydroxyvalerate) and poly(ε-caprolactone) units

Polyhydroxyalkanoates based copolymers

Polyhydroxyalkanoates (PHAs) belong to a family of natural polyesters and are produced under unbalanced growth conditions as intracellular carbon and energy reserves by a wide variety of microorganisms. Being biodegradable, biocompatible and environmental friendly thermoplastics, the PHAs are considered as future polymers to replace petrochemicals based plastics. In this review, the introduction section deals with the brief discussion on PHA nature, availability, raw materials for production, processing etc. This is followed by the discussions on modifications. The copolymer syntheses by bacterial and chemical methods have been discussed. Under chemical methods, unsaturated side chains and their derivatives, oligomer, coupling, macro-initiating, trans-esterification, radiation grafting, click chemistry, ring opening and several miscellaneous polymerization methods have been elaborated. A brief discussion on applications has been incorporated. The last section includes conclusion and future perspectives.

Nonisothermal crystallization kinetics, morphology, and tensile properties of polyphenylene sulfide/functionalized graphite nanoplatelets composites

Polyphenylene sulfide (PPS)/graphite nanoplates (GNPs) nanocomposites were manufactured by simple melt compounding. The GNPs were first functionalized using synthesized benzimidazolium salt to improve the compatibility with PPS matrix. The functionalized GNPs showed an exfoliated dispersion in PPS matrix, which also could significantly improve the tensile properties of composites. Differential scanning calorimetry was used to investigate the nonisothermal crystallization kinetics of PPS/functionalized GNPs composites. The results showed that the PPS/functionalized GNPs composites always had a higher crystallization peak temperature ( Tc) than pure PPS resin at different cooling rates due to the addition of GNPs. The GNPs could also play the role of heterogeneous nucleating agents to accelerate the crystallization; however, at high content, they could also limit the mobility of PPS macromolecular chains and hinder the crystallization. The Mo equation could be used to analyze the nonisothermal crystallization kinetics, whereas the Ozawa equation was not suitable for the nonisothermal crystallization process. Consistent with a previous analysis, the results also showed that the addition of GNPs could also decrease the crystallization activation energy ( Ec) of PPS resin at low content while increasing the Ec at high content.

Nonisothermal crystallization kinetics of polyphenylene sulfide composites based on organic clay modified by benzimidazolium salt

Polyphenylene sulfide (PPS)/organic clay nanocomposites were prepared by simple melt blending. A synthesized benzimidazolium salt was used to modify the sodium montmorillonite in order to improve the compatibility with the PPS. The nonisothermal crystallization kinetics of PPS/organic clay composites were investigated by differerntial scanning calorimetry(DSC). It was observed that the crystallization peak temperature of PPS/organic clay composites was higher than pure PPS at various cooling rates. Several models such as the Ozawa and Mo equation were used to characterize the nonisothermal cooling crystallization kinetics of the PPS/organic clay composites. The results indicated that the Ozawa equation was not successful, while the Mo equation was successful to describe the nanoisothermal ctystallization kinetics of PPS/organic clay nanocomposites. The results also indicated that organic clay not only served as heterogeneous nucleating agents for PPS crystallization at lower content but also restricted the mobility and diffusion of PPS chains at higher content. These results were further supported by the crystallization activation energy of the samples determined by the Kissinger method.

Poly(3-hydroxybutyrate) and Poly(3-hydroxybutyrate-co-3-hydroxyvalerate): Structure, Property, and Fiber

Poly(3-hydroxybutyrate) [P(3HB)] and poly(3-hydroxybutyrate-co-3-hydroxyvalerate) [P(3HB-co-3HV)] are produced by various microorganisms as an intracellular carbon and energy reserve from agricultural feedstocks such as sugars and plant oils under unbalanced growth conditions. P(3HB) and P(3HB-co-3HV) have attracted the attention of academia and industry because of its biodegradability, biocompatibility, thermoplasticity, and plastic-like properties. This review first introduced the isodimorphism, spherulites, and molecular interaction of P(3HB) and P(3HB-co-3HV). In addition, the effects of 3HV content on the melting temperature and crystallization rate were discussed. Then the drawbacks of P(3HB) and P(3HB-co-3HV) including brittleness, narrow melt processing window, low crystallization rate, slow biodegradation rate in body, and so on were summarized. At last, the preparation, structure, and properties of P(3HB) and P(3HB-co-3HV) fiber were introduced.