Diameter and density control of single-walled carbon nanotube forests by modulating Ostwald ripening through decoupling the catalyst formation and growth processes

Modifying the Molecular Structure of Carbon Nanotubes through Gas-Phase Reactants

Current approaches to carbon nanotube (CNT) synthesis are limited in their ability to control the placement of atoms on the surface of nanotubes. Some of this limitation stems from a lack of understanding of the chemical bond-building mechanisms at play in CNT growth. Here, we provide experimental evidence that supports an alkyne polymerization pathway in which short-chained alkynes directly incorporate into the CNT lattice during growth, partially retaining their side groups and influencing CNT morphology. Using acetylene, methyl acetylene, and vinyl acetylene as feedstock gases, unique morphological differences were observed. Interwall spacing, a highly conserved value in natural graphitic materials, varied to accommodate side groups, increasing systematically from acetylene to methyl acetylene to vinyl acetylene. Furthermore, attenuated total reflectance Fourier-transfer infrared spectroscopy (ATR-FTIR) illustrated the existence of intact methyl groups in the multiwalled CNTs derived from methyl acetylene. Finally, the nanoscale alignment of the CNTs grown in vertically aligned forests differed systematically. Methyl acetylene induced the most tortuous growth while CNTs from acetylene and vinyl-acetylene were more aligned, presumably due to the presence of polymerizable unsaturated bonds in the structure. These results demonstrate that feedstock hydrocarbons can alter the atomic-scale structure of CNTs, which in turn can affect properties on larger scales. This information could be leveraged to create more chemically and structurally complex CNT structures, enable more sustainable chemical pathways by avoiding the need for solvents and postreaction modifications, and potentially unlock experimental routes to a host of higher-order carbonaceous nanomaterials.

Common salts directed the growth of metal-free horizontal SWNT arrays

Acquiring metal-free horizontal single-walled carbon nanotube (SWNT) arrays is of paramount importance for the development of stable nanodevices. However, the majority of SWNTs are prepared with transition metal-based catalysts, which will inevitably leave metallic residuals and deteriorate the device performance. Here, green and low-cost NaCl is developed as a metal-free catalyst. By employing a strategy of rapid nucleation at a higher temperature followed by steady growth at a lower temperature, the production of a well-defined NaCl catalyst capable of growing metal-free horizontal SWNT arrays with an average density of ∼100 tubes per 100 μm is realized. Besides, we prove that the as-grown metal-free SWNT arrays have a unique advantage in preparing stable devices for eliminating the potential risk of local mass catalyst residuals. Hence, the current study can offer a feasible solution to promote practical applications of SWNT-based next-generation nanodevices.

Hierarchically Hybrid Porous Co3O4@NiMoO4/CoMoO4 Heterostructures for High-Performance Electrochemical Energy Storage

Hierarchical, ultrathin, and porous NiMoO₄@CoMoO₄ on Co₃O₄ hollow bones were successfully designed and synthesized by a hydrothermal route from the Co-precursor, followed by a KOH (potassium hydroxide) activation process. The hydrothermally synthesized Co₃O₄ nanowires act as the scaffold for anchoring the NiMoO₄@CoMoO₄ units but also show more compatibility with NiMoO₄, leading to high conductivity in the heterojunction. The intriguing morphological features endow the hierarchical Co₃O₄@NiMoO₄@CoMoO₄ better electrochemical performance where the capacity of the Co₃O₄@NiMoO₄@CoMoO₄ heterojunction being 272 mA·h·g^-1 at 1 A·g^-1 can be achieved with a superior retention of 84.5% over 1000 cycles. The enhanced utilization of single/few NiMoO₄@CoMoO₄ shell layers on the Co₃O₄ core make it easy to accept extra electrons, enhancing the adsorption of OH^- at the shell surface, which contribute to the high capacity. In our work, an asymmetric supercapacitor utilizing the optimized Co₃O₄@NiMoO₄@CoMoO₄ activated carbon (AC) as electrode materials was assembled, namely, Co₃O₄@NiMoO₄@CoMoO₄//AC device, yielding a maximum high energy density of 53.9 W·h·kg^-1 at 1000 W·kg^-1. It can retain 25.92 W·h·kg^-1 even at 8100 W·kg^-1, revealing its potential and viability for applications. The good power densities are ascribed to the porous feature from the robust architecture with recreated abundant mesopores on the composite, which assure improved conductivity and enhanced diffusion of OH^- and also the electron transport. The work demonstrated here holds great promise for synthesizing other heterojunction materials M₃O₄@MMoO₄@MMoO₄ (M = Fe, Ni, Sn, etc).

Precise Identification of the Active Phase of Cobalt Catalyst for Carbon Nanotube Growth by In Situ Transmission Electron Microscopy

Revealing the active phase and structure of catalyst nanoparticles (NPs) is crucial for understanding the growth mechanism and realizing the controlled synthesis of carbon nanotubes (CNTs). However, due to the high temperature and complex environment during CNT growth, precise identification of the active catalytic phase remains a great challenge. We investigated the phase evolution of cobalt (Co) catalyst NPs during the incubation, nucleation, and growth stages of CNTs under near-atmospheric pressure using an in situ close-cell environmental transmission electron microscope (ETEM). Strict statistical analysis of the electron diffractograms was performed to accurately identify the phases of the catalyst NPs. It was found that the NPs belong to an orthorhombic Co₃C phase that remained unchanged during CNT growth, with errors in lattice spacing <5% and in angle <2°, despite changes in their morphology and orientation. Theoretical calculations further confirm that Co₃C is the thermodynamically preferred phase during CNT growth, with the supply of carbon atoms through the surface and NP-CNT interfacial diffusion.

Morphological Evolvement of Carbon Nanotubes Synthesized by Using Conducting Polymer Nanofibers

Carbon nanotubes were synthesized by using a nanostructured conducting polymer—the polypyrrole nanofiber via microwave radiation. The radiation time was set to be 30, 60, and 90 seconds, respectively. The morphological evolvements of the as-synthesized carbon nanotubes with increased radiation time (e.g., shape, diameter, wall structure, and catalyst size) were carefully investigated, and the possible growth mode was discussed in detail. It was found that the growth mode of the carbon nanotubes synthesized from the conducting polymer substrate under microwave radiation was complex and cannot be simply interpreted by either a “tip” or “base” growth model. A new growth mode of the “liquifying cascade growth” was observed for the as-synthesized carbon nanotubes, as their growth was directed by a series of liquified iron nanoparticles with sequentially decreasing sizes, similar to the cascade of liquid droplets. And it could provide useful insights for the morphological and structural designs of the carbon nanotubes prepared by related microwave-based methods.

Carbon Nanotubes and Related Nanomaterials: Critical Advances and Challenges for Synthesis toward Mainstream Commercial Applications

Advances in the synthesis and scalable manufacturing of single-walled carbon nanotubes (SWCNTs) remain critical to realizing many important commercial applications. Here we review recent breakthroughs in the synthesis of SWCNTs and highlight key ongoing research areas and challenges. A few key applications that capitalize on the properties of SWCNTs are also reviewed with respect to the recent synthesis breakthroughs and ways in which synthesis science can enable advances in these applications. While the primary focus of this review is on the science framework of SWCNT growth, we draw connections to mechanisms underlying the synthesis of other 1D and 2D materials such as boron nitride nanotubes and graphene.

Vertically Aligned Carbon Nanotubes as Platform for Biomimetically Inspired Mechanical Sensing, Bioactive Surfaces, and Electrical Cell Interfacing

Vertically aligned carbon nanotubes (VACNTs) are one dimensional carbon objects anchored atop of a solid substrate. They are geometrically fixed in contrast to their counterparts, randomly oriented carbon nanotubes (CNTs). In this progress report, the breadth in which these one dimensional, mechanically flexible, though robust and electrical conducting carbon nanostructures can be employed as functional material is shown and our research is put in perspective to work in the last five to ten years. The connection between the different areas touched in this report is the biomimetic-materials approach, which rely on the hairy morphology of VACNTs. These properties in connection with their electrical conductivity offer possibilities towards new functional features and applications of VACNTs. To appreciate the possibilities of biomimetic research with VACNTs, first their material characteristics are given to make the reader familiar with specific features of their synthesis, the peculiarities in arranging and controlling the morphology of CNTs in a vertical alignment as well as a current understanding of these properties on a microscopic basis. In doing so, similarities as well as differences, which offer new possibilities for biomimetic studies of VACNTS with respect to multiwalled randomly oriented CNTs, will become clear.

A Forest of Sub-1.5-nm-wide Single-Walled Carbon Nanotubes over an Engineered Alumina Support

A precise control of the dimension of carbon nanotubes (CNTs) in their vertical array could enable many promising applications in various fields. Here, we demonstrate the growth of vertically aligned, single-walled CNTs (VA-SWCNTs) with diameters in the sub-1.5-nm range (0.98 ± 0.24 nm), by engineering a catalyst support layer of alumina via thermal annealing followed by ion beam treatment. We find out that the ion beam bombardment on the alumina allows the growth of ultra-narrow nanotubes, whereas the thermal annealing promotes the vertical alignment at the expense of enlarged diameters; in an optimal combination, these two effects can cooperate to produce the ultra-narrow VA-SWCNTs. According to micro- and spectroscopic characterizations, ion beam bombardment amorphizes the alumina surface to increase the porosity, defects, and oxygen-laden functional groups on it to inhibit Ostwald ripening of catalytic Fe nanoparticles effectively, while thermal annealing can densify bulk alumina to prevent subsurface diffusion of the catalyst particles. Our findings contribute to the current efforts of precise diameter control of VA-SWCNTs, essential for applications such as membranes and energy storage devices.

Oxygen-promoted catalyst sintering influences number density, alignment, and wall number of vertically aligned carbon nanotubes

A lack of synthetic control and reproducibility during vertically aligned carbon nanotube (CNT) synthesis has stifled many promising applications of organic nanomaterials. Oxygen-containing species are particularly precarious in that they have both beneficial and deleterious effects and are notoriously difficult to control. Here, we demonstrated diatomic oxygen's ability, independent of water, to tune oxide-supported catalyst thin film dewetting and influence nanoscale (diameter and wall number) and macro-scale (alignment and density) properties for as-grown vertically aligned CNTs. In particular, single- or few-walled CNT forests were achieved at very low oxygen loading, with single-to-multi-walled CNT diameters ranging from 4.8 ± 1.3 nm to 6.4 ± 1.1 nm over 0-800 ppm O₂, and an expected variation in alignment, where both were related to the annealed catalyst morphology. Morphological differences were not the result of subsurface diffusion, but instead occurred via Ostwald ripening under several hundred ppm O₂, and this effect was mitigated by high H₂ concentrations and not due to water vapor (as confirmed in O₂-free water addition experiments), supporting the importance of O₂ specifically. Further characterization of the interface between the Fe catalyst and Al₂O₃ support revealed that either oxygen-deficit metal oxide or oxygen-adsorption on metals could be functional mechanisms for the observed catalyst nanoparticle evolution. Taken as a whole, our results suggest that the impacts of O₂ and H₂ on the catalyst evolution have been underappreciated and underleveraged in CNT synthesis, and these could present a route toward facile manipulation of CNT forest morphology through control of the reactive gaseous atmosphere alone.

Carbon : nickel nanocomposite templates - predefined stable catalysts for diameter-controlled growth of single-walled carbon nanotubes

Carbon : nickel (C : Ni) nanocomposite templates (NCTs) were used as catalyst precursors for diameter-controlled growth of single-walled carbon nanotubes (SWCNTs) by chemical vapor deposition (CVD). Two NCT types of 2 nm thickness were prepared by ion beam co-sputtering without (type I) or with assisting Ar(+) ion irradiation (type II). NCT type I comprised Ni-rich nanoparticles (NPs) with defined diameter in an amorphous carbon matrix, while NCT type II was a homogenous C : Ni film. Based on the Raman spectra of more than 600 individual SWCNTs, the diameter distribution obtained from both types of NCT was determined. SWCNTs with a selective, monomodal diameter distribution are obtained from NCT type I. About 50% of the SWCNTs have a diameter of (1.36 ± 0.10) nm. In contrast to NCT type I, SWCNTs with a non-selective, relatively homogeneous diameter distribution from 0.80 to 1.40 nm covering 88% of all SWCNTs are obtained from NCT type II. From both catalyst templates predominantly separated as-grown SWCNTs are obtained. They are free of solvents or surfactants, exhibit a low degree of bundling and contain negligible amounts of MWCNTs. The study demonstrates the advantage of predefined catalysts for diameter-controlled SWCNT synthesis in comparison to in situ formed catalysts.

A phenomenological model for selective growth of semiconducting single-walled carbon nanotubes based on catalyst deactivation

A method for the selective semiconducting single-walled carbon nanotube (SWCNT) growth over a continuous range from 67% to 98%, within the diameter range of 0.8-1.2 nm, by the use of a "catalyst conditioning process" prior to growth is reported. Continuous control revealed an inverse relationship between the selectivity and the yield as evidenced by a 1000-times difference in yield between the highest selectivity and non-selectivity. Further, these results show that the selectivity is highly sensitive to the presence of a precise concentration of oxidative and reductive gases (i.e. water and hydrogen), and the highest selectivity occurred along the border between the conditions suitable for high yield and no-growth. Through these results, a phenomenological model has been constructed to explain the inverse relationship between yield and selectivity based on catalyst deactivation. We believe our model to be general, as the fundamental mechanisms limiting selective semiconducting SWCNT growth are common to the previous reports of limited yield.

A sweet spot for highly efficient growth of vertically aligned single-walled carbon nanotube forests enabling their unique structures and properties

We investigated the correlation between growth efficiency and structural parameters of single-walled carbon nanotube (SWCNT) forests and report the existence of a SWCNT "sweet spot" in the CNT diameter and spacing domain for highly efficient synthesis. Only within this region could SWCNTs be grown efficiently. Through the investigation of the growth rates for ∼340 CNT forests spanning diameters from 1.3 to 8.0 nm and average spacing from 5 to 80 nm, this "sweet spot" was found to exist because highly efficient growth was constrained by several mechanistic boundaries that either hindered the formation or reduced the growth rate of SWCNT forests. Specifically, with increased diameter SWCNTs transitioned to multiwalled CNTs (multiwall border), small diameter SWCNTs could only be grown at low growth rates (low efficiency border), sparse SWCNTs lacked the requirements to vertically align (lateral growth border), and high density catalysts could not be prepared (high catalyst density border). As a result, the SWCNTs synthesized within this "sweet spot" possessed a unique set of characteristics vital for the development applications, such as large diameter, long, aligned, defective, and high specific surface area.

The Application of Gas Dwell Time Control for Rapid Single Wall Carbon Nanotube Forest Synthesis to Acetylene Feedstock

One aspect of carbon nanotube (CNT) synthesis that remains an obstacle to realize industrial mass production is the growth efficiency. Many approaches have been reported to improve the efficiency, either by lengthening the catalyst lifetime or by increasing the growth rate. We investigated the applicability of dwell time and carbon flux control to optimize yield, growth rate, and catalyst lifetime of water-assisted chemical vapor deposition of single-walled carbon nanotube (SWCNT) forests using acetylene as a carbon feedstock. Our results show that although acetylene is a precursor to CNT synthesis and possesses a high reactivity, the SWCNT forest growth efficiency is highly sensitive to dwell time and carbon flux similar to ethylene. Through a systematic study spanning a wide range of dwell time and carbon flux levels, the relationship of the height, growth rate, and catalyst lifetime is found. Further, for the optimum conditions for 10 min growth, SWCNT forests with ~2500 μm height, ~350 μm/min initial growth rates and extended lifetimes could be achieved by increasing the dwell time to ~5 s, demonstrating the generality of dwell time control to highly reactive gases.

Influence of packing density and surface roughness of vertically-aligned carbon nanotubes on adhesive properties of gecko-inspired mimetics

We have systematically studied the macroscopic adhesive properties of vertically aligned nanotube arrays with various packing density and roughness. Using a tensile setup in shear and normal adhesion, we find that there exists a maximum packing density for nanotube arrays to have adhesive properties. Too highly packed tubes do not offer intertube space for tube bending and side-wall contact to surfaces, thus exhibiting no adhesive properties. Likewise, we also show that the surface roughness of the arrays strongly influences the adhesion properties and the reusability of the tubes. Increasing the surface roughness of the array strengthens the adhesion in the normal direction, but weakens it in the shear direction. Altogether, these results allow progress toward mimicking the gecko's vertical mobility.

Water-assisted growth of uniform 100 mm diameter SWCNT arrays

We report a simple method for growing high-quality single-walled carbon nanotube (SWCNT) arrays on 100 mm wafers via the addition of water vapor to highly purified gases during the CNT growth step. We show that adding a small amount of water during growth helps to create a uniform catalyst distribution and yields high-quality (Raman G/D of 26 ± 3), high-density (up to 6 × 10(11) cm(-2)) and uniform SWCNT arrays on 100 mm large wafers. We rationalize our finding by suggesting that the addition of water decreases catalyst mobility, preventing its coarsening at higher temperatures. We also report a new mechanism of catalyst inactivation in wafer-scale growth using ultrapurified gas sources by the formation of large, 5 ± 3 μm iron particles. We found such formations to be common for substrates with large temperature gradients, such as for wafers processed in a typical cold-wall chemical vapor deposition reactor.

Diameter control of single-walled carbon nanotube forests from 1.3-3.0 nm by arc plasma deposition

We present a method to both precisely and continuously control the average diameter of single-walled carbon nanotubes in a forest ranging from 1.3 to 3.0 nm with ~1 Å resolution. The diameter control of the forest was achieved through tuning of the catalyst state (size, density, and composition) using arc plasma deposition of nanoparticles. This 1.7 nm control range and 1 Å precision exceed the highest reports to date.

Absence of an ideal single-walled carbon nanotube forest structure for thermal and electrical conductivities

We report the fundamental dependence of thermal diffusivity and electrical conductance on the diameter and defect level for vertically aligned single-walled carbon nanotube (SWCNT) forests. By synthesizing a series of SWCNT forests with continuous control of the diameter and defect level over a wide range while holding all other structures fixed, we found an inverse and mutually exclusive relationship between the thermal diffusivity and the electrical conductance. This relationship was explained by the differences in the fundamental mechanisms governing each property and the optimum required structures. We concluded that high thermal diffusivity and electrical conductance would be extremely difficult to simultaneously achieve by a single SWCNT forest structure within current chemical vapor deposition synthetic technology, and the "ideal" SWCNT forest structure would differ depending on application.

A Fundamental Limitation of Small Diameter Single-Walled Carbon Nanotube Synthesis-A Scaling Rule of the Carbon Nanotube Yield with Catalyst Volume

Understanding the fundamental mechanisms and limiting processes of the growth of single-walled carbon nanotube (SWCNT) would serve as a guide to achieve further control on structural parameters of SWCNT. In this paper, we have studied the growth kinetics of a series of SWCNT forests continuously spanning a wide range of diameters (1.9–3.2 nm), and have revealed an additional fundamental growth limiting process where the mass of the individual SWCNT is determined by the individual catalyst volume. Calculation of the conversion rate of carbon atoms into CNTs per Fe atom is 2 × 10² atoms per second. This rate limiting process provides an important understanding where the larger diameter SWCNT would grow faster, and thus be more suited for mass production.