Thermal and mechanical properties of poly(lactic acid) filled with modified silicon dioxide: importance of the surface area

Robust Superhydrophobic Films Based on an Eco-Friendly Poly(l-lactic acid)/Cellulose Composite with Controllable Water Adhesion

Poly(l-lactic acid) (PLLA) featuring desirable biodegradability and biocompatibility has been recognized as one of the promising eco-friendly biomaterials. However, low crystallization and poor mechanical and chemical performances dramatically hamper its practical application. In this work, we report that functionalized cellulose/PLLA composite superhydrophobic stereocomplex films with controllable water adhesion and protein adsorption can be fabricated by a facile approach for the first time. First, cellulose is surface-modified by means of two silanization modification methods. Then, superhydrophobic cellulose/PLLA composite films are prepared through a solvent-evaporation-induced phase separation method. The two cellulose/PLLA composite films exhibit extreme water repellency but tunable water adhesion from sticky to slippery. The protein adsorption capacity of the cellulose/PLLA composite films can also be regulated. In addition, the stereocomplexation of the composite film provides excellent mechanical properties with an elongation at break of 22.36%, which is 237.8% higher than that of a pure PLLA film, which is more suitable for biomaterials. Furthermore, good biodegradability of the PLLA composite films in nature enables the bio-based composites as alternative materials to replace conventional petroleum-based polymers. The superhydrophobic films have also been demonstrated for many applications, including slippery surfaces, liquid transportation without loss, and antifouling.

A review: studying the effect of graphene nanoparticles on mechanical, physical and thermal properties of polylactic acid polymer

Polylactic acid (PLA) is a linear aliphatic polyester thermoplastic made from renewable sources such as sugar beet and cornstarch. Methods of preparation of polylactic acid are biological and chemical. The advantages of polylactic acid are biocompatibility, easily processing, low energy loss, transparency, high strength, resistance to water and fat penetration and low consumption of carbon dioxide during production. However, polylactic acid has disadvantages such as hydrophobicity, fragility at room temperature, low thermal resistance, slow degradation rate, permeability to gases, lack of active groups and chemical neutrality. To overcome the limitations of PLA, such as low thermal stability and inability to absorb gases, nanoparticles such as graphene are added to improve its properties. Extensive research has been done on the introduction of graphene nanoparticles in PLA, and all of these studies have been studied. In this study, we intend to study a comprehensive study of the effect of graphene nanoparticles on the mechanical, thermal, structural and rheological properties of PLA/Gr nanocomposites and also the effect of UV rays on the mechanical properties of PLA/Gr nanocomposites.

Effect of the Addition of Nano-Silica and Poly(ε-caprolactone) on the Mechanical and Thermal Properties of Poly(lactic acid) Blends and Possible Application in Embossing Process

In this study, the mechanical and thermal properties of poly(lactic acid) (PLA) blends with an addition of poly(ε-caprolactone) (PCL) and fumed silica (SiO₂) were evaluated to research the possibility of their use as relief printing plates for embossing processes. PCL and nano-silica were added to the PLA matrix at different concentrations. Morphological, thermal and mechanical analyses were performed to determine the properties and possible functional characteristics of the studied blends. SEM micrographs showed that unmodified PLA/PCL blends exhibit a morphology typical of incompatible blends with clearly visible spherical domains of dispersed PCL in PLA. In particular, the results of the hardness tests showed that the selected blends have the optimal hardness (between 65 SH D and 75 SH D) for use in the embossing process. The tensile tests showed that the addition of nano-silica to neat PLA and to the PLA/PCL blends 50/50 and 60/40 improved the mechanical properties of the blends, especially stiffness and toughness. The DMA results showed that the addition of smaller amounts of SiO₂ can contribute to an increase in storage modulus, which is due to good dispersion and distribution of SiO₂ in the matrix. DSC analysis showed that the addition of PCL to PLA polymer increased the thermal stability of PLA and that the addition of nano-silica increased the degree of crystallinity of PLA. The TGA results showed that the addition of nano-silica improved the thermal degradation behavior of the studied blends, especially for blends modified with 3 wt% nano-silica. The results show that it is possible to optimize the mechanical and thermal properties of the blends with the aim of using them in the embossing process.

Blends Based on Poly(ε-Caprolactone) with Addition of Poly(Lactic Acid) and Coconut Fibers: Thermal Analysis, Ageing Behavior and Application for Embossing Process

In this research a biodegradable blend of poly(ɛ-caprolactone) (PCL) and poly(lactic acid) (PLA) is proposed as a new material for the production of a relief printing plate used for special applications on packaging materials, i.e., the embossing process. Coconut fibers (CFs) were added as a natural filler to PCL/PLA blends to improve the functional properties of the prepared blends. Thermal, mechanical and surface analyses were performed on the unaged and artificially aged blends. The results showed that CF has been proven to optimize the hardness of the blend, which is crucial for the production of relief plate for embossing applications. The lowest hardness was measured on neat PCL (53.30° Sh D) and the highest value on PCL/PLA/CF 70/30/3.0 blend (60.13° Sh D). Stronger interfacial interactions were present at the PLA/CF interface because the interfacial free energy is closer to zero and the work of adhesion and spreading coefficient are higher than for the PCL/CF interface. The results of thermal analysis of unaged and aged blends showed that ageing for 3 weeks resulted in significantly lower thermal stability, especially for neat PCL and PCL/PLA 80/20 blends. Blends with a higher content of PLA and CF showed a slightly increased ageing resistance, which is attributed to the increased crystallinity of PLA after ageing due to the addition of CF showed in the DSC diagrams.