Influence of TEGDMA monomer on MMP-2, MMP-8, and MMP-9 production and collagenase activity in pulp cells

Gelatinolytic activity in dentin upon adhesive treatment

In this multi-parameter study, the effect of diverse factors related to adhesive application on the activation of host-derived gelatinases was investigated by gelatin zymography, in-situ zymography, fluorogenic DQ-gelatin assay and micro-tensile bond-strength (μTBS) testing. Gelatin zymography disclosed the presence of gelatinases in phosphoric acid-etched dentin powder, while two gold-standard adhesives generated no measurable MMP activation. In-situ zymography revealed that the interfacial gelatinolytic activity from specimens treated with the two adhesives appeared similar as that of the EDTA negative control, indicating no detectable gelatinases were activated upon adhesive treatment. In solution, MMP-2/9 activity significantly decreased upon interaction with both adhesives (two-way linear mixed effects model [LMEM]: p < 0.05); gelatinases were almost completely deactivated upon 1-week incubation at 37 °C (general linear model: p < 0.05); light-curing adhesives increased temperature up to 55 °C, which appeared sufficient to dramatically decrease MMP-2/9 activity (two-way ANOVA: p < 0.05). Finally, challenging adhesive-dentin interfaces with highly concentrated MMP-9 (at a much higher concentration than present in saliva) for 1 m did not significantly affect μTBS (two-way LMEM: p > 0.05). Taken together, the two adhesives did not activate but rather inhibited the release and activation of dentinal gelatinases.

Unlocking the Potential of Collagenases: Structures, Functions, and Emerging Therapeutic Horizons

Collagenases, a class of enzymes that are specifically responsible for collagen degradation, have garnered substantial attention because of their pivotal roles in tissue repair, remodeling, and medical interventions. This comprehensive review investigates the diversity, structures, and mechanisms of collagenases and highlights their therapeutic potential. First, it provides an overview of the biochemical properties of collagen and highlights its importance in extracellular matrix function. Subsequently, it meticulously analyzes the sources of collagenases and their applications in tissue engineering and food processing. Notably, this review emphasizes the predominant role played by microbial collagenases in commercial settings while discussing their production and screening methods. Furthermore, this study elucidates the methodology employed for determining collagenase activity and underscores the importance of an accurate evaluation for both research purposes and clinical applications. Finally, this review highlights the future research prospects for collagenases, with a particular focus on promoting wound healing and treating scar tissue formation and fibrotic diseases.

Relation between internal adaptation and degree of conversion of short-fiber reinforced resin composites applied in bulk or layered technique in deep MOD cavities

OBJECTIVE

The purpose was to evaluate the degree of conversion (DC), internal adaptation (IA) and closed porosity (CP) of short-fiber reinforced resin composites (SFRC) associated with layered or bulk restorative procedures in deep MOD cavities.

METHODS

Eighty third molars with standardized MOD cavities (5-mm-depth, 2.5-mm-width) were randomly divided into four groups and restored as follows: 1) bulk SFRC; 2) layered SFRC; 3) flowable bulk-fill resin-based composites (RBC); 4) layered conventional RBC. After one-month wet storage the samples were subjected to micro-computed tomography measurements and scanning electron microscopy to assess the IA and CP. Micro-Raman spectroscopy was used to determine the DC in different depths. Data were subjected to ANOVA and Tukey's post-hoc test, multivariate analysis and partial eta-squared statistics (p < 0.05). Pearson correlation coefficient was determined to assess the relationship among the parameters of interest.

RESULTS

Gap/total interface volume ratio ranged between 0.22-0.47%. RBCs applied in bulk revealed significantly lower gap volume (p < 0.001) and CP (p < 0.05). Each group showed complete detachment on the pulpal and partial on the lateral walls, except for group3. While the highest DC% was achieved by the conventional RBC (87.2%), followed by the flowable bulk-fill (81.2%), SFRC provided the best bottom to top DC ratio (bulk: 96.4%, layered: 98.7%). The effect of factors studied (RBC type, filling technique) on IA and DC was significant (p < 0.001).

SIGNIFICANCE

Bulk placement of RBCs exhibited lower interfacial gap volume and achieved satisfactory DC without significant correlation between these parameters. Incremental insertion of SFRC had no advantage over bulk placement in terms of IA and DC.

Does Preheating Influence the Cytotoxic Potential of Dental Resin Composites?

Resin-based dental composites (RBC) release cytotoxic components, however the extent of the elution from preheated RBCs is barely investigated. The aim was therefore to determine the cytotoxic effect of preheated conventional, bulk, and thermoviscous RBCs of clinically relevant sizes using different cell viability methods in a contact-free model. Samples (6 × 4 mm) were prepared from conventional [Estelite Sigma Quick (ESQ), Filtek Z250 (FZ)] and bulk-filled [Filtek One BulkFill Restorative (FOB), SDR Plus Bulk Flow (SDR), VisCalor Bulk (VCB)] RBCs. The pre-polymerization temperature was set to room temperature (RT) and 55/65 °C. Pulp cells were cultured, followed by a 2-day exposure to monomers released from solid RBC specimens suspended in the culture medium. Cytotoxicity was assessed using a WST-1, MTT, and LDH colorimetric viability assays. Data were analyzed using one-way ANOVA, Tukey's post hoc test, multivariate analysis, and independent t-test. The effect size (ƞp2) of material and temperature factors was also assessed. All the RBCs demonstrated cytotoxic effect upon exposure to pulp cells, but to a varying extent (ESQ >> VCB > FZ = FOB = SDR). The effect of pre-polymerization temperature was insignificant (ƞp2 < 0.03), except for the thermoviscous RBC, which showed inconsistent findings when subjected to distinct viability tests. Cell viability was predominantly dependent on the type of material used (p < 0.001) which showed a large effect size (ƞp2 > 0.90). Irrespective of the pre-polymerization temperature, RBC samples in a clinically relevant size can release monomers to such an extent, which can substantially decrease the cytocompatibility.

Considerations about Cytotoxicity of Resin-Based Composite Dental Materials: A Systematic Review

The dental material industry is rapidly developing resin-based composites (RBCs), which find widespread use in a variety of clinical settings. As such, their biocompatibility has gained increasing interest. This literature review presents a summary of research into the cytotoxicity of methacrylate-based composites published from 2017 to 2023. Subject to analysis were 14 in vitro studies on human and murine cell lines. Cytotoxicity in the included studies was measured via MTT assay, LDH assay, and WST-1 assay. The QUIN Risk of Bias Tool was performed to validate the included studies. Included studies (based entirely on the results of in vitro studies) provide evidence of dose- and time-dependent cytotoxicity of dental resin-based composites. Oxidative stress and the depletion of cellular glutathione (GSH) were suggested as reasons for cytotoxicity. Induction of apoptosis by RBCs was indicated. While composites remain the golden standard of dental restorative materials, their potential cytotoxicity cannot be ignored due to direct long-term exposure. Further in vitro investigations and clinical trials are required to understand the molecular mechanism of cytotoxicity and produce novel materials with improved safety profiles.

The effect of high-irradiance rapid polymerization on degree of conversion, monomer elution, polymerization shrinkage and porosity of bulk-fill resin composites

OBJECTIVE

The purpose was to compare the degree of conversion (DC), monomer elution (ME), polymerization shrinkage (PS) and porosity of two addition-fragmentation chain transfer (AFCT) modified resin-based composites (RBC) light-cured with rapid- (RP), turbo- (TP) or conventional polymerization (CP) settings.

METHODS

Cylindrical samples (6-mm wide, 4-mm thick) were prepared from Tetric PowerFill (TPF) and Filtek One Bulk (FOB). Four groups were established according to the polymerization settings: 3s-RP, 5s-TP, 10s-CP and 20s-CP. Samples in 1 mm thickness with 20s-CP settings served as controls. The DC at the top and bottom surfaces was measured with micro-Raman spectroscopy. ME was detected with high-performance liquid chromatography. PS and porosity were analyzed by micro-computed tomography. ANOVA and Tukey's post-hoc test, multivariate analysis and partial eta-squared statistics were used to analyze the data (p < 0.05).

RESULTS

FOB showed higher DC values (61.5-77.5 %) at the top compared to TPF (43.5-67.8 %). At the bottom TPF samples achieved higher DCs (39.9-58.5 %) than FOB (18.21-66.18 %). Extending the curing time increased DC (except the top of FOB) and decreased ME. BisGMA release was the highest among the detected monomers from both RBCs. The amount was three-fold more from TPF. The factor Material and Exposure significantly influenced DC and ME. PS (1.8-2.5 %) did not differ among the groups and RBCs except for the lowest value of TPF cured with the 3s_RP setting (p = 0.03). FOB showed 4.5-fold lower porosity (p < 0.001). Significantly higher pore volume was detected after polymerization in 3s_RP (p < 0.001).

SIGNIFICANCE

High-irradiance rapid 3-s curing of AFCT modified RBCs resulted in inferior results for some important material properties. A longer exposure time is recommended in a clinical situation.

Inducing cathepsin L expression/production, lysosomal activation, and autophagy of human dental pulp cells by dentin bonding agents, camphorquinone and BisGMA and the related mechanisms

Camphorquinone (CQ) and resin monomers are included in dentin bonding agents (DBAs) and composite resin to restore tooth defects due to abrasion, crown fracture, or dental caries. DBAs, CQ, and bisphenol A-glycidyl methacrylate (BisGMA) applications influence the biological activities of the dental pulp. The current investigation aimed to delineate the effect of DBAs, CQ, and BisGMA on cathepsin L production/expression, lysosomal activity, and autophagy induction in human dental pulp cells (HDPCs). HDPCs were exposed to DBAs, CQ, or BisGMA with/without inhibitors for 24 h. Enzyme-linked immunosorbent assay was employed to determine the cathepsin L level in culture medium. The cell layer was utilized to measure cell viability by 3-(4,5-dimethyl-thiazol-2-yl)-2,5-diphenyl -tetrazolium bromide (MTT) assay. Real-time PCR was used to evaluate the mRNA expression. Western blotting or immunofluorescent staining was used to study protein expression. Lysosomal density was evaluated by lysotracker red staining. We found that DBAs, CQ, and BisGMA stimulated cathepsin L mRNA, protein expression, and production in HDPCs. In addition, CQ and BisGMA induced lysosomal activity, Beclin1, ATG12, LC3B, Bax, and p53 expression in HDPCs, indicating the stimulation of autophagy. Glutathione (GSH) prevented CQ- and BisGMA-induced cytotoxicity. Moreover, E64d, cathepsin L inhibitor (two cathepsin inhibitors), and Pifithrin-α (a p53 inhibitor) showed little preventive effect toward CQ- and BisGMA-induced cytotoxicity. Autophagy inhibitors (NH4Cl, Lys05) mildly enhanced the CQ- and BisGMA-induced cytotoxicity. These results indicate that DBAs stimulated cathepsin L, possibly due to their content of CQ and BisGMA that may induce cathepsin L in HDPCs. CQ and BisGMA stimulated lysosomal activity, autophagy, and apoptosis, possibly via induction of Beclin 1, ATG12, LC-3B, Bax, and p53 expression. In addition, CQ and BisGMA cytotoxicity was related to redox change and autophagy. These events are important role in pulpal changes after the restoration of tooth decay using CQ- and BisGMA-containing DBAs and resin composite.