The influence of zirconia veneer thickness on the degree of conversion of resin-matrix cements: an integrative review

3D-printed intracoronal restorations, occlusal and laminate veneers: Clinical relevance, properties, and behavior compared to milled restorations; a systematic review and meta-analysis

OBJECTIVES

To assess the feasibility of producing 3D-printed intracoronal restorations, thin and ultrathin veneers, and to compare their mechanical behavior, accuracy, biological, and stain susceptibility to the currently applied milled restorations.

MATERIALS AND METHODS

The databases were comprehensively searched for relevant records up to January 2024 without language restrictions. All studies that assessed 3D-printed partial coverage restorations including inlays, onlays, laminate, and occlusal veneers were retrieved.

RESULTS

The web search yielded a total of 1142 records, with 8 additional records added from websites at a later stage. Only 17 records were ultimately included in the review. The included records compared 3D-printed; alumina-based- and zirconia ceramics, lithium disilicate ceramics, polymer infiltrated ceramics, polyetheretherketone (PEEK), resin composites, and acrylic resins to their CNC milled analogs. The pooled data indicated that it is possible to produce ultrathin restorations with a thickness of less than 0.2 mm. 3D-printed laminate veneers and intracoronal restorations exhibited superior trueness, as well as better marginal and internal fit compared to milled restorations (p < 0.05). However, it should be noted that the choice of materials and preparation design may influence these outcomes. In terms of cost, the initial investment and production expenses associated with 3D printing were significantly lower than those of CNC milling technology. Additionally, 3D printing was also shown to be more time-efficient.

CONCLUSIONS

Using additive manufacturing technology to produce restorations with a thickness ranging from 0.1 to 0.2 mm is indeed feasible. The high accuracy of these restorations, contributes to their ability to resist caries progression, surpassing the minimum clinical threshold load of failure by a significant margin and reliable adhesion. However, before 3D-printed resin restorations can be widely adopted for clinical applications, further improvements are needed, particularly in terms of reducing their susceptibility to stains.

CLINICAL SIGNIFICANCE

3D-printed intracoronal restorations and veneers are more time and cost-efficient, more accurate, and could provide a considerable alternative to the currently applied CNC milling. Some limitations still accompany the resin materials, but this could be overcome by further development of the materials and printing technology.

Advances in zirconia-based dental materials: Properties, classification, applications, and future prospects

OBJECTIVES

Zirconia (ZrO2) ceramics are widely used in dental restorations due to their superior mechanical properties, durability, and ever-improving translucency. This review aims to explore the properties, classification, applications, and recent advancements of zirconia-based dental materials, highlighting their potential to revolutionize dental restoration techniques.

STUDY SELECTION, DATA AND SOURCES

The most recent literature available in scientific databases (PubMed and Web of Science) reporting advances of zirconia-based materials within the dental field is thoroughly examined and summarized, covering the major keywords "dental zirconia, classification, aesthetic, LTD, applications, manufacturing, surface treatments".

CONCLUSIONS

An exhaustive overview of the properties, classifications, and applications of dental zirconia was presented, alongside an exploration of future prospects and potential advances. This review highlighted the importance of addressing challenges such as low-temperature degradation resistance and optimizing the balance between mechanical strength and translucency. Also, innovative approaches to improve the performances of zirconia as dental material was discussed.

CLINICAL SIGNIFICANCE

This review provides a better understanding of zirconia-based dental biomaterials for dentists, helping them to make better choice when choosing a specific material to fabricate the restorations or to place the implant. Moreover, new generations of zirconia are still expected to make progress on key issues such as the long-term applications in dental materials while maintaining both damage resistance and aesthetic appeal, defining the directions for future research.

Application of near-infrared-to-blue upconversion luminescence for the polymerization of resin cements through zirconia discs

OBJECTIVES

To investigate a near-infrared-to-blue luminescence upconversion curing method for polymerizing resin cements under zirconia discs.

METHODS

Lava zirconia discs of different thicknesses (0.5-2.0 mm) were manufactured. First, the transmittances of the NIR and two blue lights (BLs) (LED and halogen lights) through these discs were measured. Second, NaYF4:Yb3+/Tm3+ upconversion phosphor (UP) powder was milled into 0.5-μm particle sizes. A light-curable resin cement VariolinkII base was chosen as the control (UP0), and an experimental cement (UP5) was prepared by adding 5 % UPs. These two cements were examined using multiphoton excitation microscopy for particle distribution. UP5 and UP0 were polymerized with or without zirconia shielding then subjected to a microhardness test. A multifold analysis was performed to examine the effects of zirconia thickness, curing protocols (pure BL or combined BL and NIR curing), and cement type.

RESULTS

The transmittance of NIR was superior to that of BL through zirconia discs of all thicknesses. UP particles were homogeneously distributed in UP5 and emitted blue luminescence under 980-nm NIR excitation. UP5 showed higher microhardness values than UP0 under any curing protocol or zirconia shielding condition. The combination of 20-s BL and 40-s NIR curing yielded the highest microhardness in uncovered UP5. However, combining 40-s BL and 20-s NIR curing surpassed the other groups when the zirconia discs were thicker than 0.5 mm.

SIGNIFICANCE

NIR exhibits higher transmission through zirconia than BL. UP particles work as strengthen fillers and photosensitizers in cements. NIR upconversion curing could be a new strategy for polymerizing resin cements under thick zirconia restorations.

The impact of inorganic fillers, organic content, and polymerization mode on the degree of conversion of monomers in resin-matrix cements for restorative dentistry: a scoping review

PURPOSE

The main aim of the present study was to carry out a scoping review on the differences in degree of conversion of monomers regarding several types resin cements, indirect restorative materials, and light-curing procedures used in dentistry.

METHOD

A bibliographic review was performed on PubMed using the following search items: "degree of conversion" OR "filler" AND "resin cement" OR "inorganic cement" AND "organic" OR "radiopacity" OR "refractive" OR "transmittance" OR "type" AND "resin composite." The search involved articles published in English language within the last thirteen years. A research question has been formulated following the PICO approach as follow: "How different is the degree of conversion of monomers comparing several types of resin-matrix cements?".

RESULTS

Within the 15 selected studies, 8 studies reported a high degree of conversion (DC) of the organic matrix ranging from 70 up to 90% while 7 studies showed lower DC values. Dual-cured resin-matrix cements revealed the highest mean values of DC, flexural strength, and hardness when compared with light- and self-polymerized ones. DC mean values of resin-matrix cements light-cured through a ceramic veneer with 0.4 mm thickness were higher (~ 83%) than those recorded for resin-matrix cements light-cured through a thicker ceramic layer of 1.5 mm (~ 77%).

CONCLUSIONS

The highest percentage of degree of conversion of monomers was reported for dual-cured resin-matrix cements and therefore both chemical and light-induced pathways promoted an enhanced polymerization of the material. Similar degree of conversion of the same resin-matrix cement were recorded when the prosthetic structure showed a low thickness. On thick prosthetic structures, translucent materials are required to allow the light transmission achieving the resin-matrix cement.

CLINICAL RELEVANCE

The chemical composition of resin-matrix cements and the light-curing mode can affect the polymerization of the organic matrix. Thus, physical properties of the materials can vary leading to early clinical failures at restorative interfaces. Thus, the analysis of the polymerization pathways of resin-matrix cements is significantly beneficial for the clinical performance of the restorative interfaces.

Randomized clinical trial of zirconia laminate veneers sintered by using conventional versus speed process: 1-year follow-up

STATEMENT OF PROBLEM

The application of highly translucent multilayered zirconia ceramic in minimally invasive esthetic dentistry allows the achievement of both esthetics and strength with minimal thickness. Clinical studies that have assessed the performance of zirconia ultrathin veneers sintered with the conventional and speed procedure are lacking.

PURPOSE

The purpose of this clinical study was to evaluate the effect of speed sintering processes on the translucency and clinical performance of zirconia laminate veneers.

MATERIAL AND METHODS

Four participants had their teeth restored with 32 ultratranslucent zirconia laminate veneers. Based on the zirconia sintering procedure, the participants were randomly allocated into 2 groups. The teeth were prepared by selective reduction over trial restorations. Zirconia veneers were milled from multilayer zirconia blanks and sintered either by speed sintering or conventional sintering as specified by the manufacturer's recommendations. The intaglio surface of the veneers were airborne-particle abraded with 50-μm aluminum-oxide, and the veneers were then adhesively bonded to the teeth with translucent light-polymerizing resin cement. The modified California Dental Association (CDA)/Ryge criteria were used to assess participants at baseline and every 3 months for 12 months. The translucency and the color difference of the tooth before and after veneer restoration were evaluated. For statistical analysis, the Pearson chi squared test, independent t test, and paired t test were used (α=.05).

RESULTS

Translucency and color differences were significantly higher in the conventionally sintered group (P<.05). No restorations were lost. No significant differences were found between the 2 groups in the CDA/Ryge criteria or color parameter after follow-up intervals (P>.05). The primary qualitative changes observed at the final recall were marginal integrity and marginal discoloration. The color match and zirconia surface were rated Alfa.

CONCLUSIONS

After 1 year of follow-up, both conventional and speed sintered ultrathin zirconia laminates showed satisfactory functional, esthetic, and color stability outcomes.

Designing a Single Lithium Disilicate Crown: A Computer-Aided Design and Computer-Aided Manufacturing Approach With Exocad Software

This case report presents an overview of the workflow and advantages of computer-aided design and manufacture (CAD/CAM) technology in designing single crowns for anterior restoration. The workflow of CAD/CAM systems involves extraoral scanning, virtual crown design, and automated milling processes. The advantages of CAD/CAM technology include enhanced accuracy, reduced chairside time, and improved patient satisfaction. Considerations for material selection, clinical indications, and associated factors in CAD/CAM single-crown design are also discussed. Additionally, CAD/CAM provided accurate and lifelike restoration contours, ensuring optimal fit, function, and aesthetics. This technology proved highly beneficial in this case for several reasons. This case illustrates the significant advantages of CAD/CAM technology in modern dental practice, offering precise, efficient, and aesthetically pleasing solutions for single dental crowns.

Light transmittance through resin-matrix composite onlays adhered to resin-matrix cements or flowable composites

OBJECTIVE

The aim of this study was to evaluate the influence of the thickness of resin-matrix composite blocks manufactured by CAD-CAM on the light transmittance towards different resin-matrix cements or flowable composites.

METHODS

Sixty specimens of resin-matrix composite CAD-CAM blocks reinforced with 89 wt% inorganic fillers were cross-sectioned with 2 or 3 mm thicknesses. The specimens were conditioned with adhesive system and divided in groups according to the luting material, namely: two dual-cured resin-matrix cements, two traditional flowable resin-matrix composites, and one thermal-induced flowable resin-matrix composite. Specimens were light-cured at 900 mW/cm2 for 40s. Light transmittance assays were preformed using a spectrophotometer with an integrated monochromator before and after light-curing. Microstructural analysis was performed by optical and scanning electron microscopy (SEM). Nanoindentation tests were performed to evaluate mechanical properties for indirect evaluation of degree of monomers conversion.

RESULTS

Optical and SEM images revealed low thickness values for the cementation interfaces for the traditional flowable resin-matrix composite. The cement thickness increased with the size and content of inorganic fillers. The highest light transmittance was recorded for the onlay blocks cemented with the traditional flowable resin-matrix composites while a group cemented with the dual-cured resin-matrix cement revealed the lowest light transmittance. The elastic modulus and hardness increased for specimens with high content of inorganic fillers as well as it increased in function of the light transmittance.

CONCLUSIONS

The light transmittance of flowable resin-matrix composites was higher than that for resin-matrix cement after cementation to resin-matrix composites blocks. The type, size, and content of inorganic fillers of the luting material affected the thickness of the cement layer and light transmittance through the materials.

CLINICAL RELEVANCE

On chair-side light curing, the transmission of visible light can be interfered by the chemical composition and viscosity of the luting materials. The increase in size and content of inorganic fillers of resin-matrix composites and luting materials can decrease the light transmittance leading to inefficient polymerization.

Degree of conversion of light-polymerized composite resin in implant prosthesis screw access opening

PURPOSE

The mechanical and physical properties of implant screw access opening deteriorate if composite resin is not polymerized properly. Therefore, this study aimed to analyze the effect of using composite resin in implant access opening on the degree of conversion (DC).

MATERIALS AND METHODS

Two prosthetic materials (Co-Cr and zirconia), two types of composite resin (low and high viscosity), two light-cured resin depths (2 and 3 mm), and two polymerization methods (max-mode 10 s and mid-mode 20 s: 16 and 22 J/cm2 , respectively) were considered (n = 192). The DC of the polymerized composite resin was measured through Fourier-transform infrared spectroscopy. The top and bottom surfaces of the polymerized composite resin body were observed through scanning electron microscopy. Multiple linear regression analysis and analysis of variance were used to identify significant differences in DC (α = 0.05).

RESULTS

The DC was lower when the low-viscosity composite resin (β = -0.431), light-polymerized resin depth of 2 mm (β = -0.430), zirconia prosthesis (β = -0.191), and mid-mode polymerization method (β = -0.164) were used. The resin type, depth of resin to be light-cured, prosthesis material, and polymerization method had an effect on the DC.

CONCLUSIONS

Low-viscosity composite resin should be polymerized at a low irradiance and long polymerization time (such that the light-cured resin depth does not exceed 2 mm) to ensure proper composite resin polymerization in implant screw access opening.

Surface modification of zirconia or lithium disilicate-reinforced glass ceramic by laser texturing to increase the adhesion of prosthetic surfaces to resin cements: an integrative review

OBJECTIVE

The purpose of this study was to perform an integrative review on laser texturing the inner surface of lithium disilicate-reinforced glass ceramic or zirconia to increase their bond strength to resin-matrix cements.

MATERIALS AND METHOD

A bibliographic review was performed on PubMed using the following search terms: "zirconia" OR "lithium disilicate" AND "laser" AND "surface" OR "roughness" AND "bond strength" AND "luting agent" OR "resin cement." Studies published in English language until March 15, 2023, were selected regarding the purpose of this study.

RESULTS

A total of fifty-six studies were identified althoug thirteen studies were selected. The findings revealed that zirconia surfaces were significantly modified after laser irradiation resulting in macro-scale aligned retentive regions with depth values ranging from 50 to 120 µm. Average roughness values of laser-textured zirconia by Er,Cr:YSGG laser (~ 0.83 µm) were quite similar when compared to grit-blasted zirconia surfaces (~ 0.9 µm) although roughness increased up to 2.4 µm depending on the laser type and parameters. Lithium disilicate-reinforced glass ceramics textured with Er:YAG revealed an average roughness of around 3.5 µm while surfaces textured using Nd:YAG laser revealed an average roughness of 2.69 µm; that was quite similar to the roughness values recorded for etched surfaces (2.64 µm). The shear bond strength (SBS) values of zirconia surfaces textured on Nd:YVO₄ laser irradiation were slightly higher (~ 33.5 MPa) than those recorded for grit-blasted zirconia surfaces (28 MPa). Laser-textured zirconia surfaces on CO₂ laser revealed higher SBS values (18.1 ±0.8 MPa) than those (9.1 ± 0.56 MPa) recorded for untreated zirconia surfaces. On lithium disilicate-reinforced glass ceramics, higher SBS values to resin-matrix cements were recorded for specimens textured with a combination of fractional CO₂ laser irradiation and HF acid etching (~ 22-24 MPa) when compared with grit-blasted specimens (12.2 MPa). Another study revealed SBS values at around 27.5 MPa for Er:YAG-textured lithium disilicate-reinforced glass ceramics to resin-matrix cements.

CONCLUSIONS

The laser irradiation at high power increases the roughness of the inner surface of lithium disilicate-reinforced glass ceramic or zirconia leading to an enhanced bond strength to resin-matrix cements. Thus, the laser type and irradiation parameters can be adjusted to enhance the macro- and micro-scale retention of zirconia and glass ceramic surfaces to resin-matrix cements.

CLINICAL RELEVANCE

Alternative methods for surface modification of lithium disilicate-reinforced glass ceramic and zirconia surfaces have been assessed to provide proper morphological aspects for enhanced adhesion to resin-matrix cements. An increase in the bond strength of glass ceramics or zirconia to resin-matrix cements can improve the long-term performance of cemented prosthetic structures in the oral cavity.

The effects of cement thickness and cement shade on the final color of lithium disilicate crowns

PURPOSE

The aim of this study is to evaluate the effect of resin cement color, cement thickness, and thermocycling on the final color of monolithic lithium disilicate crowns.

MATERIALS AND METHODS

A total of ninety prepared central incisors of typodont teeth were restored with lithium disilicate crowns which have different cement thicknesses (40 µm, 80 µm, and 120 µm) and cement shades (clear, yellow, and white). Color parameters of restorations were measured with a spectrophotometer in three different steps 1) before cementing 2) after cementing and 3) after thermocycling with 10000 cycles. Color differences (ΔE₀₀) were calculated with the CIEDE2000 formula and evaluated according to perceptibility (0.8) and acceptability (1.8) thresholds. The ΔE₀₀ data were analyzed by using two-way ANOVA before and after thermocycling (α = .05).

RESULTS

There was no interaction between the cement shade and the cement thickness factors. After cementation, the mean ΔE₀₀ was under the perceptibility threshold in the group of 40 µm cement thickness and clear cement while it was between the perceptibility and acceptability thresholds (0.8 < ΔE₀₀ < 1.8) for all other groups. After thermocycling, the ΔE₀₀ values were between the perceptibility and acceptability thresholds for all experimental groups. Although there were no significant differences among the groups, thermocycling increased the color difference values.

CONCLUSION

The cementation of restorations with clear, yellow, and white resin cements resulted in color differences with uncemented restorations except for the group cemented with clear cement in 40 µm cement thickness. All study groups revealed perceptible color change after thermocycling.

Toxicity of resin-matrix cements in contact with fibroblast or mesenchymal cells

The main aim of this study was to perform an integrative review on the toxic effects of resin-matrix cements and their products in contact with fibroblasts or mesenchymal cells. A bibliographic search was performed on PubMed using the following search terms: "cytotoxicity" AND "fibroblast" OR "epithelial" OR "mesenchymal" AND "polymerization" OR "degree of conversion" OR "methacrylate" OR "monomer" AND "resin cement" OR "resin-based cement". The initial search in the available database yielded a total of 277 articles of which 21 articles were included in this review. A decrease in the viability of mouse fibroblasts ranged between 13 and 15% that was recorded for different resin-matrix cements after light curing exposure for 20 s. The viability of human fibroblasts was recorded at 83.11% after light curing for 20 s that increased up to 90.9% after light curing exposure for 40 s. Most of the studies linked the highest toxicity levels when the cells were in contact with Bis-GMA followed by UDMA, TEGDMA and HEMA. Resin-matrix cements cause a cytotoxic reaction when in contact with fibroblasts or mesenchymal cells due to the release of monomers from the polymeric matrix. The amount of monomers released from the resin matrix and their cytotoxicity depends on the polymerization parameters.

Effects of Translucency and Thickness of Lithium Disilicate-Reinforced Glass-Ceramic Veneers on the Degree of Conversion of a Purely Light-Curing Bonding Resin: An In Vitro Study

The objective of this study was to evaluate the variations in the degree of conversion (DC) of a light-curing composite resin when the thickness or the translucency of lithium disilicate-enriched glass-ceramic veneers are modified. IPS e. max® CAD blocks of the MT-A2, LT-A2 and MO1 types were cut to obtain four slices with thicknesses ranging from 0.6 mm to 1 mm. A strictly light-curing composite resin (G-aenial Universal Injectable) was injected in the empty part of a silicone mold so that the veneer could then be inserted under digital pressure to the stop. A 40 s light cure (1400 mW/cm2) was then performed. Resin samples were analyzed using Fourier transform infrared (FTIR) spectroscopy. When the degree of translucency of the ceramic was modified, a decrease in the resin conversion rate was noted, but with a non-significant global p-value (p = 0.062). Interestingly, the degree of conversion of the light-curing composite resin was also modified when the ceramic’s thickness increased, especially when it was over 1 mm (DC0.6 > DC0.7 > DC0.8 > DC1; p < 0.0001). This confirms that the degree of conversion of a bonding material is very dependent on the ceramic’s thickness. Contradictory data are, however, found in the literature, where there are reports of an absence of a difference between the DC obtained with thicknesses of ceramics of 0.7 and 2 mm.

Microscopic Inspection of the Adhesive Interface of Composite Onlays after Cementation on Low Loading: An In Vitro Study

Purpose: This study aimed to assess the layer thickness and microstructure of traditional resin-matrix cements and flowable resin-matrix composites at dentin and enamel to composite onlay interfaces after cementation on low loading magnitude. Materials and Methods: Twenty teeth were prepared and conditioned with an adhesive system for restoration with resin-matrix composite onlays manufactured by CAD-CAM. On cementation, tooth-to-onlay assemblies were distributed into four groups, including two traditional resin-matrix cements (groups M and B), one flowable resin-matrix composite (group G), and one thermally induced flowable composite (group V). After the cementation procedure, assemblies were cross-sectioned for inspection by optical microscopy at different magnification up to ×1000. Results: The layer thickness of resin-matrix cementation showed the highest mean values at around 405 µm for a traditional resin-matrix cement (group B). The thermally induced flowable resin-matrix composites showed the lowest layer thickness values. The resin-matrix layer thickness revealed statistical differences between traditional resin cement (groups M and B) and flowable resin-matrix composites (groups V and G) (p < 0.05). However, the groups of flowable resin-matrix composites did not reveal statistical differences (p < 0.05). The thickness of the adhesive system layer at around 7 µm and 12 µm was lower at the interfaces with flowable resin-matrix composites when compared to the adhesive layer at resin-matrix cements, which ranged from 12 µm up to 40 µm. Conclusions: The flowable resin-matrix composites showed adequate flowing even though the loading on cementation was performed at low magnitude. Nevertheless, significant variation in thickness of the cementation layer was noticed for flowable resin-matrix composites and traditional resin-matrix cements that can occur in chair-side procedures due to the clinical sensitivity and differences in rheological properties of the materials.

Fit of anterior restorations made of 3D-printed and milled zirconia: An in-vitro study

OBJECTIVES

To evaluate the fit of zirconia veneers made by either 3D printing or milling.

METHODS

A typodont maxillary central incisor was prepared for a 0.5-mm-thick veneer and was reproduced 36 times from resin. Restorations were designed with a 20-µm-wide marginal and a 60-µm-wide internal cement gap, and were made from 3D-printed zirconia (LithaCon 3Y 210, Lithoz, n = 24) and milled zirconia (Cercon ht, DentsplySirona, n = 12). For milled zirconia, a drill compensation was needed to give the milling bur access to the intaglio surface. The restorations were cemented, cross-sectioned, and the cement gap size was analyzed by two raters. Inter-rater reliability was studied at 12 3D-printed veneers (intraclass correlation coefficient, ICC, mixed model, absolute agreement). Twelve remaining 3D-printed restorations were compared with 12 milled restorations regarding fit at three locations: marginally, labially, and at the incisal edge (Mann-Whitney U-tests, α<0.05).

RESULTS

Inter-rater reliability was excellent, with an ICC single-measure coefficient of 0.944 (95%-confidence interval: [0.907; 0.966]). Gap sizes (mean ± SD / maximum) were 55 ± 9 / 143 µm at the margins, 68 ± 14 / 130 µm labially, and 78 ± 19 / 176 µm at the incisor edge for 3D-printed veneers. For milled veneers, gap sizes were 44 ± 11 / 141 µm at the margins, 85 ± 19 / 171 µm labially, and 391 ± 26 / 477 µm at the incisor edge. At the margins, the milled veneers outperformed the 3D-printed restorations (p = 0.011). The cement gap at the incisor edge was significantly smaller after 3D printing (p < 0.001).

CONCLUSIONS

3D-printed zirconia restorations showed clinically acceptable mean marginal gaps below 100 µm. Because drill compensation could be omitted with 3D printing, the fit at the sharp incisal edge was significantly tighter than with milling.

CLINICAL SIGNIFICANCE

The fit of 3D-printed ceramic anterior restorations meets clinical standards. In addition, 3D printing is associated with a greater geometrical freedom than milling. With regard to fit this feature allows tighter adaptation even after minimally invasive preparation.

A Scoping Review on the Polymerization of Resin-Matrix Cements Used in Restorative Dentistry

In dentistry, clinicians mainly use dual-cured or light-cured resin-matrix cements to achieve a proper polymerization of the organic matrix leading to enhanced physical properties of the cement. However, several parameters can affect the polymerization of resin-matrix cements. The main aim of the present study was to perform a scoping review on the degree of conversion (DC) of the organic matrix, the polymerization, and the light transmittance of different resin-matrix cements used in dentistry. A search was performed on PubMed using a combination of the following key terms: degree of conversion, resin cements, light transmittance, polymerization, light curing, and thickness. Articles in the English language published up to November 2022 were selected. The selected studies' results demonstrated that restorative structures with a thickness higher than 1.5 mm decrease the light irradiance towards the resin-matrix cement. A decrease in light transmission provides a low energy absorption through the resin cement leading to a low DC percentage. On the other hand, the highest DC percentages, ranging between 55 and 75%, have been reported for dual-cured resin-matrix cements, although the polymerization mode and exposure time also influence the DC of monomers. Thus, the polymerization of resin-matrix cements can be optimized taking into account different parameters of light-curing, such as adequate light distance, irradiance, exposure time, equipment, and wavelength. Then, optimum physical properties are achieved that provide a long-term clinical performance of the cemented restorative materials.

Post-Cure Development of the Degree of Conversion and Mechanical Properties of Dual-Curing Resin Cements

This study investigated the effect of different curing conditions on the degree of conversion and mechanical properties of contemporary dual-curing resin cements. The material specimens were either light-cured directly, light-cured through a 1-mm lithium disilicate glass-ceramic layer, or self-cured. The degree of conversion was measured in 0.1-mm films using Fourier-transform infrared spectroscopy 1 day, 7 days, and 28 days post-cure. Specimens used to study the flexural strength and modulus were prepared according to the ISO 4049 protocol, stored for 28 days post-cure, and subjected to accelerated aging by absolute ethanol immersion. The degree of conversion values ranged between 44.3–77.8%. Flexural strength varied between 11.4–111.1 MPa, while flexural modulus amounted to 0.7–5.5 GPa. The degree of conversion was significantly affected by material type, curing conditions, and post-cure time; however, variations in curing conditions were the least influential factor. A statistically significant effect of curing conditions on the degree of conversion was identified for only one of the five materials tested, whereas the flexural strength and modulus of all tested materials were significantly reduced in the experimental groups that were light-cured through a ceramic layer or self-cured. The effect size analysis showed that mechanical properties were most affected by the material type, while the differences in curing conditions were less influential. A comparison of the degree of conversion and mechanical properties indicated that different curing conditions may lead to significantly different flexural strength and modulus, which are not necessarily accompanied by identifiable variations in the degree of conversion.

The influence of inorganic fillers on the light transmission through resin-matrix composites during the light-curing procedure: an integrative review

PURPOSE

The objective of this study was to perform an integrative review on the effect the inorganic fillers on the light transmission through the resin-matrix composites during the light-curing procedure.

METHOD

A bibliographic review was performed on PubMed using the following search terms: "fillers" OR "particle" AND "light curing" OR "polymerization" AND "light transmission" OR "light absorption" OR "light irradiance" OR "light attenuation" OR "light diffusion" AND "resin composite." The search involved articles published in English language in the last 10 years.

RESULTS

Selected studies reported a decrease in biaxial strength and hardness in traditional resin-matrix composites in function of the depth of polymerization. However, there were no significant differences in biaxial strength and hardness recorded along the polymerization depth of Bulk-Fill™ composites. Strength and hardness were enhanced by increasing the size and content of inorganic fillers although some studies revealed a progressive decrease in the degree of conversion on increasing silica particle size. The translucency of glass-ceramic spherical fillers promoted light diffusion mainly in critical situations such as in the case of deep proximal regions of resin-matrix composites.

CONCLUSIONS

The amount of light transmitted through the resin-matrix composites is influenced by the size, content, microstructure, and shape of the inorganic filler particles. The decrease of the degree of conversion affects negatively the physical and mechanical properties of the resin-matrix composites.

CLINICAL RELEVANCE

The type and content of inorganic fillers in the chemical composition of resin-matrix composites do affect their polymerization. As a consequence, the clinical performance of resin-matrix composites can be compromised leading to variable physical properties and degradation. The polymerization mode of resin-matrix composites can be improved according to the type of inorganic fillers in their chemical composition.

Effects of Substrate and Cement Shade on the Translucency and Color of CAD/CAM Lithium-Disilicate and Zirconia Ceramic Materials

The aim of this in vitro study was to evaluate the effects of substrate and cement shades on the translucency and color of lithium-disilicate and zirconia CAD/CAM materials. Two light-cured resin cements (RelyX Veneer Cement; 3M; Choice 2 Veneer Cement; Bisco Dental) with a standardized thickness (0.1 mm) were tested in combination with two different monolithic CAD/CAM materials (E-Max CAD (LI2SI2O5); Ivoclar Vivadent; Katana (ZrO2); Kuraray-Noritake Dental) on two different colored composite substrates used as a dentin (Filtek Supreme XTE; 3M); for a total of 12 combinations (n = 10). The specimens’ color was measured with a spectrophotometer (Spectroshade; MHT). Measurements were taken using the CIELAB color coordinate system (L*a*b*) against black and white backgrounds. L*a*b* values were statistically analyzed for the variables Substrate, Ceramic, and Cement by applying a Three-Way ANOVA followed by the Tukey Test for post-hoc comparison (p < 0.05). Translucency Parameter (TP) and Constant Ratio (CR) were assessed to evaluate translucency; acceptability and perceptibility thresholds (ΔE00 1.8 and 0.8) were used. Statistically significant influence was found for factors ceramic material, cement shade, and substrate color (p < 0.05). Unacceptable color differences were reported for Li2Si2O5. Opacity was significantly higher when white opaque cement shade was employed. Ceramic type and cement shade significantly influenced L*a*b* color coordinates. The final translucency and color of ceramic restorations can, therefore, be influenced by ceramic material, cement shade, and substrate color.

Surface modification of zirconia dental implants by laser texturing

The aim of this work was to perform an integrative literature review on the influence of laser irradiation on zirconia implants to enhance surface topographic aspects and the biological response for osseointegration. An electronic search was carried out on the PubMed database using the following search terms: "zirconia" AND "laser" AND "surface modification" OR "surface treatment" AND "dental implants" OR "bone" OR "osteoblast" OR "osseointegration." Of the identified articles, 12 studies were selected in this review. Results reported that the laser irradiation was capable of promoting changes on the zirconia surfaces regarding topographic aspects, roughness, and wettability. An increase in roughness was recorded at micro- and nano-scale and it resulted in an enhanced wettability and biological response. Also, adhesion, spreading, proliferation, and differentiation of osteogenic cells were also enhanced after laser irradiation mainly by using a femtosecond laser at 10nJ and 80 MHz. After 3 months of osseointegration, in vivo studies in dogs revealed a similar average percentage of bone-to-implant contact (BIC) on zirconia surfaces (around 47.9 ± 16%) when compared to standard titanium surfaces (61.73 ±16.27%), denoting that there is no significant difference between such different materials. The laser  approach revealed several parameters that can be used for zirconia surface modification such as irradiation intensity, time, and frequency. Laser irradiation parameters can be optimized and well-controlled to reach desirable surface morphologic aspects and biological response concerning the osseointegration process.

Surface modification of glass fiber-reinforced composite posts to enhance their bond strength to resin-matrix cements: an integrative review

BACKGROUND

Endodontically treated teeth usually can reveal an extensive loss of dental structure and require the use of intraradicular posts to provide adequate support and retention. Retention of the post depends on the surface treatment of the endodontic post itself and on the root canal dentin as well as on the type of resin-matrix cement.

PURPOSE

The main aim of this study was to conduct an integrative review on the influence of different surface treatment methods of glass fiber-reinfored resin composite (GFRC) posts on their push-out bond strength to resin-matrix cements in endodontically treated teeth rehabiliation.

METHOD

A literature search was performed on PubMed (via National Library of Medicine) regarding articles published within the last 10 years, using the following combination of search terms: "intracanal post" OR "endodontic post" OR "root canal post" OR "intraradicular post" OR "glass fiber" AND "resin cement" AND "adhesion" OR "bond strength" OR "shear bond strength" OR "push out".

RESULTS

Results from the selected studies recorded the highest push-out bond strength around 22.5 MPa) on GFRC posts to resin-matrix cements when the surfaces were pre-treated by grit-blasting with silicate followed by silane conditioning. However, high values of push-out bond strength (21.5 MPa) were also noticed for GFRC posts after etching with hydrogen peroxide followed by silance conditioning. Thus, the highest values of bond strength of endodontic posts to the resin-matrix cements were recorded when a combined physico-chemical approach was assessed. Non-treated surfaces showed the lowest bond strength values between 5 to and 9 MPa. Surface analyses of GFRC posts showed an increased roughness after grit-blasting or etching that promoted a mechanical interlocking of the adhesive and resin-matrix cements.

CONCLUSION

The combined treatment of glass fiber-reinforced resin composite post surfaces by physical and chemical methods can promote the increase in roughness and chemical functionalization of the surfaces prior to cementation., That results in a high mechanical interlocking of the resin-matrix cements and a stable retention of the teeth root intracanal posts.

CLINICAL RELEVANCE

Combining chemical and physical modification methods of surfaces can provide the most promising adhesion-enhancing pathways of GFRC posts to resin-matrix cements, that can decrease the risk of clinical failures by fracture and detachment of endodontic posts.

Effects of shades of a multilayered zirconia on light transmission, monomer conversion, and bond strength of resin cement

OBJECTIVE

To evaluate the influence of shades of a multilayered zirconia on light transmission, resin cement degree of conversion, and shear bond strength of resin cement.

MATERIALS AND METHODS

The light transmission through opaque (OPQ) and translucent (TNS) regions of Katana UTML zirconia (Kuraray Noritake Dental) were evaluated for using a spectroradiometer (n = 5). Degree of conversion of dual-cure resin cement (Panavia V5, Kuraray Noritake Dental) was measured after light-activation through OPQ or TNS regions and direct exposure. Composition of the zirconia was analyzed with energy dispersive x-ray spectroscopy (EDS). Shear bond strength (SBS) was evaluated on the OPQ and TNS regions after 24 h and 1 year from specimen preparation (n = 15).

RESULTS

The OPQ region produced higher irradiance loss (95.1%) than TNS one (92.9%), and lower degree of conversion (52.4%) than TNS (71.2%) at 24 h post-light activation. EDS analysis did not show differences on the microstructure of the OPQ and TNS regions. There were no significant differences on the SBS between zirconia regions. For both zirconia regions, a significant reduction on the SBS occurred after aging, being 31.7% for OPQ and 38% for TNS.

CONCLUSION

Both OPQ and TNS regions affected the light transmission through the multilayered zirconia. The OPQ region yielded the highest light attenuation and the lowest degree of conversion of resin cement. Different regions of the zirconia did not influence the SBS. Clinical significance Although opaque and translucent regions of the multilayered zirconia reduced the light transmission from LED curing unit and the degree of conversion of resin cement, the regions did not affect the resin cement adhesion.

The resin-matrix cement layer thickness resultant from the intracanal fitting of teeth root canal posts: an integrative review

OBJECTIVE

The aim of this study was to perform an integrative review on the layer thickness and microstructure of resin-matrix cements around custom-made or standard teeth root intracanal posts.

MATERIALS AND METHODS

An electronic search was conducted on the PubMed using a combination of the following scientific terms: intraradicular post, root intracanal post, resin cement, thickness, adaptation, endodontic post, layer thickness, fit, shape, and endodontic core. The literature selection criteria accepted articles published in the English language, up to May 2021, involving in vitro analyses, meta-analyses, randomized controlled trials, and prospective cohort studies.

RESULTS

The search identified 154 studies, of which 24 were considered relevant to this study. The selected studies provided important data considering cement layer thickness, tooth preparation, endodontic post, and type of resin-matrix cement. The anatomical variability of root canal systems, such as the oval- or C-shaped, represents a challenge in dental restoration with tooth root intracanal posts. The fitting of intracanal posts to different root regions is variable resulting in thick and irregular layers of resin-matrix cement. Defects like pores, micro-cracks, and micro-gaps were detected in the resin-matrix cement microstructure and represent spots of stress concentration and fracture. Custom-made tooth root intracanal posts provide a proper fitting and decrease the layer thickness of resin-matrix cement.

CONCLUSIONS

In fact, the layer thickness of resin-matrix cements depends on the fitting of endodontic posts to tooth root canals. An increase of resin cement thickness causes the appearance of defects like pores, micro-cracks, and micro-gaps that can induce stress concentration and fractures at interfaces.

CLINICAL RELEVANCE

The fitting of the endodontic post into the teeth root canal determine the layer thickness of the resin-matrix cement to establish an adequate retention. However, the increase in the thickness of the resin-matrix cement layer can lead to a high number of defects like pores or cracks and therefore decrease the strength of the interface.

An integrative review on the toxicity of Bisphenol A (BPA) released from resin composites used in dentistry

The main aim of this study was to perform an integrative review on the release of bisphenol A (BPA) from resin-matrix composites and potential toxic effects. A bibliographic search was performed on the PubMed platform using the following keywords: "Bisphenol A" OR "BPA" AND "resin composite" OR "composite resin" AND "toxicity" OR "cytotoxicity" OR "release". Inclusion criteria involved in vitro and in vivo studies on the release and toxicity of BPA. Results highlighted the release of BPA from resin-matrix composites due to insufficient polymerization and/or degradation of the polymeric matrix. BPA is part of the organic matrix of resin-matrix composites and may be hydrolysed in human saliva, although studies report that low doses might not be detected by traditional chemical analysis. Studies exposing zebrafish embryos to different concentrations of Bis-GMA, showed 55% mortality at 10 μM Bis-GMA while 30% mortality was recorded at 1 μM Bis-GMA. In patients, a BPA concentration of around 2.09 × 10^-2 μg/ml was found in the saliva after placement of lingual orthodontic retainers with resin-matrix composites. Also, the BPA molecule can be swallowed and absorbed by the oral/gastrointestinal mucosa, which might result in systemic toxicity. The degradation of resin-matrix composites and release of BPA in oral environment are dependent on the organic matrix content and on the polymerization method. A increased release of BPA can lead to the absorption into oral and gastrointestinal mucosa with high risks of local and systemic toxicity.