Synthesis and characterization of organic–inorganic hybrid microspheres

High Performance Low Dielectric Polybenzocyclobutene Nanocomposites with Organic-Inorganic Hybrid Silicon Nanoparticles

In this study, benzocyclobutene-functionalized organic-inorganic hybrid spherical silicon nanoparticles (BCBNPs) with controllable size (200-600 nm) and good dispersion were synthesized by one-step sol-gel method in aqueous solution. The effect of...

The Influence of Silica Nanoparticles on the Thermal and Mechanical Properties of Crosslinked Hybrid Composites

This paper presents the synthesis and physicochemical characterization of a new hybrid composite. Its main goals are evaluating the structure and studying the thermal and mechanical properties of the crosslinked polymeric materials based on varying chemical properties of the compounds. As an organic crosslinking monomer, bisphenol A glycerolate diacrylate (BPA.GDA) was used. Trimethoxyvinylsilane (TMVS) and N-vinyl-2-pyrrolidone (NVP) were used as comonomers and active diluents. The inorganic fraction was the silica in the form of nanoparticles (_NANOSiO₂). The hybrid composites were obtained by the bulk polymerization method using the UV initiator Irqacure 651 with a constant weight ratio of the tetrafunctional monomer BPA.GDA to TMVS or NVP (7:3 wt.%) and different wt.% of silica nanoparticles (0, 1, 3%). The proper course of polymerization was confirmed by the ATR/FTIR spectroscopy and SEM EDAX analysis. In the composites spectra the signals correspond to the C=O groups from NVP at 1672–1675 cm⁻¹, and the vibrations of Si–O–C and Si–O–Si groups at 1053–1100 cm⁻¹ from TMVS and _NANOSiO₂ are visible. Thermal stabilities of the obtained composites were studied by a differential scanning calorimetry DSC. Compared to NVP the samples with TMVS degraded in one stage (422.6–425.3 °C). The NVP-derived materials decomposed in three stages (three endothermic effects on the DSC curves). The addition of _NANOSiO₂ increases the temperature of composites maximum degradation insignificantly. Additionally, the Shore D hardness test was carried out with original metrological measurements of changes in diameter after indentation in relation to the type of material. The accuracy analysis of the obtained test results was based on a comparative analysis of graphical curves obtained from experimental tests. The values of the changes course of similarity in the examined factors, represented by those of characteristic coefficients were determined based on the Fréchet’s theory.

Physicochemical and Adsorption Characteristics of Divinylbenzene-co-Triethoxyvinylsilane Microspheres as Materials for the Removal of Organic Compounds

In this work, organic-inorganic materials with spherical shape consisting of divinylbenzene (DVB) and triethoxyvinylsilane (TEVS) were synthesized and investigated by different complementary techniques. The obtained microspheres may be applied as sorbent systems for the purification of organic compounds from water. The hybrid microspheres combine the properties of the constituents depending on the morphologies and interfacial bonding. In this work, the influence of the molar ratio composition of crosslinked monomer (DVB) and silane coupling agent (TEVS) (DVB:TEVS molar ratios: 1:2, 1:1 and 2:1) on the morphology and quality of organic-inorganic materials have been examined. The materials were analysed using small angle X-ray scattering (SAXS) analysis, low-temperature nitrogen sorption, scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR) to provide information on their structural and surface properties. Moreover, thermal analysis was performed to characterize the thermal stability of the studied materials and the adsorbent-adsorbate interactions, while adsorption kinetic studies proved the utility of the synthesized adsorbents for water and wastewater treatment.

Sorption Properties of Polydivinylbenzene Polymers towards Phenolic Compounds and Pharmaceuticals

Highly cross-linked polymers are commonly used in purification and separation techniques because of their many useful features. In order to better adjust their porosity to adsorption of specific compounds, methods like surface functionalization or imprinting are used. In this work, a series of highly cross-linked polydivinylbenzenes (pDVB) were prepared using a suspension method. Toluene was applied as a pore-forming diluent. Some part of toluene (1 mL) was replaced with phenol (F), 2,4,6-trichlorophenol (T) or their mixture (M) to prepare polymers with porosity more suitable for phenols sorption. Another approach was an introduction of sulfone groups onto the polymer surface (pDVB-SO3H). The physicochemical characteristics of the synthetized adsorbents included CHN, FTIR, DSC and porosimetric analyses. Afterwards, to evaluate sorption properties of the prepared adsorbents towards phenols, ibuprofen and salicylic acid the solid phase extraction (SPE) experiments were performed. The polymers had the specific surface areas of about 440–560 m2/g created mainly by mesopores with widths ca. 3.75 and 4.75–7.15 nm. Materials obtained with the addition of porosity modifiers (phenol, trichlorophenol, mixture) had more uniform porous structure and their sorption capacity toward phenols increased ca. 5%. Similar sorption capacities were obtained for ibuprofen. Salicylic acid had low affinity to the surface of the tested polymers.

Easy fabrication of poly(butyl acrylate)/silicon dioxide core-shell composite microspheres through ultrasonically initiated encapsulation emulsion polymerization

In this study, instead of using the usual chemical methods, poly(butyl acrylate)/silicon dioxide (PBA/SiO₂) core-shell composite microspheres were prepared using a physical method-ultrasonically initiated encapsulation emulsion polymerization. The morphology and particle size of the PBA/SiO₂ microspheres were analysed using transmission electron microscopy (TEM) and dynamic light scattering (DLS). The encapsulation state was determined using X-ray photoelectron spectroscopy (XPS). The composition and thermogravimetric behavior were characterized using Fourier transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA). The TEM and DLS results show that monodisperse PBA/SiO₂ core-shell composite microspheres were successfully obtained. The diameter and shell thickness were 150 nm and 15 nm, respectively. The XPS and FTIR results show that there was no new chemical bond between the PBA shell and the SiO₂ core. They were just combined by physical adsorption. The encapsulation efficiency of SiO₂ microspheres by PBA is 8.2% through TGA. In addition, this article focuses on the formation mechanism of PBA/SiO₂ core-shell microspheres prepared through ultrasonically initiated encapsulation emulsion polymerization. Intuitive observation and the results of TEM and DLS, especially the change in zeta potential, clearly indicate an encapsulation process. Thereinto, a bilayer-structure space established by appropriate amount of cetyltrimethyl ammonium bromide (CTAB) molecules is the key to realize ultrasonically initiated encapsulation emulsion polymerization.