Enhancing the CO Preferential Oxidation (CO-PROX) of CuO–CeO2/Reduced Graphene Oxide (rGO) by Conductive rGO-Wrapping Based on the Interfacial Charge Transfer

Synthesis of nanomagnetite/copper oxide/potassium carrageenan nanocomposite for the adsorption and Photo-Fenton degradation of Safranin-O: kinetic and thermodynamic studies

In the current study, a novel nanomaterial called nanomagnetite/copper oxide/potassium carrageenan nanocomposite (MKCO) was fabricated to include Fenton (nanomagnetite, NM) and Fenton-like reagent (copper oxide nanoparticles, NCO) in a matrix of potassium carrageenan biopolymer. The prepared solid materials were characterized by different physicochemical techniques, such as TGA, N2 adsorption/desorption, SEM, TEM, XRD, DRS, pHPZC, and FTIR. The prepared MKCO showed unique properties like higher specific surface area of 652.50 m2/g, pore radius of 1.19 nm, pHPZC equals 7.80, and the presence of different surface chemical functional groups. Under various application conditions, comparative experiments between Safranin-O dye (SO) adsorption and Photo-Fenton catalytic degradation were conducted. After 24 h, MKCO had a maximum adsorption capacity of 384.61 mg/g at 42 °C, while the Photo-Fenton oxidation process took only 10 min to totally decompose 93% of SO at 21 °C. Based on the higher values of correlation coefficients, Langmuir’s adsorption model is the best-fitted adsorption model for SO onto all the prepared solid materials. Studies on SO adsorption’s kinetics and thermodynamics show that it is physisorption and that it operates according to endothermic, spontaneous, and PFO model processes. While, PFO, endothermic, and non-spontaneous processes are satisfied by the catalytic decomposition of SO. After five application cycles, MKCO demonstrated good catalyst reusability with a 3.4% decrease in degrading efficiency. For lower contaminant concentrations and shorter application times, Photo-Fenton catalytic degradation of organic pollutants is more effective than adsorption.

Graphical abstract

Fenton and Photo-Fenton degradation of Safranin-O

The noble metals M (M = Pd, Ag, Au) decorated CeO2catalysts derived from solution combustion method for efficient low-temperature CO catalytic oxidation: effects of different M loading on catalytic performances

The noble metal nanoparticles have attracted attention due to their excellent catalytic performance for CO oxidation at low temperatures. M-CeO₂(M = Pd, Ag, Au) catalysts with different atomic ratios of M/Ce were deposited via solution combustion method. Among them, 3 at% Pd-CeO₂, 5 at% Ag-CeO₂and 1 at% Au-CeO₂catalysts have better catalytic performances. Especially, 5 at% Ag-CeO₂catalyst shows better low-temperature CO oxidation performance. The catalytic activity for CO oxidation follows the follows the following sequence: 5 at% Ag-CeO₂(T₅₀ = 69 °C) > 3 at% Pd-CeO₂(T₅₀ = 99 °C) >1 at% Au-CeO₂(T₅₀ = 115 °C). Meanwhile, the catalysts are characterized by means of powder x-ray diffraction, scanning electron microscope, transmission electron microscopy, Raman spectroscopy, x-ray photoelectron spectroscopy, Brunauer-Emmett-Teller and H₂-TPR. The characterization results show that the 5 at% Ag-CeO₂catalyst has excellent catalytic activity due to the good dispersion of Ag nanoparticles, the specific surface area of the material, and the reduction catalyst between different valence ions. Moreover, the surface of the catalyst enhances the mutual synergy, effectively promotes the generation of oxygen vacancies, and increases the active oxygen content of the catalyst surface. Finally, the catalytic mechanism of M-CeO₂catalysts is summarized.

Synthesis of Micro- and Nanoparticles in Sub- and Supercritical Water: From the Laboratory to Larger Scales

The use of micro- and nanoparticles is gaining more and more importance because of their wide range of uses and benefits based on their unique mechanical, physical, electrical, optical, electronic, and magnetic properties. In recent decades, supercritical fluid technologies have strongly emerged as an effective alternative to other numerous particle generation processes, mainly thanks to the peculiar properties exhibited by supercritical fluids. Carbon dioxide and water have so far been two of the most commonly used fluids for particle generation, the former being the fluid par excellence in this field, mainly, because it offers the possibility of precipitating thermolabile particles. Nevertheless, the use of high-pressure and -temperature water opens an innovative and very interesting field of study, especially with regards to the precipitation of particles that could hardly be precipitated when CO2 is used, such as metal particles with a considerable value in the market. This review describes an innovative method to obtain micro- and nanoparticles: hydrothermal synthesis by means of near and supercritical water. It also describes the differences between this method and other conventional procedures, the most currently active research centers, the types of particles synthesized, the techniques to evaluate the products obtained, the main operating parameters, the types of reactors, and amongst them, the most significant and the most frequently used, the scaling-up studies under progress, and the milestones to be reached in the coming years.

Ceria Promoted Cu-Ni/SiO2 Catalyst for Selective Hydrodeoxygenation of Vanillin

A ceria (CeO2) promoted Cu-Ni bimetallic catalyst supported on SiO2 (Cu-Ni/CeO2-SiO2) was prepared and evaluated for catalytic hydrodeoxygenation (HDO) of vanillin. Silica supported monometallic Cu and Ni catalysts and bimetallic Cu-Ni catalyst (Cu/SiO2, Ni/SiO2, and Cu-Ni/SiO2), without a ceria promoter, were also synthesized and tested for the same application. The highest conversion of vanillin was achieved with the Cu-Ni/CeO2-SiO2 catalyst. Vanillyl alcohol was the sole product in the initial 2 h, followed by the formation of 2-methoxy-4-methylphenol, which was observed. Characterization of the synthesized catalysts revealed the presence of overlapping crystalline phases of CuO, NiO, and CeO2 on the Cu-Ni/CeO2-SiO2 surface. We extended our study to find out the results of using CeO2 as the support of the Cu-Ni bimetallic catalyst (Cu-Ni/CeO2). Partial incorporation of Cu and Ni cations into the ceria lattice took place, leading to the decrease of specific surface area and a concomitant compromise in the conversion. In the case of the Cu-Ni/CeO2-SiO2 catalyst, the higher conversion was accredited to the facile formation of Cu+ active centers by the synergistic interaction between Ce+4/Ce+3 and Cu+2/Cu+ redox couples and the incorporation of oxygen vacancies on the catalyst surface.