Electrocatalytic oxidation of methanol on Cu modified polyaniline electrode in alkaline medium

A glassy carbon electrode modified with polyaniline nanowires: An electrochemically effective surface area and an electrocatalytic activity for the oxidation of methanol under alkaline conditions

Polyaniline nanowires are directly synthesized on a glassy carbon electrode (3 mm diameter) by an electrochemical process. The polyaniline nanowires, of uniform size, a diameter of 85–95 nm, and high conductivity, distribute evenly throughout the surface of the working electrode. Electrochemical measurements are conducted in order to determine the electrochemically effective surface area of the obtained glassy carbon electrode modified with polyaniline nanowires, and an investigation of the electrocatalytic activity of polyaniline nanowires for the oxidation of methanol under alkaline conditions is carried out. The electrochemically effective surface area of the glassy carbon electrode modified with polyaniline nanowires is nearly 27 times larger than that of a glassy carbon electrode. In a cyclic voltammetry curve of the glassy carbon electrode modified with polyaniline nanowires measured in a 3.0 M CH3OH and 0.5 M KOH solution, an anodic peak corresponding to the oxidation of methanol under alkaline conditions appears at 0.17 V with a peak current of 34.4 μA.

A highly active copper-nanoparticle-based nitrate reduction electrocatalyst prepared by in situ electrodeposition and annealing

In recent years, copper-based electrodes have attracted intense attention for the electrochemical reduction of nitrate (NO₃^-), the so-called ECRN. However, these electrodes suffer from low activity and selectivity. Herein, we report a novel Cu-based electrode (IE-Cu-400) for the ECRN fabricated by loading Cu-based nanoparticles onto graphite felt using in situ electrodeposition followed by annealing. Compared with traditional Cu-based electrodes, the IE-Cu-400 is comprised of smaller particles and the copper is present in a high oxidation state (Cu²⁺ in CuO). During operation, the CuO is converted to Cu, which is the active ECRN species. In addition, an increased surface area and high density of grain boundaries resulting from the reduction of CuO were observed for IE-Cu-400. This resulted in a 3.38-fold increase in the NO₃^- removal rate and a 1.36-fold increase in NH₄⁺ selectivity. Further analyses revealed that the enhanced ECRN performance of IE-Cu-400 is linked to its increased number of active sites, as well as its improved adsorption and reduction ability for NO₂^-. Moreover, IE-Cu-400 displays high stability for the ECRN. Finally, the produced NH₄⁺ was effectively oxidised to N₂ with approximately 100% selectivity via chlorination. Hence, the two-stage treatment strategy (i.e. ECRN by IE-Cu-400 + chlorination treatment) presented here shows great potential for the complete electrocatalytic denitrification of water. Further, this work highlights the beneficial effect of decreasing the particle size and controlling the surface oxidation of Cu-based catalysts simultaneously for enhancing the ECRN and offers new suggestions for the design of high-performance electrode materials for the ECRN.

Performance Improvement of Gold Electrode towards Methanol Electrooxidation in Akaline Medium: Enhanced Current Density Achieved with Poly(aniline-co-2-hydroxyaniline) Coating at Low Overpotential

Electronically conducting poly (aniline-co-2-hydroxyaniline) (PACHA), a copolymer of aniline and 2-hydroxyaniline (2HA), was electrochemically coated on gold substrate for methanol electrooxidation in alkaline media. The electrochemical behavior of PACHA coated gold electrode towards methanol electrooxidation was investigated via cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) for application in an alkaline fuel cell. Methanol electrooxidation was observed at two different electrode potentials depending on the concentration of the base. At the PACHA coated gold electrode, the methanol oxidation peak was observed at lower overpotential (at 0.19 V) in a solution of high base concentration (1.8 M NaOH), which was 30 mV lower than the peak for the uncoated gold electrode. In addition, the Faradic current Imax obtained on the PACHA coated electrode (20 mA) was two times higher as compared to the Faradic current Imax of the un-modified gold electrode (10 mA). In solution of lower base concentration (0.06 M NaOH), the electrooxidation of methanol became sluggish on both electrodes, as indicated by peak shifting towards positive potential and with reduced faradaic current (at 0.74 V on PACHA coated electrode; Imax 10 mA). The electrooxidation of methanol at both lower and higher electrode potentials was analyzed mechanistically and discussed in light of the literature. EIS results were interpreted using Nyquist and Bode plots. The charge transfer resistance was decreased and pseudo-capacitive behavior changed to conductive behavior when external applied potential was increased from 0.1 V to 0.4 V.