The one-pot synthesis of dextran-based nanoparticles and their application in in-situ fabrication of dextran-magnetite nanocomposites

Using Nitrated Lignosulfonates for the Synthesis of a Water-Based Magnetic Fluid

Nitrated lignosulfonates were used to synthesize a water-based magnetic fluid. Lignosulfonates were nitrated by nitric acid under mild conditions and without further purification were used to synthesize a magnetic fluid. Part of the iron(II) were oxidized with an excess of nitric acid, so that the magnetoactive phase under the condensation by action of sodium hydroxide was formed. Optimum conditions for nitration of lignosulfonates and synthesis of a magnetic fluid were experimentally established. The optimum consumption of iron(II) was 1.3–1.5[Formula: see text]g per 1[Formula: see text]g of sodium lignosulfonate. Unlike the initial lignosulfonates, nitrated lignosulfonates have peptizing properties, due to which the precipitate formed during condensation was dispersed to nanoparticles (15–30[Formula: see text]nm). The resulting magnetic fluid had a high magnetic activity and was stable for a long time.

Synthesis and characterization of dextran-coated iron oxide nanoparticles

Synthesis and characterization of iron oxide nanoparticles coated with a large molar weight dextran for environmental applications are reported. The first experiments involved the synthesis of iron oxide nanoparticles which were coated with dextran at different concentrations. The synthesis was performed by a co-precipitation technique, while the coating of iron oxide nanoparticles was carried out in solution. The obtained nanoparticles were characterized by using scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction spectrometry, Fourier transform infrared spectroscopy and superconducting quantum interference device magnetometry. The results demonstrated a successful coating of iron oxide nanoparticles with large molar weight dextran, of which agglomeration tendency depended on the amount of dextran in the coating solution. SEM and TEM observations have shown that the iron oxide nanoparticles are of about 7 nm in size.