Enhanced Photocatalytic Performance of Al-Doped ZnO NPs-Reduced Graphene Oxide Nanocomposite for Removing of Methyl Orange Dye from Water Under Visible-Light Irradiation

Recent developments in photocatalysis of industrial effluents ։ A review and example of phenolic compounds degradation

Industrial expansion and increased water consumption have created water scarcity concerns. Meanwhile, conventional wastewater purification methods have failed to degrade recalcitrant pollutants efficiently. The present review paper discusses the recent advances and challenges in photocatalytic processes applied for industrial effluents treatment, with respect to phenolic compounds degradation. Key operational parameters including the catalyst loading, light intensity, initial pollutants concentration, pH, and type and concentrations of oxidants are evaluated and discussed. Compared to the other examined controlling parameters, pH has the highest effect on the photo-oxidation of contaminants by means of the photocatalyst ionization degree and surface charge. Furthermore, major phenolic compounds derived from industrial sources are comprehensively presented and the applicability of photocatalytic processes and the barriers in practical applications, including high energy demand, technical challenges, photocatalyst stability, and recyclability have been explored. The importance of energy consumption and operational costs for realistic large-scale processes are also discussed. Finally, research gaps in this area and the suggested direction for improving degradation efficiencies in industrial applications are presented. In the light of these premises, selective degradation processes in real water matrices such as untreated sewage are proposed.

Sunlight-induced photocatalytic degradation of various dyes and bacterial inactivation using CuO-MgO-ZnO nanocomposite

Novel tri-phase CuO-MgO-ZnO nanocomposite was prepared using the co-precipitation technique and investigated its physical properties using characterization techniques including XRD, FTIR, Raman, IV, UV-vis, PL, and SEM. The application of grown CuO-MgO-ZnO nanocomposite for the degradation of various dyes under sunlight and antibacterial activity against different bacteria were studied. The XRD confirmed the existence of diffraction peaks related to CuO (monoclinic), MgO (cubic), and ZnO (hexagonal) with CuO phase 40%, MgO 24%, and ZnO 36%. The optical energy gap of nanocomposite was 2.9 eV, which made it an efficient catalyst under sunlight. Raman and FTIR spectra have further confirmed the formation of the nanocomposite. SEM images revealed agglomerated rod-shaped morphology. EDX results showed the atomic percentage of a constituent element in this order Cu>Zn>Mg. PL results demonstrate the presence of intrinsic defects. The photocatalytic activity against methylene blue (MB), methyl orange (MO), rhodamine-B (RhB), cresol red (CR), and P-nitroaniline (P-Nitro) dyes has shown the excellent degradation efficiencies 88.5%, 93.5%, 75.9%, 98.8%, and 98.6% at 5 ppm dye concentration and 82.6%, 83.6%, 64.3%, 93.1%, and 94.3% at 10 ppm dye concentration in 100 min, respectively, under sunlight illumination. The higher degradation is due to the generation of superoxide and hydroxyl radicals. The recyclability test showed the reusability of catalyst up to the 5th cycle. The antibacterial activity against Escherichia coli, Klebsiella pneumoniae, Proteus Vulgaris, Staphylococcus aureus, and Pseudomonas aeruginosa bacteria with the zone of inhibition 30, 31, 30, 30, and 30 mm, respectively, was achieved.

Efficient and Rapid Photocatalytic Degradation of Methyl Orange Dye Using Al/ZnO Nanoparticles

ZnO and Aluminum doped ZnO nanoparticles (Al/ZnO NPs) were successfully synthesized by the sol-gel method. Together with the effect of calcination temperatures (200, 300 and 400 °C) and Al dosage (1%, 3%, 5% and 10%) on structural, morphological and optical properties of Al/ZnO NPs, their photocatalytic degradation of methyl orange (MO) dye was investigated. The calcination temperatures at 200, 300 and 400 °C in forming structure of ZnO NPs led to spherical nanoparticle, nanorod and nanoflake structures with a well-crystalline hexagonal wurtzite, respectively. The ZnO NPs calcined at 200 °C exhibited the highest specific surface area and light absorption property, leading to the MO removal efficiency of 80% after 4 h under the Ultraviolet (UV) light irradiation. The MO removal efficiency was approximately two times higher than the nanoparticles calcined at 400 °C. Furthermore, the 5% Al/ZnO NPs exhibited superior MO removal efficiency of 99% in only 40 min which was approximately 20 times enhancement in photocatalytic activity compared to pristine ZnO under the visible light irradiation. This high degradation performance was attributed to the extended light absorption, narrowed band gap and effective suppression of electron-hole recombination through an addition of Al metal.