Long term ageing of polyamide 6 and polyamide 6 reinforced with 30% of glass fibers: temperature effect

Influence of Accelerated Aging on the Fiber-Matrix Adhesion of Regenerated Cellulose Fiber-Reinforced Bio-Polyamide

With regard to the sustainability and biological origin of plastic components, regenerated cellulose fiber (RCF)-reinforced polymers are expected to replace other composites in the future. For use under severe conditions, for example, as a housing in the engine compartment, the resistance of the composites and the impact on the fiber and fiber-matrix adhesion must be investigated. Composites of bio-polyamide with a reinforcement of 20 wt.% RCF were compounded using a twin-screw extruder. The test specimens were manufactured with an injection molding machine and aged under conditions of high humidity at 90% r. H, a high temperature of 70 °C, and water storage using a water temperature of 23 °C for 504 h. Mechanical tests, single-fiber tensile tests (SFTT), single-fibre pull-out tests (SFPT), and optical characterization revealed significant changes in the properties of the composites. The results of the SFPT show that accelerated aging had a significant effect on the bio-polymer and an even stronger effect on the fiber, as the single-fiber tensile strength decreased by 27.5%. Supplementary notched impact strength tests revealed a correlation of the impact strength and the accelerated aging of the RCF-reinforced composites. In addition, it could be verified that the tensile strength also decreased at about 37% due to the aging effect on the RCF and a lowered fiber-matrix adhesion. The largest aging impact was on the Young's modulus with a decrease of 45% due to the accelerated aging. In summary, the results show that the strengthening effect with 20 wt.% RCF was highly decreased subsequent to the accelerated aging due to hydrolysis and debonding because of the shrinkage and swelling of the matrix and fiber. These scientific findings are essential, as it is important to ensure that this bio-based material used in the automotive sector can withstand these stresses without severe degradation. This study provides information about the aging behavior of RCF-reinforced bio-based polyamide, which provides fundamental insights for future research.

Microplastic fibres from synthetic textiles: Environmental degradation and additive chemical content

Microplastic fibres (MPFs) often make up the largest fraction of microplastic pollution in aquatic environments, yet little is known about their degradative fate and persistence. This study investigates the environmentally relevant photodegradation of common MPFs: polyester (PET), polyamide (PA) and polyacrylonitrile (PAN), their respective additive chemical profile, together with their potential for additive leaching. MPFs were subject to ultraviolet (UV) exposure in seawater and freshwater media over 10 months. PET and PA MPFs showed significant fragmentation and surface changes following UV exposure, additionally PA showed evidence of chemical changes. PAN did not undergo significant photodegradation in the same exposure period. Chemicals tentatively identified in MPFs and aqueous leachates via non-target gas chromatography-mass spectrometry include monomers, UV stabilisers and degradation products. Characterisation of several bisphenols (BPs) and benzophenones (BzPs) was performed via ultraperformance liquid chromatography tandem mass spectrometry. Bisphenol A, bisphenol S and benzophenone-3 were quantified in all MPFs and wool at concentrations between 4.3 and 501 ng/g, with wool displaying the highest sum concentration of BPs and BzPs at 863 and 27 ng/g, respectively.