Thermochemical compatibilization of reclaimed tire rubber/ poly(ethylene-co-vinyl acetate) blend using electron beam irradiation and amine-based chemical

Radiation and Radical Grafting Compatibilization of Polymers for Improved Bituminous Binders-A Review

This review scrutinizes current research on new methods for enhancing bituminous binder performance through radiation and radical grafting of polymer modifiers of bitumen. It investigates innovative methods, including using waste polymers as modifiers and applying radiation for polymer grafting, to overcome challenges like high costs, low aging resistance, and storage stability issues, of which separation of phases polymer/bitumen is the most significant obstacle. These advanced modification techniques promise sustainability through the decrease of the carbon footprint of transportation systems by improving the properties and durability of binders. Additionally, this review discusses the parameters and mechanistic aspects from a scientific perspective, shedding light on the underlying processes that contribute to the improved performance of modified bituminous binders.

Radiation Processing of Styrene-isoprene-styrene/Poly(ε-caprolactone) Blends

The irradiation consequences on styrene-isoprene-styrene (SIS)/poly(ε-caprolactone) (PCL) blends are discussed starting from the oxidation initiation. Three characterization methods: chemiluminescence, differential scanning calorimetry and FTIR spectroscopy are applied. The differences that exist between the two components are revealed, when the oxidation rates of the inspected formulas depend on the blending proportion and the degradation conditions. The relevant activation energies characterizing the oxidation strength as well as the kinetic parameters of degradation during the accelerated damaging of blended polymers are related to the inhibition protection of PCL on the faster oxidation of SIS. The interaction between mixed components is revealed by the structural modifications simultaneously accompanied by the competition of formation and decay of radicals.

GTR/Thermoplastics Blends: How Do Interfacial Interactions Govern Processing and Physico-Mechanical Properties?

In this work, GTR/thermoplastics blends (in ratio 50/50 and 75/25 wt.%) were prepared by melt-compounding in an internal mixer. During research, trans-polyoctenamer rubber (TOR), ethylene-vinyl acetate copolymer (EVA), ethylene-octene copolymer (EOC), and linear low-density polyethylene (LLDPE), were used in their thermoplastic phase. Microstructure and processing-performance property interrelationships of the studied materials were investigated by: atomic force microscopy (AFM), scanning electron microscopy (SEM), rubber process analyzer (RPA), Mooney viscometer, plastometer, gas chromatography with mass spectrometry, differential scanning calorimetry (DSC), tensile tests and swelling behavior. In blends of thermoplastics with a high content of GTR (50 and 75 wt.%), the thermoplastic modifier type had a significant impact on the processing behavior and microstructure of blends. In terms of the physico-mechanical properties, the GTR/thermoplastics ratio affected elongation at break, hardness, and density, while its effect on tensile strength was negligible. DSC analysis showed that thermoplastics, as modifiers of GTR, should be considered as binders and not plasticizers, as reflected in the almost constant glass-transition temperature of the blends. RPA measurements indicated higher values of G* and η* for GTR-rich blends. SEM showed a rubber-like interfacial break, while AFM confirmed interfacial contact between GTR and thermoplastics.

Recycling NR/SBR waste using probe sonication as a new devulcanizing method; study on influencing parameters

In this work, a vulcanized blend of natural rubber (NR) and styrene butadiene rubber (SBR) (i.e. at weight ratio of 50 : 50) as a model for tire rubber was devulcanized using probe sonication. The effect of processing parameters such as sonication media, power, temperature and time on sol/gel contents and devulcanization percent of rubbery samples was investigated. Moreover, the influence of pre-immersion of vulcanized NR/SBR samples in different liquids (i.e. water, oil and toluene) was assessed for different sonication times (i.e. 10 to 60 min) and powers (i.e. 30 to 60 W). It was found that pre-immersion of rubber particles in oil significantly increased the devulcanization percent. The optimum conditions for devulcanization of the NR/SBR blend via probe sonication were found to be 60 Watts, 20 min, oil and 24 h for sonication power, sonication time, pre-immersion/sonication media and pre-immersion time, respectively. The highest obtained devulcanization percent in this step was about 40%. The effects of two devulcanizing chemical agents (i.e. diphenyl disulfide and VitaX) on devulcanization performances of the samples were also studied. Results showed that higher devulcanization percent (i.e. about 52%) was obtained by using VitaX. It was also observed that VitaX significantly improved re-vulcanization speed (i.e. cure rate index) and decreased scorch time. It was also found that lower content of VitaX (i.e. 0.6 phr) caused better curing properties but lower mechanical properties compared to the higher content (i.e. 1.2 phr).

In this work, a vulcanized blend of natural rubber (NR) and styrene butadiene rubber (SBR) (i.e. at weight ratio of 50 : 50) as a model for tire rubber was devulcanized using probe sonicationP.