Proliferation and osteogenic differentiation of mesenchymal stem cells on three-dimensional scaffolds made by thermal sintering method

Printable hyaluronic acid hydrogel functionalized with yeast-derived peptide for skin wound healing

Targeted delivery of bioactive agents, growth factors, and drugs to skin wounds is a growing trend in biomaterials development for wound healing. This study presents a printable hyaluronic acid (HA) based hydrogel to deliver yeast-derived ACE-inhibitory peptide of VLSTSFPPW (VW-9) to the wound site. We first conjugated tyramine (Ty) on the carboxyl groups of the HA to form a phenol-functionalized HA (HA-Ty); then, the carboxylic acid groups of HA-Ty were aminated with ethylenediamine (HA-Ty-NH₂). The primary amine groups of the HA-Ty-NH₂ could then react with the carboxylic acids of the peptide. The hydrogel was then 3D printed and crosslinked with visible light. The modification of HA was confirmed by ¹H NMR and FTIR. The swelling capacity of the conjugated hydrogels was 1.5-fold higher compared to the HA-Ty-NH₂ hydrogel. The conjugated peptide did not affect on rheological properties and morphology of the hydrogels. The 3T3-L1 fibroblast cells seeded on the peptide-modified hydrogels exhibited higher viability than the hydrogels without the peptide, indicating that the peptide-enriched hydrogels may have the potential for wound healing applications.

Elastomeric Trilayer Substrates with Native-like Mechanical Properties for Heart Valve Leaflet Tissue Engineering

Heart valve leaflets have a complex trilayered structure with layer-specific orientations, anisotropic tensile properties, and elastomeric characteristics that are difficult to mimic collectively. Previously, trilayer leaflet substrates intended for heart valve tissue engineering were developed with nonelastomeric biomaterials that cannot deliver native-like mechanical properties. In this study, by electrospinning polycaprolactone (PCL) polymer and poly(l-lactide-co-ε-caprolactone) (PLCL) copolymer, we created elastomeric trilayer PCL/PLCL leaflet substrates with native-like tensile, flexural, and anisotropic properties and compared them with trilayer PCL leaflet substrates (as control) to find their effectiveness in heart valve leaflet tissue engineering. These substrates were seeded with porcine valvular interstitial cells (PVICs) and cultured for 1 month in static conditions to produce cell-cultured constructs. The PCL/PLCL substrates had lower crystallinity and hydrophobicity but higher anisotropy and flexibility than PCL leaflet substrates. These attributes contributed to more significant cell proliferation, infiltration, extracellular matrix production, and superior gene expression in the PCL/PLCL cell-cultured constructs than in the PCL cell-cultured constructs. Further, the PCL/PLCL constructs showed better resistance to calcification than PCL constructs. Trilayer PCL/PLCL leaflet substrates with native-like mechanical and flexural properties could significantly improve heart valve tissue engineering.

Designing Nanofibrous Poly(ε-caprolactone)/Hydroxypropyl Cellulose/Zinc Oxide/Melilotus Officinalis Wound Dressings Using Response Surface Methodology

Nanofibrous wound dressing is one of the most prominent stratagems for wound caring/management. This research is an approach for designing an electrospun wound dressing based on poly(ε-caprolactone)/hydroxypropyl cellulose/zinc oxide nanoparticles (PCL/HPC/n-ZnO), in which response surface methodology (RSM) was utilized to ascertain the optimum sample. It was observed that the addition of n-ZnO and Melilotus Officinalis (MO) extract could increase the fibers mean diameter, pore size, and crystallinity of mats. The mentioned quantities for a sample with the highest MO content (PHZM10) were equal to 469±105 nm, 544±370 nm, and 49.67%, respectively. Moreover, enhancing the amount of MO led to an increase in mechanical properties. In this respect, the PHZM10 sample had the modulus, strength, and toughness of 82.41±0.61, 20.45±0.30 MPa, and 4194.86 mJ, respectively. Also, according to the MTT assay, no cytotoxicity was reported from any of the manufactured samples. Besides, it was concluded that the antibacterial activity and nanofibrous structure of mats, and also their potential for release of MO extract could accelerate the wound healing. Hence, the wound closure index for the PHZM10 group was 99.3±1.1%. Based on all noted results, the PCL/HPC/n-ZnO/MO electrospun mats can be proposed as reassuring wound dressing candidates.