Synthesis and evaluation of a novel co-initiator for dentin adhesives: polymerization kinetics and leachables study

Insight into the development of versatile dentin bonding agents to increase the durability of the bonding interface

Despite the huge improvements made in adhesive technology over the past 50 years, there are still some unresolved issues regarding the durability of the adhesive interface. A complete sealing of the interface between the resin and the dentin substrate remains difficult to achieve, and it is doubtful whether an optimal interdiffusion of the adhesive system within the demineralized collagen framework can be produced in a complete and homogeneous way. In fact, it is suggested that hydrolytic degradation, combined with the action of dentin matrix enzymes, destabilizes the tooth-adhesive bond and disrupts the unprotected collagen fibrils. While a sufficient resin–dentin adhesion is usually achieved immediately, bonding efficiency declines over time. Thus, here, a review will be carried out through a bibliographic survey of scientific articles published in the last few years to present strategies that have been proposed to improve and/or develop new adhesive systems that can help prevent degradation at the adhesive interface. It will specially focus on new clinical techniques or new materials with characteristics that contribute to increasing the durability of adhesive restorations and avoiding the recurrent replacement restorative cycle and the consequent increase in damage to the tooth.

How Water Content Can Influence the Chemomechanical Properties and Physical Degradation under Aging of Experimental Adhesives

Objective

To evaluate the physicochemical (sorption (SOR), solubility (SOL), and degree of conversion (DC)) and mechanical (flexural strength (FS), modulus of elasticity (ME), and compressive strength (CS)) properties of adhesives with different water contents (D₂O).

Materials and Methods

An adhesive was formulated: 55 wt% BisGMA, 45 wt% HEMA, 0.5 wt% camphorquinone, 0.5 wt% EDMAB, and 1.0 wt% DPIHP. D₂O was added into the adhesives (0 wt%, 10 wt%, and 16 wt%). DC was monitored through the FTIR. FS, ME, CS, SOR, and SOL were tested. The adhesive samples were aged in deionized water, ethanol, and acetone. Data were submitted to ANOVA and Tukey's tests (5%).

Results

For DC, the 0 wt% group showed a significant reduction (68.09 ± 0.14_A) compared with the 10 wt% (87.07 ± 0.81_B) and 16 wt% groups (89.87 ± 0.24_B); 10 wt% showed the highest FS (MPa) mean values (141.6 ± 6.71_B) compared with the 0 wt% (109.4 ± 20.5_A) and 16 wt% (107.8 ± 15.8_A). For the CS (MPa) and ME (GPa), the 16 wt% showed the lowest mean values (98.8 ± 18.0_B and 2.2 ± 0.3_B, respectively) compared with the 10 wt% and 0 wt%. For the SOR, 16 wt% of water showed the highest mean values and the ethanol showed the lowest mean values of SOL regardless of water content.

Conclusion

The amount of water content and the types of aging solvents significantly affect the adhesive properties.

Light-cured hyaluronic acid composite hydrogels using riboflavin as a photoinitiator for bone regeneration applications

Objective

Self-healing of bone from damage caused by infection, trauma, or surgical removal of cysts is limited. Generally, external intervention is needed to increase bone repair and regeneration. In this study, biocompatible light-cured hyaluronic acid hydrogels loaded with nano-hydroxyapatite and chitosan were prepared using a new photoinitiating system based on riboflavin for bone regeneration applications.

Method

Four light-cured hydrogel groups were prepared as follows: Group I, a control group with no additions; Group II, loaded with nano-hydroxyapatite; Group III, loaded with chitosan; and Group IV, loaded with both nano-hydroxyapatite and chitosan. The new photoinitiating system consisted of riboflavin as a photoinitiator, dimethylaminoethyl methacrylate (DMAEMA) as a coinitiator (being used with riboflavin for the first time), and diphenyliodonium chloride as an accelerator. For each group, X-ray-diffraction, surface morphology by scanning electron microscope, mechanical properties, water uptake (%), and cell viability (%) were tested. The osteogenic potential was then tested in a rabbit model, and histomorphometric assessment was conducted.

Results

In the four groups, the light-cured hydrogels were obtained after a short irradiation time of 10 s using a dental light-curing unit. The prepared hydrogels were biocompatible. Simultaneous addition of nano-hydroxyapatite and chitosan increased the mechanical properties threefold and the osteogenic potential, twofold, with a statistically significant difference compared with the control group.

Conclusions

Light-cured hyaluronic acid composite hydrogels loaded with nano-hydroxyapatite and chitosan—prepared by using the new photoinitiating system—are promising materials that can be used in bone regeneration applications.

Methacrylate-functionalized proanthocyanidins as novel polymerizable collagen cross-linkers - Part 2: Effects on polymerization, microhardness and leaching of adhesives

OBJECTIVE

The aim of the study was to investigate the effects of a novel polymerizable collagen cross-linker methacrylate-functionalized proanthocyanidins (MAPA) on the polymerization, microhardness and leaching of a HEMA-based experimental dental adhesive system.

METHODS

Three MAPAs were synthesized using different methacrylate (MA) to proanthocyanidins (PA) feeding ratios of 1:2, 1:1, and 2:1 to obtain MAPA-1, MAPA-2, and MAPA-3, respectively. The resulting three MAPAs and PA were added to an experimental adhesive formulated with HEMA and a tri-component photoinitiator system (0.5 wt% CQ/EDMAB/DPIHP) at 1%, 5% and 10% MAPA or PA concentrations (wt%). The adhesive polymerization kinetics was measured continuously in real-time for 10 min using a Fourier-transform infrared spectroscopy (FTIR) with an attenuated total reflectance (ATR) accessory. Degree of conversion (DC) and Vickers microhardness (MH) of cured adhesives were measured at 72 h post-cure. The leaching of cured adhesives in DI water was monitored using UV-vis spectrophotometer. Statistical analysis was performed using one-way and two-way ANOVA, Tukey's (p < 0.05).

RESULTS

The adhesive formulations with 1%, 5% and 10% MAPAs-1, -2, -3 all generated higher rate of polymerization and 10-min DC than the formulations with PA at the same concentrations. At 72 h post-cure, the adhesive formulation with 5% MAPA-2 exhibited significantly higher DC (99.40%) and more than doubled MH (18.93) values than the formulation with 5% PA (DC = 89.47%, MH = 8.41) and the control (DC = 95.46%, MH = 9.33). Moreover, the cured adhesive with 5% MAPA-2 demonstrated significantly reduced PA leaching in comparison with cured adhesive with 5% PA.

SIGNIFICANCE

Synthesized MAPA is a novel class of polymerizable collagen cross-linker that not only stabilizes dentin collagen via its PA component, but also improves polymerization, mechanical properties and stability of HEMA-based adhesives via its MA component. By inheriting the benefit while overcoming the drawback of PA, MAPA offers a revolutionary solution for improved bond-strength and longevity of dental restorations.

Cytotoxicity and genotoxicity of DMABEE, a co-photoinitiator of resin polymerization, on CHO-K1 cells: Role of redox and carboxylesterase

The 4-dimethylaminobenzoic acid ethyl ester (DMABEE) is an important co-initiator for resin polymerization in dental resinous materials. As a radical forming chemical with high lipophilicity, the genotoxicity and cytotoxicity of DMABEE deserve prudent investigation. In this study, we found that DMABEE reduced the viability and proliferation of Chinese hamster ovary (CHO-K1) cells in a dose-dependent manner, and altered cell morphology at higher concentrations. G0/G1 cell cycle arrest was induced by DMABEE at 0.25-0.75 mM, and cell proportion of sub-G0/G1 phase was significantly elevated at 1 mM while cell apoptosis was observed. Genotoxic effect was noted when cells were treated by 0.1 mM DMABEE, as revealed by increase of micronucleus formation. Reactive oxygen species overproduction was observed as cells treated with 0.75 and 1 mM, while elevation of intracellular glutathione was noticeable since 0.1 mM. Contrary to our expectation, pretreatment by N-acetyl-l-cysteine enhanced the toxicity of DMABEE on CHO-K1 cells. Catalase mildly reduced the toxic effect and carboxylesterase showed obvious ability to reverse the toxicity of DMABEE. These findings highlight the mechanism of DMABEE toxicity and provide clues for safety improvement of its application in clinical dental treatment.

Multifunctional monomer acts as co-initiator and crosslinker to provide autonomous strengthening with enhanced hydrolytic stability in dental adhesives

OBJECTIVE

The purpose of this study was to evaluate a new synthesized multifunctional monomer, aminosilane functionalized methacrylate (ASMA), containing polymerizable methacrylate, tertiary amine, and methoxysilane functionalities in dental adhesive formulations, and to investigate the polymerization kinetics, leachates, thermal and mechanical properties of copolymers.

METHODS

Adhesive contained HEMA/BisGMA (45/55, w/w) was used as a control, and mixtures based on HEMA/BisGMA/ASMA at the mass ratio of 45/(55-x)/x were used as experimental adhesive. Adhesives were characterized with regard to water miscibility, photo-polymerization behavior (Fourier transform infrared spectroscopy, FTIR), leached co-monomers (high performance liquid chromatography, HPLC), thermal properties (modulated differential scanning calorimeter, MDSC), and mechanical properties (dynamic mechanical analyzer, DMA). Stress relaxation times and the corresponding moduli, obtained from stress relaxation tests, are used in a simulated linear loading case.

RESULTS

As compared to the control, ASMA-containing adhesives showed higher water miscibility, lower viscosity, improved monomer-to-polymer conversion, significantly greater T_g and rubbery modulus. HPLC results indicated a substantial reduction of leached HEMA (up to 85wt%) and BisGMA (up to 55wt%) in ethanol. The simulation reveals that the ASMA-containing adhesive becomes substantially stiffer than the control.

SIGNIFICANCE

ASMA monomer plays multiple roles, i.e. it serves as both a co-initiator and crosslinker while also providing autonomous strengthening and enhanced hydrolytic stability in the adhesive formulations. This multifunctional monomer offers significant promise for improving the durability of the adhesive at the composite/tooth interface.

Resin based restorative dental materials: characteristics and future perspectives

This review article compiles the characteristics of resin based dental composites and an effort is made to point out their future perspectives. Recent research studies along with few earlier articles were studied to compile the synthesis schemes of commonly used monomers, their characteristics in terms of their physical, mechanical and polymerization process with selectivity towards the input parameters of polymerization process. This review covers surface modification processes of various filler particles using silanes, wear behaviour, antimicrobial behaviour along with its testing procedures to develop the fundamental knowledge of various characteristics of resin based composites. In the end of this review, possible areas of further interests are pointed out on the basis of literature review on resin based dental materials.

Structure-property relationships for wet dentin adhesive polymers

Dentin adhesive systems for composite tooth restorations are composed of hydrophilic/hydrophobic monomers, solvents, and photoinitiators. The adhesives undergo phase separation and concomitant compositional change during their application in the wet oral environment; phase separation compromises the quality of the hybrid layer in the adhesive/dentin interface. In this work, the adhesive composition in the hybrid layer can be represented using the phase boundaries of a ternary phase diagram for the hydrophobic monomer/hydrophilic monomer/water system. The polymer phases, previously unaccounted for, play an important role in determining the mechanical behavior of the bulk adhesive, and the chemomechanical properties of the phases are intimately related to the effects produced by differences in the hydrophobic-hydrophilic composition. As the composition of the polymer phases varies from hydrophobic-rich to hydrophilic-rich, the amount of the adsorbed water and the nature of polymer-water interaction vary nonlinearly and strongly correlate with the change in elastic moduli under wet conditions. The failure strain, loss modulus, and glass transition temperature vary nonmonotonically with composition and are explained based upon primary and secondary transitions observed in dynamic mechanical testing. Due to the variability in composition, the assignment of mechanical properties and the choice of suitable constitutive models for polymer phases in the hybrid layer are not straightforward. This work investigates the relationship between composition and chemomechanical properties of the polymer phases formed on the water-adhesive phase boundary using quasistatic and dynamic mechanical testing, mass transfer experiments, and vibrational spectroscopy.

Piperonyl methacrylate: Copolymerizable coinitiator for adhesive compositions

OBJECTIVES

This study describes the synthesis of piperonyl methacrylate (PipM) and evaluates its effect when used as coinitiator in the photoinitiated radical polymerization of experimental adhesive resins.

METHODS

PipM was synthetized through an esterification reaction and characterized by FTIR and ¹H NMR spectroscopy. Adhesive resins containing camphorquinone as photoinitiator and PipM or ethyl-4-dimethyl amine benzoate (EDAB) as coinitiators were formulated. Scotchbond Multipurpose (SBMP) adhesive was used as commercial reference. All materials were analyzed for polymerization kinetics, flexural strength, elastic modulus, water sorption/solubility, shear bond strength to bovine enamel and dentin, characterization of hybrid layer by scanning electron microscopy (SEM), microbiological direct contact test, and cytotoxicity.

RESULTS

The adhesive with PipM presented higher degree of conversion and lower sorption/solubility when compared with other groups. Shear bond strength to enamel and dentin were similar for PipM and EDAB materials. The percentage of cellular viability was close to 100% and similar in the experimental groups and the commercial reference.

CONCLUSIONS

PipM presented similar or superior performance to the tertiary amine used as control, representing a potential alternative coinitiator for photopolymerizable dental materials.

CLINICAL SIGNIFICANCE

PipM could be potentially useful in the formulations of adhesive systems with enhanced chemical properties, which could mean improvement in the longevity of composite resin restorations.

Modulating pH through lysine integrated dental adhesives

OBJECTIVES

The objective of this study was to explore the effect of lysine integration to dental adhesives with respect to the polymerization kinetics, neutralization capacities in the acidic microenvironment, dynamic mechanical properties, and thermal properties.

MATERIALS AND METHOD

Lysine was incorporated into liquid resin formulations at 2.5 and 5.0wt % with additional water/ethanol co-solvents. The co-monomer system contained 2-hydroxyethyl-methacrylate (HEMA) and Bisphenol A glycerolate dimethacrylate (BisGMA) with a mass ratio of 45/55. The kinetics of photopolymerization, neutralization capacities, lysine-leaching, dynamic mechanical properties and thermal properties of the control and experimental adhesives were analyzed.

RESULTS

The degree of conversion of the experimental adhesive was increased substantially at 2.5wt% lysine as compared to the control. The experimental polymers provided acute neutralization of the acidic microenvironment. Approximately half of the lysine was released from the polymer network within one month. Under dry conditions and physiologic temperatures, the incorporation of lysine did not compromise the storage modulus. Comparison of the thermal properties suggests that the more compact structure of the control adhesive inhibits movement of the polymer chains resulting in increased T_g.

SIGNIFICANCE

Incorporating lysine in the adhesive formulations led to promising results regarding modulating pH, which may serve as one aspect of a multi-spectrum approach for enhancing the durability of composite restorations. The results provide insight and lay a foundation for incorporating amino acids or peptides into adhesive formulations for pH modulation or desired bioactivity at the interfacial margin between the composite and tooth.

Photoinitiators in Dentistry: Challenges and Advances

Photopolymerization is used in a wide range of clinical applications in dentistry and the demand for dental materials that can restore form, function and esthetics is increasing rapidly. Simultaneous with this demand is the growing need for photoinitiators that provide effective and efficient in situ polymerization of dental materials using visible light irradiation. This chapter reviews the fundamentals of Type I and II photoinitiators. The advantages and disadvantages of these photoinitiators will be considered with a particular focus on parameters that affect the polymerization process in the oral cavity. The chapter examines recent developments in photoinitiators and opportunities for future research in the design and development of photoinitiators for dental applications. Future research directions that employ computational models in conjunction with iterative synthesis and experimental methods will also be explored in this chapter.

Fabrication of hybrid crosslinked network with buffering capabilities and autonomous strengthening characteristics for dental adhesives

Ingress of bacteria and fluids at the interfacial gaps between the restorative composite biomaterial and the tooth structure contribute to recurrent decay and failure of the composite restoration. The inability of the material to increase the pH at the composite/tooth interface facilitates the outgrowth of bacteria. Neutralizing the microenvironment at the tooth/composite interface offers promise for reducing the damage provoked by cariogenic and aciduric bacteria. We address this problem by designing a dental adhesive composed of hybrid network to provide buffering and autonomous strengthening simultaneously. Two amino functional silanes, 2-hydroxy-3-morpholinopropyl (3-(triethoxysilyl)propyl) carbamate and 2-hydroxy-3-morpholinopropyl (3-(trimethoxysilyl)propyl) carbamate were synthesized and used as co-monomers. Combining free radical initiated polymerization (polymethacrylate-based network) and photoacid-induced sol-gel reaction (polysiloxane) results in the hybrid network formation. Resulting formulations were characterized with regard to real-time photo-polymerization, water sorption, leached species, neutralization, and mechanical properties. Results from real-time FTIR spectroscopic studies indicated that ethoxy was less reactive than methoxy substituent. The neutralization results demonstrated that the methoxy-containing adhesives have acute and delayed buffering capabilities. The mechanical properties of synthetic copolymers tested in dry conditions were improved via condensation reaction of the hydrolyzed organosilanes. The leaching from methoxy containing copolymers was significantly reduced. The sol-gel reaction provided a chronic and persistent reaction in wet condition-performance that offers potential for reducing secondary decay and increasing the functional lifetime of dental adhesives.

STATEMENT OF SIGNIFICANCE

The interfacial gaps between the restorative composite biomaterial and the tooth structure contributes to recurrent decay and failure of the composite restoration. The inability of the material to increase the pH at the composite/tooth interface facilitates the outgrowth of more cariogenic and aciduric bacteria. This paper reports a novel, synthetic resin that provides buffering capability and autonomous strengthening characteristics. In this work, two amino functional silanes were synthesized and the effect of alkoxy substitutions on the photoacid-induced sol-gel reaction was investigated. We evaluated the neutralization capability (monitoring the pH of lactic acid solution) and the autonomous strengthening property (monitoring the mechanical properties of the hybrid copolymers under wet conditions and quantitatively analyzing the leachable species by HPLC). The novel resin investigated in this study offers the potential benefits of reducing the risk of recurrent decay and prolonging the functional lifetime of dental adhesives.

Biophysical characterization of functionalized titania nanoparticles and their application in dental adhesives

It is demonstrated that carboxylic acid-functionalized titanium dioxide (TiO₂) NPs produce significantly higher levels of reactive oxygen species (ROS) after visible light irradiation (400-800nm, 1600mW/cm²) in comparison to nonfunctionalized TiO₂ NPs. The level of ROS produced under these irradiation conditions was not capable of generating oxidatively induced DNA damage in a cell-free system for TiO₂ concentrations of 0.5mg/L or 5mg/L. In addition, specific incorporation of the acrylic acid-functionalized TiO₂ NPs into dental composites allowed us to utilize the generated ROS to enhance photopolymerization (curing and degree of vinyl conversion (DC)) of resin adhesives and create mechanically superior and biocompatible materials for dental applications. Incorporation of the TiO₂ NPs into selected dental composites increased the mean DC values by ≈7%. The modified TiO₂ materials and dental composite materials were extensively characterized using thermogravimetric analysis, electron microscopy, Fourier transform infrared spectroscopy, and electron paramagnetic resonance. Notably, dental adhesives incorporated with acrylic acid-functionalized TiO₂ NPs produced stronger bonds to human teeth following visible light curing in comparison to traditional dental adhesives not containing NPs with an increase in the shear bond strength of ≈29%. In addition, no leaching of the incorporated NPs was detectable from the dental adhesives after 2500 thermal cycles using inductively coupled plasma-optical emission spectroscopy, indicating that biocompatibility of the adhesives was not compromised after extensive aging. These findings suggest that NP-induced ROS may be useful to produce enhanced nanocomposite materials for selected applications in the medical device field.

STATEMENT OF SIGNIFICANCE

Titanium dioxide nanoparticles (TiO₂ NPs) have unique photocatalytic, antibacterial and UV-absorbing properties that make them beneficial additives in adhesives and composites. However, there is concern that the reactive oxygen species (ROS) produced by photoactivated TiO₂ NPs might pose toxicological risks. We demonstrate that it is possible to incorporate acid-functionalized TiO₂ NPs into dental resins which can be applied as dental adhesives to human teeth. The ROS generated by these NPs through visible-light irradiation may be utilized to increase the degree of vinyl conversion of resins, leading to adhesives that have an enhanced shear-bond strength to human teeth. Investigation into the potential genotoxicity of the NPs and their potential for release from dental composites indicated a low risk of genotoxic effects.

Probing the dual function of a novel tertiary amine compound in dentin adhesive formulations

OBJECTIVES

A novel tertiary amine compound containing three methacrylate-urethane groups was synthesized for application in dentin adhesives. The synthesis, photopolymerization kinetics, and leaching were examined in an earlier study using this novel compound as the co-initiator (0.5 and 1.75wt% based on the total resin mass). The objective of this work was to investigate the potential of TUMA (8-(2-(((2-(methacryloyloxy)ethyl)carbamoyl)oxy)propyl)-6,10-dimethyl-4,12-dioxo-5,11-dioxa-3,8,13-triazapentadecane-1,15-diyl bis(2-methylacrylate)) to serve simultaneously as a co-initiator and co-monomer (15-45wt% based on the total resin mass) in dentin adhesive formulations. The polymerization kinetics, water sorption and dynamic mechanical properties of these novel formulations were determined.

MATERIALS AND METHOD

The monomer system contained Bisphenol A glycerolate dimethacrylate (BisGMA), 2-hydroxyethylmethacrylate (HEMA) and TUMA (synthesized in our lab) at the mass ratio of 45/(55-x)/x. Two photoinitiator (PI) systems were compared. One initiator system contains three components: camphorquinone (CQ), diphenyliodonium hexafluorophosphate (DPIHP) and ethyl-4-(dimethylamino) benzoate (EDMAB) and the second initiator system contains CQ and DPIHP. The control adhesive formulations are: C0-3: HEMA/BisGMA 45/55 (w/w) and 3-component PI and C0-2: HEMA/BisGMA 45/55 (w/w) and 2-component PI. These controls were used as a comparison to the experimental adhesive resins (Ex-3 or Ex-2), in which x represents the weight percentage of synthesized co-monomer (TUMA) to replace part of BisGMA. The control and experimental adhesive formulations were photo-polymerized and compared with regard to the degree of conversion (DC), polymerization rate (Rp), water sorption and dynamic mechanical analysis (DMA) under both dry and wet conditions.

RESULTS

C0-3 and Ex-3 formulations had similar DC, while the DC of Ex-2 formulation was higher than C0-2. The DC was similar when comparing the two- component with the three-component photoinitiator system when TUMA was used at the same concentration. DMA under dry conditions shows higher rubbery storage modulus for all experimental formulations, while storage modulus at rubbery region under wet conditions was decreased as compared with control (C0-3). There was no statistically significant difference for the DMA results under both dry and wet conditions when comparing two- and three-component initiator systems with the same TUMA concentration.

SIGNIFICANCE

The newly synthesized TUMA could serve simultaneously as a co-monomer and co-initiator in the absence of commercial co-initiator. This study provides information for the future development of new co-monomer/co-initiator for dentin adhesives and dental composites.

Effect of crosslinking density of polymers and chemical structure of amine-containing monomers on the neutralization capacity of dentin adhesives

OBJECTIVES

Neutralization of the acidic micro-environment at the tooth/material interface is expected to provide enhanced durability for dental composite restorations. The objective of this study is to explore the effect of amine-containing monomer formulations and the crosslinking density of the resultant polymers on the neutralization capacity.

MATERIALS AND METHODS

The co-monomer system was varied systematically to obtain different proportions of Bisphenol A glycerolate dimethacrylate (BisGMA) and 2-hydroxyethyl methacrylate (HEMA), while maintaining a constant amount of amine-containing methacrylate monomer. A series of amine-containing monomers covering a range of pKa values were examined. Crosslinking density of formed copolymers was controlled by adjusting the weight content of the dimethacrylate monomer BisGMA. Lactic acid (LA) was used as a probe to analyze the effectiveness of the basic polymers to neutralize acid. The neutralization capacity of each amine-containing crosslinked copolymer was characterized by measuring pH as a function of time when the specimens were soaked in 1-mM LA solution, and the results were compared to the control formulations composed solely of BisGMA and HEMA. Polymer surfaces were examined using the methyl orange (MO) assay to quantify the amount of accessible amine groups.

RESULTS

For each amine-containing crosslinked co-polymer, the neutralization capacity is enhanced by decreasing crosslinking density (e.g., by reducing BisGMA concentration in the formulation). In addition, more amine groups were accessible when crosslinking density was decreased. For different amine-containing polymers with the same BisGMA concentration, the neutralization capacity is higher when the amino monomers with higher pKa values were used in the formulations.

SIGNIFICANCE

This is the first time that the neutralization capacity based on crosslinked dental polymers has been studied. The information is important for future development of durable dentin adhesives.

Synthesis of fluorinated dimethacrylate monomer and its application in preparing Bis-GMA free dental resin

With the aim to reduce human exposure to Bis-phenol A derivatives, a novel fluorinated dimethacrylate monomer FUDMA was synthesized and mixed with triethyleneglycol dimethacrylate (TEGDMA) to prepare 2,2-bis[4-(2-hydroxy-3-methacryloy- loxypropyl)phenyl]propane (Bis-GMA) free dental resin system. Physicochemical properties, such as double bond conversion (DC), polymerization shrinkage (VS), water sorption (WS) and solubility (SL), flexural strength (FS) and modulus (FM), and fracture energy of FUDMA/TEGDMA resin system were investigated. Bis-GMA/TEGDMA resin system was used as a control. The results showed that, compared with Bis-GMA/TEGDMA resin system, FUDMA/TEGDMA had advantages like higher DC, lower VS, and higher fracture energy, but had no disadvantages. Therefore, FUDMA/TEGDMA resin system had better comprehensive physicochemical properties than Bis-GMA/TEGDMA resin system, and FUDMA had potential to be used as a substitute for Bis-GMA.