Effect of Acid, Alkali and Alkali–Acid Treatment on Physicochemical and Bioactive Properties of Hydroxyapatite Derived from Catla catla Fish Scales

Preparation and Characterization of Acrylonitrile Butadiene Rubber Reinforced with Bio-Hydroxyapatite from Fish Scale

This work aims to enhance the mechanical properties, oil resistance, and thermal properties of acrylonitrile butadiene rubber (NBR) by using the Nile tilapia fish scales as a filler and using bis(triethoxysilylpropyl)tetrasulfide (TESPT) as a coupling agent (CA). The prepared fish scale particles (FSp) are B-type hydroxyapatite and the particle shape is rod-like. The filled NBR with FSp at 10 phr increased tensile strength up to 180% (4.56 ± 0.48 MPa), reduced oil absorption up to 155%, and increased the decomposition temperature up to 4 °C, relative to the unfilled NBR. The addition of CA into filled NBR with FSp at 10 phr increased tensile strength up to 123% (5.62 ± 0.42 MPa) and percentage of elongation at break up to 122% relative to the filled NBR with FSp at 10 phr. This work demonstrated that the prepared FSp from the Nile tilapia fish scales can be used as a reinforcement filler to enhance the NBR properties for use in many high-performance applications.

Nano-Hydroxyapatite from White Seabass Scales as a Bio-Filler in Polylactic Acid Biocomposite: Preparation and Characterization

Nano-hydroxyapatite (nHAp) as a bio-filler used in PLA composites was prepared from fish by acid deproteinization (1DP) and a combination of acid-alkali deproteinization (2DP) followed by alkali heat treatment. Moreover, the PLA/nHAp composite films were developed using solution casting method. The mechanical and thermal properties of the PLA composite films with nHAp from different steps deproteinization and contents were compared. The physical properties analysis confirmed that the nHAp can be prepared from fish scales using both steps deproteinization. 1DP-nHAp showed higher surface area and lower crystallinity than 2DP-nHAp. This gave advantage of 1DP-nHAp for use as filler. PLA composite with 1DP-nHAp gave tensile strength of 66.41 ± 3.63 MPa and Young’s modulus of 2.65 ± 0.05 GPa which were higher than 2DP-nHAp at the same content. The addition of 5 phr 1DP-nHAp into PLA significantly improved the tensile strength and Young’s modulus. PLA composite solution with 1DP-nHAp at 5 phr showed electrospinnability by giving continuous fibers without beads.

Biodegradable Composite Nanofiber Containing Fish-Scale Extracts

A biodegradable composite nanofiber containing polyhydroxyalkanoate (PHA) or modified PHA (MPHA) and treated fish-scale powder (TFSP) was prepared and characterized. The powder (20-80 nm) was prepared by grinding after treating FSP with water, acid, and heat (450 °C) to yield the TFSP. Composite nanofibers (100-500 nm long) of TFSP/PHA and TFSP/MPHA were fabricated by electrospinning using a biaxial feed method. The TFSP, which had a high hydroxyapatite content, was suitable as a filler for composites. The Ca/P ratio of the TFSP was similar to that of the human bone. Particle size analysis and analysis of scanning electron microscopy images indicated that, compared with the PHA/TFSP composite, the MPHA/TFSP nanofibers were more uniform and bonded more strongly in the matrix. The tensile strength at failure of the MPHA/TFSP specimens was enhanced and increased with increasing TFSP content. The elongation at failure was lower and decreased with increasing TFSP concentration. The water contact angle decreased with increasing TFSP content in PHA/TFSP and MPHA/TFSP nanofiber membranes. The TFSP enhanced the hydrophilic effect of the PHA/TFSP and MPHA/TFSP nanofiber membranes and provided a more suitable environment for cell growth. This composite nanofiber has potential in many biomedical applications.

S. N. SN, Sagadevan S, Hoque ME, Kulandaivelu R. Advanced lithium substituted hydroxyapatite nanoparticles for antimicrobial and hemolytic studies

In this study, pure hydroxyapatite (HAP) and lithium substituted hydroxyapatite (Li-HAP) nanoparticles were synthesized by a sonochemical synthesis process and investigated for their antimicrobial and hemolytic activities.