How Stable is Dentin As a Substrate for Bonding?

The evolution of adhesive dentistry: From etch-and-rinse to universal bonding systems

OBJECTIVES

This review aimed at presenting the mechanisms and pitfalls of adhesion to enamel and dentin, advances in the materials science and in the development of strategies to improve hybrid layer (HL) longevity.

METHODS

Search of the literature was performed on PubMed, Scopus and Web of Science with keywords related to the structure of the dental substrate, HL degradation mechanisms and strategies to contrast them.

RESULTS

Albeit the advances in the dental materials' properties, HL degradation is still a relevant and current issue in adhesive dentistry. However, adhesive materials have become more resistant and less operator sensitive, and good adhesion is currently in the hands of every practitioner. Numerous novel strategies are being developed, able to improve the resistance of adhesive resins to degradation, their ability to infiltrate and chemically bond to dentin, to remove the unbound/residual water within the HL, reinforce the dentin collagen matrix, and inhibit endogenous metalloproteinases. Many of the strategies have turned to nature in search for powerful biomodifying compounds, and for the inspiration as to mimic naturally occurring regenerative processes.

SIGNIFICANCE

Extensive knowledge on the structure of the dental substrate and the complexity of adhesion to dentin has led to the development of improved formulations of dental adhesives and numerous valid strategies to improve the strength and longevity of the HL. Nevertheless, for many of them the road from bench to chairside still seems long. We encourage practitioners to know their materials well and use the strategies readily available to them.

Effects of proanthocyanidin-functionalized hydroxyapatite nanoparticles on dentin bonding

OBJECTIVES

To evaluate the effect of proanthocyanidin-functionalized hydroxyapatite nanoparticles (nHAp_PA) used as pretreatment at different concentrations on the microtensile bond strength (µTBS) and endogenous enzymatic activity (MMPs) on pH-cycled dentin after 24 h and 6 months of artificial aging.

MATERIALS AND METHODS

Fifty human sound dentin blocks were randomly assigned to 5 groups (n = 10): (i) negative control (no treatment); (ii) positive control (pH-cycling); (iii) pH-cycling + 2% nHAp_PA for 60s; (iv) pH-cycling + 6.5% nHAp_PA for 60s; (v) pH-cycling + 15% nHAp_PA for 60s. A self-etch adhesive was used for bonding procedures before resin composite build-ups. Specimens were tested with the µTBS test after 24 h and 6 months of laboratory storage. The proteolytic activity in each group was evaluated with gelatin zymography and in situ zymography. Data were statistically analyzed (p < 0.05).

RESULTS

At 24 h, the µTBS of the experimental groups were significantly higher than the controls (p ≤ 0.001), and no differences were observed between different concentrations (p > 0.05). Artificial aging significantly decreased bond strength in all groups (p ≤ 0.008); however, nHAp_PA 2% still yielded higher bonding values than controls (p ≤ 0.007). The groups pretreated with nHAp_PA exhibited lower MMP-9 and MMP-2 activities compared to the positive control group and almost the same enzymatic activity as the negative control group. In situ zymography showed that after 6 months of aging, nHAp_PA 2% and nHAp_PA 6,5% decreased enzymatic activity as well as the negative control.

CONCLUSIONS

Dentin pretreatment with nHAp_PA increased the bonding performance of a self-etch adhesive and decreased MMP-2 and MMP-9 activities after 6 months.

Dual-functional etchants that simultaneously demineralize and stabilize dentin render collagen resistant to degradation for resin bonding

OBJECTIVES

To develop dual-functional etchants that could demineralize and stabilize dentin collagen simultaneously, and to assess the effects of these etchants on collagen crosslinking, biostability and resin bonding properties under clinically relevant conditions.

METHODS

Dual-functional etchants were prepared by mixing 56% glycolic acid and 17% phosphoric acid and adding 1% of theaflavins (TF) or proanthocyanidins from grape seed extract (GSE). The etchant without crosslinker was used as control. The prepared human dentin specimens were treated with the 3 etchants for 30 s and analyzed for chemical interaction using Fourier transform infrared spectroscopy and resistance of the demineralized layer to collagenase degradation using electron microscopy (EM). Resin-dentin interfacial bonding properties were evaluated after 24 h and after 10,000 thermocycling through microtensile bond strength (μTBS), nanoleakage and matrix metalloproteinases (MMPs) activity via in situ zymography. Statistical analysis was done using ANOVA and post- hoc Tuckey's test.

RESULTS

Compared to control, TF and GSE dual-functional etchants were able to demineralize dentin, induce collagen crosslinking and protect the demineralized layer from collagenase degradation within 30 s. High resolution EM images showed better protection with TF etchant compared to GSE. There was a significant reduction in μTBS and an increase in nanoleakage and MMPs activity in control after thermocycling (p < 0.05) while these changes weren't seen in dual-functional etchants.

SIGNIFICANCE

Dual-functional etchants, especially TF containing, provide collagen protection against degradation and result in stable μTBS and less nanoleakage and MMPs activity under clinically relevant conditions.

Resin composite cements: Current status and a novel classification proposal

OBJECTIVES

Currently, a classification of resin cements that includes relatively recently formulated ("universal") cements is lacking. Furthermore, the terminology used to define different resin cements in the scientific reports is inconsistent. Accordingly, this work aims to: (i) propose a novel classification of resin composite cements; (ii) disambiguate the term "universal cements" and (iii) present an overview of the properties of these cements.

METHODS

An analysis of peer-reviewed literature (PubMed search), as well as market research on definitive resin composite cements were performed.

RESULTS

A tendency toward simplified and versatile luting materials was observed both in the scientific literature and on the dental market with the advent of self-adhesive/one-step resin cements. However, additional priming procedures were necessary to improve their bonding performance in certain clinical situations. Hence, several cements that can be applied both in adhesive and self-adhesive mode were introduced. These cements are associated with a universal adhesive resin, that can be used as a tooth and/or restorative material primer, without the need for other priming systems, regardless of the substrate. These systems should be considered truly universal. Therefore, we hereby suggested a new classification of resin-based cements: (1) adhesive/multi-step; (2) self-adhesive/one-step; (3) universal cements (one- or multi-step). Despite promising in vitro results, clinical trials and long-track laboratory studies are necessary to confirm the reliability of the universal cements.

CONCLUSIONS

This review presented the current advances in the field of resin-based cements, which are reflected in the proposed classification. The term "universal cement" was disambiguated, which will help standardize the terminology used in published research.

CLINICAL SIGNIFICANCE

The classification of resin-based cements and a better understanding of the proper terminology will help standardize the terminology in published research, as well as improve the understanding of the clinical practitioners of the different indications and possible modalities of use of the available cements.

The effect of carbodiimide on push-out bond strength of fiber posts and endogenous enzymatic activity

BACKGROUND

To investigate the effect of 0.3 M 1-ethyl-3(3-dimethylaminopropyl) carbodiimide (EDC) aqueous solution pretreatment on push-out bond strength (PBS) and matrix-metalloproteinases (MMPs) activity within radicular dentin when different post cementation strategies were employed.

METHODS

One hundred and twenty monoradicular human teeth were endodontically treated and randomly divided into six groups, depending on the cementation strategy and root dentin pretreatment (n = 20): EAR: cementation with an etch-and-rinse adhesive (LuxaBond Total Etch, DMG) and resin cement (LuxaCore Z Dual, DMG); EAR/EDC: 1 min EDC pretreatment after etching + EAR; SE: cementation with a self-etch primer (Multilink Primer, Ivoclar Vivadent) and corresponding cement (Multilink Automix, Ivoclar Vivadent); SE/EDC: self-etch primer + EDC pretreatment + SE; SA: cementation with a universal self-adhesive cement (RelyX Universal, 3 M); SA/EDC: EDC pretreatment + SA. Slices were submitted to PBS test and interfacial nanoleakage evaluation 24 h after cementation or after thermocycling (40.000 cycles, 5-55 °C). To investigate the effect of EDC on MMPs activity, 4 additional first maxillary premolars per group were processed for in situ zymography analysis. Multivariate ANOVA and post hoc Tukey tests were used to analyze PBS values. The data from in situ zymography were analyzed with Kruskal-Wallis test and Dunn's pairwise multiple comparison procedures (α = 0.05).

RESULTS

The variables "EDC pretreatment", "root region" and "thermocycling" significantly influenced PBS (p < 0.05), while the variable "cementation strategy" had no influence (p > 0.05). Thermocycling significantly reduced PBS in SE and SA groups (p < 0.05). EDC was effective in preserving PBS after artificial aging. EDC pretreatment significantly reduced enzymatic activity at baseline in EAR and SE groups, and in SA group after thermocycling (p < 0.05).

CONCLUSIONS

The use of EDC prevents the reduction of bond-strength values after artificial aging and silences endogenous enzymatic activity within radicular dentin when different cementation strategies were employed.

Degradation and Failure Phenomena at the Dentin Bonding Interface

Damage in the bonding interface is a significant factor that leads to premature failure of dental bonded restorations. The imperfectly bonded dentin-adhesive interface is susceptible to hydrolytic degradation and bacterial and enzyme attack, severely jeopardizing restorations' longevity. Developing caries around previously made restorations, also called "recurrent or secondary caries," is a significant health problem. The replacement of restorations is the most prevailing treatment in dental clinics, leading to the so-called "tooth death spiral". In other words, every time a restoration is replaced, more tooth tissue is removed, increasing the size of the restorations until the tooth is eventually lost. This process leads to high financial costs and detriment to patients' quality of life. Since the complexity of the oral cavity makes prevention a challenging task, novel strategies in Dental Materials and Operative fields are required. This article briefly overviews the physiological dentin substrate, features of dentin bonding, challenges and clinical relevance. We discussed the anatomy of the dental bonding interface, aspects of the degradation at the resin-dentin interface, extrinsic and intrinsic factors affecting dental bonding longevity, perspectives on resin and collagen degradation and how these subjects are connected. In this narrative review, we also outlined the recent progress in overcoming dental bonding challenges through bioinspiration, nanotechnology and advanced techniques to reduce degradation and improve dental bonding longevity.

Effect of collagen cross-linkers on dentin bond strength: A systematic review and network meta-analysis

Objective: This study aimed to evaluate the role of collagen cross-linkers in the bonding performance of the resin-dentin interface through a systematic review and a network meta-analysis. Sources: The literature search was conducted in several databases like PubMed, EMBASE, Cochrane, Scopus and Web of Science from their inception till 30 April 2022. Study selection: The inclusion criteria consisted of in vitro studies evaluating the micro-tensile and micro-shear bond strengths of different cross-linkers acting on dentin. Bayesian network meta-analysis was conducted using RStudio. Data: Out of the 294 studies evaluated in the full-text analysis, 40 were included in the systematic review and meta-analysis. Most studies have used cross-linkers as primer (65.1%), followed by incorporating them into in adhesives and acid etching agents. The application methods of the adhesive system were classified as "etch-and-rinse (ER) adhesives" (77%) and "self-etching (SE) adhesives". Moreover, there were six types of cross-linkers in this presented review, of which the most numerous were polyphenols. Conclusion: Different application methods of cross-linkers, the long-term results showed that were only effective when used for longer durations, the immediate results were not statistically different. According to immediate and long-term results, etch-and-rinse (ER) adhesives showed a greater bonding performance than the control groups (p ≤ 0.05), whereas self-etching (SE) adhesives showed similar bond strength values (p ≥ 0.05). The result of network meta-analysis (NMA) showed that Dope like compound showed higher long-term bonding performance than other cross-linkers. Clinical significance: Long-term clinical studies may be needed to determine the effect of the cross-linkers on the bonding properties.

The influence of finishing lines and margin location on enamel and dentin removal for indirect partial restorations: A micro-CT quantitative evaluation

OBJECTIVES

This in vitro research aimed to quantitatively evaluate the enamel and dentin tissue removal and the residual adhesion surface area (RAS) after different margin designs and locations for indirect partial restorations (IPR).

METHODS

A human molar was scanned using a Micro-CT and the STL file obtained was used to 3D-print 50 resin-tooth replicas. IPR standardized preparations were performed. The specimens were randomly assigned to 5 groups (n = 10), according to preparation and margin location to the dental equator (DE): 1) Rounded shoulder above the DE (SA); 2) Hollow chamfer above the DE (CA); 3) Butt joint above the DE (BJ); 4) Rounded shoulder below the DE (SB); 5) Chamfer below the DE (CB). Then, the tooth replicas were scanned and each STL file was aligned and superimposed to the original STL model file. Data of enamel and dentin volume removal and RAS were assessed and statistically analyzed (one-way ANOVA and Kruskal-Wallis tests for the two dental substrates respectively). Significance was set at p<0.05.

RESULTS

Differences in dental tissue reductions were related to the margin location. Above the equator, SA, CA, and BJ performed comparably (p>0.05). Below the equator, CB was significantly more conservative in enamel reduction than SB (p<0.05) and showed the highest enamel adhesive surface exposure among the tested preparations (p<0.05).

CONCLUSIONS

When the preparation margin is placed above DE, BJ determines a greater exposure of dentin, reducing the adhesive surface in enamel. Below DE, SB seems to be more aggressive in terms of tissue removal compared to CB.

CLINICAL SIGNIFICANCE

The results of this in vitro study suggest that in teeth requiring partial restoration with the margin below the dental equator, a chamfer preparation would be more conservative than a shoulder preparation. When above the equator, preparations with flat designs would expose more dentine providing a worse substrate for adhesion.

Post-Fatigue Fracture Resistance of Lithium Disilicate and Polymer-Infiltrated Ceramic Network Indirect Restorations over Endodontically-Treated Molars with Different Preparation Designs: An In-Vitro Study

The aim of the present study was to evaluate the fatigue to cyclic and static resistance of indirect restorations with different preparation designs made either of lithium disilicate (LS) or polymer-infiltrated ceramic network (PICN). Eighty-four (n = 84) molars were chosen, endodontically treated, and prepared with standardized MOD cavities. The molars were randomly divided into 6 study groups (n = 14) taking into account the "preparation design'' (occlusal veneer with 1.2 mm occlusal thickness; overlay with 1.6 mm occlusal thickness; adhesive crown with 2 mm occlusal thickness) and the "CAD/CAM material'' (E-max CAD, Ivoclar vivadent; Vita Enamic, Vita). A fatigue test was conducted with a chewing simulator set at 50 N for 1,500,000 cycles. Fracture resistance was assessed using a universal testing machine with a 6 mm diameter steel sphere applied to the specimens at a constant speed of 1 mm/min. A SEM analysis before the fracture test was performed to visually analyze the tooth-restoration margins. A statistical analysis was performed with a two-way ANOVA and a post-hoc pairwise comparison was performed using the Tukey test. The two-way ANOVA test showed that both the preparation design factor (p = 0.0429) and the CAD/CAM material factor (p = 0.0002) had a significant influence on the fracture resistance of the adhesive indirect restorations. The interaction between the two variables did not show any significance (p = 0.8218). The occlusal veneer had a lower fracture resistance than the adhesive crown (p = 0.042) but not lower than the overlay preparation (p = 0.095). LS was more resistant than PICN (p = 0.002). In conclusion, in the case of endodontically treated teeth, overlay preparation seems to be a valid alternative to the traditional full crown preparation, while occlusal veneers should be avoided in restoring non-vital molars with a high loss of residual tooth structure. LS material is more resistant compared to PICN.

Update on Dental Luting Materials

A dental luting material aids in the retention and stability of indirect restorations on the prepared tooth structure. In dentistry, clinicians are using a wide range of luting materials for the cementation of indirect restorations. Zinc oxide eugenol and non-eugenol cements, zinc phosphate cement, zinc polycarboxylate cement, glass ionomer cement and resin cements are common dental cements used in dentistry. Each luting material or cement possesses unique properties and clinical implications. An ideal luting cement should be biocompatible, insoluble, resistant to thermal and chemical assaults, antibacterial, aesthetic, simple and easy to use. It should have high strength properties under tension, shear and compression to resist stress at the restoration-tooth interface, as well as adequate working and setting times. So far, no luting material possesses all of these properties of an ideal cement. Scientists have been modifying the conventional luting cements to improve the material's clinical performance and developing novel materials for clinical use. To achieve the best clinical outcome, clinicians should update their knowledge and gain a good understanding of the luting materials so that they can make a wise clinical decision on the material selection and obtain an insight into the development of luting cements. Therefore, the objective of this study is to provide a discussion on the physical, chemical, adhesive and aesthetic properties of common luting materials. The clinical indications of these luting materials are suggested based on their properties. In addition, overviews of the modification of the conventional luting materials and the newly developed luting materials are provided.

Degradation and Stabilization of Resin-Dentine Interfaces in Polymeric Dental Adhesives: An Updated Review

Instability of the dentine-resin interface is owed to the partial/incomplete penetration of the resin adhesives in the collagen fibrils. However, interfacial hydrolysis of the resin-matrix hybrid layer complex activates the collagenolytic and esterase enzymes that cause the degradation of the hybrid layer. Adequate hybridization is often prevented due to the water trapped between the interfibrillar spaces of the collagen network. Cyclic fatigue rupture and denaturation of the exposed collagen fibrils have been observed on repeated application of masticatory forces. To prevent interfacial microstructure, various approaches have been explored. Techniques that stabilize the resin–dentine bond have utilized endogenous proteases inhibitors, cross linking agents’ incorporation in the exposed collagen fibrils, an adhesive system free of water, and methods to increase the monomer penetration into the adhesives interface. Therefore, it is important to discover and analyze the causes of interfacial degradation and discover methods to stabilize the hybrid layer to execute new technique and materials. To achieve a predictable and durable adhesive resin, restoration is a solution to the many clinical problems arising due to microleakage, loss of integrity of the restoration, secondary caries, and postoperative sensitivity. To enhance the longevity of the resin-dentine bond strength, several experimental strategies have been carried out to improve the resistance to enzymatic degradation by inhibiting intrinsic collagenolytic activity. In addition, biomimetic remineralization research has advanced considerably to contemporary approaches of both intrafibrillar and extrafibrillar remineralization of dental hard tissues. Thus, in the presence of biomimetic analog complete remineralization of collagen, fibers are identified.

Finite element and in vitro study on biomechanical behavior of endodontically treated premolars restored with direct or indirect composite restorations

Objectives of the study were to investigate biomechanical properties of severely compromised premolars restored with composite restorations using finite element analysis (FEA), and in vitro fracture resistance test. A 3-D model of an endodontically treated premolar was created in Solidworks. Different composite restorations were modelled (direct restoration-DR; endo-crown-EC; post, core, and crown-C) with two different supporting tissues: periodontal ligament/alveolar bone (B), and polymethyl methacrylate (PMMA). Models were two-point axially loaded occlusally (850 N). Von Mises stresses and strains were calculated. The same groups were further tested for static fracture resistance in vitro (n = 5, 6.0 mm-diameter ball indenter, vertical load). Fracture resistance data were statistically analyzed (p < 0.050). The highest stresses and strains in all FEA models were observed on occlusal and vestibular cervical surfaces, corresponding to fracture propagation demonstrated in vitro. C showed the lowest stress in dentin, while EC showed lower stresses and strains in crown cement. B models demonstrated larger high stress areas in the root than PMMA models. No significant differences in fracture resistance (N) were observed between groups (DR: 747.7 ± 164.0, EC: 867.3 ± 108.1, C: 866.9 ± 126.3; p = 0.307). More conservative restorations seem a feasible alternative for endodontically treated premolars to conventional post-core-crown.

Clinical Behavior of the Gingival Margin following Conservative “Coronally Dynamic” Restorations in the Presence of Non-Carious Cervical Lesions Associated with Gingival Recession: A Pilot Study

Gingival recessions (GR) are often associated with the presence of non-carious cervical lesions (NCCL). The latter result in the disappearance of the cement–enamel junction (CEJ), with consequent difficulties both in measuring the recession itself and in performing root coverage techniques. The restoration of cervical lesions is consequently an important aspect in the treatment of GR, with the re-establishment of a “new” CEJ. This pilot study aimed to verify whether restorative therapy alone, with the execution of a restoration that mimics the convexity of the natural CEJ and thanks to a slight horizontal over-contour, can stabilize a clot in the intrasulcular site and consequently is able to change the position of the gingival margin in a coronal direction. In periodontally healthy patients, with a non-thin gingival phenotype, 10 GR-associated NCCL restorations were performed using a protocol inspired by concepts of prosthetic conditioning, with a progressively reduced convexity (“coronally dynamic restoration”) and de-epithelialization of the gingival sulcus. We observed that 70% of the treated teeth showed a reduction in crown length after 15 days (−0.267 mm), without an increase in probing depth. While considering the limitations of the sample and the need to evaluate the different parameters that can affect the result, the coronally dynamic restoration of NCCL with GR was able to influence the position of the gingival margin in a coronal direction.

The First Step in Standardizing an Artificial Aging Protocol for Dental Composites—Evaluation of Basic Protocols

The clinical performance of a dental restoration is strongly influenced by the complex and dynamically-changing oral environment; however, no standard procedure exists to evaluate this lifetime. This research provides an in-depth analysis of the effect of different aging procedures on the flexural strength (FS), diametral tensile strength (DTS) and hardness (HV) of selected dental materials (Resin F, Flow-Art and Arkon). Material structure was evaluated by scanning electron microscopy. It was found that each aging protocol had some influence on the tested properties, with continual erosion and degradation being observed. Greater mechanical degradation was observed for Resin F (neat resin) after the applied aging protocols, suggesting that a resin matrix is more susceptible for degradation. The most aggressive aging protocol was Protocol 5: 0.1 M NaOH, seven days, 60 °C. Further studies on the effect of artificial aging on dental materials should include a study of the thermal and chemical factors. A standardized aging procedure is crucial for improving the resistance of dental resin composite to oral conditions and their clinical performance.

The Influence of Different Bleaching Protocols on Dentinal Enzymatic Activity: An In Vitro Study

This study aimed to investigate matrix metalloproteinase (MMP) activity in human dentin using in-situ and gelatin zymography, after at-home and in-office bleaching, related to their clinical exposure times. Dentin specimens (n = 5) were treated with 35% hydrogen peroxide (50 min per session/4 sessions), 10% carbamide peroxide (180 min/21 sessions), or no treatment. All were subjected to in-situ zymography. Dentin slices were, subsequently, obtained, covered with fluorescein-conjugated gelatin, and examined with confocal laser-scanning microscopy. The fluorescence intensity was quantified and statistically analyzed using one-way ANOVA and Bonferroni tests (α = 0.05). Furthermore, gelatin zymography was performed on protein extracts obtained from dentin powder (N = 8 teeth), treated with hydrogen peroxide or carbamide peroxide, with different exposure times (10/50 min for hydrogen peroxide; 252/1260 min for carbamide peroxide). The results of the in-situ zymography showed no statistical differences between the bleached specimens and the control group, with a medium level of gelatinolytic activity expressed in the dentin tubules. The results of gelatin zymography showed an increased expression of pro-MMP-9 in carbamide peroxide groups. The expression of pro-MMP-2 decreased in all the experimental groups. The bleaching treatments performed on the enamel of sound teeth do not influence dentinal enzymatic activity. However, when unprotected dentin tissue is bleached, matrix metalloproteinases are more expressed, particularly when carbamide peroxide is used, proportional to the exposure time.

Clinical outcome of bonded partial indirect posterior restorations on vital and non-vital teeth: a systematic review and meta-analysis

OBJECTIVES

The survival rate of indirect partial adhesive restorations on vital versus endodontically treated teeth is still controversial. The hypothesis is that there may be a difference in the survival rate of partial adhesive restorations performed on non-vital teeth compared to vital teeth.

MATERIALS AND METHODS

This systematic review was conducted following the PRISMA guidelines. The considered clinical studies investigated the outcomes of adhesive inlays, onlays, and overlays conducted over the past 40 years, focusing on Kaplan-Meier survival curves to calculate the hazard ratio (primary objective) and the survival rate (secondary objective) between vital and non-vital teeth. The risk of bias was assessed using the Newcastle-Ottawa Scale. Studies included in the review were identified through bibliographic research on electronic databases ("PubMed," "Scopus," "Cochrane Central Register of Controlled Trial," and "Embase"). The K agreement between the two screening reviewers was evaluated.

RESULTS

A total of 55,793 records were identified on PubMed, Scopus, and other bibliographic sources, and after the application of the eligibility and inclusion criteria, eight articles were included for qualitative analysis and six for quantitative analysis. The meta-analysis of the primary and secondary outcomes demonstrated that hazard ratios (HR = 8.41, 95% CI: [4.50, 15.72]) and survival rates (OR = 3.24, 95% CI: [1.76, 5.82]) seemed more favorable for indirect partial adhesive restorations on vital teeth than for those on endodontically treated teeth.

CONCLUSIONS

Within the limits of this study, these findings suggest that the risk of failure of indirect partial adhesive restorations on endodontically treated teeth is higher than on vital teeth.

CLINICAL RELEVANCE

The use of partial adhesive restorations on vital and endodontically treated teeth showed different long-term clinical outcomes.

Influence of Low-pH Beverages on the Two-Body Wear of CAD/CAM Monolithic Materials

The aim of this in vitro study is to evaluate the effect of different acidic media on volumetric wear and surface roughness of CAD/CAM monolithic materials. Forty-eight rectangular specimens were prepared using different CAD/CAM monolithic materials: nanohybrid composite (Grandio Blocks, Voco), resin-based composite (Cerasmart, GC), lithium disilicate (E-Max, Ivoclar), and high-translucency zirconia (Katana STML, Kuraray Noritake). After storage in distilled water at 37 °C for two days, the specimens were tested using a chewing machine with a stainless-steel ball as an antagonist (49N loads, 250,000 cycles). Testing was performed using distilled water, Coca-Cola, and Red Bull as abrasive media. Wear and surface roughness analyses of the CAD/CAM materials were performed using a 3D profilometer and analyzed with two-way analysis of variance and post hoc pairwise comparison procedures. Worn surfaces were examined using scanning electron microscopy. Resin-based materials suffered higher volumetric wear than ceramics (p = 0.00001). Water induced significantly less volumetric wear than the other tested solutions (p = 0.0014), independent of the material tested. High-translucency zirconia showed less surface roughness than all the other materials tested. The selection of monolithic CAD/CAM materials to restore worn dentition due to erosive processes could impact restorative therapy stability over time. Resin-based materials seem to be more influenced by the acidic environment when subjected to a two-body wear test.

Endogenous Enzymatic Activity in Dentin Treated with a Chitosan Primer

The aim of this study was to evaluate the effect of different concentrations of chitosan polymer on dentinal enzymatic activity by means of gelatin and in situ zymography. Human dentin was frozen and ground in a miller. Dentin powder aliquots were demineralized with phosphoric acid and treated with three different concentrations of lyophilized chitosan polymer (1, 0.5 and 0.1 wt%) dissolved in distilled water. Dentin proteins were extracted from each experimental group and electrophoresed under non-reducing conditions in 10% SDS-PAGE containing fluorescein-labeled gelatin. After 48 h in the incubation buffer at 37 °C, proteolytic activity was registered under long-wave UV light scanner and quantified by using Image J software. Furthermore, additional teeth (n = 4) were prepared for the in situ zymographic analysis in unrestored as well as restored dentin pretreated with the same chitosan primers. The registered enzymatic activity was directly proportional to the chitosan concentration and higher in the restored dentin groups (p < 0.05), except for the 0.1% chitosan primer. Chitosan 0.1% only showed faint expression of enzymatic activity compared to 1% and 0.5% concentrations. Chitosan 0.1% dissolved in water can produce significant reduction in MMPs activity and could possibly contribute to bond strength preservation over time.

Endogenous Enzymatic Activity of Primary and Permanent Dentine

Matrix metalloproteinases (MMPs) play an important role in tooth development and influence caries development and hybrid layer degradation. Literature is scant on the differences in the activity of MMPs between primary and permanent dentine. Accordingly, the aim of the present study was to investigate endogenous gelatinolytic activity in primary and permanent dentine. Separate batches of dentine powder were obtained from intact human primary and permanent molars (n = 6). Each batch was divided in two subgroups: (1) mineralised; and (2) demineralised with 10% H₃PO₄. After protein extraction, gelatine zymography was performed. Furthermore, in situ zymography was performed on dentine sections of the same groups (n = 3). The slices were polished, covered with fluorescein-conjugated gelatine and evaluated using a confocal microscope. In situ zymography data were analysed using two-way analysis of variance and post hoc Holm–Šidák statistics (α = 0.05). Primary dentine showed poorly defined bands in the zymograms that vaguely corresponded to the pro-form and active form of MMP-2 and the pro-form of MMP-9. In permanent dentine, demineralised powder demonstrated stronger gelatinolytic activity than mineralised powder. In situ zymography identified stronger enzymatic activity in primary etched dentine (p < 0.05). Stronger enzymatic activity recorded in primary dentine may be related to the differences in morphology and composition between primary and permanent dentine.

Dentin Cross-linking Effect of Carbodiimide After 5 Years

Carbodiimide (EDC)-based dentin primers preserve hybrid layer (HL) integrity. However, aging >1 y has not been investigated. The present study examined whether the cross-linking effect of EDC was reflected in dentin bond strength, endogenous enzymatic activity, and the chemical profile of the HL after 5-y aging in artificial saliva. Noncarious human third molars (N = 42) were cut to expose middle/deep coronal dentin and treated as follows: group 1, dentin etched with 35% H₃PO₄, pretreated with a 0.3M aqueous EDC primer for 1 min and restored with XP Bond (Dentsply Sirona); group 2, as in group 1 but without EDC pretreatment; group 3, Clearfil SE Bond (Kuraray-Noritake) primer applied to dentin surface, followed by EDC pretreatment as in group 1 and application of bond; group 4, as in group 3 without EDC pretreatment. After composite buildup, the specimens were cut into sticks or slabs, depending on the experiment. All tests were performed at baseline (T0) and after 5 y of aging (T5) in artificial saliva at 37 °C. Microtensile bond strength (µTBS) was tested at a crosshead speed of 1 mm/min until failure. Endogenous enzymatic activity was investigated with in situ zymography. The chemical profile of HL was determined via Raman spectroscopy. Three-way analysis of variance and post hoc Tukey test were used to analyze µTBS and in situ zymography data (α = 0.05). EDC pretreatment and aging significantly influenced µTBS and in situ zymography results (P < 0.05). Higher bond strength and lower gelatinolytic activity were identified in the EDC-treated groups at T5 (P < 0.05), especially in the etch-and-rinse groups. Raman spectra revealed less defined amide III peaks in control specimens at T5. The EDC cross-linking effect persisted in the HL for 5 y in terms of bond strength, collagen structure preservation, and dentinal enzyme silencing.

Physicochemical properties, metalloproteinases inhibition, and antibiofilm activity of doxycycline-doped dental adhesive

OBJECTIVES

To evaluate the incorporation of doxycycline (DOX) into a commercial dental adhesive regarding physicochemical properties, microtensile bond strength (μTBS), nanoleakage (NL), nanohardness (NH) and Young's modulus (YM), metalloproteinases (MMP) inhibition, and antibiofilm activity.

METHODS

DOX was incorporated into the adhesive at 0.05, 0.1, 0.5, and 1 wt%. Restored teeth were evaluated for μTBS, NL, NH, and YM after 24 -hs and 1-year of water storage. Biofilms of Streptococcus mutans were grown on top of these adhesives and determined for bacterial viability and amount of biomass. The inhibitory effect on MMP was analyzed by in situ zymography under confocal microscopy.

RESULTS

Adhesives with 0.5 and 1 wt% of DOX presented reduced pH and degree of conversion. The incorporation of DOX did not affect μTBS and hybrid layer YM. The control group (no DOX) had a decrease in μTBS and the densest silver nitrate areas after 1-year storage. Hybrid layer NH values increased with 0.1 wt% DOX compared to control and 1 wt% DOX groups, at 24 -hs. After 1-year storage, NH of 1 wt% DOX adhesive decreased compared to the control group. The 0.5 and 1 wt% concentrations of DOX decreased the bacterial viability and the biofilm biomass. Confocal images suggest an increased MMP inhibition proportional to the percentage of DOX.

CONCLUSION

At any concentration, DOX-doped dental adhesives were able to inhibit MMP activity, diminish nanoleakage, and maintain the resin-dentin bond-strength after 1 year of artificial aging.

CLINICAL SIGNIFICANCE

Doxycycline-doped dental adhesive inhibited metalloproteinases activity and preserved interface bond strength. This formulation has a potential to improve adhesive restorations clinical longevity.

The use of clays for chlorhexidine controlled release as a new perspective for longer durability of dentin adhesion

The adhesive systems have the function to establish the connection between the restorative material and dental tissue, therefore it is of fundamental importance, because failures in the adhesive interface can reduce the life of a dental restoration. This study investigated the possibility of using the adhesive layer as a chlorhexidine modified release system evaluating their impact on the properties of these systems as well as evaluating the impact of these systems on immediate and post-aging dentin adhesion. Were used a matrix with BisGMA, UDMA, HEMA and TEGDMA copolymer and clay particles (Dellite 67G); associated with a chlorhexidine and a camphorquinone photoinitiator system. The properties of these systems were evaluated by the XRD, FTIR spectrophotometer, flexural strength, elasticity modulus, drug release, enzymatic inhibition and dentin adhesion resistance. The presence of the clay can raise the mechanical properties of the adhesive systems engendering a more resistant hybrid layer and led to a more sustained release of chlorhexidine in the systems, allowing a longer effective period of MMP-2 inhibition. The hypothesis that the addition of clays as release modulators could increase the effectiveness of these drugs in inhibiting the dentin's MPPs and consequently enhancing the adhesive durability was confirmed. These results indicate that the controlled release of chlorhexidine is able to reduce the process of loss of adhesion presenting itself as a promising system to increase the longevity of dental restorations.

Effect of benzalkonium chloride on dentin bond strength and endogenous enzymatic activity

OBJECTIVE

This in vitro study evaluated at baseline (T0) and over time (T12 months), the effect of a multi-mode universal adhesive compared with two experimental formulations blended with different concentrations of benzalkonium chloride (BAC), on bond strength and endogenous enzymatic activity.

METHODS AND MATERIALS

Specimens were assigned to the following groups according to the adhesive protocol: G1) All-Bond Universal (ABU) self-etch (SE); G2) ABU + 0.5% BAC SE; G3) ABU + 1% methacrylate BAC SE; G4) ABU etch-and-rinse (E&R); G5) ABU + 0.5% BAC E&R; G6) ABU + 1% methacrylate BAC E&R. Gelatin zymography was performed on dentin powder obtained from eight human third molars. Endogenous enzymatic activity within the hybrid layer was examined using in situ zymography after 24 h (T0) or 1-year storage in artificial saliva (T12). Forty intact molars were prepared for microtensile bond strength test at T0 and T12. Results were statistically analyzed with three-way ANOVA (α = 0.05).

RESULTS

Gelatin zymography assay and in situ zymography quantification analyses indicated that all the BAC-containing formulations decreased matrix metalloproteinase expression. However, in situ zymography showed a general trend of enzymatic activity increase after aging. Microtensile bond-strength testing showed decrease in bond strength over time in all the tested groups; performances of the 1% methacrylate BAC experimental groups were worse than the control.

CONCLUSIONS

BAC-containing adhesives reduce endogenous enzymatic activity both immediately and over time. However, independently from the adhesive employed, increase in the gelatinolytic activity over time and decrease in bond strength was found (especially in the BAC + 1% methacrylate groups), probably due to impaired polymerization properties.

CLINICAL SIGNIFICANCE

Adhesives containing protease inhibitors are practical and efficient tools in clinical practice for enhancement of the longevity of dental restorations. However, extensive investigation of the mechanical and adhesive properties of the material is necessary prior to their clinical use.

Resin-Dentin Bonding Interface: Mechanisms of Degradation and Strategies for Stabilization of the Hybrid Layer

Several studies have shown that the dentin-resin interface is unstable due to poor infiltration of resin monomers into the demineralized dentin matrix. This phenomenon is related to the incomplete infiltration of the adhesive system into the network of exposed collagen fibrils, mainly due to the difficulty of displacement and subsequent replacement of trapped water between interfibrillar spaces, avoiding adequate hybridization within the network of collagen fibrils. Thus, unprotected fibrils are exposed to undergo denaturation and are susceptible to cyclic fatigue rupture after being subjected to repetitive loads during function. The aqueous inclusions within the hybrid layer serve as a functional medium for the hydrolysis of the resin matrix, giving rise to the activity of esterases and collagenolytic enzymes, such as matrix metalloproteinases, which play a fundamental role in the degradation process of the hybrid layer. Achieving better interdiffusion of the adhesive system in the network of collagen fibrils and the substrate stability in the hybrid layer through different strategies are key events for the interfacial microstructure to adequately function. Hence, it is important to review the factors related to the mechanisms of degradation and stabilization of the hybrid layer to support the implementation of new materials and techniques in the future. The enzymatic degradation of collagen matrix, together with resin leaching, has led to seeking strategies that inhibit the endogenous proteases, cross-linking the denudated collagen fibrils and improving the adhesive penetration removing water from the interface. Some of dentin treatments have yielded promising results and require more research to be validated. A longer durability of adhesive restorations could resolve a variety of clinical problems, such as microleakage, recurrent caries, postoperative sensitivity, and restoration integrity.