Copper distribution and oxidation states near corroded fasteners in treated wood

Diffusion in Intact Secondary Cell Wall Models of Plants at Different Equilibrium Moisture Content

Secondary plant cell walls are composed of carbohydrate and lignin polymers, and collectively represent a significant renewable resource. Leveraging these resources depends in part on a mechanistic understanding for diffusive processes within plant cell walls. Common wood protection treatments and biomass conversion processes to create biorefinery feedstocks feature ion or solvent diffusion within the cell wall. X-ray fluorescence microscopy experiments have determined that ionic diffusion rates are dependent on cell wall hydration as well as the ionic species through non-linear relationships. In this work, we use classical molecular dynamics simulations to map the diffusion behavior of different plant cell wall components (cellulose, hemicellulose, lignin), ions (Na⁺, K⁺, Cu²⁺, Cl^-) and water within a model for an intact plant cell wall at various hydration states (3-30 wt% water). From these simulations, we analyze the contacts between different plant cell wall components with each other and their interaction with the ions. Generally, diffusion increases with increasing hydration, with lignin and hemicellulose components increasing diffusion by an order of magnitude over the tested hydration range. Ion diffusion depends on charge. Positively charged cations preferentially interact with hemicellulose components, which include negatively charged carboxylates. As a result, positive ions diffuse more slowly than negatively charged ions. Measured diffusion coefficients are largely observed to best fit piecewise linear trends, with an inflection point between 10 and 15% hydration. These observations shed light onto the molecular mechanisms for diffusive processes within secondary plant cell walls at atomic resolution.

Oxidation states of copper in preservative treated wood as studied by X-ray absorption near edge spectroscopy (XANES)

Copper is a common component in wood preservatives and is used to protect the wood against fungal degradation. Previous research has shown that the Cu⁺⁺ oxidation state provides the best wood protection, and Cu⁺⁺ is widely believed to be the oxidation state of most copper within treated wood. A recent study using X-ray absorption near edge spectroscopy (XANES) reported high amounts of Cu⁺ in wood that had been in contact with corroded fasteners. This study uses XANES to examine the copper oxidation states in wood treated with several different wood preservatives as a function of time after treatment. In contrast with previous literature which focused on the fixation reaction in the first few hours after treatment, this paper examines the oxidation state of Cu in treated wood at longer times (up to 1-year) after treatment. The results showed in nearly all cases, Cu was in the Cu⁺⁺ oxidation state to within the measurement uncertainty. Cu XANES patterns taken approximately 1-year after treatment showed no discernable differences between preservative systems, indicating that regardless of the starting treatment the final Cu speciation is the same within one year. The results confirm previously held beliefs about the Cu oxidation states in wood and give further insights into the corrosion mechanism of metals embedded in treated wood.

Revealing the structural and chemical properties of copper-based nanoparticles released from copper treated wood

Copper-based preservatives consisting of micronized and nanoscale copper particles have been widely used in applications for wood protection. The widespread use of these preservatives along with the potential release of copper-containing nanoparticles (Cu NPs) during the life cycle of treated wood, has raised concerns over the impacts on the environment and occupational exposure. Along with assessing the potential hazards of these materials, a critical step is determining the chemical and morphological characteristics of the copper species released from copper-treated wood. Therefore, a combination of scanning transmission electron microscopy (STEM) and electron energy-loss spectroscopy (EELS) was utilized to characterize and differentiate the released copper-containing particles based on their structures, sizing, and chemical properties. Airborne wood dust samples were collected during the abrasion and sawing of micronized copper (MC) treated wood in a laboratory testing system. Based on the signature Cu L_2,3 edge of EEL spectra, three different copper species (i.e., basic copper carbonate, copper, and copper–wood complex) were identified as major components of the embedded particles in wood dust. In addition, two types of individual Cu NPs consisting of basic copper carbonate and copper were identified. The variation of morphologies and chemical properties of copper-containing particles indicates the importance of copper–wood interactions to determine the formation and distribution of copper species in wood components. Our findings will advance the fundamental understanding of their released forms, potential transformation, and environmental fate during the life cycle.

A combination of analytical electron microscopy and electron energy loss spectroscopy enables effective speciation and characterization of airborne copper nanoparticles released from copper-treated wood.

Corrosiveness of Thermally Modified Wood

Thermally modified wood is becoming commercially available in North America for use in outdoor applications. While there have been many studies on how thermal modification affects the dimensional stability, water vapor sorption, and biodeterioration of wood, little is known about whether thermally modified wood is corrosive to metal fasteners and hangers used to hold these members in place. As thermally modified wood is used in outdoor applications, it has the potential to become wet which may lead to corrosion of embedded fasteners. Here, we examine the corrosiveness of thermally modified ash and oak in an exposure test where stainless steel, hot-dip galvanized steel, and carbon steel nails are driven into wood and exposed to a nearly 100% relative humidity environment at 27 °C for one year. The corrosion rates were compared against control specimens of untreated and preservative-treated southern pine. Stainless steel fasteners did not corrode in any specimens regardless of the treatment. The thermal modification increased the corrosiveness of the ash and oak, however, an oil treatment that is commonly applied by the manufacturer to the wood after the heat treatment reduced the corrosiveness. The carbon steel fasteners exhibited higher corrosion rates in the thermally modified hardwoods than in the preservative-treated pine control. Corrosion rates of galvanized fasteners in the hardwoods were much lower than carbon steel fasteners. These data can be used to design for corrosion when building with thermally modified wood, and highlight differences between corrosion of metals embedded in wood products.