Atomic level observation and structural analysis of phosphoric-acid ester interaction at dentin

The influence of neutral MDP-Na salt on dentin bond performance and remineralization potential of etch-&-rinse adhesive

OBJECTIVES

To investigate the effect of neutral 10-methacryloyloxydecyl dihydrogen phosphate salt (MDP-Na) on the dentin bond strength and remineralization potential of etch-&-rinse adhesive.

METHODS

Two experimental etch-&-rinse adhesives were formulated by incorporating 0 wt% (E0) or 20 wt% (E20) neutral MDP-Na into a basic primer. A commercial adhesive, Adper Single Bond 2 (SB, 3 M ESPE), served as the control. Sixty prepared teeth were randomly allocated into three groups (n = 20) and bonded using either one of the experimental adhesives or SB. Following 24 h of water storage, the bonded specimens were sectioned into resin-dentin sticks, with four resin-dentin sticks obtained from each tooth for microtensile bond strength (MTBS) test. Half of the sticks from each group were immediately subjected to tensile loading using a microtensile tester at a crosshead speed of 1 mm/min, while the other half underwent tensile loading after 6-month incubation in artificial saliva (AS). The degree of conversion (DC) of both the control and experimental adhesives (n = 6 in each group) and the adsorption properties of MDP-Na on the dentin organic matrix (n = 5 in each group) were determined using Fourier-transform infrared spectrometry. Furthermore, the effectiveness of neutral MDP-Na in promoting the mineralization of two-dimensional collagen fibrils and the adhesive-dentin interface was explored using transmission electron microscopy and selected-area electron diffraction. Two- and one-way ANOVA was employed to assess the impact of adhesive type and water storage on dentin bond strength and the DC (α = 0.05).

RESULTS

The addition of MDP-Na into the primer increased both the short- and long-term MTBS of the experimental adhesives (p = 0.00). No difference was noted in the DC between the control, E0 and E20 groups (p = 0.366). The MDP-Na remained absorbed on the demineralized dentin even after thorough rinsing. The intra- and extra-fibrillar mineralization of the two-dimensional collagen fibril and dentin bond hybrid layer was confirmed by transmission electron microscopy and selected-area electron diffraction when the primer was added with MDP-Na.

CONCLUSIONS

The use of neutral MDP-Na results in high-quality hybrid layer that increase the dentin bond strength of etch-&-rinse adhesive and provides the adhesive with remineralizing capability. This approach may represent a suitable bonding strategy for improving the dentin bond strength and durability of etch-&-rinse adhesive.

From Tooth Adhesion to Bioadhesion: Development of Bioabsorbable Putty-like Artificial Bone with Adhesive to Bone Based on the New Material "Phosphorylated Pullulan"

Bioabsorbable materials have a wide range of applications, such as scaffolds for regenerative medicine and cell transplantation therapy and carriers for drug delivery systems. Therefore, although many researchers are conducting their research and development, few of them have been used in clinical practice. In addition, existing bioabsorbable materials cannot bind to the body's tissues. If bioabsorbable materials with an adhesive ability to biological tissues can be made, they can ensure the mixture remains fixed to the affected area when mixed with artificial bone or other materials. In addition, if the filling material in the bone defect is soft and uncured, resorption is rapid, which is advantageous for bone regeneration. In this paper, the development and process of a new bioabsorbable material "Phosphorylated pullulan" and its capability as a bone replacement material were demonstrated. Phosphorylated pullulan, which was developed based on the tooth adhesion theory, is the only bioabsorbable material able to adhere to bone and teeth. The phosphorylated pullulan and β-TCP mixture is a non-hardening putty. It is useful as a new resorbable bone replacement material with an adhesive ability for bone defects around implants.

High-Performance Bioinspired Microspheres for Boosting Dental Adhesion

Dental adhesives are widely used in daily practice for minimally invasive restorative dentistry but suffer from bond degradation and biofilm attack. Bio-inspired by marine mussels having excellent surface-adhesion capability and high chemical affinity of polydopamine (PDA) to metal ions, herein, experimental zinc (Zn)-containing polydopamine-based adhesive formulation, further being referred to as "Zn-PDA@SiO2"-incorporated adhesive is proposed as a novel dental adhesive. Different Zn contents (5 and 10 mm) of Zn-PDA@SiO2 are prepared. Considering the synergistic effect of Zn and PDA, Zn-PDA@SiO2 not only presents excellent antibacterial potential and notably inhibits enzymatic activity (soluble and matrix-bound proteases), but also exhibits superior biocompatibility and biosafety in vitro/vivo. The long-term bond stability is substantially improved by adding 5 wt% 5 mm Zn-PDA@SiO2 to the primer. The aged bond strength of the experimentally formulated dental adhesives applied in self-etch (SE) bonding mode is 1.9 times higher than that of the SE gold-standard adhesive. Molecular dynamics calculations indicate the stable formation of covalent bonds, Zn-assisted coordinative bonds, and hydrogen bonds between PDA and collagen. Overall, this bioinspired dental adhesive provides an avenue technology for innovative biomedical applications and has already revealed promising perspectives for dental restorative dentistry.

The effect of restorative material selection and cementation procedures on the durability of endocrowns in the anterior teeth: an in-vitro study

OBJECTIVE

To investigate the fracture resistance and failure modalities of anterior endocrown restorations fabricated employing diverse ceramic materials, and bonded using various cementation methodologies.

MATERIALS AND METHODS

Forty maxillary central incisors were divided into two main groups based on the ceramic materials used; GroupI (Zir): zirconia endocrwons (Zolid HT+, Ceramill, Amanngirrbach) and GroupII (E-Max): e-max endocrowns (IPS e.max CAD, Ivoclar Vivadent). Both groups were further split into two subgroups depending on the cementation protocols; subgroup IA "ZirMDP": endocowns cemented with MDP primer + MDP resin cement, subgroup IB (ZirNon-MDP): cemented with MDP primer + non-MDP resin cement, subgroup IIA (E-maxMDP): cemented with MDP primer + MDP resin cement, subgroup IIB (E-maxNon-MDP): cemented with MDP primer + non-MDP resin cement. (n = 10/subgroup). Endocrowns were manufactured using CAD/ CAM. Teeth were subjected to 10,000 thermal cycles. The fracture test was performed at 45o with a palatal force direction until the fracture occurred. Test results were recorded in Newton. The failure mode was examined using a stereomicroscope. A One-way ANOVA test was utilized to compare different groups regarding fracture strength values. Tukey`s Post Hoc was utilized for multiple comparisons.

RESULTS

The comparative analysis of fracture strength across the diverse groups yielded non-significant differences, as indicated by a p-value exceeding 0.05. Nonetheless, an observable trend emerged regarding the mode of failure. Specifically, a statistically significant prevalence was noted in fractures localized within the endocrown/tooth complex below the cementoenamel junction (CEJ) across all groups, except for Group IIB, "E-max Non-MDP," where fractures within the endocrown/tooth complex occurred above the CEJ.

CONCLUSIONS

Combining an MDP-based primer with an MDP-based resin cement did not result in a significant effect on the anterior endocrown fracture strength.

CLINICAL RELEVANCE

Regardless of the presence of the MDP monomer in its composition, adhesive resin cement achieved highly successful fracture strength when used with MDP-based ceramic primers. Additionally, ceramic materials exhibiting elastic moduli surpassing those of dentin are discouraged due to their propensity to induce catastrophic fractures within the tooth structure.

Composite Containing Calcium Phosphate Particles Functionalized with 10-MDP

The phosphate ester monomer 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) is capable of bonding to hydroxyapatite and, for this reason, is a key component of several self-etch adhesives. In this study, dicalcium phosphate dihydrate particles (DCPD; CaHPO4.2H2O) were functionalized with 10-MDP and used to formulate an experimental composite with 50 vol% inorganic content (3:1 DCPD:silanated barium glass ratio) dispersed in a BisGMA/TEGDMA matrix. The tested hypothesis was that DCPD functionalization would improve the composite's mechanical performance without compromising Ca2+ release. Composites containing nonfunctionalized DCPD or only reinforcing glass (in both cases, with or without 10-MDP mixed in the resin phase) were used as controls. Materials were tested for degree of conversion (DC; by Fourier transform infrared spectroscopy), water sorption (WS) and solubility (SL; according to ISO 4049), biaxial flexural strength (BFS)/modulus (FM) after 24 h and 5 mo in water, and 28-d Ca2+ release in water (by plasma-coupled optical emission spectroscopy). Data were analyzed using analysis of variance/Tukey test (alpha: 5%). DCPD functionalization did not interfere with DC. The composite containing functionalized DCPD showed significantly lower WS and SL in comparison with the material formulated with nonfunctionalized particles. The presence of 10-MDP (as a functionalizing agent or dispersed in the resin phase) reduced the composite's initial BFS and FM. After 5 mo in water, the composite with functionalized DCPD and both glass-only composites were able to maintain their mechanical properties at levels statistically similar to what was observed after 24 h. Ca2+ release was significantly reduced in both formulations containing 10-MDP. In conclusion, DCPD functionalization with 10-MDP increased the composite's resistance to hydrolytic degradation, improving its mechanical stability after prolonged water storage. However, the impaired water transit at the particle-matrix interface led to a reduction in Ca2+ release.

Effects of Nd:YAG laser irradiation at different energy densities on dentin bond durability under simulated pulpal pressure

OBJECTIVES

To evaluate the effects of Nd:YAG laser irradiation on the microstructures of dentin surfaces and the long-term bond strength of dentin under simulated pulpal pressure.

MATERIALS AND METHODS

Under simulated pulp pressure, 30 freshly extracted caries-free third molars were cut into 2-mm-thick dentin samples and then divided into five groups: the control and laser groups (93.3 J/cm2; 124.4 J/cm2; 155.5 J/cm2; 186.6 J/cm2). Scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR), and Vickers hardness were used to analyze the surface morphology, composition, and mechanical properties of the dentin before and after laser irradiation. Another 80 caries-free third molars were removed and treated as described above, and the resin was bonded to the dentin surface with Single Bond Universal (SBU) adhesive in self-etch mode to make stick specimens. Microtensile bond strength (µTBS), confocal laser scanning microscopy (CLSM), and interfacial silver nanoleakage tests before and after 10,000 times thermocycling were then performed to analyze the bonding properties and interfacial durability of each group.

RESULTS

SEM observations revealed that the surfaces of all laser group specimens were rough with open dentin tubules. Laser irradiation altered the surface composition of dentin while removing some collagen fibers but did not affect its surface hardness or crystallographic characteristics. Furthermore, laser irradiation with an energy density of 124.4 J/cm2 significantly promoted the immediate and aging bond strengths and reduced nanoleakage compared to those of the control group.

CONCLUSIONS

Under simulated pulp pressure, Nd:YAG laser pretreatment altered the chemical composition of dentin and improved the immediate and long-term bond strength.

CLINICAL RELEVANCE

This study investigated the optimal parameters for Nd:YAG laser pretreatment of dentin, which has potential as a clinical method to strengthen bonding.

Dentin surface modification by MDP to improve dentin bonding stability: Topological enhancement and mineralization of collagen structure in hybrid layers

Decades of research have been conducted on 10-Methacryloyloxydecyl dihydrogen phosphate (MDP) through numerous studies. The mechanisms by which its residual calcium salts benefit dentin bonding remain undetermined. The objective of the research was to investigate the role and process of remaining calcium salts in the priming procedure and their capacity for remineralization. The investigation focused on the variations in topological structure, mechanical properties, and chemical interactions between the main agent and the dentin surface. Two adhesive modes including prime-and-rinse(P&R) and prime-and-nonrinse (P&NR) utilized to evaluate the bonding performance and remineralization ability. The findings indicated that both P&R and P&NR methods could eliminate the smear-layer, uncover dentinal-tubules, and generate a textured/rough surface on the dentin. Collagen fibrils exhibited a greater presence of inorganic minerals in the P&NR mode. Compared to control group, both P&R and P&NR groups improved immediate and aging bond strength significantly (P < 0.05). AFM and 3D-STORM revealed MDP and its residual calcium salts distributed in collagen fibrils and expanded collagen matrix. In the P&NR group, TEM revealed that the dentin collagen matrix experienced some remineralization, and there was also mineralization within the collagen fibrils embedded in the bonding interface. Thus, MDP priming improved dentin bonding stability. Residual calcium salts of P&NR process can enhance topological structure of the collagen matrix and induce intrafibrillar mineralization.

MDP-salts as an adhesion promoter with MDP-primers and self-adhesive resin cement for zirconia cementation

PURPOSE

To evaluate the effect of zirconia priming with MDP-Salt before MDP containing primers and self-adhesive cement on the shear bond strength.

MATERIALS AND METHODS

Fully sintered high translucent zirconia specimens (n = 120) were assigned into 2 groups (n = 60 each): Control (No Pretreatment) and Methacryloyloxydecyl dihydrogen phosphate salt (MDP-Salt) pretreated. Each group was divided into 3 subgroups (n = 20) according to cementation protocol: 1) MDP + Silane primer and conventional resin cement, 2) MDP+ Bisphenyl dimethacrylate (BPDM) primer and conventional resin cement, and 3) MDP containing self-adhesive resin cement. Shear bond strength (SBS) was measured after 10,000 thermocycling. Contact angle was measured for tested groups. Surface topography was assessed using a 3D confocal laser scanning microscope (CLSM). Weibull analysis was performed for SBS and one-way ANOVA for contact angle and surface topography measurements (α = 0.05).

RESULTS

The use of MDP-Salt significantly improved the SBS (p < .05) for all tested subgroups. Self-adhesive cement showed an insignificant difference with MDP + Silane group for both groups (p > .05). MDP + BPDM showed a significantly lower characteristic strength compared to self-adhesive resin cement when both were pretreated with MDP-Salt. No difference between all tested groups in the surface topographic measurements while MDP-Salt showed the highest contact angle.

CONCLUSION

MDP-Salt pretreatment can improve bonding performance between zirconia and MDP containing products.

Are universal adhesives in etch-and-rinse mode better than old 2-step etch-and-rinse adhesives? One-year evaluation of bonding properties to dentin

OBJECTIVES

This study compared the bonding properties of dentin of three 2-step etch-and-rinse adhesives (2-ERAs) to those of three universal adhesives (UAs) applied with an etch-and-rinse strategy (ER), immediately and after 1 year of water storage.

METHODS

Sixty caries-free molars were divided into 6 groups according to the adhesive systems used (n = 10). The 2-ERA systems included were: 1) Adper Single Bond 2 (SB), 2) Tetric N-Bond (TB), and 3) Ambar (AM); and the UAs systems were: 4) Single Bond Universal (SBU) 5) Tetric N-Bond Universal (TBU), and 6) Ambar Universal (AMU). The occlusal third of each tooth was removed and the adhesives were applied. After the composite build-up, specimens were sectioned and tested for microtensile bond strength (µTBS) and nanoleakage (NL) immediately and after 1 year of water storage. In situ degree of conversion (DC) was only evaluated in the immediate time. For water sorption (WS), solubility (SO), and mass change (MC) tests, 48 disk-shaped specimens were prepared (n = 8) and assessed according to ISO 4049:2009.

RESULTS

UAs showed higher µTBS and lower NL values than 2-ERAs did after 1 year of water storage (p = 0.001). Regarding DC, 2-ERAs showed higher DC values than UAs (p = 0.001). Regarding WS, 2-ERAs showed higher WS values than those of UAs (p = 0.00001), except for AM and AMU. Lower WS was observed for AM than for other 2-ERAs (p = 0.00001).

CONCLUSION

The use of UAs applied with the ER strategy seems to be a more effective technique for maintaining adhesion to dentin substrate than 2-ERAS.

CLINICAL SIGNIFICANCE

This study may support clinicians in selecting the most adequate adhesive system to be used in ER strategy in dentin, demonstrating that UAs were more effective, considering the longevity of the resin restorations.

Bond Strength and Adhesion Mechanisms of Novel Bone Adhesives

Bone adhesives offer distinct advantages over the use of screws to attached internal fixation plates (IFPs). As the chemical composition of bone is similar to dentine, it is possible that the types of monomers used to make dentine adhesives could be utilised to affix IFPs to bone. The ability to attach a bio-resorbable IFP to porcine bone was assessed for the monomer 10-methacryloyloxydecyl dihydrogen phosphate (MDP), used either as a homopolymer or a copolymer with urethane dimethacrylate (MDP + U). Additionally, the addition of a priming step (MDP + U + P) was evaluated. The chemical interactions of the monomers with bone were assessed using XRD and imaged using TEM, revealing the formation of nano-layered structures with the MDP primer, something we believe has not been reported on bone. In a 6-week artificial aging study both MDP + U and MDP + U + P demonstrated adequate shear bond strength to affix bio-resorbable IFPs. The cytotoxicity profiles of the adhesive formulations were determined using indirect and direct contact with MC3T3 cells, with indirect conditions suggesting the MDP + U + P is as cytocompatible as the resorbable IFP. The findings of this study suggest our newly developed adhesive has the potential to be used as a bone adhesive to affix bioresorbable IFPs.

The roles of 10-methacryloyloxydecyl dihydrogen phosphate and its calcium salt in preserving the adhesive-dentin hybrid layer

OBJECTIVES

10-Methacryloyloxydecyl dihydrogen phosphate (MDP) has been regarded as the most effective dentin-bonding monomer for more than 20 years. Although the dentin-bonding promoting effect of MDP has been well demonstrated, the mechanisms by which it benefits the stably of collagen within the adhesive-dentin hybrid layer are not currently fully understood. The objective of this study was to investigate the roles of MDP and its calcium salt in preserving the adhesive-dentin hybrid layer.

METHODS

MDP-conditioned collagen was investigated by Fourier-transform infrared spectroscopy, Ultraviolet-visible spectroscopy, and molecular docking. The structural changes to the dentin surface upon acid-etching and MDP-conditioning were observed by SEM. X-ray diffraction and nuclear magnetic resonance were used to investigate the chemical interactions between MDP and HAp. The collagen-protecting effects of MDP and its Ca salt were investigated using in-situ zymography, rhMMP-9 colorimetric assay, hydroxyproline assay, and molecular docking.

RESULTS

MDP forms a stable collagen-phosphate complex through hydrogen bonding with the collagen in dentin. Furthermore, it generates MDP-Ca salts that are deposited on the dentin collagen scaffold, protecting it from degradation. Moreover, both free MDP and the MDP-Ca salt inhibit matrix metallopeptidase and exogenous proteases, with the inhibitory effect of the calcium salt being significantly stronger than that of the free form.

SIGNIFICANCE

MDP-based adhesives preserve the collagen within the hybrid layer by simultaneously improving collagen's resistance to exogenous enzymes and inhibiting MMP activity, both of which contribute to the longevity of dentin-resin bonding.

Role of 3-Methacryloxypropyltrimethoxysilane in Dentin Bonding

In this study, we aimed to examine the effect of 3-methacryloxypropyltrimethoxysilane (MPS) on dentin collagen and the impact of MPS and 10-methacryloyloxydecyl dihydrogen phosphate (MDP) together and separately on resin-dentin bonding. Eight groups of primers were prepared: control group, MDP, MPS5, MPS5 + MDP, MPS10, MPS10 + MDP, MPS15, and MPS15 + MDP. The potential interaction between MPS and collagen was assessed by molecular dynamics, contact angle measurement, zeta potential measurement, and chemoanalytic characterization using X-ray photoelectron spectroscopy, Raman spectroscopy, Fourier-transform infrared (FTIR) spectroscopy, and ultraviolet-visible spectroscopy. Microtensile bond strength (μTBS) and nanoleakage were evaluated after 24 h or 12 months of water storage. In situ zymography was used to evaluate the enzyme activity at the bonded interface. According to chemoanalytic characterization and molecular dynamics, a weak interaction between MPS and collagen was observed. MPS enhanced the hydrophobicity and negative charge of the collagen surface (P < 0.05). Applying an MDP-containing primer increased μTBS (P > 0.05) and reduced fluorescence after 24 h of water storage. Water storage for 12 months decreased μTBS (P < 0.05) and increased nanoleakage for all groups. MPS conditioning did not change μTBS and nanoleakage after 24 h of water storage or aging. The MPS10 + MDP and MPS15 + MDP groups presented more silver nitrate and μTBS decrease than the MDP group (P < 0.05). These results indicated that MPS had a weak interaction with collagen that enhanced its surface negative charge and hydrophobicity without adversely affecting dentin bonding. However, compared to MDP alone, mixing MDP with MPS impaired their effectiveness and made the dentin bonding unstable.

Interactions of two phosphate ester monomers with hydroxyapatite and collagen fibers and their contributions to dentine bond performance

OBJECTIVES

To evaluate the interactions of two phosphate ester monomers [10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) and dipentaerythritol penta-acrylate phosphate (PENTA)] with hydroxyapatite and collagen and understand their influence on dentine bonding.

METHODS

Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, X-ray diffraction, nuclear magnetic resonance, ultraviolet-visible, and molecular docking were applied for separately evaluating the interactions of two monomers with hydroxyapatite and collagen. Hydrophilicity tests and morphological observation were employed to characterize pretreated dentine. Microtensile bond strength (μTBS) and nanoleakage were investigated to evaluate the bonding performance. Hydroxyproline assay, in situ zymography, and matrix metalloproteinase-9 (MMP-9) activity assay were used to confirm the MMP inhibition.

RESULTS

Chemoanalytic characterization confirmed the interactions of 10-MDP and PENTA with hydroxyapatite and collagen. The interactions of PENTA were weaker than 10-MDP. PENTA possessed better dentine tubule sealing after etching than 10-MDP. Dentine treated with PENTA was more hydrophilic than 10-MDP. 10-MDP and PENTA treating significantly increased the initial μTBS than the control group without primer conditioning. μTBS decreased significantly during aging, and the decrease was more severe in the PENTA group than 10-MDP. The 10-MDP and PENTA groups exhibited relatively less fluorescence than the control. The relative inhibition percentages of MMP-9 decreased in the order of 10-MDP-Ca salt, 10-MDP and PENTA. The 10-MDP, PENTA, and 10-MDP-Ca salt groups showed significantly lower hydroxyproline contents than the control.

CONCLUSIONS

Although PENTA adsorbed on hydroxyapatite, it did not form a stable calcium salt. The interactions of 10-MDP with hydroxyapatite and collagen are different than those of PENTA.

CLINICAL SIGNIFICANCE

The sealing of dentinal tubules by PENTA and the inhibition of MMP by 10-MDP and its calcium salts contribute to improving the dentine bonding durability.

Influence of Acidic Environment on Hydrolytic Stability of MDP-Ca Salts with Nanolayered and Amorphous Structures

Purpose

This study aimed to investigate the hydrolytic stability of 10-methacryloyloxydecyl dihydrogen phosphate calcium (MDP-Ca) salts with nanolayered and amorphous structures in different pH environments.

Methods

The MDP-Ca salts were synthesized from MDP and calcium chloride and characterized by X-ray diffraction (XRD), nuclear magnetic resonance (NMR), and transmission electron microscopy (TEM). Inductively coupled plasma-mass spectrometry (ICP-MS) was used to quantify the release of calcium from the synthesized MDP-Ca salt, MDP-treated hydroxyapatite (MDP-HAp), and untreated HAp after soaking in acidic and neutral solutions for 1, 7, and 30 days. To study the hydrolytic process, we carried out molecular dynamics (MD) simulations of the nanolayered MCS-MD (monocalcium salt of the MDP dimer) and DCS-MD (dicalcium salt of the MDP dimer) structures, as well as of the amorphous-phase MCS-MM (monocalcium salt of the MDP monomer).

Results

The TEM images showed that the nanolayered structures were partially degraded by acid attack. Based on the ICP-MS results, the hydrolysis rate of the MDP-Ca salt in acidic and neutral environments followed the order HAp > MDP-HAp > MDP-Ca salt. The MD simulations showed that, in acidic environments, clusters of MDP remained aggregated and all Ca²⁺ ions separated from the MDP monomer to interact with water molecules in aqueous solution. In neutral environments, Ca²⁺ ions always interacted with phosphate groups, OH⁻ ions, and water molecules to form clusters centered on Ca²⁺ ions.

Conclusion

MDP-Ca presented higher hydrolysis rates in acidic than neutral environments. Nanolayered MCS-MD possessed the highest resistance to acidic hydrolysis, followed by amorphous MCS-MM and DCS-MD.

MDP Salts: A New Bonding Strategy for Zirconia

Durable resin-ceramic adhesion may influence the clinical success of ceramic restorations, which has been one of the challenging issues in dentistry. The present study assessed the bond strength and chemical interaction of 10-methacryloxydecyl dihydrogen phosphate (MDP), MDP+silane, and MDP-salt primers to alumina-blasted zirconia ceramic by tensile bond strength test, surface elemental composition with x-ray photoelectron spectroscopy analysis, contact angle measurement, surface morphology with scanning electron microscopy, and surface topography with 3-dimensional confocal laser scanning microscope analyses. MDP-salt showed the highest tensile bond strength before and after thermocycling when compared with MDP and MDP+silane (P < 0.05). The measured contact angle values differed significantly (P < 0.001) in the order of MDP-salt > control (no chemical pretreatment) > MDP+silane > MDP. There was no difference in surface roughness (P = 0.317) and surface topography among all tested groups. Zirconia treated with MDP-salt showed phosphorus peaks in addition to zirconia and alumina peaks. MDP-salt has zirconia priming properties, which improves bonding performance to resin cement.

Evaluation of a Hypersensitivity Inhibitor Containing a Novel Monomer That Induces Remineralization-A Case Series in Pediatric Patients

BACKGROUND

Recently, tooth deformities have been frequently encountered by pediatric dentists. Severe enamel hypomineralization sometimes induces pain such as hyperesthesia, but composite resin restoration is difficult because it often detaches without any cavity preparation. Resin-based hypersensitivity inhibitors for tooth physically seal the dentinal tubules. It was reported that hypersensitivity inhibitor containing novel adhesive monomers forms apatite and induces remineralization in vitro. Therefore, these case series assessed the clinical effects of remineralization and the suppression of hypersensitivity by Bio Coat Ca (Sun Medical, Shiga, Japan).

METHODS

After mechanical tooth cleaning was performed, the hypersensitivity inhibitors were applied and cured by light exposure. Changes in hypersensitivity were determined by visual analog scale (VAS). The improvement of hypomineralization was evaluated by the change in color tone based on the digital images of intraoral photographs.

RESULTS

After repeated monthly treatments, these cases showed decreased hypersensitivity after the fourth application, while the opaque white and brownish color improved on the seventh application.

CONCLUSION

This novel hypersensitivity inhibitor with calcium salt of 4-methacryloxyethyl trimellitic acid (C-MET) and 10-methacryloyloxydecyl dihydrogen calcium phosphate (MDCP) not only suppressed hypersensitivity but also improved cloudiness and brown spots in recently erupted permanent teeth in presented cases.

Improved bond performances of self-etch adhesives to enamel through increased MDP-Ca salt formation via phosphoric acid pre-etching

OBJECTIVES

The chemical affinity between 10-methacryloyloxydecyl dihydrogen phosphate (MDP) and hydroxyapatite (HAp) is an important factor in the enamel bonding provided by MDP-based self-etch (SE) adhesives, besides microinterlocking mechanisms. This study aimed to investigate how phosphoric acid pre-etching affects MDP-Ca salt formation in the application of MDP-based SE adhesives.

METHODS

Single Bond Universal (SBU), All Bond Universal (ABU), Clearfil Universal Bond Quick (CBQ), and a MDP-based all-in-one adhesive (EXP) were used in both SE and etch-and-rinse (ER) modes, along with Clearfil SE Bond and untreated enamel (UE) as controls. The MDP-Ca salts produced with or without etching were examined by nuclear magnetic resonance, Raman spectroscopy, X-ray photoelectron spectroscopy, X-ray diffraction, and Fourier-transform infrared spectroscopy. Zeta potential, contact angle, and scanning electron microscopy measurements were employed to elucidate the mechanism behind the changes in MDP/HAp chemical affinity upon pre-etching.

RESULTS

The percentage of MDP-Ca salt in EXP_ER (73.13%) was higher than that in EXP_SE (43.27%). Characteristic CH₂ (1130, 1441, 2853, and 2909 cm^-1), CC (1641 cm^-1), and CO (1718 cm^-1) bands were observed in the Raman spectra of EXP_ER. Pre-etching increased the negative zeta potential of the enamel surface compared to that of UE (P < 0.001). The contact angles of MDP-based adhesives applied to pre-etched enamel were significantly lower than those of the self-etched surface (P < 0.05).

SIGNIFICANCE

The increased MDP-Ca salt formation is a significant advantage of phosphoric acid pre-etching, improving the MDP/HAp chemical affinity in addition to increasing surface wettability.

Dentin interaction with universal adhesive containing isopropanol solvent studied by solid-state NMR spectroscopy

OBJECTIVE

This study investigated the chemical and structural changes in the mineral phase and collagen of dentin during application of a mild universal adhesive. Particular attention was paid to the role of isopropanol and changes in water molecules.

METHODS

In vitro application of the mild universal adhesive on dentin with two established etching modes (self-etch and etch-and-rinse) was studied using solid state nuclear magnetic resonance spectroscopy.

RESULTS

It was evidenced that the etch-and-rinse mode leads to a decrease of the inorganic apatite and a reorganization of the residual mineral phase with a low amount of adhesive phosphate monoesters calcium salt formed, compared to the self-etch mode. In contrast, the adhesive interacts very similarly to the level of dentin collagen in both protocols, with a strong decrease in the amount of the free water molecules induced by the presence of isopropanol as the adhesive solvent, but without significant changes in the initial collagen structure. For both modes, the adhesive acrylates monomers remain mobile and can infiltrate the collagen.

SIGNIFICANCE

Understanding the molecular interactions between dentin and adhesive solutions is a major challenge for designing products that lead to the formation of ideal dentin resin hybrid layer. Notably, one point considered essential is the presence of unbound water which, over time, is associated with a hydrolytic degradation of the organic matrix. Isopropanol, as an adhesive solvent, leads to a decrease in the amount of the less stable water molecules while the water molecules strongly attached to the collagen are retained, thus preserving the collagen structure.

Influence of 10-methacryloyloxydecyl dihydrogen phosphate (MDP) incorporated experimental cleaners on the bonding performance of saliva-contaminated zirconia ceramic

OBJECTIVES

To assess the efficacy of experimental cleaners containing 10-methacryloyloxydecyl dihydrogen phosphate (MDP) on the saliva decontamination of ceramic and their influence in restoring zirconia's adherence to resin cement.

MATERIALS AND METHODS

Four hundred sixty alumina-blasted zirconia specimens were categorized into saliva-contaminated and uncontaminated groups which were treated with ceramic primer (P), experimental cleaner 1 (C1), C1 followed by P (C1P), experimental cleaner 2 (C2), and C2 followed by P (C2P). Stainless-steel rods were then attached to the specimens using PanaviaV5 cement (Kuraray Noritake Dental; Tokyo, Japan). Tensile bond strength (TBS) test was performed after 24 h and 5000 thermocycling processes. X-ray photoelectron spectroscopy (XPS) analysis and contact angle measurement of the specimen were performed. The TBS data were analyzed by Weibull analysis and three-way ANOVA. Contact angle data were analyzed by two-way ANOVA (α = 0.05).

RESULTS

C2P groups showed the highest TBS in all conditions among tested groups. Saliva contamination led to a significant reduction of TBS in primer- and cleaner-treated groups, with no significant impact on C2P. Adhesive failure was predominant in contaminated groups except with the C1P and C2P groups. XPS revealed that a nitrogen peak was observed on contaminated groups but not in primed groups. The contact angle was significantly affected by saliva contamination, the cleaners, and/or ceramic primer usage (p < 0.001).

CONCLUSIONS

The MDP cleaner followed by the MDP primer protocol may overcome the effect of saliva contamination and improve the resin-ceramic bond strength.

CLINICAL RELEVANCE

It is recommended to use a combination of MDP-containing cleaner 2 and ceramic primer as a chair-side chemical pretreatment for zirconia substrate with or without saliva contamination.

Effects of Solvents and pH Values on the Chemical Affinity of 10-Methacryloyloxydecyl Dihydrogen Phosphate toward Hydroxyapatite

This study aimed to investigate the effects of solvents and pH values on the chemical interaction between 10-methacryloyloxydecyl dihydrogen phosphate (MDP) and hydroxyapatite (HAp). The chemical affinity of MDP toward HAp dissolved in different solvents (E-MDP: 10 wt % MDP and 90 wt % ethanol; E-W-MDP₁: 10 wt % MDP, 75 wt % ethanol, and 15 wt % water; A-W-MDP: 10 wt % MDP, 75 wt % acetone, and 15 wt % water; and E-W-MDP₂: 10 wt % MDP, 45 wt % ethanol, and 45 wt % water) was investigated. The pH of E-W-MDP₂ was increased from 2.04 to 5 (E-W-MDP_2/5) and to 7 (E-W-MDP_2/7). The reaction products were characterized by Fourier transform infrared spectroscopy, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA), and nuclear magnetic resonance (NMR). XRD and NMR results revealed that no MDP-calcium salt formed in E-MDP. XRD, TGA, and XPS results indicated that MDP interacted with HAp, producing the MDP-calcium salt in all groups except E-MDP. NMR results revealed that the dicalcium salt of the MDP dimer (DCS-MD) and the MDP tripolymer (DCS-MT) and the monocalcium salt of the MDP monomer and the MDP dimer were formed in E-W-MDP₁. DCS-MD and DCS-MT were also formed in E-W-MDP₂ and A-W-MDP. In E-W-MDP_2/5 and E-W-MDP_2/7, DCS-MD was obtained. Both the solvents and pH values affect the chemical interactions between MDP and HAp and the types of reaction products formed. MDP and HAp do not form any MDP-calcium salt in pure ethanol; the structural stability of MDP-calcium salts is dependent on the solvent water content and the pH value. The ethanol/water mixture is recommended as the main solvent in an MDP-containing primer, and the ideal pH value is 2-7; if these conditions are satisfied, sufficient amounts of MDP-calcium salts with stable structures are expected to be formed, thus improving the longevity of dentin/enamel bonding.

Varying 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) level improves polymerisation kinetics and flexural strength in self-adhesive, remineralising composites

OBJECTIVES

To assess the influence of systematically varying concentrations of 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) versus 3% 4-META on the polymerisation kinetics and shrinkage, biaxial flexural strength (BFS) and modulus of remineralising composites.

METHODS

Composites were prepared by adding poly(propylene glycol) dimethacrylate (24 wt%), camphorquinone (1 wt%) and MDP (0%, 5%, 10%, 15% and 20 wt%) or 4-META (3%) to urethane dimethacrylate. These were mixed with glass fillers containing 8 wt% monocalcium phosphate and 4 wt% polylysine (powder-liquid ratio of 3:1). Continuous spectral changes, following 20 s light exposure (37 °C), were assessed with an ATR-FTIR to monitor polymerisation kinetics (n = 3). Final extrapolated conversions (D_C,max) were employed to calculate polymerisation shrinkage. BFS and modulus of 24-h dry stored disc specimens (10 × 1 mm; n = 10) were determined using a ball-on-ring jig setup.

RESULTS

Maximum rate of polymerisation and D_C,max increased linearly from 2.5 to 3.5% s^-1 and 67 to 83%, respectively, upon increasing MDP from 0 to 20 wt%. Values with 3% 4-META were 2.6% s^-1 and 78%. Shrinkage was 3.8 ± 0.3% for all formulations. Raising 4-META or MDP from 0 to 3 versus 5%, respectively, increased strength from 106 to 145 versus 136 MPa. A decreasing trend with higher MDP concentrations was noted. Elastic modulus showed no specific trend upon MDP increase.

SIGNIFICANCE

Whilst final conversion levels were enhanced by 3% 4-META or >5% MDP, trends did not correlate with strength. Peak strengths with 3% 4-META or 5% MDP may therefore be due to acidic monomers providing linkage between the hydrophilic, non-silane treated particles and the polymer matrix.

Chemical interaction between 10-methacryloyloxydecyl dihydrogen phosphate and methacryloxypropyltrimethoxysilane in one-bottle dental primer and its effect on dentine bonding

In the present study, we investigated the chemical interaction between 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) and methacryloxypropyltrimethoxysilane (gamma-MPS) in one-bottle primer solutions and its effect on dentine bonding performance. Solutions containing 10 wt% 10-MDP and/or gamma-MPS at 0, 1, 5, 10, or 15 wt% were prepared, providing 10 experimental groups (labeled MDP/MPSxx or MPSxx, where MDP indicates the presence of 10 wt% MDP and xx is the wt% of gamma-MPS in the solution). Phosphoric-acid-etched dentine blocks were prepared from human molars and conditioned in the solutions before being used to build resin-dentine-bonded specimens, which were subsequently subjected to microtensile bond strength (μTBS) testing after 24-h or six-months water storage. Interfacial nanoleakage was evaluated by SEM observation. All the primer-conditioned samples showed significantly higher initial μTBS values than that of the control group, and six-months water storage significantly lowered the μTBS for all the groups; however, the decreases for MDP/MPS10 and MDP/MPS15 were significantly greater than those for MDP/MPS1 and the control solution. Furthermore, MDP/MPS10 and MDP/MPS15 groups also showed more serious nanoleakage. Fourier-transform infrared spectroscopy, X-ray photoelectron spectroscopy, and X-ray diffraction analyses were used to investigate the chemical affinity between 10-MDP and hydroxyapatite (HAp). In XRD analysis, the intensities of peaks assigned to 10-MDP-calcium salts were lower for the solutions containing gamma-MPS. Overall, the results indicate that the copresence of gamma-MPS (above 10 wt%) and 10-MDP in one-bottle primer solutions inhibit the formation of 10-MDP-calcium salts, leading to increased long-term nanoleakage and decreased bonding durability.

Effects of Phosphoric Acid Pre-Etching on Chemisorption between Enamel and MDP-Containing Universal Adhesives: Chemical and Morphological Characterization, and Evaluation of Its Potential

This study aimed to provide evidence that phosphoric acid pre-etching is necessary for the chemisorption between enamel and 10-methacryloyloxydecyl dihydrogen phosphate (MDP)-containing universal adhesives. Three MDP-containing universal adhesives: Single Bond Universal (SBU), All Bond Universal (ABU), and Clearfil Universal Bond Quick (CBQ), as well as an experimental MDP-containing adhesive (EX) were investigated. Clearfil SE Bond (CSE) was a control and untreated enamel (UE) was another control. Self-etch (SE) and etch-and-rinse (ER) bonding modes were employed for universal adhesives. The enamel surfaces with different treatments were observed with a scanning electron microscope (SEM). The chemical bonds in the enamel reactants were determined using Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), and nuclear magnetic resonance (NMR). The charge changes with phosphoric acid pre-etching or without were characterized by ζ-potential. FTIR confirmed the chemisorption between enamel and MDP-containing adhesives. XPS and ³¹P NMR studies detected improved chemical affinity to the phosphoric acid etching + MDP-containing universal adhesives applied with enamel. The ζ-potential of MDP-containing universal adhesives absorbed with enamel, with or without etching became more negative compared with that of UE (P < 0.05). Furthermore, single etching created a negative ζ-potential with a higher absolute value (P = 0.009). Phosphoric acid pre-etching can increase the negative charge on the enamel surface and facilitate the chemical reactions of MDP and hydroxyapatite (HAp) to produce more calcium salts, thus improving the chemisorption between enamel and MDP-containing universal adhesives.

Touch-Cure Polymerization at the Composite Cement-Dentin Interface

Ceramic restorations are often adhesively luted onto the tooth prep. The so-called touch-cure concept was developed to yield optimum polymerization of composite cement at the restoration-cement-tooth interface for immediate bond stabilization. Although this touch cure is theorized to initiate polymerization at the interface when the accelerator in the primer makes contact with the cement, this process has not yet been proven. This study aimed to elucidate the mechanism of touch cure by measuring the degree of conversion (DC) of composite cement applied with or without an accelerator-containing tooth primer (TP) versus an accelerator-free primer using real-time Fourier-transform infrared spectroscopy (RT-FTIR) and attenuated total reflection (ATR)-FTIR. Interfacial bond strength was measured in shear mode, the accelerator composition confirmed by X-ray fluorescence analysis (XRF), and the interfacial interaction of TP and composite cement with dentin investigated by X-ray diffraction (XRD), focused-ion-beam scanning electron microscopy (FIB-SEM) with 3-dimensional interface reconstruction, and transmission electron microscopy (TEM). RT/ATR-FTIR revealed the significantly highest DC when the composite cement was applied with the accelerator-containing primer. XRF disclosed a vanadium compound as a novel chemical accelerator within TP, instead of a classic chemical curing initiator system, to set off touch cure as soon the cement contacts the previously applied primer. Although the TP contains the acidic functional monomer 10-MDP for adhesion to tooth tissue, touch cure using the accelerator-containing TP combined the fastest/highest DC with the highest bond strength. FIB-SEM and TEM confirmed the tight interfacial interaction at dentin with submicron hybridization along with stable 10-MDP also Ca-salt nanolayering.

Nano-Layering Adds Strength to the Adhesive Interface

X-ray diffraction (XRD) surface analysis and ultrastructural interfacial characterization using transmission electron microscopy (TEM) confirmed that the functional monomer 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) self-assembles into nano-layers at adhesive-tooth interfaces. Self-assembled nano-layering is thought to contribute to the durability of bonding to tooth dentin, although this has not been proven yet. In order to disclose this potential bond-durability contribution of nano-layering, we observed the 3-dimensional (3D) spreading of nano-layering by a series of focused-ion-beam (FIB) milled cross sections by scanning electron microscopy (FIB-SEM) and examined the mechanical properties of self-assembled nano-layering using scanning probe microscopy (SPM). A commercial 10-MDP-containing 3-step self-etch adhesive partially demineralized dentin up to submicron depth, forming a submicron hydroxyapatite-rich hybrid layer. TEM chemically and ultrastructurally confirmed the formation of interfacial nano-layering. FIB-SEM 3D reconstructions disclosed a 3D network of self-assembled nano-layering extending from the hybrid layer up to within the adjacent adhesive-resin layer. SPM revealed that nano-layering within the adhesive-resin layer possessed a higher elastic modulus than that of the surrounding adhesive resin, hereby suggesting that nano-layering contributes to the mechanical strength of adhesives like filler particles do. Nano-layering's 3D expanded structure is expected to strengthen the surrounding resin, as well to better interconnect the adhesive-resin layer to the hybrid layer. In conclusion, this exploratory study demonstrated that nano-layering constitutes a strong phase at the adhesive interface, which may contribute to the clinical longevity of the 10-MDP-based bond to dentin.

Mechanical Properties of Nanohybrid Resin Composites Containing Various Mass Fractions of Modified Zirconia Particles

PURPOSE

The aim of this study was to investigate the effect of various mass fractions of 10-methacry-loyloxydecyl dihydrogen phosphate (MDP)-conditioned or unconditioned zirconia nano- or micro-particles with different initiator systems on the mechanical properties of nanohybrid resin composites.

METHODS

Both light-cured (L) and dual-cured (D) resin composites were prepared. When the mass fraction of the nano- or micro-zirconia fillers reached 55 wt%, resin composites were equipped with dual-cured initiator systems. We measured the three-point bending-strength, elastic modulus, Weibull modulus and translucency parameter of the nanohybrid resin composites containing various mass fractions of MDP-conditioned or unconditioned zirconia nano- or micro-particles (0%, 5 wt%, 10 wt%, 20 wt%, 30 wt% and 55 wt%). A Cell Counting Kit (CCK)-8 was used to test the cell cytotoxicity of the experimental resin composites. The zirconia nano- or micro-particles with MDP-conditioning or not were characterized by transmission electron microscopy (TEM), Fourier infrared spectroscopy (FTIR), and X-ray photoelectron spectroscopy (XPS).

RESULTS

Resin composites containing 5-20 wt% MDP-conditioned or unconditioned nano-zirconia fillers exhibited better three-point bending-strength than the control group without zirconia fillers. Nano- or micro-zirconia fillers decreased the translucence of the nanohybrid resin composites. According to the cytotoxicity classification, all of the nano- or micro-zirconia fillers containing experimental resin composites were considered to have no significant cell cytotoxicity. The FTIR spectra of the conditioned nano- or micro-fillers showed new absorption bands at 1719 cm-1 and 1637 cm-1, indicating the successful combination of MDP and zirconia particles. The XPS analysis measured Zr-O-P peak area on MDP-conditioned nano- and micro-zirconia fillers at 39.91% and 34.89%, respectively.

CONCLUSION

Nano-zirconia filler improved the mechanical properties of nanohybrid resin composites, but cannot be the main filler to replace silica filler. The experimental dual-cured composites can be resin cements with better opacity effects and a low viscosity.

Five-year clinical evaluation of a universal adhesive: A randomized double-blind trial

OBJECTIVE

To evaluate the five-year clinical performance of Scotchbond Universal Adhesive (SU; 3M Oral Care, St. Paul, MN, USA) in non-carious cervical lesions (NCCLs) using two evaluation criteria.

METHODS

Thirty-nine patients participated in this study. Two hundred restorations were assigned to four groups: SU-ERm: etch-and-rinse + moist dentin; SU-ERd: etch-and-rinse + dry dentin; SU-Set: selective enamel etching; and SU-SE: self-etch. A nanofilled composite resin was placed incrementally. The restorations were evaluated at baseline and after 5 years using both the World Dental Federation (FDI) and the United States Public Health Service (USPHS) criteria. The survival rates (retention/fractures) were calculated with the Kaplan-Meier and the log-rank test. For the secondary outcomes, Friedman repeated measures analysis of variance by rank was applied (α = 0.05).

RESULTS

After 5 years the recall rate was 86%. The retention/fracture rates were 93% for Erm and ERd, 88.4% for SEet and 81.4% for SE. A significant difference was observed for SE vs. ERd and SE vs. ERm (p = 0.01). Also, marginal discoloration and adaptation showed significant differences with ERm and ERd resulting in fewer marginal discrepancies than SE (p < 0.05).

SIGNIFICANCE

After 5 years, the clinical behavior of the universal adhesive in the etch-and-rinse strategy was better when compared to the self-etch strategy. The use of selective enamel etching is highly recommended for the self-etch strategy. The FDI and USPHS evaluation criteria showed similar results after 5 years.

Zinc-Calcium-Fluoride Bioglass-Based Innovative Multifunctional Dental Adhesive with Thick Adhesive Resin Film Thickness

Apart from producing high bond strength to tooth enamel and dentin, a dental adhesive with biotherapeutic potential is clinically desirable, aiming to further improve tooth restoration longevity. In this laboratory study, an experimental two-step universal adhesive, referred to as Exp_2UA, applicable in both the etch-and-rinse (E&R) and self-etch (SE) modes and combining a primer, containing 10-methacryloyloxydecyldihydrogen phosphate as a functional monomer with chemical binding potential to hydroxyapatite, with a bioglass-containing hydrophobic adhesive resin, was multifactorially investigated. In addition to primary property assessment, including measurement of bond strength, water sorption, solubility, and polymerization efficiency, the resultant adhesive-dentin interface was characterized by transmission electron microscopy (TEM), the filler composition was analyzed by energy-dispersive X-ray spectroscopy, and the bioactive potential of the adhesive was estimated by measuring the long-term ion release and assessing its antienzymatic and antibacterial potential. Four representative commercial adhesives were used as reference/controls. Application in both the E&R and SE modes resulted in a durable bonding performance to dentin, as evidenced by favorable 1 year aged bond strength data and a tight interfacial ultrastructure that, as examined by TEM, remained ultramorphologically unaltered upon 1 year of water storage aging. TEM revealed a 20 μm thick hydrophobic adhesive layer with a homogeneous bioglass filler distribution. Adequate polymerization conversion resulted in extremely low water sorption and solubility. In situ zymography revealed reduced endogenous proteolytic activity, while Streptococcus mutans biofilm formation was inhibited. In conclusion, the three-/two-step E&R/SE Exp_2UA combines the high bonding potential and bond degradation resistance with long-term ion release, rendering the adhesive antienzymatic and antibacterial potential.

Silane-coupling effect of a silane-containing self-adhesive composite cement

OBJECTIVE

Hydrofluoric-acid etching followed by silanization is a routine clinical protocol for durable bonding to glass ceramics. Simplifying ceramic-bonding procedures, new technological developments involve the inclusion of a silane coupling agent in a self-adhesive composite cement. To investigate the effectiveness of the incorporated silane coupling agent, shear bond strength (SB) to ceramic and dentin, contact angle of water (CA), transmission electron microscopy (TEM), X-ray diffraction (XRD) and ²⁹Si nuclear magnetic resonance (NMR) assessments were correlatively conducted.

MATERIALS AND METHODS

SB to glass ceramic was measured without ('immediate') and with ('aged') 50K thermocycles upon application of (1) the silane-containing self-adhesive composite cement Panavia SA Cement Universal ('SAU'), being light-cured: 'SAU_light', (2) 'SAU_chem': chemically cured SAU, (3) 'SAP_light': light-cured Panavia SA Cement Plus ('SAP'), and (4) 'SAP_CP': SAP light-cured after separate silanization using Clearfil Ceramic Primer Plus ('CP'). CA was also measured on glass ceramic. The cement pastes before and upon mixing were characterized using ²⁹Si NMR. SB of SAU or SAP onto dentin was measured. Finally, the cement-dentin interface was characterized by TEM and XRD.

RESULTS

The immediate and aged SB to glass ceramic of SAU did not significantly differ from those of SAP_CP, while they were significantly higher than those of SAP. CA of SAU did not significantly differ from that of SAP_CP, but it was significantly higher than CA of SAP. ²⁹Si NMR revealed siloxane bonds after mixture. SB of SAU and SAP to dentin did not show any significant difference. SEM, TEM and XRD confirmed tight and chemical interaction, respectively.

SIGNIFICANCE

Incorporating silane in a 10-MDP-based self-adhesive composite cement combined efficient silane-coupling ability at the ceramic surface with effective bonding ability at dentin.