Low Wear at 10-Year Follow-Up of a Second-Generation Highly Cross-Linked Polyethylene in Total Hip Arthroplasty

Safety of using a large femoral head on thin polyethylene for total hip arthroplasty based on different types of polyethylene

The use of a large femoral head in total hip arthroplasty (THA) to stabilize and reduce the incidence of dislocation is on the increase, but concerns arise when combining them with small acetabular components due to potential mechanical failures in thin polyethylene (PE) liners. A single-institution, retrospective cohort study was conducted on 116 patients with minimum 2-year follow-up who received 36-mm femoral heads and acetabular components ≤ 52 mm, using either remelted highly cross-linked polyethylene (remelted HXLPE) or vitamin E-infused HXLPE (VEPE). Osteolysis and implant loosening were not observed in either group. Although a fracture of the PE liner was observed in each group (1.7%), the clinical outcomes were excellent, as the mean modified Harris Hip Score (mHHS) at the last follow-up was 93.5. Moreover, the mean linear wear rates measured by digital imaging software in both groups were low, with 0.035 mm/y in remelted HXLPE and 0.030 mm/y in VEPE. In conclusion, The use of a large femoral head on a thin PE liner can be a viable treatment option in patients who need to prioritize stability; however, careful attention should be paid to mechanical fractures of the PE liner.

Large articulations do not increase wear rates of thin second-generation highly cross-linked polyethylene liners at ten years

Aims

Radiostereometric analysis (RSA) is the most accurate radiological method to measure in vivo wear of highly cross-linked polyethylene (XLPE) acetabular components. We have previously reported very low wear rates for a sequentially irradiated and annealed X3 XLPE liner (Stryker Orthopaedics, USA) when used in conjunction with a 32 mm femoral heads at ten-year follow-up. Only two studies have reported the long-term wear rate of X3 liners used in conjunction with larger heads using plain radiographs which have poor sensitivity. The aim of this study was to measure the ten-year wear of thin X3 XLPE liners against larger 36 or 40 mm articulations with RSA.

Methods

We prospectively reviewed 19 patients who underwent primary cementless THA with the XLPE acetabular liner (X3) and a 36 or 40 mm femoral head with a resultant liner thickness of at least 5.8 mm. RSA radiographs at one week, six months, and one, two, five, and ten years postoperatively and femoral head penetration within the acetabular component were measured with UmRSA software. Of the initial 19 patients, 12 were available at the ten-year time point.

Results

The median proximal, 2D, and 3D wear rates calculated between one and ten years were all less than 0.005 mm/year, with no patient recording a proximal wear rate of more than 0.021 mm/year. Importantly, there was no increase in the wear rate between five and ten years.

Conclusion

The very low wear rate of X3 XLPE liners with larger articulations remains encouraging for the future clinical performance of this material.

Risk factors for liner wear and head migration in total hip arthroplasty: a systematic review

Total hip arthroplasty (THA) is a successful orthopaedic surgical procedure, and its longevity depends on bearing components and implant fixation. Optimizing polyethylene and ceramics has led to improved wear parameters and contributed to improved long-term outcomes. The present systematic review investigated whether time span from implantation, patient characteristics and performance status exert an influence on liner wear and head migration in THA. This study was conducted in conformity to the 2020 PRISMA guidelines. All the clinical investigations which reported quantitative data on the amount of liner wear and head migration in THA were considered. Only studies which reported quantitative data at least on one of the following patient characteristics were suitable: mean age, mean BMI (kg/m2), sex, side, time span between the index THA and the last follow-up (months) were eligible. A multiple linear model regression analysis was employed to verify the association between patient characteristics and the amount of liner wear and/or head migration. The Pearson Product-Moment Correlation Coefficient was used to assess the association between variables. Data from 12,629 patients were considered. The mean length of the follow-up was 90.5 ± 50.9 months. The mean age of patients at surgery was 58.4 ± 9.4 years, and the mean BMI was 27.2 ± 2.5 kg/m2. 57% (7199 of 12,629 patients) were women, and in 44% (5557 of 12,629 patients) THAs were performed on the left. The mean pre-operative Harris hip score was 46.5 ± 6.0 points. There was evidence of a moderate positive association between the amount of liner wear and the time elapsed between the index surgery to the follow-up (P = 0.02). There was evidence of a moderate positive association between the amount of head migration and the time elapsed between the index surgery to the follow-up (P = 0.01). No further statistically significant association was found. The time elapsed between the index surgery to the follow-up was the most important factor which influence the head migration and liner wear in THA. Patients' characteristics and preoperative physical activity did not influence the amount of head migration and liner wear.

Ultra-High-Molecular-Weight Polyethylene in Hip and Knee Arthroplasties

Ultra-high-molecular-weight polyethylene (UHMWPE) wear and particle-induced osteolysis contribute to the failure of total hip arthroplasty (THA) and total knee arthroplasty (TKA). Highly crosslinked polyethylene (HXLPE) was developed in the late 1990s to reduce wear and has shown lower wear rates and loosening than conventional UHMWPE in THA. The irradiation dose for crosslinking is up to 100 kGy. However, during crosslinking, free radical formation induces oxidation. Using HXLPE in THA, the cumulative revision rate was determined to be significantly lower (6.2%) than that with conventional UHMWPE (11.7%) at a mean follow-up of 16 years, according to the Australian Orthopaedic Association National Joint Replacement Registry. However, HXLPE does not confer to TKA the same advantages it confers to THA. Several alternatives have been developed to prevent the release of free radicals and improve polymer mechanical properties, such as thermal treatment, phospholipid polymer 2-methacryloyloxyethyl phosphorylcholine grafting, remelting, and vitamin E addition. Among these options, vitamin E addition has reported good clinical results and wear resistance similar to that of HXLPE without vitamin E, as shown by short-term clinical studies of THA and TKA. This review aims to provide a comprehensive overview of the development and performance of UHMWPE in THA and TKA.