Peat-based activated carbons as adsorbents for simultaneous separation of organic molecules from mixed solution of poly(acrylic acid) polymer and sodium dodecyl sulfate surfactant

Preparation of multi-modified/carbonized/gelatinized starch and its de-risking effect on Cd(II) and hymexazol in wastewater

In this study, starch (S) was gelatinized and carbonized to prepare carbonized/gelatinized S (CGS) as the research material. Then, peat extract (Pe) and surfactants with different ratios were single- and multi-modified on CGS, respectively, to prepare Pe-modified CGS (Pe-CGS) and multi-modified CGS, respectively. The microscopic morphology of multi-modified CGS was studied using various testing methods. The de-risking effect on Cd(II) and hymexazol in wastewater was investigated, and the effects of temperature, pH, and ionic strength were compared. The spheroidal structure of S was destroyed after carbonization, and Pe and surfactants were modified on the surface and changed the surface properties of CGS. The adsorption processes of Cd(II) and hymexazol were suitable to be described by the Langmuir and Freundlich models, respectively. The maximum adsorption capacities (qm) of Cd(II) and adsorption capacity parameter (k) of hymexazol on different modified CGSs presented the peak value at BS/Pe-CGS. With the increase in the modification ratio of Pe, BS, and SDS, qm and k increased, which showed a high value at 100 % modification. Increases in temperature and pH were beneficial to Cd(II) adsorption but were not conducive to hymexazol adsorption. The adsorption amount decreased for Cd(II) and increased first and then reduced for hymexazol with the rise in ionic strength. The adsorption process exhibited spontaneity, endothermic behavior for Cd(II), exothermic behavior for hymexazol, and an entropy-increasing reaction. The adsorption amount of Cd(II) and hymexazol by multi-modified CGS maintained approximately 81 % of the original sample after three rounds of regeneration.

Physicochemical and Adsorption Properties of Nanoporous Activated Biocarbons from Thermochemical Treatment of Horsetail Herb

In this study, the adsorption characteristics of novel activated biocarbons prepared from horsetail herb (a popular and troublesome weed) by physical activation (using carbon dioxide) and chemical one (using phosphoric(V) acid) in the process of simultaneous proteins immobilization in multicomponent solutions were examined. The carbon materials were characterized in terms of their porous structure, acidic-basic properties, and surface morphology. The binding mechanisms of such proteins as bovine serum albumin (BSA) and lysozyme (LSZ), differing in internal stability, were determined alone and in their blends. This was done based on the comprehensive analysis of the results of adsorption/desorption, surface, electrokinetic and stability measurements. These experiments were carried out over a wide pH range of 3-11. They included the following issues: (1) determination of the protein adsorbed/desorbed amounts on/from a surface of activated biocarbons; (2) study of the kinetics of these processes; (3) examination of the macromolecules impact on the surface charge density and zeta potential of the carbon materials; and (4) determination of the suspension stability and size of aggregates formed in the examined systems. The analysis of the obtained results indicated the differences in the binding mechanism of both proteins that is of key importance for their simultaneous immobilization on activated biocarbons surface in the soil environment.

Adsorption Capacity of Carbon-Silica Composites Towards Diclofenac in Poly(acrylic acid) Containing Systems: A Crucial Study on Common Wastewater Contaminants

Diclofenac is one of the most popular over-the-counter non-steroidal anti-inflammatory drug and poly(acrylic acid) is a frequently used as thickener, filler or stabilizer. For these reasons, they are common organic contaminants in raw wastewater. The purpose of the presented studies was to compare the adsorption capacity of three carbon-silica composites - metal-free C/SiO2, iron-enriched C/Fe/SiO2 and manganese-enriched C/Mn/SiO2 towards diclofenac. The studies were carried out in single, and mixed systems in the presence of poly(acrylic acid) polymer. Adsorption, desorption and kinetics of the adsorption process were investigated. The concentration of diclofenac in the supernatants was determined using high-performance liquid chromatography. The solids were also characterized with an ASAP apparatus using low-temperature nitrogen desorption adsorption isotherms at liquid nitrogen temperature. In addition, potentiometric titrations and electrophoretic mobility measurements, as well as stability tests of the studied suspensions were carried out. The most efficient composite among investigated ones proved to be C/Fe/SiO2 removing diclofenac at the level of 46.68 mg/g for its initial concentration of 90 ppm. The results obtained clearly demonstrated that the carbon-silica composites are effective in separation of drugs from aqueous solutions and can be successfully used in the future for the removal of organic pollutants from water environment.

Removal of Organic Dyes, Polymers and Surfactants Using Carbonaceous Materials Derived from Walnut Shells

A series of new granular carbonaceous adsorbents was prepared via single-stage physical and chemical activation of walnut shells. Their suitability for removing various types of organic pollutants (represented by dyes, surfactants and water-soluble polymers) from the liquid phase was assessed. The activation of the precursor was carried out with CO2 and H3PO4 using conventional heating. Activated biocarbons were characterized in terms of chemical composition, acidic-basic nature of the surface, textural and electrokinetic properties as well as thermal stability. Depending on the type of activating agent used during the activation procedure, the obtained biocarbons differed in terms of specific surface area (from 401 to 1361 m2/g) and the type of porous structure produced (microporosity contribution in the range of 45-75%). Adsorption tests proved that the effectiveness of removing organic pollutants from the liquid phase depended to a large extent on the type of prepared adsorbent as well as the chemical nature and the molecular size of the adsorbate used. The chemically activated sample showed greater removal efficiency in relation to all tested pollutants. Its maximum adsorption capacity for methylene blue, poly(acrylic acid), poly(ethylene glycol) and Triton X-100 reached the levels of 247.1, 680.9, 38.5 and 61.8 mg/g, respectively.

Adsorption of Organic Pollutants on Carbonaceous Adsorbents Prepared by Direct Activation of Sweet Cherry Stones

The main objective of this study was to assess the usefulness of the sweet cherry stones for the production of carbonaceous adsorbents by means of direct physical activation method, using conventional and microwave variant of heating. The adsorbents were characterized in terms of textural parameters, acidic-basic character of the surface, electrokinetic properties and their suitability for drinking water purification. Adsorption tests were carried out against three organic compounds - Triton X-100 (surfactant), bovine serum albumin (protein) and methylene blue (synthetic dye). Depending on the variant of heating applied during activation procedure, the obtained activated biochars differed significantly in terms of the elemental composition, acidic-basic properties as well as degree of specific surface development and the type of porous structure generated. Adsorption tests have showed that the efficiency of organic pollutants removal from aqueous solutions depends significantly not only on the type of the adsorbent and adsorbate applied, but also on the temperature and pH of the system. The sample prepared by microwave-assisted direct activation proved to be very effective in terms of all tested organic pollutants adsorption. The maximum sorption capacity toward Triton X-100, bovine serum albumin and methylene blue reached the level of 86.5, 23.4 and 81.1 mg/g, respectively.

Investigation of Ionic Polymers' Stabilizing and Flocculating Properties in Dispersed Activated Carbons Systems

Activated carbons obtained via the thermochemical treatment of lemon balm and mint herbs were applied for ionic polymers adsorption, which directly affects the stability of these types of aqueous suspensions. The examined carbonaceous materials were characterized by well-developed specific surface area (approximately 1000 m2/g) and mesoporous structure. The adsorbed amounts of anionic poly(acrylic acid) and cationic polyethyleneimine from one-component solutions reached significant levels, but the efficiency of adsorption of these compounds from binary solutions slightly decreased. Moreover, the ionic polymers showed stabilizing properties towards the activated carbons suspensions. For both adsorbents, the most stable suspensions were systems containing both types of polymeric macromolecules with different ionic characters. This was due to the occurrence of electrosteric and depletion stabilization mechanisms. Furthermore, the zeta potential and size of particle aggregates were also influenced by the presence of polymers in the aqueous suspensions of activated carbons.

Management of hazardous fly-ash energy waste in the adsorptive removal of diclofenac by the use of synthetic zeolitic materials

Zeolite-carbon composites (Na-P1(C), Na-X(C)) and pure zeolites (Na-P1, Na-X) were synthesized from hazardous high-carbon fly ash waste (HC FA) via hydrothermal reaction with sodium hydroxide (NaOH). These solids were applied in the removal of diclofenac (DCF) from aqueous solution, with and without poly(acrylic acid) (PAA). The experiments included adsorption-desorption measurements, as well as electrokinetic and stability analyses. The obtained results showed that HC FA and Na-P1(C) had the greatest adsorption capacity towards DCF, i.e., 26.51 and 21.19 mg/g, respectively. PAA caused considerable decrease in the DCF adsorption due to the competition of both adsorbates of anionic character for active sites. For example, the adsorbed amount of DCF on Na-P1 without PAA was 14.11 mg/g, whereas the one measured with PAA was 5.08 mg/g. Most of prepared solids were effectively regenerated by the use of NaOH. Desorption degree reached even 73.65% in the single systems (with one adsorbate) and 97.24% in the mixed ones (with two adsorbates). Zeolitic materials formed suspensions of rather low stability, which underwent further deterioration in the organic molecules presence. All the results obtained in this study indicated that HC FA can be successfully managed in the removal of organic substances.

Production of Activated Carbons from Food/Storage Waste

This paper deals with the adsorption of organic and inorganic pollutants on the surface of carbonaceous adsorbents prepared via the chemical activation of expired or broken food products-the solid residue of the "cola-type" drink as well as spoilt grains of white rice and buckwheat groats. The activation process was conducted in the microwave furnace with the use of two activating agents of different chemical nature-potassium carbonate and orthophosphoric acid. The activated carbons were characterized based on the results of elemental analysis, low-temperature nitrogen adsorption/desorption, Boehm titration, thermal analysis, and scanning electron microscopy. Additionally, the suitability of the materials prepared as the adsorbents of methylene blue and iodine from the aqueous solutions was estimated. The materials obtained via chemical activation with H₃PO₄ turned out to be much more effective in terms of both model pollutant adsorptions. The maximum sorption capacity toward iodine (1180 mg/g) was found for the white-rice-based activated carbon, whereas the most effective in the methylene blue removal (221.3 mg/g) was the sample obtained from the solid residue of the expired "cola-type" drink. For all carbonaceous materials, a better fit for the experimental adsorption data was obtained with the Langmuir isotherm model than the Freundlich one.

Temperature Effect on Ionic Polymers Removal from Aqueous Solutions Using Activated Carbons Obtained from Biomass

The main aim of this study was the determination of temperature influence on adsorption mechanisms of anionic poly(acrylic acid) (PAA) and cationic polyethylenimine (PEI) on the surface of activated carbons (AC) obtained via chemical activation of nettle (NE) and sage (SA) herbs. All measurements were performed at pH 3 at three temperature values, i.e., 15, 25 and 35 °C. The adsorption/desorption of these polymers from single and mixed solution of adsorbates was also investigated. The viscosity studies were additionally performed to obtain hydrodynamic radius values characterizing polymeric macromolecules conformation in the solution. These data are very important for the explanation of changes of linear dimensions of polymer chains with the rise of temperature caused by the modification of polymer-solvent interactions. Moreover, the XPS studies for the systems showing the highest adsorbed amounts in the specific temperature conditions were carried out. These were the systems containing PEI, PAA and NE-AC activated carbon at 25 °C. In such a case, the maximum adsorption capacity towards PAA macromolecules from a single solution of adsorbate reaches the value of 198.12 mg/g. Additionally, the thermodynamic parameters including the free energies of adsorption, as well as changes in free enthalpy and entropy were calculated.

Simultaneous Removal of Polymers with Different Ionic Character from Their Mixed Solutions Using Herb-Based Biochars and Activated Carbons

Nettle and the sage herbs were used to obtain carbonaceous adsorbents. For the biochar preparation the precursors were dried and subjected to conventional pyrolysis. Activated carbons were obtained during precursor impregnation with phosphoric(V) acid and multistep pyrolysis. The textural parameters and acidic-basic properties of the obtained adsorbents were studied. The activated carbons prepared from the above herbs were characterized by the largely developed specific surface area. The obtained carbonaceous adsorbents were used for polymer removal from aqueous solution. Poly(acrylic acid) (PAA) and polyethylenimine (PEI) were chosen, due to their frequent presence in wastewater resulting from their extensive usage in many industrial fields. The influence of polymers on the electrokinetic properties of activated carbon were considered. PAA adsorption caused a decrease in the zeta potential and the surface charge density, whereas PEI increased these values. The activated carbons and biochars were used as polymer adsorbents from their single and binary solutions. Both polymers showed the greatest adsorption at pH 3. Poly (acrylic acid) had no significant effect on the polyethylenimine adsorbed amount, whereas PEI presence decreased the amount of PAA adsorption. Both polymers could be successfully desorbed from the activated carbons and biochar surfaces. The presented studies are innovatory and greatly required for the development of new environment protection procedures.

Nanoporous carbon materials as a sustainable alternative for the remediation of toxic impurities and environmental contaminants: A review

Due to rapidly deteriorating water resources, the world is looking forward to a sustainable alternative for the remediation of noxious pollutants such as heavy metals and organic and gaseous contaminants. To address this global issue of environmental pollution, nanoporous carbon materials (NPCMs) can be used as a one-stop solution. They are widely applied as adsorbents for many toxic impurities and environmental contaminants. The present review provides a detailed overview of the role of different synthesis factors on the porous characteristics of carbon materials, activating agents, reagent-precursor ratio and their potential application in the remediation. Findings revealed that synthetic parameters result in the formation of microporous NPCMs (S_BET: >4000 m³/g; V_Total (cm³/g) ≥ 2; V_Micro (cm³/g) ≥ 1), micromesoporous (S_BET: >2500 m³/g; V_Total (cm³/g) ≥ 1.5; V_Micro (cm³/g) ≥ 0.7) and mesoporous (S_BET: >2500 m³/g; V_Total (cm³/g) ≥ 1.5; V_Micro (cm³/g) ≥ 0.5) NPCMs. Moreover, it was observed that a narrow pore size distribution (0.5-2.0 nm) yields excellent results in the remediation of noxious contaminants. Further, chemical activating agents such as NaOH, KOH, ZnCl₂, and H₃PO₄ were compared. It was observed that activating agents KОН, H₃PO₄, and ZnCl₂ were generally used and played a significant role in the possible large-scale production and commercialization of NPCMs. Thus, it can be interpreted that with a well-planned strategy for the synthesis, NPCMs with a "tuned" porosity for a specific application, in particular, microporosity for the accumulation and adsorption of energetically important gases (CO₂, CH₄, H₂), micro-mesoporosity and mesoporosity for high adsorption capacity for towards metal ions and a large number of dyes, respectively.

Carbon-Silica Composite as Adsorbent for Removal of Hazardous C.I. Basic Yellow 2 and C.I. Basic Blue 3 Dyes

Treatment of wastewaters containing hazardous substances such as dyes from the textile, paper, plastic and food industries is of great importance. Efficient technique for the removal of highly toxic organic dyes is adsorption. In this paper, adsorptive properties of the carbon-silica composite (C/SiO2) were evaluated for the cationic dyes C.I. Basic Blue 3 (BB3) and C.I. Basic Yellow 2 (BY2). The sorption capacities were determined as a function of temperature (924.6-1295.9 mg/g for BB3 and 716.3-733.2 mg/g for BY2 at 20-60 °C) using the batch method, and the Langmuir, Freundlich and Temkin isotherm models were applied for the equilibrium data evaluation using linear and non-linear regression. The rate of dye adsorption from the 100 mg/L solution was very fast, after 5 min. of phase contact time 98% of BB3 and 86% of BY2 was removed by C/SiO2. Presence of the anionic (SDS), cationic (CTAB) and non-ionic (Triton X-100) surfactants in the amount of 0.25 g/L caused decrease in BB3 and BY2 uptake. The electrokinetic studies, including determination of the solid surface charge density and zeta potential of the composite suspensions in single and mixed adsorbate systems, were also performed. It was shown that presence of adsorption layers changes the structure of the electrical double layer formed on the solid surface, based on the evidence of changes in ionic composition of both surface layer and the slipping plane area. The greatest differences between suspension with and without adsorbates was obtained in the mixed dye + SDS systems; the main reason for this is the formation of dye-surfactant complexes in the solution and their adsorption at the interface.

Study on Adsorption and Aggregation in the Mixed System of Polyacrylamide, Cu(II) Ions and Innovative Carbon-Silica Composite

The paper presents an original study on adsorption and aggregation phenomena in a mixed system consisting of a macromolecular compound, heavy metal ions and an innovative adsorbent. The authors used ionic polyacrylamides (PAM), Cu(II) ions and carbon–silica composite (C-SiO₂) in the experiments. Such a system has not yet been described in the literature and therefore, the article is of significant novelty and great importance. The composite was prepared by mixing phenol–formaldehyde resin with silica and pyrolysis at 800 °C. The adsorbed amounts of Cu(II) ions and PAM were determined spectrophotometrically. C-SiO₂ was characterized using potentiometric titration, microelecrophoresis and Fourier Transform Infrared Spectroscopy (FTIR) analysis. In turn, the C-SiO₂ aggregation was established turbidimetrically as well as using a particle size analyzer. The obtained results indicated that both Cu(II) ions and ionic polyacrylamide were adsorbed on the composite surface at pH 6. The highest noted adsorbed amounts were 9.8 mg/g for Cu(II) and 35.72 mg/g for CT PAM-25%. Cu(II) ions increased the anionic PAM adsorbed and reduced the cationic PAM one. The adsorption of anionic PAM (50 ppm) stimulated the solid aggregation significantly. What is more, Cu(II) ions enhanced this process. The size of particles/aggregates formed without additives equaled 0.44 μm, whereas in the mixed Cu(II)/AN PAM system, they were even at 1.04 μm.