Synergistic flame retardancy of linear low-density polyethylene with surface modified intumescent flame retardant and zinc borate

Synergistic effect of modified anhydrous magnesium carbonate and hexaphenoxycyclotriphosphazene on flame retardancy of ethylene-vinyl acetate copolymer

Ethylene-vinyl acetate copolymer (EVA) is widely used in various applications; however, its flammability limits its application in wire and cable industries. In this study, 3-methacryloxypropyltrimethoxysilane (KH570) was successfully grafted onto the surface of anhydrous magnesium carbonate (AMC) by alkali activation treatment. The KH570 modified AMC (AMC@KH570) was then introduced into the EVA matrix along with hexaphenoxycyclotriphosphazene (HPCTP) to assess their effects on the flame retardancy and mechanical properties of EVA composites. The results illustrate a significant synergistic effect in enhancing the flame retardancy of EVA composites by using AMC@KH570 and HPCTP, and the limiting oxygen index (LOI) and vertical burning test (UL-94) of EVA filled with 5 wt% HPCTP and 45 wt% AMC@KH570 (mAMC/H-45-5) reached 27.6% and V-0, respectively. The flame retardant mechanism was investigated by thermogravimetric/infrared (TG-IR) spectroscopy and residual carbon composition analysis. The results show that the thermal decomposition of AMC@KH570 and HPCTP consists of gas dilution, free radical quenching, and catalytic carbonization. Furthermore, KH570 works as a bridge to improve the compatibility of AMC and EVA matrix, which offsets the mechanical loss of EVA to some extent. The present research provides a new path to modify AMC and fabricate EVA composites with excellent flame retardant properties.

Effect of Functionalized Polyethylene Wax on the Melt Processing and Properties of Highly Filled Magnesium Hydroxide/Linear Low-Density Polyethylene Composites

The poor processing and rheological properties of highly filled composites caused by the high loading of fillers can be improved with the use of maleic anhydride grafted polyethylene wax (PEWM) as compatibilizer and lubricant. In this study, two PEWMs with different molecular weights were synthesized by melt grafting, and their compositions and grafting degrees were characterized by Fourier transform infrared (FTIR) spectroscopy and acid-base titration. Subsequently, magnesium hydroxide (MH)/linear low-density polyethylene (LLDPE) composites with 60 wt% of MH were prepared using polyethylene wax (PEW) and PEWM, respectively. The equilibrium torque and melt flow index tests indicate that the processability and fluidity of MH/MAPP/LLDPE composites are significantly improved with the addition of PEWM. The addition of PEWM with a lower molecular weight leads to a substantial reduction in viscosity. The mechanical properties are also increased. The limiting oxygen index (LOI) test and cone calorimeter test (CCT) show that both PEW and PEWM have adverse effects on flame retardancy. This study provides a strategy to simultaneously improve the processability and mechanical properties of highly filled composites.

Synergistic Flame Retardant Properties of Polyoxymethylene with Surface Modified Intumescent Flame Retardant and Calcium Carbonate

Ammonium polyphosphate (APP) was successfully modified by a titanate coupling agent which was compounded with benzoxazine (BOZ) and melamine (ME) to become a new type of intumescent flame retardant (Ti-IFR). Ti-IFR and CaCO₃ as synergists were utilized to modify polyoxymethylene (POM), and the flame-retardant properties and mechanism of the composites were analyzed by vertical combustion (UL-94), limiting oxygen index (LOI), TG-IR, and cone calorimeter (Cone), etc. The results show that Ti-IFR can enhance the gas phase flame retardant effect, while CaCO₃ further strengthens the barrier effect in the condensed phase. When they were used together, they can exert their performance, respectively, at the same time showing excellent synergistic effect. The FR-POM composite with 29% Ti-IFR and 1% CaCO₃ can pass the UL-94 V0 level. The LOI reaches 58.2%, the average heat release (Av HRR) is reduced by 81.1% and the total heat release (THR) is decreased by 35.3%.

Recent Advances in Halogen-Free Flame Retardants for Polyolefin Cable Sheath Materials

With the continuous advancements of urbanization, the demand for power cables is increasing to replace overhead lines for energy transmission and distribution. Due to undesirable scenarios, e.g., the short circuit or poor contact, the cables can cause fire. The cable sheath has a significant effect on fire expansion. Thus, it is of great significance to carry out research on flame-retardant modification for cable sheath material to prevent fire accidents. With the continuous environmental concern, polyolefin (PO) is expected to gradually replace polyvinyl chloride (PVC) for cable sheath material. Moreover, the halogen-free flame retardants (FRs), which are the focus of this paper, will replace the ones with halogen gradually. The halogen-free FRs used in PO cable sheath material can be divided into inorganic flame retardant, organic flame retardant, and intumescent flame retardant (IFR). However, most FRs will cause severe damage to the mechanical properties of the PO cable sheath material, mainly reflected in the elongation at break and tensile strength. Therefore, the cooperative modification of PO materials for flame retardancy and mechanical properties has become a research hotspot. For this review, about 240 works from the literature related to FRs used in PO materials were investigated. It is shown that the simultaneous improvement for flame retardancy and mechanical properties mainly focuses on surface treatment technology, nanotechnology, and the cooperative effect of multiple FRs. The principle is mainly to improve the compatibility of FRs with PO polymers and/or increase the efficiency of FRs.