Effect of polyacrylic acid on dentin protease activities

Impact of cathepsin K-induced proteoglycans degradation on dentin collagen

OBJECTIVES

This study aimed to investigate the effects of cathepsin K (catK) on proteoglycans (PGs) and the subsequent impacts on dentin collagen degradation.

MATERIALS AND METHODS

Demineralized dentin samples were prepared and divided into the following groups: deionized water (DW), 0.1 U/mL chondroitinase ABC (C-ABC), and 1 μM odanacatib (ODN). Then, they were immersed for 48 h and then incubated in 1 mL of PBS (pH=5.5) at 37 °C for 5 d. Glycosaminoglycan (GAG) were examined to explore the degradation of PGs by catK. To determine the effect of catK-mediated PGs on dentin collagen degradation, hydroxyproline (HYP) assays, assessment of the degree of dentin crosslinking, and scanning electron microscopy (SEM) were assessed. Statistical analysis was conducted using one-way ANOVA followed by Tukey's tests or Welch's ANOVA followed by Dunnett's tests at a significance level of 0.05.

RESULTS

The production of GAG was significantly lower in the ODN group than in the DW group (P < 0.05), revealing that PG degradation was reduced in dentin after ODN treatment. Additionally, ODN treatment minimized the gaps in collagen fibers, improved fiber arrangement, and significantly increased the degree of collagen crosslinking, subsequently reducing the total amount of collagen fiber degradation in the dentin (P < 0.05).

CONCLUSIONS

CatK-mediated degradation of PGs negatively impacted the stability of collagen fibers, promoted gaps, led to a less organized arrangement of dentin collagen fibers, ultimately increasing collagen degradation.

Longitudinal bond strength of a universal adhesive and chemical dentin characterization under different acid etching protocols

OBJECTIVE

This study aimed to analyze the longitudinal bond strength of a universal adhesive and chemically characterize the dentin substrate under different acid etching protocols.

METHODOLOGY

Dentin samples were etched with polyacrylic acid 25% (PAA) for 10 seconds (n=3) and phosphoric acid 32% (PA) for 15 seconds (n=3) and analyzed by Fourier transform infrared spectroscopy - attenuated total reflectance (FTIR-ATR) before and after treatment. For collagen degradation, samples (n=12) were divided into 3 groups: PAA, PA, and Deionized water (control), and analyzed by the quantity of solubilized type I collagen C-terminal cross-linked telopeptides and solubilized C-terminal peptide in relation to total protein concentration (ICTPtp and CTXtp) and by their ultimate tensile strength (UTS). For the adhesive interface analysis, dentin samples (n=72) were divided into 3 groups: PAA, PA, and Self-etch (SE), and subdivided into 2 groups: 24 h (baseline) and 1 year. The following tests were performed: microtensile bond strength (μTBS) (n=48), scanning electron microscopy (SEM) (n=12), and nanoleakage (n=12).

RESULTS

The FTIR of PAA showed lower reduction of the peaks in the phosphate group when compared to PA. For ICTPtp, PA showed a significantly higher value. For CTXtp, PA and PAA groups failed to statically differ from each other. UTS was significantly lower for PA. For μTBS, storage time significantly affected bond strength. The results were unaffected by the etching protocol. For SEM, after 1 year, PA had little evidence of degradation in the upper third of the adhesive interface in comparison to the other groups. Nanoleakage showed no considerable silver impregnation after 1 year in the SE group.

CONCLUSION

The use of PAA prior to a universal adhesive (when compared to PA) represents a less aggressive type of etching to dentin. However, self-etching still seems to be the best option for universal adhesive systems that have functional monomers in their composition.

Mineralization promotion and protection effect of carboxymethyl chitosan biomodification in biomimetic mineralization

Biomimetic mineralization emphasizes reversing the process of dental caries through bio-inspired strategies, in which mineralization promotion and collagen protection are equally important. In this study, carboxymethyl chitosan (CMC) was deemed as an analog of glycosaminoglycan for biomimetic modification of collagen, both of the mineralization facilitation and collagen protection effect were evaluated. Experiments were carried out simultaneously on two-dimensional monolayer reconstituted collagen model, three-dimensional reconstituted collagen model and demineralized dentin model. In three models, CMC was successfully cross-linked onto collagen utilizing biocompatible 1-Ethyl-3(3-dimethylaminopropyl) carbodiimide hydrochloride and N-hydroxy sulfosuccinimide sodium salt to achieve biomodification. Results showed that CMC biomodification increased collagen's hydrophilicity, calcium absorption capacity and thermal degradation resistance. In demineralized dentin model, the activity of endogenous matrix metalloproteinases was significantly inhibited by CMC biomodification. Furthermore, CMC biomodification significantly improved cross-linking and intrafibrillar mineralization of collagen, especially in the two-dimensional monolayer reconstituted collagen model. This study provided a biomimetic mineralization strategy with comprehensive consideration of collagen protection, and enriched the application of chitosan-based materials in dentistry.

Effect of Odanacatib on the release of NTX (Amino Terminal Telopeptide) from LPS contaminated type I dentin collagen

OBJECTIVE

To evaluated the Odanacatib inhibitor treatment on lipopolysaccharide (LPS) contamination effect on cathepsin-K mediated dentin degradation by analysis of type I collagen C- and N-termini telopeptides.

METHODS

Pulverized and disks of human dentin were demineralized and LPS contaminated, or stored in deionized water (DW) for 12 h. Samples were challenged with lactic acid (LA). Aliquots of dentin powder were treated with 1 mL Odanacatib or stored in DW for 30 min. Dentin collagen degradation was determined by sub-product release of C-terminal (ICTP and CTX) and N-terminal (NTX) telopeptides, normalized to total protein (tp) concentration (n = 3). Dentin matrix was evaluated for gravimetric (n = 8) and ultrastructural changes. Data were analyzed by Student t-test, one-way ANOVA and Tukey's test (α = 5 %).

RESULTS

LA incubation significantly increased telopeptide release compared with DW (p < 0.05). In untreated groups, significantly higher CTXtp, NTXtp telopeptide rates were observed for LA+LPS samples compared with DW (p < 0.01). Odanacatib significantly reduced ICTPtp, CTXtp, and NTXtp telopeptide release for LPS, LA, and LA+LPS conditions. In untreated groups, LPS and LA+LPS challenge significantly increased dentin weight loss (p = 0.02). Within each storage condition, Odanacatib treatment did not affect weight change (p > 0.05) of dentin disks.

SIGNIFICANCE

This study showed that LPS contamination resulted in significantly higher rates of NTX than CTX from dentin matrix. Odanacatib significantly reduced telopeptide release rates of LPS contaminated dentin matrix.

The inhibitory effects of various ions released from S-PRG fillers on dentin protease activity

This study investigates the effect of ions released from S-PRG fillers on host-derived enzymatic degradation of dentin collagen matrices. Dentin beams (n=80) were demineralized and distributed to eight groups following baseline dry mass and total MMP activity assessments. Each group treated with boron, fluoride, sodium, silicone, strontium, aluminium, or S-PRG eluate solutions for 5 min. Untreated beams served as control. After pre-treatment, MMP activity was reassessed, beams were incubated in complete medium for 1 week, dry mass was reassessed. Incubation media were analyzed for MMP and cathepsin-K-mediated degradation fragments. Data were analyzed with ANOVA and Tukey's test. All pretreatment groups showed significant reduction in total MMP activity (p<0.05) that was sustainable after incubation in all groups except for boron and silicone groups (p<0.05). Cathepsin-K activity did not differ between control or treatment groups. The results indicated that ions released from S-PRG fillers have the potential to partly inhibit MMP-mediated endogenous enzymatic activity.

Dual function of quercetin as an MMP inhibitor and crosslinker in preventing dentin erosion and abrasion: An in situ/in vivo study

OBJECTIVE

The aim of the present study was to evaluate the in situ/in vivo effect of quercetin on dentin erosion and abrasion.

METHODS

Human dentin blocks (2 × 2 × 2 mm) were embedded and assigned to 6 groups: 75 μg/mL, 150 μg/mL and 300 μg/mL quercetin (Q75, Q150, Q300); 120 μg/mL chlorhexidine (CHX, positive control); and deionized water and ethanol (the negative controls). The specimens were treated with the respective solutions for 2 min and then subjected to in situ/in vivo erosive/abrasive challenge for 7 d as follows: in vivo erosion 4 times a day and then in vivo toothbrush abrasion after the first and last erosive challenges of each day. Dentin loss was assessed by profilometry. An additional dentin specimen was used to evaluate the penetration depth of quercetin into dentin by tracking the spatial distribution of its characteristic Raman peak. Moreover, dentin blocks (7 × 1.7 × 0.7 mm) were used to detect the impact of quercetin on dentin-derived matrix metalloproteinase (MMP) inhibition by in situ zymography, and the inhibition percentage (%) was calculated. Additionally, the potential collagen crosslinking interactions with quercetin were detected by Raman spectroscopy, and the crosslinking degree was determined with a ninhydrin assay. Fully demineralized dentin beams (0.5 × 0.5 × 10 mm) were used to evaluate the impact of quercetin on the mechanical properties of dentin collagen fibre by the ultimate micro-tensile strength test (μUTS). The data were analysed by one-way analysis of variance and Tukey's test (α = 0.05).

RESULTS

Compared to the negative controls, all treatment solutions significantly reduced dentin loss. The dentin loss of Q150 and Q300 was significantly less than that of CHX (all P < 0.05). The amount of quercetin decreased with increasing dentin depth, and the maximum penetration depth was approximately 25-30 µm. In situ zymography showed that quercetin significantly inhibited the activities of dentin-derived MMPs. The inhibitory percentages of Q75 and Q150 were significantly lower than that of CHX (all P < 0.05), but no significant difference was found between Q300 and CHX (P = 0.58). The collagen crosslinking interactions with quercetin primarily involved hydrogen bonding and the degree of crosslinking increased in a concentration-dependent manner. Statistically significant increases in μUTS values were observed for demineralized dentin beams after quercetin treatment compared with those of the control treatments (all P < 0.05).

SIGNIFICANCE

This study provides the first direct evidence that quercetin could penetrate approximately 25-30 µm into dentin and further prevent dentin erosion and abrasion by inhibiting dentin-derived MMP activity as well as crosslinking collagen of the demineralized organic matrix.

Captopril inhibits matrix metalloproteinase activity and improves dentin bonding durability

OBJECTIVES

We investigated the inhibitory effects of captopril on matrix metalloproteinases (MMPs) and its effect as a primer on dentin bonding durability.

MATERIALS AND METHODS

One hundred fifty human third molars were selected. Flat surfaces of the middle dentin were exposed, etched 15 s, and followed by pretreatment with a primer for 60 s, including distilled water (control, the negative control primer), 2% chlorhexidine digluconate (CHD, the positive control primer), and captopril solution. Inhibitory effects of primers on MMPs were evaluated by hydroxyproline and gelatinase activity tests. All primers were applied on dentin followed by bonding. Some of the samples were sliced into slabs, placed in a fluorescent solution containing gelatin, and incubated for in situ zymography. Some were cut into sticks, and after aging for 1 day, 12 months, or 24 months, microtensile bonding strength was tested. Some were cut into slabs, aged for 1 day, 12 months, or 24 months, and taken out for nanoleakage tests to reveal interface defects.

RESULTS

Hydroxyproline and gelatinase activity analyses showed that captopril exerted better inhibitory effects on MMPs, relative to 2% CHD (p < 0.05). A 0.2% captopril aqueous solution (0.2% CapW) was chosen to apply to the dentin. In situ zymography showed that inhibitory effects of captopril on gelatinase were significantly higher compared to 2% CHD (p < 0.01). Microtensile strength revealed that the bonding effects of the 0.2% CapW group lasted longer, compared to the control and 2% CHD groups (p < 0.05). Interface defects, detected by nanoleakage, were significantly reduced in the 0.2% CapW group, compared to the control and 2% CHD groups (p < 0.05).

CONCLUSIONS

Captopril inhibits dentin MMP activities and effectively improves dentin bonding durability.

CLINICAL RELEVANCE

Captopril is a promising dentin bonding primer for improving bonding durability.

The effect of phytic acid on enzymatic degradation of dentin

We evaluated the effect of phytic acid on matrix metalloproteinase (MMP)- or cysteine cathepsin (CC)-mediated dentin degradation. Demineralized dentin beams were divided into five groups (n = 12) and treated with 1%, 2%, or 3% phytic acid or with 37% phosphoric acid. Untreated demineralized beams served as controls. After incubation for 1 or 3 wk, dry mass loss was determined and aliquots of incubation media were analysed for cross-linked telopeptide of type I collagen (ICTP) fragments for MMP-mediated and c-terminal telopeptide of type I collagen (CTX) for cathepsin-k-mediated degradation. The direct effect of phytic acid was evaluated using MMP activity assay. Data were analysed using repeated-measures anova. ICTP releases with 1% and 2% phytic acid treatment were statistically significantly lower than those following phosphoric acid treatment at 3 wk. The CTX release for phytic acid-treated beams at 3 wk was not significantly different from that of untreated control beams, but it was significantly lower than that of phosphoric acid-treated beams. Their MMP activities at 3 wk were not significantly different from those of the controls but they were significantly lower than those seen for phosphoric acid-treated beams. Compared to phosphoric acid, phytic acid treatment resulted in a reduced dentinal host-derived endogenous enzymatic activity and collagen degradation.

Effect of protease inhibitor specificity on dentin matrix properties

OBJECTIVE

To evaluate protease activity of dentin matrices subjected to treatment with non-specific (chlorhexidine - CHX), cysteine cathepsin specific (E-64), and cysteine cathepsin-K (CT-K) specific (Odanacatib - ODN) inhibitors.

METHODS

Pulverized dentin powder obtained from human dentin disks (0.5 mm thickness) completely demineralized with 10% H₃PO₄ were challenged in 1 mL lactic acid (LA) (0.1M, pH 5.5) or stored in deionized water for 30 min. Aliquots of dentin powder were then immersed in 1 mL of CHX (2%), E-64 (10 μM and 20 μM) or Odanacatib (0.2 nM and 1 μM) for 30min. Degradation of dentin collagen was determined by telopeptide assays measuring the sub-product release of C-terminal cross-linked telopeptides (ICTP) and C-terminal peptide (CTX) in incubation media, which correlates with matrix metalloproteinases (MMP) and CT-K activities respectively (n = 3). The ICTP and CTX data were normalized to concentration of total protein (ICTP_tp and CTX_tp) in the media, measured by bicinchoninic acid assay. Dentin matrix properties were also measured by gravimetric change (n = 8) and ultimate tensile strength (UTS) (n = 10). Data were analyzed by one-way ANOVA followed by Tukey's post-hoc test and independent t-test (α = 5%).

RESULTS

Telopeptide assays showed significantly lower CTX_tp values after treatment with E-64 and Odanacatib. E-64 and Odanacatib at all tested concentrations significantly reduced the release of ICTP_tp. Gravimetric analysis showed no significant difference between the tested inhibitors and control except for CHX after lactic acid challenge. UTS results showed significantly higher values for E-64 (20 μM) and Odanacatib (0.2 nM and 1 μM) groups in deionized water.

SIGNIFICANCE

Dentin therapies targeting enzymes such as CT-K by specific inhibitors may provide superior pharmacokinetics and optimum efficacy due to precise protein binding, consequently limiting collagen degradation directly or indirectly by enzyme related pathways.

Alternative model for cathepsin K activation in human dentin

OBJECTIVE

To evaluate the protease activity in dentin matrices subjected to lactic acid (LA) in comparison to polyacrylic acid (PAA) challenge model at cathepsin K (CT-K) optimum pH 5.5 to assess effectiveness of inhibitors in dentin collagen degradation.

METHODS

Dentin disks measuring 0.5mm prepared from human molars were completely demineralized in 10% H₃PO₄. Demineralized dentin disks were challenged with 0.1M LA, 1.1mM PAA, artificial saliva (AS), or deionized water (C) for 24h or 7-days. Dentin collagen properties were tested by measurement of %dry mass change, and ultimate tensile strength (UTS). Degradation of dentin type I collagen was measured by telopeptide assays measuring the sub-product release of C-terminal cross-linked telopeptides (ICTP) and C-terminal peptide (CTX) in the incubation media in relation to total protein concentration, which correlates with matrix metalloproteinases (MMPs) and CT-K activities.

RESULTS

Gravimetric analysis showed statistically significant difference between C and other groups (p<0.04) at 24h. LA specimens showed significantly higher weight loss from 24h to 7-days (p=0.02). UTS revealed statistically significant difference between AS and LA at 24h and 7-days. UTS at 24h and 7-days for C and AS had significantly higher mean values compared to LA and PAA. Telopeptide assays reported that CTX_tp results showed that LA at 24h had significantly higher mean values compared to C and AS.

SIGNIFICANCE

LA has the ability to activate endogenous CT-K in dentin as measured by the release of CTX (CT-K specific telopeptide). This LA based model has the potential application for further investigations on the activity and possible inhibitors of CT-K in human dentin.

Inhibition of dentin matrix-bound cysteine cathepsins by potassium fluoride

Matrix metalloproteinases (MMPs) and cysteine cathepsins (CCs) can break down unprotected type I collagen fibrils in dentin matrix. This study investigated the use of potassium fluoride (KF) as a potential inhibitor of MMPs and CCs in dentin. Demineralized dentin beams were divided into groups (n = 10 in each group) and incubated in artificial saliva (AS, control), either alone or with one of seven concentrations of KF (6-238 mM fluoride) for 1, 7, and 21 d. After 21 d, all groups were further aged in AS for 6 months. Total MMP activity was screened using the colorimetric MMP assay. The activities of MMP-2 and MMP-9 were investigated using gelatin zymography. At the end of each incubation, changes in loss of dry mass and CC-mediated or total dissolution of collagen peptides were measured via precision weighing, C-terminal crosslinked telopeptide of type I collagen (CTX), and hydroxyproline (HYP) assays. The beams were examined using scanning electron microscopy. After 21 d, total MMP activities, dry mass loss, and CTX release for the groups exposed to 179 and 238 mM fluoride were significantly lower compared with the control group. After 6 months, all groups showed similar total MMP activity, dry mass loss, and HYP release, and CTX levels were significantly lower when the fluoride concentration was ≥24 mM. Calcium fluoride (CaF₂ )-like precipitates were observed over the beams. In summary, KF significantly inhibited the catalytic activity of dentin matrix-bound CCs but did not seem to be effective for MMP-mediated activity.

Effects of caffeic acid phenethyl ester application on dentin MMP-2, stability of bond strength and failure mode of total-etch and self-etch adhesive systems

OBJECTIVE

Investigate the long-term effect of dentin pretreatment with 0.05 or 0.1% caffeic acid phenethyl ester (CAPE) on (1) bond strength of resin composite to dentin by a three-step etch-and-rinse (Adper Scotchbond Multipurpose/ ASB) or a two-step self-etch adhesive system (Clearfil SE Bond/ CSE), (2) their fracture mode, (3) the micromorphological features of the hybrid layer formed; and (4) the level of MMP-2 in dentin (after application, using a correlative immunoexpression/quantification approach).

DESIGN

Composite resin blocks were fabricated on 48 third molars (n = 6), according to the type of adhesive and treatment (control, CAPE 0.05% and CAPE 0.1%). Slices were obtained for scanning electron microscopy (SEM) evaluation, and sticks were fabricated for microtensile tests (24 h and 1 year). Aliquots of dentin powder were distributed (n = 12) according to the treatment and the MMP-2 concentration was determined by ELISA.

RESULTS

Tukey test showed that ASB groups presented higher BS in 24 h than CSE groups. ASB presented a reduction in BS values after 1-year. ASB and CSE presented no significant differences in BS after 1-year. CAPE had no effect on BS for both adhesive systems. The predominant failure mode for the ASB groups were adhesive; when 0.1% CAPE was applied there was a predominance of mixed fractures. Regarding the CSE group, 0.05% CAPE led to more adhesive failures, and the 0.1% concentration resulted in a higher number of cohesive failures in dentin. Higher MMP-2 concentrations were detected for the groups that did not undergo demineralization treatment, and the lowest values for the ASB groups treated with CAPE. SEM analysis showed no influence of pretreatment with CAPE.

CONCLUSIONS

CAPE did not influence the BS of the adhesives tested, or the micromorphology of the hybrid layer, irrespective of concentration or storage time. CAPE affected the fracture pattern at 24 h, depending on the concentration and the adhesive system used. Immunoassay analysis showed that CAPE 0.1% reduced the MMP-2 concentration in the ASB adhesive without affecting bond strength to dentin.

Epigallocatechin-3-gallate and Epigallocatechin-3-O-(3-O-methyl)-gallate Enhance the Bonding Stability of an Etch-and-Rinse Adhesive to Dentin

This study evaluated epigallocatechin-3-gallate (EGCG) and epigallocatechin-3-O-(3-O-methyl)-gallate (EGCG-3Me) modified etch-and-rinse adhesives (Single Bond 2, SB 2) for their antibacterial effect and bonding stability to dentin. EGCG-3Me was isolated and purified with column chromatography and preparative high performance liquid chromatography. EGCG and EGCG-3Me were incorporated separately into the adhesive SB 2 at concentrations of 200, 400, and 600 µg/mL. The effect of cured adhesives on the growth of Streptococcus mutans (S. mutans) was determined with scanning electron microscopy and confocal laser scanning microscopy; the biofilm of bacteria was further quantified via optical density 600 values. The inhibition of EGCG and EGCG-3Me on dentin-originated collagen proteases activities was evaluated with a proteases fluorometric assay kit. The degree of conversion (DC) of the adhesives was tested with micro-Raman spectrum. The immediate and post-thermocycling (5000 cycles) bond strength was assessed through Microtensile Bond Strength (MTBS) test. Cured EGCG/EGCG-3Me modified adhesives inhibit the growth of S. mutans in a concentration-dependent manner. The immediate MTBS of SB 2 was not compromised by EGCG/EGCG-3Me modification. EGCG/EGCG-3Me modified adhesive had higher MTBS than SB 2 after thermocycling, showing no correlation with concentration. The DC of the adhesive system was affected depending on the concentration of EGCG/EGCG-3Me and the depth of the hybrid layer. EGCG/EGCG-3Me modified adhesives could inhibit S. mutans adhesion to dentin–resin interface, and maintain the bonding stability. The adhesive modified with 400 µg/mL EGCG-3Me showed antibacterial effect and enhanced bonding stability without affect the DC of adhesive.

Influence of Etching Mode on Enamel Bond Durability of Universal Adhesive Systems

The purpose of this study was to determine the enamel bond durability of three universal adhesives in different etching modes through fatigue testing. The three universal adhesives used were Scotchbond Universal, Prime&Bond Elect universal dental adhesive, and All-Bond Universal light-cured dental adhesive. A single-step self-etch adhesive, Clearfil S³ Bond Plus was used as a control. The shear bond strength (SBS) and shear fatigue strength (SFS) to human enamel were evaluated in total-etch mode and self-etch mode. A stainless steel metal ring with an internal diameter of 2.4 mm was used to bond the resin composite to the flat-ground (4000-grit) tooth surfaces for determination of both SBS and SFS. For each enamel surface treatment, 15 specimens were prepared for SBS and 30 specimens for SFS. The staircase method for fatigue testing was then used to determine the SFS of the resin composite bonded to the enamel using 10-Hz frequencies for 50,000 cycles or until failure occurred. Scanning electron microscopy was used to observe representative debonded specimen surfaces and the resin-enamel interfaces. A two-way analysis of variance and the Tukey post hoc test were used for analysis of the SBS data, whereas a modified t-test with Bonferroni correction was used for the SFS data. All adhesives in total-etch mode showed significantly higher SBS and SFS values than those in self-etch mode. Although All-Bond Universal in self-etch mode showed a significantly lower SBS value than the other adhesives, there was no significant difference in SFS values among the adhesives in this mode. All adhesives showed higher SFS:SBS ratios in total-etch mode than in self-etch mode. With regard to the adhesive systems used in this study, universal adhesives showed higher enamel bond strengths in total-etch mode. Although the influence of different etching modes on the enamel-bonding performance of universal adhesives was found to be dependent on the adhesive material, total-etch mode effectively increased the enamel bond strength and durability, as measured by fatigue testing.

NaF Inhibits Matrix-Bound Cathepsin-Mediated Dentin Matrix Degradation

Matrix metalloproteinases (MMPs) and cysteine cathepsins (CCs) degrade the collagen fibrils of demineralized dentin. Sodium fluoride (NaF) has previously been shown to inhibit recombinant MMP-2 and MMP-9. This study aimed to evaluate the efficacy of NaF on the inhibition of dentin-bound MMPs and CCs. Dentin beams were completely demineralized in 10% phosphoric acid. The baseline total MMP activity and dry masses were measured. Beams were assigned to test groups based on similar MMP activity and dry mass (n = 10/group), and incubated in artificial saliva (control) or artificial saliva with NaF containing 6-238 mM fluoride for 1, 7 and 21 days. The dry mass loss and MMP activities were reassessed at each time point. The proteolytic activity was screened by gelatin zymography. ICTP and CTX released to the incubation medium were analyzed as indices of MMP and cathepsin K activity, respectively. The beams were examined under scanning electron microscopy. All NaF doses reduced the dry mass loss after 21 days (p < 0.05). NaF inhibition of the total MMP activity ranged between 5 and 80%. In gelatin zymography, the bands of MMP-2 and MMP-9 became less prominent with increasing NaF levels. NaF did not decrease the released ICTP (p > 0.05). Less CTX release was detected with F ≥179 mM (p < 0.05). CaF2-like minerals were observed on the beams. High levels of NaF may slow the degradation of the dentin matrix due to the inhibition of cathepsin K. Fluoride does not seem effective in the direct inhibition of proteolysis by dentin matrix-bound MMPs.