Electrosorption of hydrogen into palladium–rhodium alloys

Effect of Hydrogen Electrosorption on Mechanical and Electronic Properties of Pd80Rh20 Alloy

The interaction of hydrogen with Pt-group metals and alloys is at the center of research in the fields of electrochemistry, electrocatalysis, hydrogen technologies and fuel cells developed under the Hydrogen Economy. In this work, the material under study was Pd₈₀Rh₂₀ alloy (50 μm foil) subjected to hydrogen electrosorption at potentials corresponding to formation of α, α-β and β phase in 0.1 M H₂SO₄ at 25 °C. The total amount of hydrogen adsorbed at the surface and absorbed in octahedral interstitial positions of fcc Pd₈₀Rh₂₀ alloy, was determined from the oxidation charges. The H/(Pd+Rh) was 0.002, 0.4 and 0.8 for α, α-β, and β Pd₈₀Rh₂₀H, respectively. Microindentation hardness testing and nanoindentation showed weakening of mechanical properties of the Pd₈₀Rh₂₀ alloy after hydrogen electrosorption due to internal stresses. Decrease of work function with increasing amount of hydrogen absorbed occurred due to the surface roughness changes and the presence of electropositive hydrogen atoms absorbed in the crystal lattice responsible for the dipole interaction. The detailed mechanism of hydrogen absorption/diffusion in the Pd₈₀Rh₂₀ alloy structure is discussed. The obtained results give a new insight into the relationship between the amount of absorbed hydrogen and mechanical and electronic properties of the Pd₈₀Rh₂₀ alloy at the micro- and nanoscale.

On the Nature of Voltammetric Signals Originating from Hydrogen Electrosorption into Palladium-Noble Metal Alloys

Hydrogen sorption/desorption signals observed on cyclic voltammograms in experiments on hydrogen electrosorption into Pd-noble metal alloys (Pd-Au, Pd-Pt, Pd-Rh, Pd-Ru, Pd-Pt-Rh, Pd-Pt-Au) were characterized. The influence of electrosorption potential, scan rate and alloy bulk composition on the features of the hydrogen peaks was investigated. The experimental results were compared with those obtained on the basis of a model taken from the literature. It was confirmed that the rate of the α-β phase transition controls the overall rate of the process of hydrogen absorption/desorption into/from thin Pd-based electrodes. It was demonstrated that from the analysis of the changes of the hydrogen oxidation peak potential with the hydrogen electrosorption potential in cyclic voltammetric experiments it is possible to determine the limiting Pd bulk content, below which the β-phase in the alloy-hydrogen system is not formed.

Hydrogen electrosorption into Pd-Cd nanostructures

Hydrogen-absorbing materials are crucial for both the purification and storage of hydrogen. Pd and Pd-based alloys have been studied extensively for their use as both hydrogen dissociation catalysts and hydrogen selective membrane materials. It is known that incorporating metal atoms of different sizes into the Pd lattice has a major impact on the hydrogen absorption process. In this paper, hydrogen electrosorption into nanostructured Pd-Cd alloys has been studied for different compositions of Cd that varied from 0 to 15 at. %. The low cost of Cd makes it an attractive material to combine with Pd for hydrogen sorption. A combination of chronoamperometry and cyclic voltammetric experiments was used to determine the ratio of the H/(Pd + Cd) and the kinetics of hydrogen sorption into these Pd-Cd alloys at different potentials. It was found that the maximum H/(Pd + Cd) value was 0.66 for pure Pd, and this decreased with increasing the amount of Cd. Also, the alpha (solid solution) to beta phase (metal hydride) hydrogen transition was determined to be the slowest step in the absorption process and was practically eliminated when an optimum amount of Cd atoms was doped (i.e., Pd-Cd(15%)). With increasing the amount of Cd, more hydrogen was absorbed into the Pd-Cd nanostructures at the higher potentials (the alpha phase region). The faster kinetics, along with the decrease in the phase transition of hydrogen sorption into the Pd-Cd nanostructures when compared to pure Pd, makes the Pd-Cd nanostructures attractive for use as a hydrogen dissociation catalytic capping layer for other metal hydrides or as a hydrogen selective membrane.