Development of an Al3+ ion-selective microelectrode for the potentiometric microelectrochemical monitoring of corrosion sites on 2098−T351 aluminum alloy surfaces

Effect of Redox Mediators on Corrosion Behavior and Scanning Electrochemical Microscopy Response

Scanning electrochemical microscopy (SECM) is widely used to measure local electrochemical reactivity of corroding surfaces. A major criticism of using SECM in feedback mode for corrosion studies is the requirement of an external redox mediator (RM) as it could react with the metal and affect the Nernst potential at the metal-solution interface. Consequently, it becomes challenging to differentiate the interference caused by the RM from the local reactivity of the metal. Herein, a multiscale electrochemical approach is presented to investigate the effect of RM choice on the corroding substrate. Two common RMs, ferrocenemethanol and hexaammineruthenium(III) chloride, were used to perform SECM over copper and aluminum. It was found during macroscale electrochemical measurements that Ru(NH)63+ acted as an oxidant and promoted corrosion. The SECM feedback behavior varied for copper depending on the RM used, suggesting that the corrosion reactions controlled the negative feedback mechanism, not the formation of an insulating passive film. The passivated aluminum surface consistently exhibited negative feedback, regardless of the RM used. SECM approach curves also displayed a distortion in the steady state current, which was caused by the deposition of substrate-generated species on the microelectrode. These deviations in feedback response were accounted for during analysis through incorporation into a finite element model to accurately extract the RM kinetic rate constants. The importance of understanding these processes is highlighted to avoid misinterpretation of passive behavior and advances toward a more quantitative use of SECM for corrosion studies.

Crevice Corrosion Behavior of 201 Stainless Steel in NaCl Solutions with Different pH Values by In Situ Monitoring

Crevice corrosion (CC) behavior of 201 stainless steel (SS) in 1 M NaCl + x M HCl/y M NaOH solutions with various pH was investigated using SECM and optical microscopic observations. Results show that the CC was initiated by the decrease in pH value within the crevice. The pH value near the crevice mouth falls rapidly to 1.38 in the first 2 h in the strongly acidic solution, while the pH value was observed to rise firstly and then decrease in the neutral and alkaline solutions. It indicates there is no incubation phase in the CC evolution of 201-SS in a pH = 2.00 solution, while an incubation phase was observed in pH = 7.00 and 11.00 solutions. Additionally, there appeared to be a radial pH variation within the gap over time. The pH value is the lowest at the gap mouth, which is in line with the in situ optical observation result that the severely corroded region is at the mouth of the gap. The decrease in pH value inside results in the negative shift of open circuit potential (OCP) and the initiation of CC of 201-SS. The increased anodic dissolution rate in the acidic solution accelerates the breakdown of passive film inside, reducing the initiation time and stimulating the spread of CC.