Synthesis, molecular structure and catalytic performance of heterocycle-fused cyclopentadienyl-amido CGC of Ti (IV) in ethylene (co)polymerization: The formation and precision rheometry of long-chain branched polyethylenes

Mechanistic Insights of Ethylene Polymerization on Phillips Chromium Catalysts

Silica-supported chromium oxide catalysts, also named Phillips chromium catalysts (PCCs), provide more than half of the world's production of high- and medium-density polyethylenes. PCCs are usually prepared in the Cr(VI)/SiO2 form, which is subjected to reductive activation. It has been explicitly proven that CO reduces Cr(VI) to Cr(II) species that initiate ethylene polymerization; ethylene activates Cr(VI) sites as well, but the nature of the catalytic species is complicated by the presence of the ethylene oxidation products. It is widely accepted that the catalytic species are of a Cr(III)-alkyl nature, but this common assumption faces the challenge of "extra" hydrogen: the formation of similar species under the action of even-electron reducing agents requires an additional H atom. Relatively recently, it was found that saturated hydrocarbons can also activate CrOx/SiO2, and alkyl fragments turn out to be bonded with a polyethylene chain. In recent years, there have been numerous experimental and theoretical studies of the structure and chemistry of PCCs at the different stages of preparation and activation. The use of modern spectral methods (such as extended X-ray absorption fine structure (EXAFS), X-ray absorption near-edge structure (XANES), and others); operando IR, UV-vis, EPR, and XAS spectroscopies; and theoretical approaches (DFT modeling, machine learning) clarified many essential aspects of the mechanisms of CrOx/SiO2 activation and catalytic behavior. Overall, the Cosse-Arlman mechanism of polymerization on Cr(III)-alkyl centers is confirmed in many works, but its theoretical support required the development of nontrivial and contentious mechanistic concepts of Cr(VI)/SiO2 or Cr(II)/SiO2 activation. On the other hand, conflicting experimental data continue to be obtained, and certain mechanistic concepts are being developed with the use of outdated models. Strictly speaking, the main question of what type of catalytic species, Cr(II), Cr(III), or Cr(IV), comes into polymerization still has not received an unambiguous answer. The role of the chemical nature of the support-through the prism of the nature, geometry, and distribution of the active sites-is also not clear in depth. In the present review, we endeavored to summarize and discuss the recent studies in the field of the preparation, activation, and action of PCCs, with a focus on existing contradictions in the interpretation of the experimental and theoretical results.

Asphaltenes from Heavy Crude Oil as Ultraviolet Stabilizers against Polypropylene Aging

The destruction of polymers under the influence of ultraviolet (UV) radiation is the cause of their aging and deterioration of strength properties. Asphaltenes are low-value waste products after the refining and deasphalting of heavy crude oil, which absorb UV radiation well. Asphaltenes require rational utilization, which suggests their use as UV stabilizing agents for polymers. In this work, asphaltenes were used to prevent UV aging of polypropylene (PP) by adding them in a mass fraction from 5% to 30% within an asphaltene/PP composite material. Rheometry, calorimetry, X-ray diffraction analysis, and tensile strength of PP films containing asphaltenes were performed before and after their intense UV irradiation for accelerated aging. Asphaltenes slightly reduce the viscosity, crystallinity, and mechanical strength of the initial PP due to their plasticizing effect. However, this deterioration in properties is more than compensated when studying UV-aged samples. Intense UV aging causes multiple catastrophic drops in the viscosity and strength of pure PP with the preservation of crystallinity due to the break of polymer chains and a decrease in molecular weight by approximately eight times. Asphaltenes suppress the destruction of PP, which is expressed in a significantly smaller decline in its viscosity and strength due to UV aging. The most optimal content of asphaltenes is 20%, which suppresses UV destruction by six times and best preserves the strength properties of PP.

Dispersant and Protective Roles of Amphiphilic Poly(ethylene phosphate) Block Copolymers in Polyester/Bone Mineral Composites

Composites of synthetic bone mineral substitutes (BMS) and biodegradable polyesters are of particular interest for bone surgery and orthopedics. Manufacturing of composite scaffolds commonly uses mixing of the BMS with polymer melts. Melt processing requires a high homogeneity of the mixing, and is complicated by BMS-promoted thermal degradation of polymers. In our work, poly(L-lactide) (PLLA) and poly(ε-caprolactone) (PCL) composites reinforced by commercial β-tricalcium phosphate (βTCP) or synthesized carbonated hydroxyapatite with hexagonal and plate-like crystallite shapes (hCAp and pCAp, respectively) were fabricated using injection molding. pCAp-based composites showed advanced mechanical and thermal characteristics, and the best set of mechanical characteristics was observed for the PLLA-based composite containing 25 wt% of pCAp. To achieve compatibility of polyesters and pCAp, reactive block copolymers of PLLA or PCL with poly(tert-butyl ethylene phosphate) (C1 and C2, respectively) were introduced to the composite. The formation of a polyester-b-poly(ethylene phosphoric acid) (PEPA) compatibilizer during composite preparation, followed by chemical binding of PEPA with pCAp, have been proved experimentally. The presence of 5 wt% of the compatibilizer provided deeper homogenization of the composite, resulting in a marked increase in strength and moduli as well as a more pronounced nucleation effect during isothermal crystallization. The use of C1 increased the thermal stability of the PLLA-based composite, containing 25 wt% of pCAp. In view of positive impacts of polyester-b-PEPA on composite homogeneity, mechanical characteristics, and thermal stability, polyester-b-PEPA will find application in the further development of composite materials for bone surgery and orthopedics.

Asphaltene-Stabilized Polyisobutylene Pressure-Sensitive Adhesives for Ultraviolet Protection and Surface Bonding

The usual way to protect indoor areas from solar UV radiation is to use UV-absorbing materials, which are applied as a thin film on the surface of the windowpane. Asphaltenes are useless wastes from crude oil refining that absorb UV radiation well, which gave the idea of their use in protective coatings. Pressure-sensitive adhesives based on polyisobutylene containing from 5 to 30 wt% of asphaltenes were obtained. Deterioration of the adhesive properties with the introduction of 5-20 wt% of asphaltenes was shown by adhesion tests, which can be associated with the plasticization of the polymer matrix. At the same time, the use of 30 wt% of asphaltenes leads to the polymer matrix reinforcement with the restoration of adhesive properties to the original level or even slightly higher. The rheological study of adhesives at 25 °C and 120 °C showed the structural network formation by asphaltenes at a content of 30 wt%, explaining the increase in adhesion performance. According to microscopy, asphaltenes are flat brown glass shards in a polymer matrix. They absorb electromagnetic radiation, predominantly in the UV range, while maintaining relative translucency in the visible range. This makes it possible to obtain thin films from the asphaltene-filled adhesive for bonding glass sheets to produce UV-blocked and tinted windowpanes.