Forghani S, Almasi H. Characterization and performance evaluation of colorimetric pH-sensitive indicator based on Ҡ-carrageenan/quince seed mucilage hydrogel as freshness/spoilage monitoring of rainbow trout fillet. Food Chem 2024; 457:140072. [PMID: 38905838 DOI: 10.1016/j.foodchem.2024.140072] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 04/18/2024] [Revised: 06/03/2024] [Accepted: 06/10/2024] [Indexed: 06/23/2024]
Abstract
The aim of research was to fabricate a novel indicator by using κ-carrageenan and quince seed mucilage (QSM) hydrogels and red cabbage anthocyanin. The porosity of the hydrogel was controlled using different ratios of κ-carrageenan(C):QSM(Q) (C90:Q10, C70:Q30, and C50:Q50). The hardness of hydrogels decreased from 28.6 ± 0.3 N for C90Q10 to 11.0 ± 1.0 N for C50Q50 sample. However, according to field emission scanning electron microscopy (FE-SEM) analysis, the C50R50 sample had the best morphology with smooth surface and uniform interconnected porous network. Hydrogen bonding interactions among anthocyanins, QSM, and κ-carrageenan were confirmed by Fourier transforms infrared (FT-IR) spectroscopy. The indicator showed a color variation from red to yellow over the pH range of 2-12. Also, the indicator exhibited high sensitivity to ammonia vapors (SRGB = 115%) and good color stability. The C50QRA indicator was used for monitoring rainbow trout fillet spoilage and revealed a visually-detectable color change from red to green upon detecting total volatile basic nitrogen (TVB-N) content produced throughout storage at 4 °C. Generally, the halochromic hydrogel developed in this research can be suggested as a more sensitive and accurate freshness indicator than conventional indicator solid supports.
Collapse
Affiliation(s)
- Samira Forghani
- Department of Food Science and Technology, Faculty of Agriculture, Urmia University, Urmia, P.O. Box 57561-51818, Iran
| | - Hadi Almasi
- Department of Food Science and Technology, Faculty of Agriculture, Urmia University, Urmia, P.O. Box 57561-51818, Iran.
| |
Collapse
|
2
|
Fatima Z, Fatima S, Muhammad G, Hussain MA, Raza MA, Amin M, Majeed A. Stimuli-responsive glucuronoxylan polysaccharide from quince seeds for biomedical, food packaging, and environmental applications. Int J Biol Macromol 2024; 273:133016. [PMID: 38876235 DOI: 10.1016/j.ijbiomac.2024.133016] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/26/2024] [Revised: 05/25/2024] [Accepted: 06/06/2024] [Indexed: 06/16/2024]
Abstract
Mucilage is a gelatinous mixture of polysaccharides secreted from the seed coat and/or pericarp of many plant seeds when soaked in water. Mucilage affected seed germination while maintaining hydration levels during scarcity. Cydonia oblonga (quince) seeds are natural hydrocolloids extruding biocompatible mucilage mainly composed of polysaccharides. Quince seed mucilage (QSM) has fascinated researchers due to its applications in the food and pharmaceutical industries. On a commercial scale, QSM preserved the sensory and physiochemical properties of various products such as yogurt, desserts, cakes, and burgers. QSM is responsive to salts, pH, and solvents and is mainly investigated as edible coatings in the food industry. In tablet formulations, modified and unmodified QSM as a binder sustained the release of various drugs such as cefixime, capecitabine, diclofenac sodium, theophylline, levosulpiride, diphenhydramine, metoprolol tartrate, and acyclovir sodium. QSM acted as a reducing and capping agent to prepare nanoparticles for good antimicrobial resistance, photocatalytic characteristics, and wound-healing potential. The present review discussed the extraction optimization, chemical composition, stimuli-responsiveness, and viscoelastic properties of mucilage. The potential of mucilage in edible films, tissue engineering, and water purification will also be discussed.
Collapse
Affiliation(s)
- Zain Fatima
- Department of Chemistry, Government College University Lahore, 54000 Lahore, Pakistan
| | - Seerat Fatima
- Department of Chemistry, Pakistan Institute of Engineering and Applied Sciences, Islamabad, Pakistan
| | - Gulzar Muhammad
- Department of Chemistry, Government College University Lahore, 54000 Lahore, Pakistan.
| | - Muhammad Ajaz Hussain
- Centre for Organic Chemistry, School of Chemistry, University of the Punjab, Lahore 54590, Pakistan
| | - Muhammad Arshad Raza
- Department of Chemistry, Government College University Lahore, 54000 Lahore, Pakistan
| | - Muhammad Amin
- Department of Chemistry, University of Lahore, Sargodha Campus, Pakistan
| | - Aamna Majeed
- Department of Chemistry, Government College University Lahore, 54000 Lahore, Pakistan
| |
Collapse
|
3
|
Yildirim-Semerci Ö, Bilginer-Kartal R, Arslan-Yildiz A. Arabinoxylan-based psyllium seed hydrocolloid: Single-step aqueous extraction and use in tissue engineering. Int J Biol Macromol 2024; 270:131856. [PMID: 38693000 DOI: 10.1016/j.ijbiomac.2024.131856] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/15/2024] [Revised: 04/16/2024] [Accepted: 04/23/2024] [Indexed: 05/03/2024]
Abstract
Biomacromolecules derived from natural sources offer superior biocompatibility, biodegradability, and water-holding capacity, which make them promising scaffolds for tissue engineering. Psyllium seed has gained attention in biomedical applications recently due to its gel-forming ability, which is provided by its polysaccharide-rich content consisting mostly of arabinoxylan. This study focuses on the extraction and gelation of Psyllium seed hydrocolloid (PSH) in a single-step water-based protocol, and scaffold fabrication using freeze-drying method. After characterization of the scaffold, including morphological, mechanical, swelling, and protein adsorption analyses, 3D cell culture studies were done using NIH-3 T3 fibroblast cells on PSH scaffold, and cell viability was assessed using Live/Dead and Alamar Blue assays. Starting from day 1, high cell viability was obtained, and it reached 90 % at the end of 15-day culture period. Cellular morphology on PSH scaffold was monitored via SEM analysis; cellular aggregates then spheroid formation were observed throughout the study. Collagen Type-I and F-actin expressions were followed by immunostaining revealing a 9- and 10-fold increase during long-term culture. Overall, a single-step and non-toxic protocol was developed for extraction and gelation of PSH. Obtained results unveiled that PSH scaffold provided a favorable 3D microenvironment for cells, holding promise for further tissue engineering applications.
Collapse
Affiliation(s)
- Özüm Yildirim-Semerci
- Department of Bioengineering, Izmir Institute of Technology (IZTECH), 35430 Izmir, Turkey
| | | | - Ahu Arslan-Yildiz
- Department of Bioengineering, Izmir Institute of Technology (IZTECH), 35430 Izmir, Turkey.
| |
Collapse
|
4
|
Köksal B, Kartal RB, Günay US, Durmaz H, Yildiz AA, Yildiz ÜH. Fabrication of gelatin-polyester based biocomposite scaffold via one-step functionalization of melt electrowritten polymer blends in aqueous phase. Int J Biol Macromol 2024; 265:130938. [PMID: 38493814 DOI: 10.1016/j.ijbiomac.2024.130938] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 08/19/2023] [Revised: 02/29/2024] [Accepted: 03/14/2024] [Indexed: 03/19/2024]
Abstract
The rapid manufacturing of biocomposite scaffold made of saturated-Poly(ε-caprolactone) (PCL) and unsaturated Polyester (PE) blends with gelatin and modified gelatin (NCO-Gel) is demonstrated. Polyester blend-based scaffold are fabricated with and without applying potential in the melt electrowriting system. Notably, the applied potential induces phase separation between PCL and PE and drives the formation of PE rich spots at the interface of electrowritten fibers. The objective of the current study is to control the phase separation between saturated and unsaturated polyesters occurring in the melt electro-writing process and utilization of this phenomenon to improve efficiency of biofunctionalization at the interface of scaffold via Aza-Michael addition reaction. Electron-deficient triple bonds of PE spots on the fibers exhibit good potential for the biofunctionalization via the aza-Michael addition reaction. PE spots are found to be pronounced in which blend compositions are PCL-PE as 90:10 and 75:25 %. The biofunctionalization of scaffold is monitored through CN bond formation appeared at 400 eV via X-ray photoelectron spectroscopy (XPS) and XPS chemical mapping. The described biofunctionalization methodology suggest avoiding use of multi-step chemical modification on additive manufacturing products and thereby rapid prototyping of functional polymer blend based scaffolds with enhanced biocompatibility and preserved mechanical properties. Additionally one-step additive manufacturing method eliminates side effects of toxic solvents and long modification steps during scaffold fabrication.
Collapse
Affiliation(s)
- Büşra Köksal
- Department of Chemistry, Izmir Institute of Technology, 35430 Urla, İzmir, Turkey
| | | | - Ufuk Saim Günay
- Department of Chemistry, Istanbul Technical University, 34469 Maslak, İstanbul, Turkey
| | - Hakan Durmaz
- Department of Chemistry, Istanbul Technical University, 34469 Maslak, İstanbul, Turkey
| | - Ahu Arslan Yildiz
- Department of Bioengineering, Izmir Institute of Technology, 35430 Urla, İzmir, Turkey
| | - Ümit Hakan Yildiz
- Department of Chemistry, Izmir Institute of Technology, 35430 Urla, İzmir, Turkey; Department of Polymer Science and Engineering, Izmir Institute of Technology, 35430 Urla, İzmir, Turkey.
| |
Collapse
|
5
|
Ahmadzadeh-Hashemi S, Varidi M, Nooshkam M. Hydro- and aerogels from quince seed gum and gelatin solutions. Food Chem X 2023; 19:100813. [PMID: 37780320 PMCID: PMC10534173 DOI: 10.1016/j.fochx.2023.100813] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 03/04/2023] [Revised: 07/15/2023] [Accepted: 07/24/2023] [Indexed: 10/03/2023] Open
Abstract
The composite hydro/aerogels were designed using gelatin and quince seed gum (QSG) at total polymer concentration (TPC) of 1, 1.5 and 2% and gelatin/QSG ratio of 1:0, 1:0.5 and 1:1. The gel syneresis decreased significantly with increase in TPC and QSG. Although, hydrogels with 2% TPC had remarkably higher gel strength and elasticity than 1% TPC ones, the addition of high levels of QSG to the gelatin (i.e., gelatin/QSG 1:1) led to a decrease in its gel strength (∼0.97-fold) and elasticity (∼3,463-fold). The temperature-sweep test showed higher melting points in gelatin/QSG hydrogels (>60 °C) compared to the gelatin ones (∼58 °C). Additionally, QSG addition to the gelatin led to more porous networks with higher gel strength, thermal stability, and crystallinity, as observed by scanning electron microscopy, differential scanning calorimetry, and X-ray diffractometer. Therefore, QSG could be used as a natural hydrocolloid to modify gelatin functionality.
Collapse
Affiliation(s)
- Saba Ahmadzadeh-Hashemi
- Department of Food Science and Technology, Faculty of Agriculture, Ferdowsi University of Mashhad (FUM), Mashhad, Iran
| | - Mehdi Varidi
- Department of Food Science and Technology, Faculty of Agriculture, Ferdowsi University of Mashhad (FUM), Mashhad, Iran
| | - Majid Nooshkam
- Department of Food Science and Technology, Faculty of Agriculture, Ferdowsi University of Mashhad (FUM), Mashhad, Iran
| |
Collapse
|
6
|
Goksen G, Demir D, Dhama K, Kumar M, Shao P, Xie F, Echegaray N, Lorenzo JM. Mucilage polysaccharide as a plant secretion: Potential trends in food and biomedical applications. Int J Biol Macromol 2023; 230:123146. [PMID: 36610576 DOI: 10.1016/j.ijbiomac.2023.123146] [Citation(s) in RCA: 18] [Impact Index Per Article: 18.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 10/12/2022] [Revised: 12/05/2022] [Accepted: 01/01/2023] [Indexed: 01/05/2023]
Abstract
Current trends are shifting away from using synthetic compounds in favor of discovering new natural component sources that will allow them to create goods that are healthful, environmentally friendly, sustainable, and profitable. The food industry, in light of these trends, has opted to look for safe natural ingredients that will allow the production of low-fat, artificial-additive-free, gluten-free, prebiotic, and fortified foods. Similarly, the pharmaceutical and medical industries have attempted to apply natural ingredients to address the challenges related to biomaterials more efficiently than synthetic ingredients. Against this background, plant mucilage has proven to be a polysaccharide with excellent health features and technological properties, useful for both food and biomedical applications. Many studies have shown that its inclusion in different food matrices improves the quality of the products obtained under appropriate reformulations. At the same time, plant mucilage has been indicated to be a very interesting matrix in biomedical field especially tissue engineering applications since it has been emerged to favor tissue regeneration with its highly biocompatible structure. This concise review discusses the most recent advances of the applications of plant mucilage in different foods as well as its recent use in biomedical field. In this context, firstly, a general definition of mucilage was made and information about plant-based mucilage, which is frequently used, about the plant parts they are found in, their content and how they are obtained are presented. Then, the use of mucilage in the food industry including bakery products, meat emulsions, fermented dairy products, ice cream, and other foods is presented with case studies. Afterwards, the use of plant mucilage in the biomedical field, which has attracted attention in recent years, especially in applications with tissue engineering approach such as scaffolds for tissue regeneration, wound dressings, drug delivery systems and pharmaceutical industry was evaluated.
Collapse
Affiliation(s)
- Gulden Goksen
- Department of Food Technology, Vocational School of Technical Sciences at Mersin Tarsus Organized Industrial Zone, Tarsus University, 33100 Mersin, Turkey
| | - Didem Demir
- Department of Chemistry and Chemical Process Technologies, Vocational School of Technical Sciences at Mersin Tarsus Organized Industrial Zone, Tarsus University, 33100 Mersin, Turkey
| | - Kuldeep Dhama
- Division of Pathology, ICAR-Indian Veterinary Research Institute (IVRI), Izatnagar, 243122 Bareilly, Uttar Pradesh, India
| | - Manoj Kumar
- Chemical and Biochemical Processing Division, ICAR-Central Institute for Research on Cotton Technology, Mumbai 400019, India
| | - Ping Shao
- Department of Food Science and Technology, Zhejiang University of Technology, Zhejiang, Hangzhou 310014, PR China
| | - Fengwei Xie
- School of Engineering, Newcastle University, Newcastle upon Tyne NE1 7RU, United Kingdom
| | - Noemí Echegaray
- Centro Tecnológico de la Carne de Galicia, Parque Tecnológico de Galicia, San Cibrao das Viñas, Avd. Galicia N° 4, 32900 Ourense, Spain
| | - Jose Manuel Lorenzo
- Centro Tecnológico de la Carne de Galicia, Parque Tecnológico de Galicia, San Cibrao das Viñas, Avd. Galicia N° 4, 32900 Ourense, Spain; Área de Tecnología de los Alimentos, Facultad de Ciencias de Ourense, Universidade de Vigo, 32004 Ourense, Spain.
| |
Collapse
|
7
|
Huang X, Ding Y, Pan W, Lu L, Jin R, Liang X, Chang M, Wang Y, Luo X. A Comparative Study on Two Types of Porcine Acellular Dermal Matrix Sponges Prepared by Thermal Crosslinking and Thermal-Glutaraldehyde Crosslinking Matrix Microparticles. Front Bioeng Biotechnol 2022; 10:938798. [PMID: 35992352 PMCID: PMC9388789 DOI: 10.3389/fbioe.2022.938798] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Grants] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 05/08/2022] [Accepted: 06/23/2022] [Indexed: 11/13/2022] Open
Abstract
Common commercial porcine acellular dermal matrix (PADM) products take the form of a thin membrane. Given its dense structure, delaying vascularization after implantation remains an issue to be solved. In addition, overlaying multiple sheets to address deep wounds and large tissue defects that are difficult to repair by self-tissues could hinder tissue ingrowth, angiogenesis, and integration. Here, we creatively prepared PADM microparticles through a homogenizing treatment and crosslinked them to ADM sponges by thermal crosslinking (VT-ADM) and thermal-glutaraldehyde crosslinking (GA-ADM). The resulting VT-ADM was thicker than GA-ADM, and both maintained the natural dermal matrix microstructure and thermal stability. The porosity of GA-ADM (mean 82%) was lower than that of VT-ADM (mean 90.2%), but the mechanical strength and hydrophilicity were significantly higher. The two types of ADM sponges showed no obvious difference in cell adhesion and proliferation without cytotoxicity. Furthermore, the human adipose stem cells were co-cultured with ADM sponges which promoted proliferation, tube formation, and migration of endothelial cells, and the GA-ADM group exhibited better migration behavior. There were no markable differences among expressions of pro-angiogenesis genes, including vascular endothelial growth factor, insulin-like growth factor-1, and epidermal growth factor. In a nude mouse model, the VT-ADM and GA-ADM pre-cultured with human adipose stem cells for 1 week in advance were implanted subcutaneously. The VT-ADM and the GA-ADM showed great histocompatibility without local redness, swelling, or necrosis. The vascular density of the local skin flap above the material was visualized using indocyanine green and showed no statistical difference between the two groups. The collagen tissue deposition in the pores and vessel formation within the sponges increased with time. Although VT-ADM had a higher degradation rate in vivo, the integrity of the two scaffolds was preserved. Collectively, the VT-ADM and the GA-ADM retained a natural matrix structure and presented biocompatibility. Thus, the above-mentioned two crosslinking methods for ADM sponges are safe and practicable. The novel ADM sponges with good physicochemical and biological properties are no longer limited to membrane tissue regeneration but could also realize structure remodeling where they act as scaffolds for a soft tissue filler and three-dimensional reconstruction of the tissue with strength requirements.
Collapse
Affiliation(s)
- Xing Huang
- Department of Plastic and Reconstructive Surgery, Shanghai 9th People’s Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai, China
- Shanghai Key Lab of Tissue Engineering, Shanghai 9th People’s Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai, China
| | - Yi Ding
- Department of Plastic and Reconstructive Surgery, Shanghai 9th People’s Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai, China
| | - Wenqian Pan
- Jiangsu Unitrump Biomedical Technology Co.,Ltd., Jiangsu, China
| | - Lin Lu
- Department of Plastic and Reconstructive Surgery, Shanghai 9th People’s Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai, China
| | - Rui Jin
- Department of Plastic and Reconstructive Surgery, Shanghai 9th People’s Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai, China
| | - Xiao Liang
- Department of Plastic and Reconstructive Surgery, Shanghai 9th People’s Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai, China
| | - Mengling Chang
- Department of Plastic and Reconstructive Surgery, Shanghai 9th People’s Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai, China
| | - Yinmin Wang
- Department of Plastic and Reconstructive Surgery, Shanghai 9th People’s Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai, China
- *Correspondence: Yinmin Wang, ; Xusong Luo,
| | - Xusong Luo
- Department of Plastic and Reconstructive Surgery, Shanghai 9th People’s Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai, China
- *Correspondence: Yinmin Wang, ; Xusong Luo,
| |
Collapse
|
8
|
Naz FF, Shah KU, Niazi ZR, Zaman M, Lim V, Alfatama M. Polymeric Microparticles: Synthesis, Characterization and In Vitro Evaluation for Pulmonary Delivery of Rifampicin. Polymers (Basel) 2022; 14:2491. [PMID: 35746067 PMCID: PMC9230634 DOI: 10.3390/polym14122491] [Citation(s) in RCA: 4] [Impact Index Per Article: 2.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 05/26/2022] [Revised: 06/13/2022] [Accepted: 06/15/2022] [Indexed: 12/10/2022] Open
Abstract
Rifampicin, a potent broad-spectrum antibiotic, remains the backbone of anti-tubercular therapy. However, it can cause severe hepatotoxicity when given orally. To overcome the limitations of the current oral therapy, this study designed inhalable spray-dried, rifampicin-loaded microparticles using aloe vera powder as an immune modulator, with varying concentrations of alginate and L-leucine. The microparticles were assessed for their physicochemical properties, in vitro drug release and aerodynamic behavior. The spray-dried powders were 2 to 4 µm in size with a percentage yield of 45 to 65%. The particles were nearly spherical with the tendency of agglomeration as depicted from Carr’s index (37 to 65) and Hausner’s ratios (>1.50). The drug content ranged from 0.24 to 0.39 mg/mg, with an association efficiency of 39.28 to 96.15%. The dissolution data depicts that the in vitro release of rifampicin from microparticles was significantly retarded with a higher L-leucine concentration in comparison to those formulations containing a higher sodium alginate concentration due to its hydrophobic nature. The aerodynamic data depicts that 60 to 70% of the aerosol mass was emitted from an inhaler with MMAD values of 1.44 to 1.60 µm and FPF of 43.22 to 55.70%. The higher FPF values with retarded in vitro release could allow sufficient time for the phagocytosis of synthesized microparticles by alveolar macrophages, thereby leading to the eradication of M. tuberculosis from these cells.
Collapse
Affiliation(s)
- Faiqa Falak Naz
- Faculty of Pharmacy, Gomal University, Dera Ismail Khan 29050, Pakistan; (F.F.N.); (K.U.S.); (Z.R.N.); (M.Z.)
| | - Kifayat Ullah Shah
- Faculty of Pharmacy, Gomal University, Dera Ismail Khan 29050, Pakistan; (F.F.N.); (K.U.S.); (Z.R.N.); (M.Z.)
| | - Zahid Rasul Niazi
- Faculty of Pharmacy, Gomal University, Dera Ismail Khan 29050, Pakistan; (F.F.N.); (K.U.S.); (Z.R.N.); (M.Z.)
| | - Mansoor Zaman
- Faculty of Pharmacy, Gomal University, Dera Ismail Khan 29050, Pakistan; (F.F.N.); (K.U.S.); (Z.R.N.); (M.Z.)
| | - Vuanghao Lim
- Advanced Medical and Dental Institute, Universiti Sains Malaysia, Bertam, Kepala Batas 13200, Penang, Malaysia
| | - Mulham Alfatama
- Faculty of Pharmacy, Universiti Sultan Zainal Abidin, Besut Campus, Besut 22200, Terengganu, Malaysia
| |
Collapse
|
9
|
Baniasadi H, Kimiaei E, Polez RT, Ajdary R, Rojas OJ, Österberg M, Seppälä J. High-resolution 3D printing of xanthan gum/nanocellulose bio-inks. Int J Biol Macromol 2022; 209:2020-2031. [PMID: 35500781 DOI: 10.1016/j.ijbiomac.2022.04.183] [Citation(s) in RCA: 12] [Impact Index Per Article: 6.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/14/2022] [Revised: 04/05/2022] [Accepted: 04/25/2022] [Indexed: 01/19/2023]
Abstract
The current study provides a comprehensive rheology study and a survey on direct ink writing of xanthan gum/cellulose nanocrystal (XG/CNC) bio-inks for developing 3D geometries that mimic soft tissue engineering scaffolds' physical and mechanical properties. The presence of CNC was found to be a critical prerequisite for the printability of XG bio-inks; accordingly, the hybrid XG/CNC bio-inks revealed the excellent viscoelastic properties that enabled precise control of hydrogel shaping and printing of lattice structures composed of up to eleven layers with high fidelity and fair resolution without any deformation after printing. The lyophilized 3D scaffolds presented a porous structure with open and interconnected pores and a porosity higher than 70%, vital features for tissue engineering scaffolds. Moreover, they showed a relatively high swelling of approximately 11 g/g, facilitating oxygen and nutrient exchange. Furthermore, the elastic and compressive moduli of the scaffolds that enhanced significantly upon increasing CNC content were in the range of a few kPa, similar to soft tissues. Finally, no significant cell cytotoxicity was observed against human liver cancer cells (HepG2), highlighting the potential of these developed 3D printed scaffolds for soft tissue engineering applications.
Collapse
Affiliation(s)
- Hossein Baniasadi
- Polymer Technology, School of Chemical Engineering, Aalto University, Kemistintie 1, 02150 Espoo, Finland
| | - Erfan Kimiaei
- Department of Bioproducts and Biosystems, School of Chemical Engineering, Aalto University, P.O. Box 16300, FIN-00076 Aalto Espoo, Finland
| | - Roberta Teixeira Polez
- Department of Bioproducts and Biosystems, School of Chemical Engineering, Aalto University, P.O. Box 16300, FIN-00076 Aalto Espoo, Finland
| | - Rubina Ajdary
- Department of Bioproducts and Biosystems, School of Chemical Engineering, Aalto University, P.O. Box 16300, FIN-00076 Aalto Espoo, Finland
| | - Orlando J Rojas
- Department of Bioproducts and Biosystems, School of Chemical Engineering, Aalto University, P.O. Box 16300, FIN-00076 Aalto Espoo, Finland; Bioproducts Institute, Departments of Chemical and Biological Engineering, Department of Chemistry and Wood Science, The University of British Columbia, 2360 East Mall, Vancouver, BC V6T 1Z3, Canada
| | - Monika Österberg
- Department of Bioproducts and Biosystems, School of Chemical Engineering, Aalto University, P.O. Box 16300, FIN-00076 Aalto Espoo, Finland
| | - Jukka Seppälä
- Polymer Technology, School of Chemical Engineering, Aalto University, Kemistintie 1, 02150 Espoo, Finland.
| |
Collapse
|
10
|
Akram Ghumman S, Mahmood A, Noreen S, Rana M, Hameed H, Ijaz B, Hasan S, Aslam A, Fayyaz ur Rehman M. Formulation and evaluation of quince seeds mucilage - sodium alginate microspheres for sustained delivery of cefixime and its toxicological studies. ARAB J CHEM 2022. [DOI: 10.1016/j.arabjc.2022.103811] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/17/2022] Open
|
11
|
Cetin Genc C, Yilmaz HD, Karaca B, Kiran F, Arslan YE. Nano-hydroxyapatite incorporated quince seed mucilage bioscaffolds for osteogenic differentiation of human adipose-derived mesenchymal stem cells. Int J Biol Macromol 2022; 195:492-505. [PMID: 34921891 DOI: 10.1016/j.ijbiomac.2021.12.054] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 09/15/2021] [Revised: 12/03/2021] [Accepted: 12/08/2021] [Indexed: 12/28/2022]
Abstract
In this study, the therapeutic hydrocolloid quince seed mucilage (QSM) from Cydonia oblonga Miller fruit is enriched with needle-like nano-hydroxyapatite (nHAp) crystals to fabricate a novel biomimetic osteogenic bioscaffold. The molecular weight (Mw) of water-based extracted QSM was measured with GPC (8.67 × 105 g/mol), and the composite blend was prepared at a ratio of 1:1 (w/w) QSMaq and nHAp. The porous bioscaffolds were manufactured by the freeze-drying method, and evaluated in-depth with advanced analyses. The XRD, ATR-FTIR, SEM-EDX, and elemental mapping analyses revealed a uniform coated semi-crystalline structure with no covalent bindings between QSM and nHAp. Moreover, due to the hydrocolloid backbone, a supreme swelling ratio (w/w, 6523 ± 190%) with suitable pore size (208.12 ± 99.22 μm) for osteogenic development was obtained. Further, the cytocompatible bioscaffolds were evaluated for osteogenic differentiation in vitro using human adipose-derived mesenchymal stem cells (hAMSCs). The immuno/histochemical (I/HC) staining revealed that the cells with the spherical morphology invaded the pores of the prepared bioscaffolds. Also, relatively early up-regulated osteogenic markers were observed by the qRT-PCR analyses. Overall, it is believed that the QSM-nHAp bioscaffolds might be favorable in non-load bearing applications, especially in the cranio-maxillofacial region, due to their regenerative, bendable, and durable features.
Collapse
Affiliation(s)
- Cigdem Cetin Genc
- Department of Oral and Maxillofacial Surgery, Faculty of Dentistry, Canakkale Onsekiz Mart University, 17100 Canakkale, Turkey
| | - Hilal Deniz Yilmaz
- Regenerative Biomaterials Laboratory, Department of Bioengineering, Faculty of Engineering, Canakkale Onsekiz Mart University, 17100 Canakkale, Turkey
| | - Burak Karaca
- Regenerative Biomaterials Laboratory, Department of Bioengineering, Faculty of Engineering, Canakkale Onsekiz Mart University, 17100 Canakkale, Turkey
| | - Fadime Kiran
- Pharmabiotic Technologies Research Laboratory, Department of Biology, Faculty of Science, Ankara University, 06100 Ankara, Turkey
| | - Yavuz Emre Arslan
- Regenerative Biomaterials Laboratory, Department of Bioengineering, Faculty of Engineering, Canakkale Onsekiz Mart University, 17100 Canakkale, Turkey.
| |
Collapse
|
12
|
Yildirim Ö, Arslan-Yildiz A. Development of a hydrocolloid bio-ink for 3D bioprinting. Biomater Sci 2022; 10:6707-6717. [DOI: 10.1039/d2bm01184k] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/21/2022]
Abstract
Development of new hydrocolloid bio-ink from quince seed and utilization for 3D cell culture.
Collapse
Affiliation(s)
- Özüm Yildirim
- Department of Bioengineering, Izmir Institute of Technology (IZTECH), 35430 Izmir, Turkey
| | - Ahu Arslan-Yildiz
- Department of Bioengineering, Izmir Institute of Technology (IZTECH), 35430 Izmir, Turkey
| |
Collapse
|
13
|
3D printing and properties of cellulose nanofibrils-reinforced quince seed mucilage bio-inks. Int J Biol Macromol 2021; 192:1098-1107. [PMID: 34666132 DOI: 10.1016/j.ijbiomac.2021.10.078] [Citation(s) in RCA: 19] [Impact Index Per Article: 6.3] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 08/25/2021] [Revised: 10/05/2021] [Accepted: 10/11/2021] [Indexed: 01/16/2023]
Abstract
Plant-based hydrogels have attracted great attention in biomedical fields since they are biocompatible and based on natural, sustainable, cost-effective, and widely accessible sources. Here, we introduced new viscoelastic bio-inks composed of quince seed mucilage and cellulose nanofibrils (QSM/CNF) easily extruded into 3D lattice structures through direct ink writing in ambient conditions. The QSM/CNF inks enabled precise control on printing fidelity where CNF endowed objects with shape stability after freeze-drying and with suitable porosity, water uptake capacity, and mechanical strength. The compressive and elastic moduli of samples produced at the highest CNF content were both increased by ~100% (from 5.1 ± 0.2 kPa and 32 ± 1 kPa to 10.7 ± 0.5 and 64 ± 2 kPa, respectively). These values ideally matched those reported for soft tissues; accordingly, the cell compatibility of the printed samples was evaluated against HepG2 cells (human liver cancer). The results confirmed the 3D hydrogels as being non-cytotoxic and suitable to support attachment, survival, and proliferation of the cells. All in all, the newly developed inks allowed sustainable 3D bio-hydrogels fitting the requirements as scaffolds for soft tissue engineering.
Collapse
|
14
|
Dybka-Stępień K, Otlewska A, Góźdź P, Piotrowska M. The Renaissance of Plant Mucilage in Health Promotion and Industrial Applications: A Review. Nutrients 2021; 13:nu13103354. [PMID: 34684354 PMCID: PMC8539170 DOI: 10.3390/nu13103354] [Citation(s) in RCA: 17] [Impact Index Per Article: 5.7] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 09/02/2021] [Revised: 09/20/2021] [Accepted: 09/22/2021] [Indexed: 12/13/2022] Open
Abstract
Plant mucilage is a renewable and cost-effective source of plant-based compounds that are biologically active, biodegradable, biocompatible, nontoxic, and environmentally friendly. Until recently, plant mucilage has been of interest mostly for technological purposes. This review examined both its traditional uses and potential modern applications in a new generation of health-promoting foods, as well as in cosmetics and biomaterials. We explored the nutritional, phytochemical, and pharmacological richness of plant mucilage, with a particular focus on its biological activity. We also highlighted areas where more research is needed in order to understand the full commercial potential of plant mucilage.
Collapse
|
15
|
Zhang M, Wang G, Zhang X, Zheng Y, Lee S, Wang D, Yang Y. Polyvinyl Alcohol/Chitosan and Polyvinyl Alcohol/Ag@MOF Bilayer Hydrogel for Tissue Engineering Applications. Polymers (Basel) 2021; 13:3151. [PMID: 34578053 PMCID: PMC8468989 DOI: 10.3390/polym13183151] [Citation(s) in RCA: 2] [Impact Index Per Article: 0.7] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 08/12/2021] [Revised: 08/28/2021] [Accepted: 09/10/2021] [Indexed: 02/06/2023] Open
Abstract
In this paper, polyvinyl alcohol/Ag-Metal-organic framework (PVA/Ag@MOF) and polyvinyl alcohol/chitosan (PVA/CS) were used as the inner and outer layers to successfully prepare a bilayer composite hydrogel for tissue engineering scaffold. The performance of bilayer hydrogels was evaluated. The outer layer (PVA/CS) has a uniform pore size distribution, good water retention, biocompatibility and cell adhesion ability. The inner layer (PVA/Ag@MOF) has good antibacterial activity and poor biocompatibility. PVA, PVA/0.1%Ag@MOF, PVA/0.5%Ag@MOF, and PVA/1.0%Ag@MOF show anti-microbial activity in ascending order. However, its use as an inner layer avoids direct contact with cells and prevents infection. The cell viability of all samples was above 90%, indicating that the bilayer hydrogel was non-toxic to A549 cells. The bilayer hydrogel scaffold combines the advantages of the inner and outer layers. In summary, this new bilayer composite is an ideal lung scaffold for tissue engineering.
Collapse
Affiliation(s)
- Meng Zhang
- College of Environment and Safety Engineering, Qingdao University of Science and Technology, Qingdao 266042, China; (M.Z.); (G.W.); (X.Z.); (Y.Z.)
- Shandong Engineering Research Center for Marine Environment Corrosion and Safety Protection, Qingdao University of Science and Technology, Qingdao 266042, China
- Shandong Engineering Technology Research Center for Advanced Coating, Qingdao University of Science and Technology, Qingdao 266042, China
| | - Guohui Wang
- College of Environment and Safety Engineering, Qingdao University of Science and Technology, Qingdao 266042, China; (M.Z.); (G.W.); (X.Z.); (Y.Z.)
- Shandong Engineering Research Center for Marine Environment Corrosion and Safety Protection, Qingdao University of Science and Technology, Qingdao 266042, China
- Shandong Engineering Technology Research Center for Advanced Coating, Qingdao University of Science and Technology, Qingdao 266042, China
| | - Xin Zhang
- College of Environment and Safety Engineering, Qingdao University of Science and Technology, Qingdao 266042, China; (M.Z.); (G.W.); (X.Z.); (Y.Z.)
- Shandong Engineering Research Center for Marine Environment Corrosion and Safety Protection, Qingdao University of Science and Technology, Qingdao 266042, China
- Shandong Engineering Technology Research Center for Advanced Coating, Qingdao University of Science and Technology, Qingdao 266042, China
| | - Yuqi Zheng
- College of Environment and Safety Engineering, Qingdao University of Science and Technology, Qingdao 266042, China; (M.Z.); (G.W.); (X.Z.); (Y.Z.)
- Shandong Engineering Research Center for Marine Environment Corrosion and Safety Protection, Qingdao University of Science and Technology, Qingdao 266042, China
- Shandong Engineering Technology Research Center for Advanced Coating, Qingdao University of Science and Technology, Qingdao 266042, China
| | - Shaoxiang Lee
- College of Environment and Safety Engineering, Qingdao University of Science and Technology, Qingdao 266042, China; (M.Z.); (G.W.); (X.Z.); (Y.Z.)
- Shandong Engineering Research Center for Marine Environment Corrosion and Safety Protection, Qingdao University of Science and Technology, Qingdao 266042, China
- Shandong Engineering Technology Research Center for Advanced Coating, Qingdao University of Science and Technology, Qingdao 266042, China
| | - Dong Wang
- College of Environment and Safety Engineering, Qingdao University of Science and Technology, Qingdao 266042, China; (M.Z.); (G.W.); (X.Z.); (Y.Z.)
- Shandong Engineering Research Center for Marine Environment Corrosion and Safety Protection, Qingdao University of Science and Technology, Qingdao 266042, China
- Shandong Engineering Technology Research Center for Advanced Coating, Qingdao University of Science and Technology, Qingdao 266042, China
| | - Yang Yang
- National Marine Data and Information Service, Tianjin 300171, China;
| |
Collapse
|