Rapid and efficient ultrasonic-assisted removal of lead(II) in water using two copper- and zinc-based metal-organic frameworks

Understanding the Mechanism for Adsorption of Pb(II) Ions by Cu-BTC Metal-Organic Frameworks

With the growing population, industrialization, and agriculture, water contamination not only affects people but entire ecosystems. Metal-organic frameworks (MOFs), because of their large surface area and porosity, show great potential as adsorbents for removing pollutants, such as heavy metals, from contaminated water. The current research aims at examining copper (II) benzene-1,3,5-tricarboxylate (Cu-BTC) MOFs and understanding the mechanism for their adsorption of Pb(II) from aqueous solution. The Cu-BTC samples were characterized using FTIR and XRD, and their surface area and porosity were determined based on N₂ adsorption isotherms. The concentration of Pb(II) in the solutions was measured using atomic absorption spectroscopy (AAS). Both kinetic and equilibrium adsorption data were collected and then analyzed using numerical models. The analyses led to the findings that the limiting steps in the adsorption of Pb(II) on Cu-BTC are (a) pore diffusion of Pb(II) and (b) the availability of the active sites on Cu-BTC MOFs. It was further revealed that the former step is more dominant in the adsorption of Pb(II) when the lead concentration is low. The latter step, which is directly proportional to the surface areas of the MOFs, affects the adsorption to a greater extent when the lead concentration is high. The results also show that adsorption of Pb(II) ions on Cu-BTC is mainly a multi-layer heterogeneous process.

State of the art on the ultrasonic-assisted removal of environmental pollutants using metal-organic frameworks

The environmental and health issues of drinking water and effluents released into nature are among the major area of contention in the past few decades. With the growth of ultrasound-based approaches in water and wastewater treatment, promising materials have also been considered to employ their advantages. Metal-organic frameworks (MOFs) are among the porous materials that have received great attention from researchers in recent years. Features such as high porosity, large specific surface area, electronic properties like semi-conductivity, and the capacity to coordinate with the organic matter have resulted in a substantial increase in scientific researches. This work deals with a comprehensive review of the application of MOFs for ultrasonic-assisted pollutant removal from wastewater. In this regard, after considering features and synthesis methods of MOFs, the mechanisms of several ultrasound-based approaches including sonocatalysis, sonophotocatalysis, and sono-adsorption are well assessed for removal of different organic compounds by MOFs. These methods are compared with some other water treatment processes with the application of MOFs in the absence of ultrasound. Also, the main concern about MOFs including environmental hazards and water stability is fully discussed and some techniques are proposed to reduce hazardous effects of MOFs and improve stability in humid/aqueous environments. Economic aspects for the preparation of MOFs are evaluated and cost estimates for ultrasonic-assisted AOP approaches were provided. Finally, the future outlooks and the new frontiers of ultrasonic-assisted methods with the help of MOFs in global environmental pollutant removal are presented.

Application of zeolitic imidazolate framework for hexavalent chromium removal: A feasibility and mechanism study

The mechanisms and effectiveness of using zeolitic imidazolate framework (ZIF-8) [a sub-family of metal-organic framework (MOF)] particles on hexavalent chromium [Cr(VI)] removal were evaluated. The ultrasonic mixing method was applied for the preparation of ZIF-8, and chemicals used for ZIF-8 synthesis included ammonium hydroxide, zinc nitrate hexahydrate, and 2-methylimidazole. ZIF-8 particle had a clear rhombic dodecahedron morphology shape and a strong peak intensity with high crystallinity. The adsorption capacity (AC) of ZIF-8 was 30.3 mg of Cr(VI)/g of ZIF-8 [Cr(VI) = 50 mg/L]. The AC of Cr(VI) raised to 34.3 mg/g under acidic conditions (pH = 5), and the AC dropped to below 13.7 mg/g with a pH range from 7 to 11. It could be because of the competitive effects between CrO₄ ^2- and hydroxide ions for adsorption locations of ZIF-8. Cr(VI) removal relied on the amount of Cr(VI) adsorbed on the particles of ZIF-8, and the mechanisms of Cr(VI) adsorption by ZIF-8 included chemical/physical processes and the rate-limiting step was the chemical adsorption. A fraction of sorbed Cr(VI) was reduced to Cr(III), and thus, ZIF-8 could serve as a reducing agent during Cr(VI) reduction. Cr(VI) was removed effectively from the water phase by ZIF-8 via adsorption and reduction mechanisms. PRACTITIONER POINTS: ZIF-8 particles had an adsorption capacity of 30.33 mg of Cr(VI)/g of ZIF-8. Cr(VI) sorption by ZIF-8 has chemical (rate-limiting step) and physical processes. ZIF-8 can serve as a reducing agent for Cr(VI) reduction. Cr(VI) can be removed by ZIF-8 via the adsorption and reduction mechanisms.

A novel and facile green synthesis method to prepare LDH/MOF nanocomposite for removal of Cd(II) and Pb(II)

To date, many nanoadsorbents have been developed and used to eliminate heavy metal contamination, however, one of the challenges ahead is the preparation of adsorbents from processes in which toxic organic solvents are used in the least possible amount. Herein, we have developed a new carboxylic acid-functionalized layered double hydroxide/metal-organic framework nanocomposite (LDH/MOF NC) using a simple, effective, and green in situ method. UiO-66-(Zr)-(COOH)₂ MOF nanocrystals were grown uniformly over the whole surface of COOH-functionalized Ni₅₀Co₅₀-LDH ultrathin nanosheets in a green water system under a normal solvothermal condition at 100 °C. The synthesized LDH/MOF NC was used as a potential adsorbent for removal of toxic Cd(II) and Pb(II) from water and the influence of important factors on the adsorption process was monitored. Various non-linear isotherm and kinetic models were used to find plausible mechanisms involved in the adsorption, and it was found that the Langmuir and pseudo-first-order models show the best agreement with isotherm and kinetic data, respectively. The calculated maximum adsorption capacities of Cd(II) and Pb(II) by the LDH/MOF NC were found to be 415.3 and 301.4 mg g^-1, respectively, based on the Langmuir model (pH = 5.0, adsorbent dose = 0.02 g, solution volume = 20 mL, contact time = 120 min, temperature = 25 ℃, shaking speed 200 rpm).