Microbial activities in hydrocarbon-laden wastewaters: Impact on diesel fuel stability and the biocorrosion of carbon steel

Characterization of crude oil degrading bacterial communities and their impact on biofilm formation

In the present study, produced water sample collected from the Indian crude oil reservoir is used to enrich the bacterial communities. The impact of these enriched bacterial communities on the biodegradation of crude oil, biofilm formation, and biocorrosion process are elucidated. A crude oil degradation study is carried out with the minimal salt medium and 94% of crude oil was utilized by enriched bacterial communities. During the crude oil degradation many enzymes including alkane hydroxylase, alcohol dehydrogenase, and lipase are playing a key role in the biodegradation processes. The role of enriched bacterial biofilm on biocorrosion reactions are monitored by weight loss studies and electrochemical analysis. Weight loss study revealed that the biotic system has vigorous corrosion attacks compared to the abiotic system. Both AC-Impedance and Tafel analysis confirmed that the nature of the corrosion reaction take place in the biotic system. Very less charge transfer resistance and higher corrosion current are observed in the biotic system than in the abiotic system. Scanning electron microscope confirms that the dense biofilm formation favoured the pitting type of corrosion. X-ray diffraction analysis confirms that the metal oxides formed in the corrosion systems (biotic). From the metagenomic analysis of the V3-V4 region revealed that presence of diverse bacterial communities in the biofilm, and most of them are uncultured/unknown. Among the known genus, Bacillus, Halomonas, etc are dominant in the enriched bacterial biofilm sample. From this study, we conclude that the uncultured bacterial strains are found to be playing a key role in the pitting type of corrosion and they can utilize crude oil hydrocarbons, which make them succeeded in extreme oil reservoir environments.

Community succession in an anaerobic long-chain paraffin-degrading consortium and impact on chemical and electrical microbially influenced iron corrosion

Community compositional changes and the corrosion of carbon steel in the presence of different electron donor and acceptor combinations were examined with a methanogenic consortium enriched for its ability to mineralize paraffins. Despite cultivation in the absence of sulfate, metagenomic analysis revealed the persistence of several sulfate-reducing bacterial taxa. Upon sulfate amendment, the consortium was able to couple C28H58 biodegradation with sulfate reduction. Comparative analysis suggested that Desulforhabdus and/or Desulfovibrio likely supplanted methanogens as syntrophic partners needed for C28H58 mineralization. Further enrichment in the absence of a paraffin revealed that the consortium could also utilize carbon steel as a source of electrons. The severity of both general and localized corrosion increased in the presence of sulfate, regardless of the electron donor utilized. With carbon steel as an electron donor, Desulfobulbus dominated in the consortium and electrons from iron accounted for ∼92% of that required for sulfate reduction. An isolated Desulfovibrio spp. was able to extract electrons from iron and accelerate corrosion. Thus, hydrogenotrophic partner microorganisms required for syntrophic paraffin metabolism can be readily substituted depending on the availability of an external electron acceptor and a single paraffin-degrading consortium harbored microbes capable of both chemical and electrical microbially influenced iron corrosion.

Anaerobic biodegradation of biofuels and their impact on the corrosion of a Cu-Ni alloy in marine environments

Fuel biodegradation linked to sulfate reduction can lead to corrosion of the metallic infrastructure in a variety of marine environments. However, the biological stability of emerging biofuels and their potential impact on copper-nickel alloys commonly used in marine systems has not been well documented. Two potential naval biofuels (Camelina-JP5 and Fisher-Tropsch-F76) and their petroleum-derived counterparts (JP5 and F76) were critically assessed in seawater/sediment incubations containing a metal coupon (70/30 Cu-Ni alloy). Relative to a fuel-unamended control (1.2 ± 0.4 μM/d), Camelina-JP5 (86.4 ± 1.6 μM/d) and JP5 (77.6 ± 8.3 μM/d) stimulated much higher rates of sulfate reduction than either FT-F76 (11.4 ± 2.7 μM/d) or F76 (38.4 ± 3.7 μM/d). The general corrosion rate (r² = 0.91) and pitting corrosion (r² = 0.92) correlated with sulfate loss in these incubations. Despite differences in microbial community structure on the metal or in the aqueous or sediment phases, sulfate reducing bacteria affiliated with Desulfarculaceae and Desulfobacteraceae became predominant upon fuel amendment. The identification of alkylsuccinates and alkylbenzylsuccinates attested to anaerobic metabolism of fuel hydrocarbons. Sequences related to Desulfobulbaceae were highly enriched (34.2-64.8%) on the Cu-Ni metal surface, regardless of whether the incubation received a fuel amendment. These results demonstrate that the anaerobic metabolism of biofuel linked to sulfate reduction can exacerbate the corrosion of Cu-Ni alloys. Given the relative lability of Camelina-JP5, particular precaution should be taken when incorporating this hydroprocessed biofuel into marine environments serviced by a Cu-Ni metallic infrastructure.

Responses of Microbial Community Composition to Temperature Gradient and Carbon Steel Corrosion in Production Water of Petroleum Reservoir

Oil reservoir production systems are usually associated with a temperature gradient and oil production facilities frequently suffer from pipeline corrosion failures. Both bacteria and archaea potentially contribute to biocorrosion of the oil production equipment. Here the response of microbial populations from the petroleum reservoir to temperature gradient and corrosion of carbon steel coupons were investigated under laboratory condition. Carbon steel coupons were exposed to production water from a depth of 1809 m of Jiangsu petroleum reservoir (China) and incubated for periods of 160 and 300 days. The incubation temperatures were set at 37, 55, and 65°C to monitoring mesophilic, thermophilic and hyperthermophilic microorganisms associated with anaerobic carbon steel corrosion. The results showed that corrosion rate at 55°C (0.162 ± 0.013 mm year^-1) and 37°C (0.138 ± 0.008 mm year^-1) were higher than that at 65°C (0.105 ± 0.007 mm year^-1), and a dense biofilm was observed on the surface of coupons under all biotic incubations. The microbial community analysis suggests a high frequency of bacterial taxa associated with families Porphyromonadaceae, Enterobacteriaceae, and Spirochaetaceae at all three temperatures. While the majority of known sulfate-reducing bacteria, in particular Desulfotignum, Desulfobulbus and Desulfovibrio spp., were predominantly observed at 37°C; Desulfotomaculum spp., Thermotoga spp. and Thermanaeromonas spp. as well as archaeal members closely related to Thermococcus and Archaeoglobus spp. were substantially enriched at 65°C. Hydrogenotrophic methanogens of the family Methanobacteriaceae were dominant at both 37 and 55°C; acetoclastic Methanosaeta spp. and methyltrophic Methanolobus spp. were enriched at 37°C. These observations show that temperature changes significantly alter the microbial community structure in production fluids and also affected the biocorrosion of carbon steel under anaerobic conditions.