Characterization of a novel enamel sealer for bioactive remineralization of white spot lesions

Protecting primary teeth from dental erosion through bioactive glass

OBJECTIVES

The present study aimed to evaluate the effectiveness of bioactive glass (BAG) in preventing dental erosion in primary teeth.

METHODS

Enamel and dentin specimens (2 × 2 × 2 mm) were obtained from extracted primary teeth, which were randomly divided into the following groups based on the pretreatments (n = 12): DW (deionized water), NaF (2 % sodium fluoride), 2BAG (2 % BAG), 4BAG (4 % BAG), 6BAG (6 % BAG), and 8BAG (8 % BAG). The specimens were immersed in the respective solutions for 2 min and subjected to in vitro erosive challenges (4 × 5 min/d) for 5 d. The erosive enamel loss (EEL), erosive dentin loss (EDL), and the thickness of the demineralized organic matrix (DOM) were measured using a contact profilometer. The surface microhardness (SMH) was measured, and the percentage of SMH loss (%SMHL) was calculated. The surface morphology and mineral composition were evaluated by scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS), respectively.

RESULTS

After the erosive challenges, the EEL, EDL, and%SMHL of the 2BAG, 4BAG, 6BAG, and 8BAG groups significantly reduced, with the greatest reduction was observed in the 6BAG (EEL: 6.5 ± 0.2 μm;%SMHL in enamel: 12.8 ± 2.6; EDL: 7.9 ± 0.3 μm; %SMHL in dentin: 22.1 ± 2.7) and 8BAG groups (EEL: 6.4 ± 0.4 μm;%SMHL in enamel: 11.0 ± 1.9; EDL: 7.8 ± 0.5 μm; %SMHL in dentin: 22.0 ± 2.5) (P < 0.05). With increasing BAG concentrations, the number of surface deposits containing Ca, P, and Si increased.

CONCLUSIONS

6BAG was the most effective for preventing dental erosion in primary teeth and showed a particularly strong potential for dentin erosion prevention.

CLINICAL SIGNIFICANCE

Bioactive glass, especially at a 6 % concentration, has proven effective in reducing erosive tooth wear and surface microhardness loss while also protecting demineralized organic matrix in primary dentin.

White spot lesions in fixed orthodontic treatment: Etiology, pathophysiology, diagnosis, treatment, and future research perspectives

White spot lesions (WSLs) refer to localized areas of hypo-mineralization limited to the enamel of the teeth surface, which is noticeable clinically to the naked eye on drying of the teeth. During fixed orthodontic treatment, it is very hard for the patient to maintain excellent oral hygiene as the brackets, bands, wires, elastics, and other appliances and attachments worn intra-orally provide a platform for food retention, plaque formation, and then colonization by acidogenic bacteria like Streptococcus mutans and Lactobacillus. This review aims to elaborate and focus on etiology, pathophysiology, diagnosis, treatment aspect, and future scope for research about the WSLs occurring due to fixed orthodontic treatment.

Enamel Matrix Derivative, 58S5 Bioactive Glass, and Fluoride Varnish for Enamel Remineralization: A Multi-analysis Approach

PURPOSE

This study aimed to evaluate the enamel remineralization efficacy of enamel matrix derivative (EMD), experimental bioactive glass (BAG), and fluoride varnish in vitro.

METHODS AND MATERIALS

Artificial initial caries lesions were developed on fifty human enamel specimens using demineralization solution (pH 4.5, 37°C, 96 hours). Specimens were randomly assigned to five groups (n=10): I-5% NaF varnish (Enamelast), II-experimental 58S5 BAG+37% phosphoric acid (PA), III-EMD (Emdogain) + Ethylenediaminetetraacetic Acid (EDTA), IV-EMD+37% PA, V-Control (untreated). All remineralization agents were applied with pH cycling for seven days. The specimens were scanned by spectral domain optical coherence tomography (SD-OCT) at baseline, at demineralization, and after pH cycling. Lesion depths were measured using image analysis software (ImageJ). Lesions were evaluated using surface microhardness (SMH) and two fluorescence methods (FluoreCam and DIAGNOdent Pen [DDPen]). The data were statistically analyzed by Kruskal Wallis, Friedman, and Wilcoxon tests (α=0.05).

RESULTS

According to SD-OCT results, fluoride varnish was found to be the most effective agent in reducing lesion depth (p=0.005). All agents increased the SMH values after pH cycling. No significant difference was found among fluoride varnish, BAG, and EMD+PA groups. These SMH values were significantly higher than EMD+EDTA and control groups (p<0.001). All groups showed lower DDPen scores compared with the control group (p<0.001), however, no significant difference was found among the remineralization agents. In FluoreCam assessment, size and intensity values of all treated groups showed improvement. However, there was no significant difference between the treatment groups in terms of FluoreCam size measurements (p=0.186).

CONCLUSION

58S5 BAG and EMD+PA have remineralization capacity as effective as fluoride varnish. EMD+PA showed better SMH and lesion intensity results than EMD+EDTA.

New generation of orthodontic devices and materials with bioactive capacities to improve enamel demineralization

OBJECTIVE

The article reviewed novel orthodontic devices and materials with bioactive capacities in recent years and elaborated on their properties, aiming to provide guidance and reference for future scientific research and clinical applications.

DATA, SOURCES AND STUDY SELECTION

Researches on remineralization, protein repellent, antimicrobial activity and multifunctional novel bioactive orthodontic devices and materials were included. The search of articles was carried out in Web of Science, PubMed, Medline and Scopus.

CONCLUSIONS

The new generation of orthodontic devices and materials with bioactive capacities has broad application prospects. However, most of the current studies are limited to in vitro studies and cannot explore the true effects of various bioactive devices and materials applied in oral environments. More research, especially in vivo researches, is needed to assist in clinical application.

CLINICAL SIGNIFICANCE

Enamel demineralization (ED) is a common complication in orthodontic treatments. Prolonged ED can lead to dental caries, impacting both the aesthetics and health of teeth. It is of great significance to develop antibacterial orthodontic devices and materials that can inhibit bacterial accumulation and prevent ED. However, materials with only preventive effect may fall short of addressing actual needs. Hence, the development of novel bioactive orthodontic materials with remineralizing abilities is imperative. The article reviewed the recent advancements in bioactive orthodontic devices and materials, offering guidance and serving as a reference for future scientific research and clinical applications.

A multifunctional polydopamine/genipin/alendronate nanoparticle licences fibrin hydrogels osteoinductive and immunomodulatory potencies for repairing bone defects

Here, we fabricated a hybrid nanoparticle composed of polydopamine nanoparticles (pNPs), alendronate (Al) and genipin (GP) for cranial bone defect repair. Al was crosslinked into pNPs via GP (Al@pNPs), after which hybrid nanoparticles were obtained. By embedding these Al@pNPs into the fibrin hydrogels, a multifunctional bone repair scaffold was fabricated (Al@pNPs/Fg). The Al@pNPs/Fg exhibited three synergistic effects on the bone microenvironment: i) enhanced ectomesenchymal stem cell (EMSC) osteogenic differentiation by activating the piezo 1 channel; ii) inhibited the formation and function of osteoclasts related to the NF-κB signaling pathways; and iii) promoted M2 polarization and anti-inflammatory factor expression under normal and simulated inflammatory conditions. Al@pNPs/Fg ultimately promoted cranial bone defect regeneration in an SD rat model. This simple and low-cost technology provides a new approach to constructing an efficient delivery system and has desirable biological properties, providing a tissue-committed niche for the repair of bone defects.

Comparative analysis of the effect of Bioactive Glass 45S5 on enamel erosion progression in human dentitions (in vitro study)

OBJECTIVES

The aim of the present study was to compare the surface morphology alterations, mineral content, and surface roughness of eroded enamel surface versus eroded enamel surface which was preceded by Bioactive Glass 45S5 (BAG45S5) application in both primary and permanent human dentitions.

MATERIALS AND METHODS

Fifty-two primary teeth and fifty-two permanent teeth were selected. Teeth were randomly divided into 4 groups of twenty-six teeth each. Groups A1 and B1 underwent erosion with 1% citric acid, while groups A2 and B2 were subjected to application of BAG45S5 powder followed by the same erosive conditions as A1 and B1. Measurements were performed by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and surface profilometry. They were used to examine the surface morphology alterations, mineral content, and surface roughness, respectively.

RESULTS

SEM of enamel which received BAG45S5 showed smoother surface in primary teeth post erosion. EDX analysis showed that enamel exhibited crucial resistance to mineral loss in the group which received BAG45S5 prior to inducing erosion as compared to the induced erosion-only group. This was significant (p < 0.005) in both human dentitions. Erosion-only groups showed significantly less surface roughness in permanent teeth (p < 0.045). A marked decrease in surface roughness was observed in surfaces receiving BAG45S5, primary teeth (p < 0.001), and permanent teeth (p < 0.001).

CONCLUSIONS

Bioactive Glass 45S5 proved successful against erosive conditions in both primary and permanent teeth with better performance in the permanent teeth so it can be regarded as a means of prevention.

CLINICAL RELEVANCE

Bioactive Glass 45S5 powder could be used not only to remove stains but also as a prophylactic preventive measure against the multiple episodes of acidic food and beverage consumption in children.

Evaluation of Resin Infiltration, Fluoride and the Biomimetic Mineralization of CPP-ACP in Protecting Enamel after Orthodontic Inter-Proximal Enamel Reduction

BACKGROUND

This study investigated the effect of using different agents for protecting enamel proximal surfaces against acidic attack after interproximal reduction (IPR) using the trans micro radiography technique.

METHODS

Seventy-five sound-proximal surfaces were obtained from extracted premolars for orthodontic reasons. All teeth were measured miso-distally and mounted before being stripped. The proximal surfaces of all teeth were hand stripped with single-sided diamond strips (OrthoTechnology, West Columbia, SC, USA) followed by polishing via Sof-Lex polishing strips (3M, Maplewood, MN, USA). Three-hundred micrometers of enamel thickness was reduced from each proximal surface. The teeth were randomly divided into 5 groups: group 1 (control un-demineralized) received no treatment, group 2 (control demineralized) had their surfaces demineralized after the IPR procedure, group 3 (fluoride) specimens were treated with fluoride gel (NUPRO, DENTSPLY, Charlotte, NC, USA) after the IPR, group 4 (Icon) resin infiltration material (Icon Proximal Mini Kit, DMG, Bielefeld, Germany) was applied after IPR, group 5 (MI varnish) specimens were treated with Casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) containing varnish (MI Varnish, G.C, USA, St. Alsip, IL, USA) after the IPR. The specimens in (groups 2-5) were stored in a 4.5 pH demineralization solution for 4 days. The trans-micro-radiography (TMR) technique was conducted to evaluate the mineral loss (∆Z) and lesion depth of all specimens after the acid challenge. The obtained results were analyzed statistically using a one-way ANOVA at a significance level of α = 0.05.

RESULTS

The MI varnish recorded significant ∆Z and lesion depth values compared to the other groups p > 0.05. There was no significant difference in ∆Z and lesion depth between the control demineralized, Icon, and fluoride groups p < 0.05.

CONCLUSION

The MI varnish increased the enamel resistance to acidic attack, and thus can be considered an agent capable of protecting the proximal enamel surface after IPR.

Using Copper-Doped Mesoporous Bioactive Glass Nanospheres to Impart Anti-Bacterial Properties to Dental Composites

Experimental dental resin composites containing copper-doped mesoporous bioactive glass nanospheres (Cu-MBGN) were developed to impart anti-bacterial properties. Increasing amounts of Cu-MBGN (0, 1, 5 and 10 wt%) were added to the BisGMA/TEGDMA resin matrix containing micro- and nano-fillers of inert glass, keeping the resin/filler ratio constant. Surface micromorphology and elemental analysis were performed to evaluate the homogeneous distribution of filler particles. The study investigated the effects of Cu-MBGN on the degree of conversion, polymerization shrinkage, porosity, ion release and anti-bacterial activity on S. mutans and A. naeslundii. Experimental materials containing Cu-MBGN showed a dose-dependent Cu release with an initial burst and a further increase after 28 days. The composite containing 10% Cu-MBGN had the best anti-bacterial effect on S. mutans, as evidenced by the lowest adherence of free-floating bacteria and biofilm formation. In contrast, the 45S5-containing materials had the highest S. mutans adherence. Ca release was highest in the bioactive control containing 15% 45S5, which correlated with the highest number of open porosities on the surface. Polymerization shrinkage was similar for all tested materials, ranging from 3.8 to 4.2%, while the degree of conversion was lower for Cu-MBGN materials. Cu-MBGN composites showed better anti-bacterial properties than composites with 45S5 BG.

Evaluation of Bioactive Glass and Low Viscosity Resin as Orthodontic Enamel Sealer: An In Vitro Study

The study aimed to evaluate the effect of applying fluoride bioactive glass (FBAG) and Alpha-Glaze® (resin sealer) on the shear bond strength of orthodontic brackets to enamel bonded by Transbond XT, brushing−abrasion durability, and their protective effect against simulated cariogenic acidic attack. Materials include 135 extracted premolars that were divided into three groups—FBAG, Alpha-Glaze, and control. The shear bond strength test was measured using an Instron Universal Testing Machine. The brushing abrasion challenge took place with a tooth-brushing simulator. Transmitted light microscopy examinations were performed after the specimens were demineralized for 4 days. The results show that the shear bond strength values of the three groups did not report any statistically significant differences: FBAG (28.1 ± 5.5 Mpa), Alpha-Glaze (32.5 ± 7.4 Mpa), and control (30.7 ± 6.5 Mpa) p < 0.05. The Adhesive Remenant Index (ARI) study showed chipping of enamel in 6.6% of Alpha-Glaze and control specimens and 40% of specimens had their enamel surface covered with resin. Furthermore, 30% of the FBAG and 100% of the Alpha-Glaze sealer specimens resisted the abrasion test. In conclusion, FBAG can serve as an orthodontic-sealer capable of protecting the enamel surface surrounding orthodontic brackets. However, the Alpha-Glaze sealer did not offer the capability of protecting the enamel.

Bioactive Restorative Dental Materials-The New Frontier

Bioactive materials for dental resin restorations are a rising field of investigation exploring treatment strategies for reducing the recurrence of carious lesions. The current effort has been directed toward developing dental materials that can inhibit biofilms and prevent tooth mineral loss. Bioactive resin materials have shown the potential to interfere with polymicrobial consortia in vivo and help maintain the lifespan of restorations.

Effect of citric acid erosion on enamel and dentin and possible protection by a novel bioactive borate adhesive system

OBJECTIVES

This study examined the ability of a borate adhesive to protect enamel/dentin surfaces from acidic erosion and its effect on the shear bond strength (SBS) of enamel/dentin to resin composite.

MATERIALS AND METHODS

180 human enamel/dentin specimens were utilized. Enamel buccal surfaces were etched with phosphoric-acid then divided into: (EBG) borate glass adhesive group; (ERS) resin-adhesive system group; (EF) fluoride gel 1.23% group, and enamel control (EC) group; followed by bonding to orthodontic-buttons. The dentin specimens were conditioned by EDTA (Ethylene-diamine-tetra-acetic acid) and divided into: (DBG) borate glass resin, (DRS) resin adhesive; (DDA) group had a dentin-desensitizing agent VivaSens (VivaDent, Liechtenstein) and (DC) control group. The treated enamel/dentin specimens had their SBS to composite. The enamel/dentin specimens were exposed to 1% citric acid (18 min). Enamel/dentin specimens were examined by (SEM/EDS) scanning-electron-microscope equipped with electron-dispersive-spectroscopy and (FTIR/ATR). Analysis-of-Variance (ANOVA) was used to compare the SBS and Wilcoxon-signed-rank test was used to compare the enamel/dentin areas protected by the applied agents before/after erosion (p = 0.05).

RESULTS

There was no significance difference in SBS among all groups except for (DDA) group that showed significant decrease p < 0.05. (EBG) and (DBG) groups were the only groups significantly protected enamel and dentin from erosion p < 0.05. FTIR/ATR showed that erosion altered the chemical structure of (DRS), (DDA), and (DC) groups but did not affect the other enamel/dentin groups. Degree of conversion of the borate-adhesive system was acceptable.

CONCLUSION

The Borate adhesive system released calcium and phosphate compounds that decreased the erosive activity of the citric acid resulting in protecting simulated dentin-hypersensitive areas and enamel from erosion without affecting the SBS to resin-composite.

CLINICAL SIGNIFICANCE

A Borate adhesive system can be adopted as a therapeutic agent in a fully integrated program for protecting dentin-hypersensitive areas and in enamel next to orthodontic fixed appliances.

Fabrication and characterisation of novel algin incorporated bioactive-glass 58S calcium-silicate-based root canal sealer

Background/purpose

The usage of bioceramic-based root canal sealers has escalated over the years due to their excellent properties. The present study aimed to fabricate a novel algin incorporated bioactive glass 58S calcium-silicate (Bio-G) sealer and characterise its surface microstructure and chemical compositions in comparison to commercially available bioceramic sealers (BioRoot RCS and iRoot SP).

Materials and methods

The powder form of experimental Bio-G sealer consisted of synthesised BG 58S particle, calcium silicate, zirconia dioxide, calcium carbonate and alginic acid powder as binder. The liquid composed of 5% calcium chloride solution. Five standardised disc specimens were prepared for each sealer group according to the manufacturer's instructions. Subsequently, sealer disc-specimens were placed in an incubator at 37 °C, 95% relative humidity for 72 h to allow setting prior to testing under scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), Fourier transformed infrared spectroscopy (FTIR) and X-ray diffraction (XRD).

Results

Experimental Bio-G sealer revealed irregular micro-sized particles ranging from 0.5 μm to 105 μm aggregated in clusters comparable to those of BioRoot RCS and iRoot SP. EDS microanalysis showed that Bio-G had high content of oxygen, silicon, and calcium, with the presence of aluminium and chloride similar to BioRoot RCS. Meanwhile, the FTIR and XRD findings suggested that all sealers predominantly contained calcium silicate hydrate, calcium carbonate, and zirconium dioxide, while calcium aluminium silicate oxide was detected in Bio-G.

Conclusion

The present novel Bio-G sealer demonstrated desirable particle size distribution and acceptable degree of purity. Future studies are warranted to explore its properties and clinical application.

Acid neutralizing and remineralizing orthodontic adhesive containing hydrated calcium silicate

OBJECTIVES

The objective of this study was to evaluate an orthodontic adhesive containing hydrated calcium silicate (hCS) in terms of its bond strength with the enamel surface and its acid-neutralization and apatite-forming abilities.

METHODS

The experimental orthodontic adhesives were composed of 30 wt.% resin matrix and 70 wt.% filler, which itself was a mixture of silanized glass filler and hCS in weight ratios of 100% glass filler (hCS 0), 17.5% hCS (hCS 17.5), 35% hCS (hCS 35.0), and 52.5% hCS (hCS 52.5). The degree of conversion (DC) and shear bond strength (SBS) of bovine enamel surfaces were tested. pH measurements were performed immediately upon submersion of the specimens in a lactic acid solution. The surface precipitates that formed on specimens immersed in phosphate-buffered saline (PBS) were analyzed by scanning electron microscopy with energy dispersive spectroscopy (SEM-EDS) and Raman spectroscopy after 15, 30, and 90 days.

RESULTS

The experimental groups exhibited no significant differences in DC and had clinically acceptable SBS values. The hCS-containing groups showed increasing pH values as more hCS was added. hCS 52.5 produced Ca- and P-containing surface precipitates after PBS immersion, and hydroxyapatite deposition was detected after 15, 30, and 90 days.

CONCLUSIONS

These results suggest that orthodontic adhesives containing hCS are effective for acid neutralization. Furthermore, hCS has an apatite-forming ability for enamel remineralization.

CLINICAL SIGNIFICANCE

The novel orthodontic adhesive containing hCS exhibits a potential clinical benefit against demineralization and enhanced remineralization of the enamel surface around or beneath the orthodontic brackets.

Remineralization of early enamel lesions with a novel prepared tricalcium silicate paste

To evaluate the remineralization potential of prepared tricalcium silicate (TCS) paste compared to silver diamine fluoride-potassium iodide (SDF-KI) and casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) on artificial enamel lesions. Thirty permanent sound molars were collected for the study. After cleaning, root cutting, and applying acid-resistant nail varnish, leaving a 4 × 4 mm buccal window, the teeth were subjected to demineralization process. The teeth were divided into three treatment groups (n = 10). In each group, the teeth were sectioned buccolingually to obtain two halves (30 self-control and 30 experimental halves). The self-control halves were subjected to cross-sectional microhardness (CSMH), energy-dispersive X-ray spectroscopy at 50, 100, and 150 µm from the external enamel surface, and micromorphological analysis at the superficial enamel surface. The experimental halves were subjected to the same tests after 30 days of remineralization. Three-way analysis of variance (ANOVA) outcomes showed no significant difference in CSMH after treatment among the three different groups at the different levels (p > 0.05). Meanwhile, three-way ANOVA outcomes showed a significant difference in calcium/ phosphate ratio after treatment among the three different groups at the different levels. (p < 0.05). The tricalcium silicate paste used in this study showed potential remineralization in subsurface enamel lesions.

A Bioactive Enamel Sealer Can Protect Enamel during Orthodontic Treatment: An In Vitro Study

Background: This study aimed to evaluate the effectiveness of an experimental bioactive enamel resin sealer in protecting the enamel adjacent to orthodontic brackets against erosion. Methods: Orthodontic brackets (n = 50) were bonded to freshly extracted, sound maxillary premolars using Transbond™ XT Primer (3M Unitek, Monrovia, CA, USA) and Transbond Plus Color Change adhesive (3M Unitek, USA). Five experimental groups (n = 10) had the following treatments applied: a resin bioactive sealer with 45S5 bioglass, 35% by weight; a resin sealer without bioactive glass; fluoride; the orthodontic sealer, Opal Seal (Opal-Orthodontics, South Jordan, UT, USA); and, in the control group, an untreated surface. All the specimens were stored for 18 min in 1% citric acid. All the specimens were examined by SEM and electron dispersive spectroscopy (EDS). The Wilcoxon signed-rank test was used to compare the enamel surfaces covered by the sealers before and after the acid challenge. Attenuated total reflectance Fourier transform infrared spectroscopy detected the degree of the experimental resins’ conversion to verify their suitability for clinical use. Results: The percentage of the bioactive resin sealer and Opal Seal groups’ protection against enamel erosion was 100%, which was significantly more than the other groups, p < 0.05. The degree of conversion for the bioactive and unfilled resins was 42.4% ± 3.6% and 48.57% ± 5%, respectively. Conclusion: The bioactive resin sealer and the Opal Seal both protected the enamel from erosion.

An Extensive Comparison of the Clinical Efficiency of Acidulated Phosphate Fluoride (APF) and Neutral Sodium Fluoride (NaF) Oral Rinses in the Prevention of White Spot Lesions during Fixed Orthodontic Treatment: A Randomized Controlled Trial

Background

The purpose of this randomized trial is to compare the efficacy of weekly once regime of neutral sodium fluoride (NaF) oral rinse with that of acidulated phosphate (APF) formulated daily mouth rinse in the reduction of white spot lesions (WSLs) associated with fixed orthodontic appliance treatment.

Methods

The participants (n = 90) of this single-center, two-arm parallel study without a control group were randomly assigned with 1 : 1 distribution to each of the two groups after the bonding of brackets. Group A/test group 1 (n = 45) was given weekly rinse of neutral sodium fluoride (Colgate® PreviDent® Dental Rinse-0.2% NaF), and for group B/test group 2 (n = 45), an APF formulated daily oral rinse (Colgate® Ortho Defense^@ PhosFlur® Rinse-0.044% w/v of NaF) was given for six months. The outcome was assessed by the International Caries Detection and Assessment System (ICDAS) index for scoring the demineralization, and for scoring gingivitis, Loe and Silness gingival index (GI) was utilized. Four different time points “T0”immediately before bonding procedures, “T1” after 4weeks, “T2” after 12 weeks, and “T3” after 24 weeks were taken to assess the ICDAS and GI scores.

Results

The mean ICDAS scores for group A (NaF) were 0.025, 0.051, 0.093, and 0.113 and for group B (APF) were 0.014, 0.022, 0.038, and 0.015 at different points of time. The GI scores for group A were 0.008, 0.22, 0.33, and 0.38 and for group B were 0.003, 0.136, 0.181, and 0.097 at different time points. There was a statistically significant difference (p < 0.05) for both groups in terms of reducing WSL and GI.

Conclusion

APF formulated daily oral rinse—0.044% w/v of NaF—is more effective than the weekly once regimen of 0.2% NaF oral rinse to prevent white spot lesions.

Root Canal Obturation by Electrochemical Precipitation of Calcium Phosphates

Achieving adequate disinfection and preventing reinfection is the major goal in endodontic treatment. Variation in canal morphology and open porosity of dentine prevents achieving complete disinfection. Questionable biocompatibility of materials as well as a lack of sealing ability questions the usefulness of current obturation methods. With a novel disinfection approach based on the use of boron-doped diamond (BDD) electrodes having shown promising results it was the goal of this series of experiments to investigate the possibility of BDD-mediated in situ forming of a biocompatible obturation material. A combination of calcium phosphate and maleic acid was used as precursor solution while Ion Chromatography Mass Spectrometry (IC-MS), Raman spectroscopy (RAMAN), X-ray diffraction (XRD), energy dispersive X-ray spectroscopy (EDX), scanning electron microscopy (SEM), dye penetration and micro-computed tomography (µCT) were applied for characterizing the precipitate. It was possible to achieve a BDD-mediated precipitation of brushite in a clinically applicable timeframe. However, tight sealing of the canal system based on brushite could not be achieved.

Unravelling the effects of ibuprofen-acetaminophen infused copper-bioglass towards the creation of root canal sealant

Impact towards the tuneable characteristics of bioactive glasses (BAG) has been explored; as there is no root canal sealant till date with ideal characteristics competent enough to manoeuvre the perplexing root canal architecture. Combeite, calcite and traces of cuprorivaite crystalline phases were validated for material formation, in which Cu 2P [XPS] peak authenticating the presence of copper in bioglass network (Cu-BAG). Spherical and platelet-like morphologies were observed and the grain size of Cu-BAG (~100 nm) was lesser as compared to BAG (~ 1 µm). These particle distributions impacted the porosity, and dominant non-bridging oxygens in Cu-BAG influences ionic dissolution, which subsequently enhanced the mineralization. These bioactive materials were loaded with acetaminophen and ibuprofen, corresponding organic moieties was confirmed through FT-IR. These drugs loaded bioactive materials exhibited tremendous anti-inflammatory and anti-microbial behavior with better sealing ability. Drug loaded bioglass paste filled in biomechanically prepared root canal was estimated for sealing potential, mineralization, micro leakage, and fracture resistance properties. Hydroxyl apatite growth was noted on the sealants, flower like protuberance confirmed the sealing potential of the prepared material. Bioglass exhibited promising characteristics required in a root canal sealant. This investigation is a step further towards tailoring the properties of bioactive materials as promising candidates in root canal obturation and thereof.

Dentinal tubule blockage using nanobioglass in the presence of diode (980 nm) and Nd:YAG lasers: an in vitro study

OBJECTIVES

The main objective of this study was to enhance the blockage of dentinal tubules using nanobioglass in the presence of diode (980 nm) and Nd:YAG lasers in order to reduce permeability and dentin hypersensitivity.

MATERIALS AND METHODS

Thirty-six dentinal samples were randomly divided into 6 subgroups (n = 6): (A) control, (B) diode laser (980 nm, 3-W), (C) Nd:YAG laser (1064, 1.0-W), (D) nanobioglass, (E) nanobioglass + diode laser (980 nm), (F) nanobioglass + Nd:YAG laser. The average number of open dentinal tubules was qualitatively and quantitatively evaluated by scanning electron microscopy (SEM). Data were evaluated by SPSS software version 22, Kruskal-Wallis test, and Mann-Whitney tests with Bonferoni's correction (α = 0.008).

RESULTS

Based on the results of Mann-Whitney test, there was a significant difference in the mean number of open dentinal tubules between the control group and the other groups (p < 0.008). However, the difference among the other groups was not statistically significant (p > 0.008).

CONCLUSIONS

Findings of this study showed that high-power laser radiation, such as Nd:YAG and diode (980 nm) alone or with nanobioglass, has a significant effect on the blockage of dentinal tubules.

CLINICAL RELEVANCE

Introduction of non-invasive methods with long-term and lasting effect on reducing pain and discomfort caused by dentin hypersensitivity.

Effects of 45S5 bioactive glass on the remineralization of early carious lesions in deciduous teeth: an in vitro study

Background

Early childhood caries has been designated as a serious public health problem. The traditional restoration method is very challenging, especially in uncooperative patients. Non-invasive therapy, like remineralization agents, which have been developed to reverse the demineralization progress at the early stage of caries, may be a better choice. This study aimed to evaluate the remineralization efficacy of different concentrations of 45S5 bioactive glass (BAG) on artifical carious lesions of deciduous enamel.

Methods

65 caries-like enamel lesions of the deciduous teeth were assigned to 5 groups (n = 13) and transported to a 14 days pH-cycling: Group A: 2%BAG, Group B: 4%BAG, Group C: 6%BAG, Group D: 8%BAG, and Group E: deionized water (DDW, negative control). 8 sound (Group F) and 8 demineralized teeth (Group G) were prepared for contrast. The recovery power of mechanical property was evaluated by Vickers hardness test through the recovery of enamel microhardness (%REMH). Surface morphology, mass fraction of Ca and P ions, and Ca/P atomic ratio were analyzed by scanning electron microscopy coupled with energy-dispersive X-ray spectroscopy (EDX). Moreover, Fourier transform infrared spectroscopy equipped with attenuated total reflectance was used to identify the chemical structure of newly formed compounds.

Results

% REMH were (42.65 ± 1.35), (52.59 ± 2.96), (57.40 ± 1.72), (52.91 ± 2.55), (12.46 ± 2.81) in 2%BAG, 4%BAG, 6%BAG, 8%BAG, and DDW groups respectively. Micro-spherical particles were deposited in all BAG groups and 6% BAG showed the densest and most uniform surface. EDX analysis identified significantly higher Ca(wt%) and P(wt%) in four BAG groups than in the demineralized group (p < 0.005), while 6% BAG showed the highest mineral gain efficacy. The infrared spectrum demonstrated that newly mineralized crystals were consisted of type-B hydroxycarbonate apatite.

Conclusion

BAG possessed a promising remineralization effect on artificial lesions in deciduous enamel by recovering enamel surface mechanical property, morphology and chemical elements. Among them, 6% BAG performed the greatest overall efficacy. Acting as a new caries-arresting biomaterial, 45S5 BAG has the potential to facilitate the adaptation of better carious prevention strategies in children.

Effect of Amelogenin Solution in the Microhardness of Remineralized Enamel and Shear Bond Strength of Orthodontic Brackets

Objectives

To evaluate the microhardness of tooth enamel remineralized with enamel matrix protein solution as well as the shear bond strength of orthodontic brackets bonded to this surface.

Materials and Methods

In total, 24 human premolars were selected and divided into 3 experimental groups (n = 8): SE—sound enamel, DE—demineralized enamel, and TE—demineralized enamel treated with amelogenin solution. Samples from DE and TE groups were subjected to pH cycling to induce initial artificial caries lesion. TE group was treated with amelogenin solution. Samples were placed in artificial saliva for 7 days. Knoop microhardness was measured before any intervention (T0), after pH cycling (T1) and after amelogenin solution treatment application (T2). Twenty-four hours after ceramic orthodontic brackets were bonded, samples were subjected to shear test in a universal testing machine. Microhardness and shear measurement distributions were subjected to Kolmogorov–Smirnov normality test, which was followed by parametric tests (α = 0.05): 2-way analysis of variance (factors: enamel condition × treatment) and Tukey posttest for all three groups (SE, DE, and TE) in T0 and T2 for microhardness; analysis of variance and Tukey's test, for shear bond strength test.

Results

Means recorded for Knoop microhardness in T2, for the SE (366.7 KHN) and TE (342.8 KHN) groups, were significantly higher than those recorded for the DE group (263.5 KHN). The shear bond strength of the SE (15.44 MPa) and TE (14.84 MPa) groups statistically differed from that of the DE group (11.95 MPa).

Conclusion

In vitro demineralized enamel treatment with amelogenin solution was capable of taking samples' hardness back to levels similar to those observed for sound enamel. The shear bond strength on the enamel subjected to this treatment was similar to that observed for healthy enamel and higher than that observed for demineralized enamel.