Crystal Facet Controlled Stable PbO2 Electrode for Efficient Degradation of Tetracycline

Stabilized Hf-doped Ti/Sb-SnO2 electrode for efficient degradation of tetracycline

The electrochemical advanced oxidation process (EAOP) has shown significant promise in the field of refractory organic wastewater treatment due to its high efficiency and environmentally friendly nature. In this study, Ti/Sb-SnO2 electrodes with varying proportions of Hf were prepared using the sol-gel method. The addition of Hf transformed the original collapsing and broken surface into a flat and regular surface. The results demonstrated that Ti/Sb-SnO2-Hf electrode doped with 6% Hf exhibited a higher oxygen evolution potential (OEP) and excellent stability. The OEP increased from 2.315 V without Hf-doping to 2.482 V, and the corresponding actual life was 321.05% higher than that without Hf. The current density (5-40 mA·cm-2), electrolyte concentration (0.02-0.2 mol·L-1), pH (3-11), and initial pollutant concentration (5-80 mg·L-1) were evaluated to confirm the tetracycline (TC) degradation characterization of Ti/Sb-SnO2-6%Hf electrodes. It was concluded that under the optimal degradation conditions, the removal rate of TC could reach 99.66% within 2 h. The degradation of TC follows first-order reaction kinetics. The oxidative degradation of TC was achieved through indirect oxidation, with ·OH playing a dominant role. TC's electrochemical oxidation degradation pathway has been proposed: Based on LC-MS results, three main pathways are speculated. During the electrocatalytic oxidation process, decarboxylation, deamidation, and ring-opening reactions occur under ·OH attack, producing intermediate compounds with m/z values of 427, 433, 350, 246, 461, 424, 330, 352, 309, 263, and 233. These intermediates are further oxidized to intermediate compounds with an m/z value of 218. This work introduces a new efficient anode electrochemical catalyst for the degradation of TC, providing a strategy for industrial applications.

Detection and treatment of mono and polycyclic aromatic hydrocarbon pollutants in aqueous environments based on electrochemical technology: recent advances

Mono and polycyclic aromatic hydrocarbons are widely distributed and severely pollute the aqueous environment due to natural and human activities, particularly human activity. It is crucial to identify and address them in order to reduce the dangers and threats they pose to biological processes and ecosystems. In the fields of sensor detection and water treatment, electrochemistry plays a crucial role as a trustworthy and environmentally friendly technology. In order to accomplish trace detection while enhancing detection accuracy and precision, researchers have created and studied sensors using a range of materials based on electrochemical processes, and their results have demonstrated good performance. One cannot overlook the challenges associated with treating aromatic pollutants, including mono and polycyclic. Much work has been done and good progress has been achieved in order to address these challenges. This study discusses the mono and polycyclic aromatic hydrocarbon sensor detection and electrochemical treatment technologies for contaminants in the aqueous environment. Additionally mentioned are the sources, distribution, risks, hazards, and problems in the removal of pollutants. The obstacles to be overcome and the future development plans of the field are then suggested by summarizing and assessing the research findings of the researchers.

Robust PbO2 modified by co-deposition of ZrO2 nanoparticles for efficient degradation of ceftriaxone sodium

In recent years, PbO2 electrodes have received widespread attention due to their high oxygen evolution reaction (OER) activity. However, due to the brittle nature of the plating layer, it is easy to cause the active layer to fall off. Pb2+ will leach out with the electrochemical process causing secondary pollution. The starting point of this study is established to improve the stability and adhesion of the electrode coating. Electrochemical oxidation technology has the characteristics of high treatment efficiency, wide range of applications, and non-polluting environment. In this study, conventional PbO2 electrodes were modified by using co-deposition of ZrO2 nanoparticles. In addition, α-PbO2 was added to increase the stability of the electrodes. At a high current density of 1 A/cm2, the accelerated life of the pure PbO2 electrode is 648 h, the accelerated life of the PbO2-ZrO2 electrode is 1.37 times that of the pure PbO2, and the electrode with an added α-PbO2 layer is 1.69 times that of the pure PbO2 electrode. The amount of dissolved Pb2+ was only 29% of that of pure PbO2. The electrochemical performance of the electrode is evaluated by studying the degradation effect of ceftriaxone sodium (CXM). The addition of ZrO2 nanoparticles alters the particle size and deposition content of PbO2, leading to a unique crystal structure distinct from pure PbO2. Compared to conventional PbO2 electrodes, the PbO2-ZrO2 can remove chemical oxygen demand (COD) and pollutants more efficiently, removing for 59% increased by 38.47%. Therefore, PbO2-ZrO2 is of great value in the field of electrochemical degradation of industrial pollutants.

B4C/Ce co-modified Ti/PbO2 dimensionally stable anode: Facile one-step electrodeposition preparation and highly efficient electrocatalytic degradation of tetracycline

The application of PbO2 for electrochemical oxidation technology is limited by its low electrocatalytic activity and short service life. Herein, based on the facile one-step electrodeposition, we prepared a boron carbide (B4C) and cerium (Ce) co-modified Ti/PbO2 (Ti/PbO2-B4C-Ce) electrode to overcome these shortcomings. Compared with Ti/PbO2 electrode, the denser surface is displayed by Ti/PbO2-B4C-Ce electrode. Meanwhile, electrochemical characterization indicates that the introduction of B4C and Ce significantly enhance the electrochemical performance of PbO2 electrode. In degradation experiments, under optimized conditions (current density 20 mA cm-2, pH 9, 0.15 M Na2SO4 and 30 °C), the fully degradation of tetracycline (TC) can be completed within 30 min. Furthermore, the trapping experiment demonstrates that ∙OH and SO4·- radicals have a synergistic effect in the degradation process of TC. Based on results of liquid chromatography-mass spectrometer, the generated ·OH preferentially attacks amides, phenols and conjugated double bond groups in TC. Importantly, Ti/PbO2-B4C-Ce electrode maintains a constant degradation efficiency even after 10 recycling tests, and its service life is 2.4 times of traditional Ti/PbO2 electrode. Hence, Ti/PbO2-B4C-Ce electrode is a promising electrode for degradation of organic wastewater containing amides, phenols, and conjugated double bond groups.

Development of SDS-Modified PbO2 Anode Material Based on Ti3+ Self-Doping Black TiO2NTs Substrate as a Conductive Interlayer for Enhanced Electrocatalytic Oxidation of Methylene Blue

Efficient and stable electrode materials are urgently required for wastewater treatment in the electrocatalytic degradation of toxic and refractory organic pollutants. Ti3+ self-doping black TiO2 nanotube arrays (Ti/B-TiO2-NTs) as an interlayer were used for preparing a novel PbO2 electrode via an electrochemical reduction technology, and a sodium dodecyl sulfate (SDS)-modified PbO2 catalytic layer was successfully achieved via an electrochemical deposition technology. The physicochemical characterization tests showed that the Ti/B-TiO2-NTs/PbO2-SDS electrodes have a denser surface and finer grain size with the introduction of Ti3+ in the interlayer of Ti/TiO2-NTs and the addition of SDS in the active layer of PbO2. The electrochemical characterization results showed that the Ti3+ self-doping black Ti/TiO2-NTs/PbO2-SDS electrode had higher oxygen evolution potential (2.11 V vs. SCE), higher electrode stability, smaller charge-transfer resistance (6.74 Ω cm-2), and higher hydroxyl radical production activity, leading to it possessing better electrocatalytic properties. The above results indicated that the physicochemical and electrochemical characterization of the PbO2 electrode were all enhanced significantly with the introduction of Ti3+ and SDS. Furthermore, the Ti/B-TiO2-NTs/PbO2-SDS electrodes displayed the best performance on the degradation of methylene blue (MB) in simulated wastewater via bulk electrolysis. The removal efficiency of MB and the chemical oxygen demand (COD) could reach about 99.7% and 80.6% under the optimal conditions after 120 min, respectively. The pseudo-first-order kinetic constant of the Ti/B-TiO2-NTs/PbO2-SDS electrode was 0.03956 min-1, which was approximately 3.18 times faster than that of the Ti/TiO2-NTs/PbO2 electrode (0.01254 min-1). In addition, the Ti/B-TiO2-NTs/PbO2-SDS electrodes showed excellent stability and reusability. The degradation mechanism of MB was explored via the experimental identification of intermediates. In summary, the Ti3+ self-doping black Ti/TiO2-NTs/PbO2-SDS electrode is a promising electrode in treating wastewater.