Ce-promoted Mn/ZSM-5 catalysts for highly efficient decomposition of ozone

The research on CO oxidation over Ce-Mn oxides: The preparation method effects and oxidation mechanism

A series of CeO₂-MnO_x for highly efficient catalytical oxidation of carbon monoxide were prepared by citrate sol-gel (C), hydrothermal (H) and hydrothermal-citrate complexation (CH) methods. The outcome indicates that the catalyst generated using the CH technique (CH-1:8) demonstrated the greatest catalytic performance for CO oxidation with a T₅₀ of 98 °C, and also good stability in 1400 min. Compared to the catalysts prepared by C and H method, CH-1:8 has the highest specific surface of 156.1 m² g^-1, and the better reducibility of CH-1:8 was also observed in CO-TPR. It is also observed the high ratio of adsorbed oxygen/lattice oxygen (1.5) in the XPS result. Moreover, characterizations by the TOF-SIMS method indicated that obtained catalyst CH-Ce/Mn = 1:8 had stronger interactions between Ce and Mn oxides, and the redox cycle of Mn³⁺+Ce⁴⁺ ↔ Mn⁴⁺+Ce³⁺ was a key process for CO adsorption and oxidation process. According to in-situ FTIR, the possible reaction pathway for CO was deduced in three ways. CO directly oxidize with O₂ to CO₂, CO adsorbed on Mn⁴⁺ and Ce³⁺ reacts with O to form intermediates (COO^-) (T > 50 °C) and carbonates (T > 90 °C), which are further oxidized into CO₂.

Selective Oxidation of Triethylamine Catalyzed by Mn-Ce/ZSM-5

The selective catalytic oxidation (SCO) of triethylamine (TEA) to harmless nitrogen (N₂), carbon dioxide (CO₂), and water (H₂O) is of green elimination technology. In this paper, Mn-Ce/ZSM-5 with different proportions of MnO_x/CeO_x were studied for the selective catalytic combustion of TEA. The catalysts were characterized by XRD, BET, H₂-TPR, XPS, and NH₃-TPD and their catalytic activities were analyzed. The results showed that MnO_x was the main active component. The addition of a small amount of CeO_x promotes the generation of high-valence Mn ions, which reduces the reduction temperature of the catalyst and increases the redox capacity of the catalyst. In addition, the synergistic effect between CeO_x and MnO_x significantly improves the mobility of reactive oxygen species on the catalyst, thus improving the catalytic performance of the catalyst. The catalytic oxidation performance of TEA over 15Mn5Ce/ZSM-5 is the highest. TEA can be completely converted at 220 °C, and the selectivity for N₂ is up to 80%. The reaction mechanism was studied by in situ diffuse reflectance infrared Fourier transform spectroscopy (in situ DRIFTS).

Heterojunctioned CuO/Cu2O catalyst for highly efficient ozone removal

In recent years, near surface ozone pollution, has attracted more and more attention, which necessitates the development of high efficient and low cost catalysts. In this work, CuO/Cu₂O heterojunctioned catalyst is fabricated by heating Cu₂O at high temperature, and is adopted as ozone decomposition catalyst. The results show that after Cu₂O is heated at 180°C conversion of ozone increases from 75.2% to 89.3% at mass space velocity 1,920,000 cm³/(g·hr) in dry air with 1000 ppmV ozone, which indicates that this heterojunction catalyst is one of the most efficient catalysts reported at present. Catalysts are characterized by electron paramagnetic resonance spectroscopy and ultraviolet photoelectron spectroscopy, which confirmed that the heterojunction promotes the electron transfer in the catalytic process and creates more defects and oxygen vacancies in the CuO/Cu₂O interfaces. This procedure of manufacturing heterostructures would also be applicable to other metal oxide catalysts, and it is expected to be more widely applied to the synthesis of high-efficiency heterostructured catalysts in the future.

Catalytic Decomposition of Residual Ozone over Cactus-like MnO2 Nanosphere: Synergistic Mechanism and SO2/H2O Interference

Ground-level ozone is an irritant and is harmful to human respiratory and nervous systems. Thus, four manganese oxides with different crystals were hydrothermally synthesized to decompose residual ozone (deO₃) in an ozone synergistic-oxidation system. Among them, a cactus-like MnO₂-IV nanosphere exhibited the highest deO₃ activity, with excellent tolerance to water vapor and SO₂/H₂O, which could maintain >88% deO₃ efficiency in the high-humidity and sulfur-containing conditions. It benefits from the unique morphology, high specific surface area, superior redox properties, oxygen chemisorption capabilities, abundant surface-active hydroxyl species, and low valence Mn species. More importantly, the detailed interference mechanism of O₂/O₃/H₂O/SO₂ molecules on MnO₂-IV was revealed utilizing in situ diffused reflectance infrared Fourier transform spectroscopy and X-ray photoelectron spectroscopy. H₂O generally caused recoverable deactivation, but that caused by SO₂ was irreversible. The synergistic effect of SO₂/H₂O promoted the formation of an unstable sulfate species, thereby deepening the deactivation but inhibiting the irreversible poisoning. Finally, nine specific steps to decompose ozone via surface-active hydroxyl/intermediates were established.

High performance ozone decomposition over MnAl-based mixed oxide catalysts derived from layered double hydroxides

Mesoporous and dispersed MnAl-based mixed metal oxide catalysts (Mn_xAlO) were fabricated via the calcination of layered double hydroxide (LDH) precursors prepared by the coprecipitation method. Their physiochemical properties were characterized and their catalytic activities for ozone decomposition were evaluated. The results indicate that the prepared Mn_xAlO catalysts have excellent catalytic activity owing to their large specific surface area, abundant surface oxygen vacancies and lower average Mn oxidation states. The Mn/Al atomic ratio and calcination temperature are found to significantly affect the textural properties and catalytic activity for ozone decomposition. The Mn₂AlO-400 catalyst (Mn/Al = 2, calcined at 400 °C) exhibited 84.8% ozone conversion after 8 h reaction under an initial ozone concentration of 45 ± 2 ppm, 30 ± 1 °C, a relative humidity of 50% ± 3%, and a space velocity of 550 000 h⁻¹. The results also show that the catalytic activity of Mn₂AlO-400, which was deactivated owing to the accumulation of oxygen-related intermediates, was recovered by calcination at 400 °C under a N₂ atmosphere for 1 h. A possible reason for catalyst deactivation and regeneration is proposed. This work provides a facile method for fabricating Mn_xAlO catalysts with excellent characteristics to achieve better catalytic activity, which are promising candidates for practical ozone decomposition.

Mesoporous and highly dispersed MnAl-based mixed metal oxide catalysts (Mn_xAlO) were fabricated via the calcination of layered double hydroxides (LDHs), which presented excellent catalytic activity for ozone decomposition.

Enhanced activity and water tolerance promoted by Ce on MnO/ZSM-5 for ozone decomposition

Catalytic decomposition is a promising way to eliminate ozone using manganese oxides. However, water-induced deactivation of the catalysts remains a challenge for further application. In this work, a series of Ce-promoted MnO supported on ZSM-5 (Mn-xCe/ZSM-5) were developed for ozone decomposition, which exhibited superior catalytic performance. The catalysts were characterized by multiple techniques. It is indicated that MnO was highly dispersed on ZSM-5 (Mn/ZSM-5), accounting for the high performance of ozone decomposition. Addition of Ce in Mn/ZSM-5 formed abundant redox pairs that promoted electron transfer, and thus exhibited superior ozone decomposition activity. Mn-3Ce/ZSM-5 with medium Ce loading showed the maximum activity by exposing the most active sites. Furthermore, Mn-3Ce/ZSM-5 was highly water-resistant in comparison with Mn/ZSM-5 by modulating the surface acidic property to be beneficial for the water desorption. This work provides an efficient and facile way to fabricate Ce-promoted Mn with low valence for effective and stable decomposition of ozone at room temperature.