A cross-linked charring strategy for mitigating the hazards of smoke and heat of aluminum diethylphosphonate/polyamide 6 by caged octaphenyl polyhedral oligomeric silsesquioxanes

Engineering Sulfur-Containing Polymeric Fire-Retardant Coatings for Fire-Safe Rigid Polyurethane Foam

With the advantages of lightweight and low thermal conductivity properties, polymeric foams are widely employed as thermal insulation materials for energy-saving buildings but suffer from inherent flammability. Flame-retardant coatings hold great promise for improving the fire safety of these foams without deteriorating the mechanical-physical properties of the foam. In this work, four kinds of sulfur-based flame-retardant copolymers are synthesized via a facile radical copolymerization. The sulfur-containing monomers serve as flame-retardant agents including vinyl sulfonic acid sodium (SPS), ethylene sulfonic acid sodium (VS), and sodium p-styrene sulfonate (VSS). Additionally, 2-hydroxyethyl acrylate (HEA) and 4-hydroxybutyl acrylate are employed to enable a strong interface adhesion with polymeric foams through interfacial H-bonding. By using as-synthesized waterborne flame-retardant polymeric coating with a thickness of 600 µm, the coated polyurethane foam (PUF) can achieve a desired V-0 rating during the vertical burning test with a high limiting oxygen index (LOI) of >31.5 vol%. By comparing these sulfur-containing polymeric fire-retardant coatings, poly(VS-co-HEA) coated PUF demonstrates the best interface adhesion capability and flame-retardant performance, with the lowest peak heat release rate of 166 kW m-2 and the highest LOI of 36.4 vol%. This work provides new avenues for the design and performance optimization of advanced fire-retardant polymeric coatings.

Enhancing Char Formation and Flame Retardancy of Ethylene-Vinyl Acetate Copolymer (EVA)/Aluminum Hydroxide (ATH) Composites by Grafting Ladder Phenyl/Vinyl Polysilsesquioxane (PhVPOSS)

The ladder phenyl/vinyl polysilsesquioxane (PhVPOSS) was used to improve the flame-retardancy performances of ethylene-vinyl acetate copolymer (EVA)/aluminum hydroxide (ATH) composites due to the reactivity of its vinyl groups. FTIR, XPS, 1H NMR, and SEM-EDS data demonstrated the PhVPOSS grafting onto EVA molecular chains. The PhVPOSS improved the thermal stability of EVA/ATH composites, as shown by the thermogravimetric analysis (TGA). Furthermore, with the cone calorimeter (CONE) experiments, EVA/ATH/PhVPOSS showed better fire safety than the EVA/ATH composites, with the PHRR, PSPR, and PCOP reduced by 7.89%, 57.4%, and 90.9%, respectively. The mechanism investigations of flame retardancy revealed that the charring behaviors of the EVA/ATH/PhVPOSS composites were improved by the formation of Si-C bonds and Si-O bonds, and a more compact and denser char layer can contribute more to the barrier effect.

Influence of the Crystal Structure of Melamine Trimetaphosphate 2D Supramolecules on the Properties of Polyamide 6

To explore the influence of the crystal structure difference of melamine trimetaphosphate (MAP) on the application performance of its polymer composites, an intumescent flame retardant with the optimal crystal type was designed and synthesized to improve the mechanical properties and flame retardancy of polyamide 6 (PA6). I-MAP and II-MAP were obtained using different concentrations of MA and sodium trimetaphosphate (STMP) in an acidic aqueous solution. The morphology, chemical composition, and thermal stability were comprehensively characterized by Fourier transform infrared (FTIR) spectroscopy, X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), X-ray diffraction (XRD), and thermogravimetric analysis (TGA). The dispersion, mechanical properties, and flame retardancy of PA6/I-MAP and PA6/II-MAP were evaluated by SEM, stress and strain, limiting oxygen index test (LOI), vertical burning test (UL-94), cone calorimetry (CONE) test, and char residue analysis. The conclusion is as follows: I-MAP and II-MAP have a greater influence on the physical properties of PA6 but less influence on the chemical properties. Compared with PA6/I-MAP, the tensile strength of PA6/II-MAP is 104.7% higher, the flame rating reaches V-0, and PHRR is reduced by 11.2%.

Flame Retardancy and Mechanical Properties of Melt-Spun PA66 Fibers Prepared by End-Group Blocking Technology

Preparing flame-retardant polyamide 66 (PA66) fibers through melt spinning remains one of the biggest challenges nowadays. In this work, dipentaerythritol (Di-PE), an eco-friendly flame retardant, was blended into PA66 to prepare PA66/Di-PE composites and fibers. It was confirmed that Di-PE could significantly improve the flame-retardant properties of PA66 by blocking the terminal carboxyl groups, which was conducive to the formation of a continuous and compact char layer and the reduced production of combustible gas. The combustion results of the composites showed that the limiting oxygen index (LOI) increased from 23.5% to 29.4%, and underwriter laboratories 94 (UL-94) passed the V-0 grade. The peak of heat release rate (PHRR), total heat release (THR), and total smoke production (TSP) decreased by 47.3%, 47.8%, and 44.8%, respectively, for the PA66/6 wt% Di-PE composite compared to those recorded for pure PA66. More importantly, the PA66/Di-PE composites possessed excellent spinnability. The prepared fibers still had good mechanical properties (tensile strength: 5.7 ± 0.2 cN/dtex), while maintaining good flame-retardant properties (LOI: 28.6%). This study provides an outstanding industrial production strategy for fabricating flame-retardant PA66 plastics and fibers.

Thermal degradation and flame retardancy of nylon 6/aluminum methylmethoxy phosphonate composites

An aluminum methylmethoxyphosphonate (AlPo)-based flame retardant (FR) was synthesized. Thermal degradation and flame retardancy of nylon 6 (PA6)/AlPo composites were examined and compared with PA6/commercial aluminum diethylphosphinate (AlPi) composites. The PA6/AlPo composite achieved a V-0 rating at 20 wt% loading during the UL-94 test, and it exhibited the formation of a charred layer that protected the polymer from burning and reduced the release of gases during the combustion of PA6. AlPo demonstrated exceptional performance in gaseous and condensed phases in the PA6 matrix, whereas AlPi only worked in the gaseous phase. The differences between the thermal degradation mechanisms and flame retardancies of AlPi and AlPo were investigated via Fourier-transform infrared (FT-IR) spectroscopy, thermogravimetric analysis (TGA), scanning electron microscopy (SEM), and cone calorimetry. A suitable degradation mechanism was proposed to aid the development of flame retardants in the future.

Co-curing preparation of flame retardant and smoke-suppressive epoxy resin with a novel phosphorus-containing ionic liquid

Phosphorus-containing ionic liquid derivatives have been proven to be effective flame retardants for epoxy resin (EP). Flame retardants can accelerate the curing process and improve flame retardancy and smoke suppression of EP composites, which is challenging. In this paper, a novel phosphorus-containing ionic liquid (TPP-PF₆) was synthesized and used both as a co-curing agent with 4,4'-diaminodiphenylmethane (DDM) and as a highly effective flame retardant for EP. It has been found that TPP-PF₆ was conducive to improve the char formation of EP to inhibit the smoke release at high temperatures. For EP/TPP-PF₆ composites, the flame-retardant performance was enhanced rapidly with the increase of TPP-PF₆. With only 2 wt% of TPP-PF₆, EP/2.0TPP-PF₆ reached a UL-94 V-0 rating and a limiting oxygen index of 30.3%. The peak heat release rate, total heat release, and total smoke production values of EP/2.0TPP-PF₆ were reduced by 36.32%, 45.81%, and 15.1% compared with those of pure EP, respectively. The thermal degradation products and flame retardant mechanism in gas and condensed phases were studied. It was found that TPP-PF₆ had flame retardant effect in the barrier effect of the condensed phase and the quenching effect of the gas phase. This work explores the high-efficiency flame retardant and smoke-suppressive structures with co-curing properties for EP, thus promoting the wide application of EP materials.

Wood-Based Self-Supporting Nanoporous Three-Dimensional Electrode for High-Efficiency Battery Deionization

Developing highly efficient advanced battery deionization (BDI) electrode materials at a low cost is vital for seawater desalination. Herein, a high-efficiency wood-based BDI electrode has been fabricated for seawater desalination, benefiting from the self-supporting three-dimensional (3D) nanoporous structure and rich redox-active sites. The finely tuned rich electrochemical redox active C═O groups on the surface of the wood electrode derived from the facile thermochemical conversion of lignin play a crucial role in the Faradaic cation removal dynamics of BDI. Coupling the 3D wood electrode and a polyaniline-modified wood electrode as the cathode and anode, an all-wood-electrode-based deionization battery has been successfully assembled with a state-of-the-art ion removal capacity of up to 164 mg g^-1 in seawater. Our work reported an example of utilizing wood as the BDI electrode via fine-tuning the redox-active sites, demonstrating a novel resource utilization pathway of converting cheap biomass into BDI electrodes for highly efficient seawater desalination.