Combined effect of corona discharge and enzymatic treatment on the mechanical and surface properties of wool

Synthesis of grafted bromoisobutyryl esterified starch using electron transfer atom transfer radical polymerization method with high-performance adhesion and film properties

Nowadays, few investigations on the process parameters of grafted starch synthesized using electron transfer atom transfer radical polymerization (ARGET ATRP) and its applications in warp sizing and paper-making are presented. Therefore, this study aimed to survey the appropriate process parameters of bromoisobutyryl esterified starch-g-poly(acrylic acid) (BBES-g-PAA) synthesized by the ARGET ATRP, and also aimed to provide a new biobased BBES-g-PAA adhesive. The appropriate synthesis process parameters were 1.2, 0.32, and 0.6 in the molar ratios of vitamin C, CuBr2, and pentamethyldivinyltriamine to BBES, respectively, at 40 °C for 5 h. The BBES-g-PAA samples with a grafting ratio range of 4.63-14.14 % exhibited bonding forces of 57.8-64.6 N to wool fibers [55.5 N (BBES) and 53.8 N (ATS)], and their films showed breaking elongations of 3.29-3.80 % [2.74 % (BBES) and 2.49 % (ATS)] and tensile strengths of 29.1-25.4 MPa [30.4 MPa (BBES) and 34.7 MPa (ATS)]. Compared with BBES, significantly increased bonding forces and film elongations, and decreased film strengths for the BBES-g-PAA samples with grafting ratios ≥10.54 % were displayed (p < 0.05). The time (100-42 s) taken for the BBES-g-PAA films was significantly shorter than that of ATS (246 s) and BBES (196 s) films (p < 0.05), corresponding to better desizability.

Photocatalytic Properties of Core-Shell Structured Wool-TiO2 Hybrid Composite Powders

In this study, a special core–shell structured wool-TiO2 (WT) hybrid composite powder also having TiO2 nanoparticles incorporated inside cortical cells was reported. The wool pallets were pulverized from wool fibers using vibration-assisted ball milling technique and the WT powders having mesopores and macropores were produced in hydrothermal process. Experimental results indicated that the infiltrated TiO2 nanoparticles were amorphous structure, while the coated TiO2 nanoparticles were anatase phase structure. The crystallized TiO2 nanoparticles were grafted with wool pallets by the N−Ti4+/S−Ti4+/O−Ti4+ bonds. The BET surface area was measured as 153.5 m2/g and the particle sizes were in the 600–3600 nm and 4000–6500 nm ranges. The main reactive radical species of the WT powders were holes, and •O2−, 1O2, and •OH were also involved in the photodegradation of MB dye under visible light irradiation. The experimental parameters for photodegradation of MB dye solution were optimized as follows: 0.25 g/L of WT powders was added in 40 mL of 3 mg/L MB dye solution containing 50 mL/L H2O2, which resulted in the increases of COD value of degraded MB dye solution up to 916.9 mg/L at 120 min. The WT powders could be used for repeatedly photodegradation of both anionic and cationic dyes.