Large area electrolyte coating through surface and interface engineering in roll-to-roll slot-die coating process

Effect of Radial Stress on the Nanoparticle-Based Electrolyte Layer in a Center-Wound Roll with Roll-to-Roll Systems

Recently, slot-die coating based on the roll-to-roll process has been actively used to fabricate nanoparticle-based electrolyte layers because it is advantageous for high-speed processes and mass production of uniformly thick electrolyte layers. In this process, the fabricated electrolyte layer is stored as a wound roll throughout the rewinding process. We analyzed the defects and geometric changes in an electrolyte layer, i.e., gadolinium-doped cerium oxide (GDC), due to the radial stress in the wound roll. We found that the thickness of the coated layer could be decreased by increasing the radial stress, i.e., cracks can be generated in the coated layer if excessively high radial stress is applied to the wound-coated layer. More thickness changes and crack defects were generated with time due to the residual stress in the wound roll. Finally, we analyzed the effects of taper tension profiles on the defects of the coated layer in the wound roll and determined the taper tension profile to minimize defects.

Transmittance Control of a Water-Repellent-Coated Layer on a Tensioned Web in a Roll-to-Roll Slot-Die Coating System

Solar cells are important alternatives to fossil fuels for energy generation in today's world, where the demand for alternative, renewable sources of energy is increasing. However, solar cells, which are installed outdoors, are susceptible to pollution by environmental factors. A solution to overcome this limitation involves coating solar cell surfaces with functional coatings. In this study, we propose a transmittance control method for a tensioned web in a roll-to-roll, transparent, water-repellent film coating. First, we analyzed the effects of process conditions on the transmittance and contact angle of the transparent water-repellent film during roll-to-roll slot-die coating. It was confirmed that the tension was the most dominant factor, followed by the coating gap. Through the tension control, the transmittance was changed by 3.27%, and the contact angle of the DI water was changed by 17.7°. In addition, it was confirmed that the transmittance was changed by 0.8% and the contact angle of DI water by 3.9° via the coating gap control. Based on these results, a transmittance prediction model was developed according to the tension and coating gap, and was then verified experimentally. Finally, a water-repellent film with a high transmittance of 89.77% was obtained using this model.

Numerical Modeling of Ink Widening and Coating Gap in Roll-to-Roll Slot-Die Coating of Solid Oxide Fuel Cell Electrolytic Layer

Slot-die coatings are advantageous when used for coating large-area flexible devices; in particular, the coating width can be controlled and simultaneous multi-layer coatings can be processed. To date, the effects of ink widening and the coating gap on the coating thickness have only been considered in a few studies. To this end, we developed two mathematical models to accurately estimate the coating width and thickness that consider these two effects. We used root mean square deviation (RMSD) to experimentally verify the developed method. When the coating gap was increased, the coating width increased and the coating thickness decreased. Experimental results showed that the estimated performances of the coating width and thickness models were as high as 98.46% and 95.8%, respectively. We think that the developed models can be useful for determining the coating conditions according to the ink properties to coat a functional layer with user-defined widths and thicknesses in both lab- and industrial-scale roll-to-roll slot-die coating processes.

Web Unevenness Due to Thermal Deformation in the Roll-to-Roll Manufacturing Process

In roll-to-roll (R2R) processing, web uniformity is a crucial factor that can guarantee high coating quality. To understand web defects due to thermal deformation, we analyzed the effect of web unevenness on the coating quality of an yttria-stabilized zirconia (YSZ) layer, a brittle electrolyte of solid oxide fuel cells (SOFCs). We used finite-element analysis to study thermal and mechanical deformations at different drying temperature levels. A YSZ layer was also coated using R2R slot-die coating to observe the effect of web unevenness on coating quality. Web unevenness was generated by thermal deformation due to conduction and convection heat from the dryer. Because of varying web unevenness with time, the YSZ layer developed cracks. At higher drying temperatures, more coating defects with larger widths were generated. Results indicated that web unevenness at the coating section led to coating defects that could damage the SOFCs and decrease yield in the R2R process. Coating defects generated by web unevenness caused by convection and conduction heat should be considered in the high-volume production of brittle electrolytes using the R2R process.