Role of non-carious cervical lesions multicausality in the behavior of respective restorations

Influence of carbonated acid beverage on fracture resistance and marginal gap formation in different restorative approaches to non-carious cervical lesions

OBJECTIVE

This study is to evaluate fracture resistance, failure mode, and gap formation at the restorative interface of unrestored or restored non-carious cervical lesions (NCCLs) submitted to a short-term erosive environment.

MATERIALS AND METHODS

Artificial NCCLs were produced in vitro in bovine incisors, and were randomly divided into four restorative resins groups (n = 22): nanohybrid-NR; bulk-fill-BR; flow with a nanohybrid layer-FNR; bulk-fill with a nanohybrid layer-BNR; and a group unrestored-UR (n = 16). Half of the specimens were submitted to an erosive challenge (per 5 min, 3 × a day for 7 days, before and after restoration), and the other half, was immersed in artificial saliva. After, all teeth undergone thermal (5 ºC, 37 ºC, and 55 ºC, 3600 cycles) and mechanical (50 N, 2 Hz, 300,000 cycles) aging. Eighty teeth were subjected to compressive loading, and resistance and failures were analyzed, while 24 teeth were evaluated for gaps by microcomputed tomography. Statistical tests were performed (p < 0.05).

RESULTS

The restorative approaches affected fracture resistance (η2p = 0.14, p = 0.023), and gap formation (η2 = 0.18, p = 0.012) and so did the immersion medium (fracture η2p = 0.09, p = 0.008; gap η2 = 0.09, p = 0.017). BNR showed the highest resistance, while UR the lowest. FNR showed the highest gaps in both immersion media. Neither the resin groups nor the immersion media were associated with failure mode.

CONCLUSIONS

The erosive immersion medium based in acid beverages has been shown to affect NCCLs with or without restoration, but when Bulk-Fill resin is covered by nanohybrid resin, the performance is good.

CLINICAL RELEVANCE

Erosion negatively affects restorations, but unrestored NCCL shows worse biomechanical performance in stress-bearing situations.

Numerical Study of the Mechanical Behaviour of Wedge-Shaped Defect Filling Materials

This paper deals with direct restorations of teeth with non-carious cervical lesions (NCCL). NCCL defects are capable of gradual growth and are accompanied by the degradation of the surrounding tissue. Direct restorative treatment, in which the cavity is filled with a cementing agent, is considered to be an accessible and common treatment option. The study included simulations of the teeth without lesions, the teeth with V and U lesions and the tooth-restorative system. Parameterised numerical tooth models were constructed. Two cases with defect depths of 0.8 mm and ~1.7 mm and three variants with fillet radii of the defect end of 0.1, 0.2 and 0.3 mm were considered. The effect of two biomaterials for restorations was studied, namely Herculite XRV (Kerr Corp, Orange, CA, USA) and Charisma (Heraeus Kulzer GmbH, Hanau, Germany). The models were deformed with a vertical load of 100 to 1000 N from the antagonist tooth. The tooth-restorative system was considered, taking into consideration the contact interaction in the interface areas with the tooth tissues. Within the limits of the research, the character of the distribution of the deformation characteristics and their dependence on the level of loading, the depth of the defect and the radius of the curvature of the "wedge" were established.