Engineering and repair of diaphragm using biosheet (a collagenous connective tissue membrane) in rabbits

Diaphragmatic hernia repair porcine model to compare the performance of biodegradable membranes against Gore-Tex®

BACKGROUND

Patch repair of congenital diaphragmatic hernia (CDH) using Gore-Tex® is associated with infection, adhesions, hernia recurrence, long-term musculoskeletal sequels and poor tissue regeneration. To overcome these limitations, the performance of two novel biodegradable membranes was tested to repair CDH in a growing pig model.

METHODS

Twelve male pigs were randomly assigned to 3 different groups of 4 animals each, determined by the type of patch used during thoracoscopic diaphragmatic hernia repair (Gore-Tex®, polycaprolactone electrospun membrane-PCLem, and decellularized human chorion membrane-dHCM). After 7 weeks, all animals were euthanized, followed by necropsy for diaphragmatic evaluation and histological analysis.

RESULTS

Thoracoscopic defect creation and diaphragmatic repair were performed without any technical difficulty in all groups. However, hernia recurrence rate was 0% in Gore-Tex®, 50% in PCLem and 100% in dHCM groups. At euthanasia, Gore-Tex® patches appeared virtually unchanged and covered with a fibrotic capsule, while PCLem and dHCM patches were replaced by either floppy connective tissue or vascularized and floppy regenerated membranous tissue, respectively.

CONCLUSION

Gore-Tex® was associated with a higher survival rate and lower recurrence. Nevertheless, the proposed biodegradable membranes were associated with better tissue integration when compared with Gore-Tex®.

Development and systematic evaluation of decellularization protocols in different application models for diaphragmatic tissue engineering

BACKGROUND

Tissue engineered bioscaffolds based on decellularized composites have gained increasing interest for treatment of various diaphragmatic impairments, including muscular atrophies and diaphragmatic hernias. Detergent-enzymatic treatment (DET) constitutes a standard strategy for diaphragmatic decellularization. However, there is scarce data on comparing DET protocols with different substances in distinct application models in their ability to maximize cellular removal while minimizing extracellular matrix (ECM) damage.

METHODS

We decellularized diaphragms of male Sprague Dawley rats with 1 % or 0.1 % sodium dodecyl sulfate (SDS) and 4 % sodium deoxycholate (SDC) by orbital shaking (OS) or retrograde perfusion (RP) through the vena cava. We evaluated decellularized diaphragmatic samples by (1) quantitative analysis including DNA quantification and biomechanical testing, (2) qualitative and semiquantitative analysis by proteomics, as well as (3) qualitative assessment with macroscopic and microscopic evaluation by histological staining, immunohistochemistry and scanning electron microscopy.

RESULTS

All protocols produced decellularized matrices with micro- and ultramorphologically intact architecture and adequate biomechanical performance with gradual differences. The proteomic profile of decellularized matrices contained a broad range of primal core and ECM-associated proteins similar to native muscle. While no outstanding preference for one singular protocol was determinable, SDS-treated samples showed slightly beneficial properties in comparison to SDC-processed counterparts. Both application modalities proved suitable for DET.

CONCLUSION

DET with SDS or SDC via orbital shaking or retrograde perfusion constitute suitable methods to produce adequately decellularized matrices with characteristically preserved proteomic composition. Exposing compositional and functional specifics of variously treated grafts may enable establishing an ideal processing strategy to sustain valuable tissue characteristics and optimize consecutive recellularization. This aims to design an optimal bioscaffold for future transplantation in quantitative and qualitative diaphragmatic defects.

Research progress of biomaterials and innovative technologies in urinary tissue engineering

Substantial interests have been attracted to multiple bioactive and biomimetic biomaterials in recent decades because of their ability in presenting a structural and functional reconstruction of urinary tissues. Some innovative technologies have also been surging in urinary tissue engineering and urological regeneration by providing insights into the physiological behavior of the urinary system. As such, the hierarchical structure and tissue function of the bladder, urethra, and ureter can be reproduced similarly to the native urinary tissues. This review aims to summarize recent advances in functional biomaterials and biomimetic technologies toward urological reconstruction. Various nanofirous biomaterials derived from decellularized natural tissues, synthetic biopolymers, and hybrid scaffolds were developed with desired microstructure, surface chemistry, and mechanical properties. Some growth factors, drugs, as well as inorganic nanomaterials were also utilized to enhance the biological activity and functionality of scaffolds. Notably, it is emphasized that advanced approaches, such as 3D (bio) printing and organoids, have also been developed to facilitate structural and functional regeneration of the urological system. So in this review, we discussed the fabrication strategies, physiochemical properties, and biofunctional modification of regenerative biomaterials and their potential clinical application of fast-evolving technologies. In addition, future prospective and commercial products are further proposed and discussed.

Application of Biosheets as Right Ventricular Outflow Tract Repair Materials in a Rat Model

Purposes

We report the experimental use of completely autologous biomaterials (Biosheets) made by “in-body tissue architecture” that could resolve problems in artificial materials and autologous pericardium. Here, Biosheets were implanted into full-thickness right ventricular outflow tract defects in a rat model. Their feasibility as a reparative material for cardiac defects was evaluated.

Methods

As the evaluation of mechanical properties of the biosheets, the elastic moduli of the biosheets and RVOT-free walls of rats were examined using a tensile tester. Biosheets and expanded polytetrafluoroethylene sheet were used to repair transmural defects surgically created in the right ventricular outflow tracts of adult rat hearts (n = 9, each patch group). At 4 and 12 weeks after the operation, the hearts were resected and histologically examined.

Results

The strength and elastic moduli of the biosheets were 421.3 ± 140.7 g and 2919 ± 728.9 kPa, respectively, which were significantly higher than those of the native RVOT-free walls (93.5 ± 26.2 g and 778.6 ± 137.7 kPa, respectively; P < 0.005 and P < 0.001, respectively). All patches were successfully implanted into the right ventricular outflow tract-free wall of rats. Dense fibrous adhesions to the sternum on the epicardial surface were also observed in 7 of 9 rats with ePTFE grafts, whereas 2 of 9 rats with biosheets. Histologically, the vascular-constructing cells were infiltrated into Biosheets. The luminal surfaces were completely endothelialized in all groups at each time point. There was also no accumulation of inflammatory cells.

Conclusions

Biosheets can be formed easily and have sufficient strength and good biocompatibility as a patch for right ventricular outflow tract repair in rats. Therefore, Biosheet may be a suitable material for reconstructive surgery of the right ventricular outflow tract.

A new method of primary engineering of esophagus using orthotopic in-body tissue architecture

PURPOSE

Tissue engineering of esophagus is required for management of long-gap esophageal atresia (LGEA). Collagenous connective tissue membranes fabricated by in-body tissue architecture (iBTA), called biosheets, can repair esophageal defects and generate tissues similar to native esophagus. However, iBTA requires second-stage surgery because of heterotopic preparation of biosheets. Our aim was to develop orthotopic iBTA for primary engineering of the esophagus by interposing a tubular mold to the esophageal defect.

METHOD

The cervical esophagus of six rats was transected. An acrylic tube (internal diameter 2.6 mm, length 7.0 mm) was inserted and fixed between the ends of the upper and lower esophagus, and a 3 mm-long esophageal defect was created. Four weeks later, the rats were sacrificed for histological analysis.

RESULTS

Postoperatively the rats could intake liquid food. After four weeks, the esophageal defects were filled with regenerated tissues. Histologically the new esophageal walls stained positive for collagen type I. The inner surfaces were covered with stratified squamous epithelium that expressed pan-cytokeratin. In only one of six rats, regeneration of muscular-like tissue was suggested by positive immunohistochemical staining for desmin.

CONCLUSION

Orthotopic iBTA can regenerate a substitute esophagus with esophageal epithelium and collagenous wall. This technique may be a novel treatment for esophageal atresia with gaps of various lengths including LGEA.

Three-month outcomes of aortic valve reconstruction using collagenous membranes (biosheets) produced by in-body tissue architecture in a goat model: a preliminary study

BACKGROUND

Autologous pericardium is widely used as a plastic material in intracardiac structures, in the pulmonary artery, and in aortic valve leaflets. For aortic valve reconstruction (AVRec) using the Ozaki procedure, it has produced excellent clinical results over a 10-year period. In-body tissue architecture (iBTA), which is based on the phenomenon of tissue encapsulation of foreign materials, can be used to prepare autologous prosthetic tissues. In this preliminary study, we examined whether biosheets can be used as valve leaflet material for glutaraldehyde-free AVRec by subchronic implantation experiments in goats and evaluated its performance compared with glutaraldehyde-treated autologous pericardium for AVRec.

METHODS

Biosheets were prepared by embedding molds for two months into the dorsal subcutaneous spaces of goats. Autogenic biosheets (n = 4) cut into the shape of the valve were then implanted to the aortic valve annulus of four goats for three months without glutaraldehyde treatment. Autologous pericardium (n = 4) was used in four goats as a control. Valve function was observed using echocardiography.

RESULTS

All goats survived the three-month study period. With biosheets, the leaflet surfaces were very smooth and, on histology, partially covered with a thin neointima (including endothelial cells). Biosheets were more thoroughly assimilated into the aortic root compared with autologous pericardium.

CONCLUSIONS

For the first time, biosheets were used for large animal AVRec. Biosheets could function as leaflets in the aortic position and may have the ability to assimilate into native valves.

Aortic valve neocuspidization with in-body tissue-engineered autologous membranes: preliminary results in a long-term goat model

OBJECTIVES

Aortic valve neocuspidization has shown satisfactory clinical outcomes; however, autologous pericardium durability is a concern for young patients. This study applied an autologous collagenous membrane (Biosheet®), produced by in-body tissue architecture, to aortic valve neocuspidization and investigated its long-term outcome in a goat model.

METHODS

Moulds were embedded subcutaneously in 6 goats. After 2 months, Biosheets formed in the moulds. We performed aortic valve neocuspidization using a portion of the sheets with a thickness of 0.20-0.35 mm, measured by optical coherence tomography. Animals were subjected to echocardiography and histological evaluation at 6 months (n = 3) and 12 months (n = 3). As a control, the glutaraldehyde-treated autologous pericardium was used in 4 goats that were similarly evaluated at 12 months.

RESULTS

All animals survived the scheduled period. At 6 months, Biosheets maintained valve function and showed a regeneration response: fusion to the annulus, cell infiltration to the leaflets and appearance of elastic fibres at the ventricular side. After 12 months, the regenerative structure had changed little without regression, and there was negligible calcification in the 1/9 leaflets. However, all cases had one leaflet tear, resulting in moderate-to-severe aortic regurgitation. In the pericardium group, three-fourths of the animals experienced moderate-to-severe aortic regurgitation with a high rate of calcification (9/12 leaflets).

CONCLUSIONS

Biosheets may have regeneration potential and anti-calcification properties in contrast to autologous pericardium. However, in order to obtain reliable outcome, further improvements are required to strictly control and optimize its thickness, density and homogeneity.

Urinary bladder reconstruction using autologous collagenous connective tissue membrane "Biosheet®" induced by in-body tissue architecture: A pilot study

INTRODUCTION

In-body tissue architecture (iBTA) technology, based on cell-free tissue engineering, can produces collagenous tissues for implantation by subcutaneous embedding a designed mold. The aim of this study was to evaluate the biocompatibility of iBTA-induced "Biosheet®" collagenous sheets, as scaffold materials for bladder reconstruction.

METHODS

Canine Biosheet® implants were prepared by embedding molds into subcutaneous pouches in beagles for 8 weeks. A part of canine bladder wall was excised (2 × 2 cm) and repaired by patching the same sized autologous Biosheet®. The Biosheet® implants were harvested 4 weeks (n = 1) and 12 weeks (n = 3) after the implantation and evaluated histologically.

RESULTS

No disruption of the patched Biosheet® implants or urinary leakage into the peritoneal cavity was observed during the entire observation periods. There were no signs of chronic inflammation or Biosheet® rejection. The urine-contacting surface of luminal surface of the Biosheet® was covered with a multicellular layer of urothelium cells 4 weeks after implantation. α-SMA-positive muscle cells were observed at the margin of the Biosheet® implants at 12 weeks after the implantation. In addition, in the center of the Biosheet® implants, the formation of microvessels stained as α-SMA-positive was observed.

CONCLUSION

Biosheet® implants have biocompatibility as a scaffold for bladder reconstruction, indicating that they may be applicable for full-thickness bladder wall substitution. Further studies are required for definitive evaluation as a scaffold for bladder reconstruction.

Design and fabrication of polycaprolactone/gelatin composite scaffolds for diaphragmatic muscle reconstruction

Diaphragmatic wall defects caused by congenital disorders or disease remain a major challenge for physicians worldwide. Polymeric patches have been extensively explored within research laboratories and the clinic for soft tissue and diaphragm reconstruction. However, patch usage may be associated with allergic reaction, infection, granulation, and recurrence of the hernia. In this study, we designed and fabricated a porous scaffold using a combination of 3D printing and freeze-drying techniques. A 3D printed polycaprolactone (PCL) mesh was used to reinforcegelatin scaffolds, representing an advantage over previously reported examples since it provides mechanical strength and flexibility. In vitro studies showed that adherent cells were anchorage-dependent and grew as a monolayer attached to the scaffolds. Microscopic observations indicated better cell attachments for the scaffolds with higher gelatin content as compared with the PCL control samples. Tensile testing demonstrated the mechanical strength of samples was significantly greater than adult diaphragm tissue. The biocompatibility of the specimens was investigated in vivo using a subcutaneous implantation method in Bagg albino adult mice for 20 days, with the results indicating superior cellular behavior and attachment on scaffolds containing gelatin in comparison to pure PCL scaffolds, suggesting that the porous PCL/gelatin scaffolds have potential as biodegradable and flexible constructs for diaphragm reconstruction.

Fabrication of an anatomy-mimicking BIO-AIR-TUBE with engineered cartilage

Introduction

We devised a strategy for the fabrication of an ‘anatomy-mimicking’ cylinder-type engineered trachea combined with cartilage engineering. The engineered BIOTUBEs are used to support the architecture of the body tissue, for long-segment trachea (>5 cm) with carinal reconstruction. The aim of the present study was to fabricate an anatomy-mimicking cylinder-type regenerative airway, and investigate its applicability in a rabbit model.

Methods

Collagen sponge rings (diameter: 6 mm) were arranged on a silicon tube (diameter: 6 mm) at 2-mm intervals. Chondrocytes from the auricular cartilage were seeded onto collagen sponges immediately prior to implantation in an autologous manner. These constructs were embedded in dorsal subcutaneous pouches of rabbits. One month after implantation, the constructs were retrieved for histological examination. In addition, cervical tracheal sleeve resection was performed, and these engineered constructs were implanted into defective airways through end-to-end anastomosis.

Results

One month after implantation, the engineered constructs exhibited similar rigidity and flexibility to those observed with the native trachea. Through histological examination, the constructs showed an anatomy-mimicking tracheal architecture. In addition, the engineered constructs could be anastomosed to the native trachea without air leakage.

Conclusion

The present study provides the possibility of generating anatomy-mimicking cylinder-type airways, termed BIO-AIR-TUBEs, that engineer cartilage in an in-vivo culture system. This approach involves the use of BIOTUBEs formed via in-body tissue architecture technology. Therefore, the BIO-AIR-TUBE may be useful as the basic architecture of artificial airways.

iBTA-induced bovine Biosheet for repair of abdominal wall defects in a beagle model: proof of concept

INTRODUCTION

We evaluated the usefulness of xeno-Biosheets, an in-body tissue architecture-induced bovine collagenous sheet, as repair materials for abdominal wall defects in a beagle model.

MATERIALS AND METHODS

Biosheets were prepared by embedding cylindrical molds into subcutaneous pouches of three Holstein cows for 2-3 months and stored in 70% ethanol. The Biosheets were 0.5 mm thick, cut into 2 cm × 2 cm, and implanted to replace defects of the same size in the abdominal wall of nine beagles. The abdominal wall and Biosheets were harvested and subjected to histological evaluation at 1, 3, and 5 months after implantation (n = 3 each).

RESULTS

The Biosheet and bovine pericardiac patch (control) were not stressed during the suture operation and did not split, and patches were easily implanted on defective wounds. After implantation, the patch did not fall off and was not perforated, and healing was observed nacroscopically in all cases. During the first month of implantation, accumulation of inflammatory cells was observed along with decomposition around the Biosheet. Decomposition was almost complete after 3 months, and the Biosheet was replaced by autologous collagenous connective tissue without rejection. After 5 months, the abdominal wall muscle elongated from the periphery of the newly formed collagen layer and the peritoneum was formed on the peritoneal cavity surface. Regeneration of almost all layers of the abdominal wall was observed. However, almost all pericardium patches were remained even at 5 months with inflammation.

CONCLUSION

Bovine Biosheets requiring no special post-treatment can be useful as off-the-shelf materials for abdominal wall repair.