Surface effects on deuterium permeation through vanadium membranes

Influence of Gas for Thermal Treatment on Hydrogen Permeation in V-Ni Alloy Membranes

Hydrogen separation is an important step for the utilization of hydrogen energy. Metallic alloys, such as vanadium-nickel, are potential hydrogen separation materials. Due to the strong propensity of vanadium to form oxides and hydrides, vanadium alloy has a lower hydrogen permeability, and it is difficult to maintain the permeability over time. Therefore, special preparation processes such as Pd coating have been suggested for hydrogen separation vanadium-based membranes. However, aside from the prohibitive price of palladium, the interdiffusion of palladium and vanadium makes the coated membrane inviable to be used at a high temperature. Thermal treatment with inert gas was investigated in this study to assess the applicability of the vanadium alloy without palladium coating for hydrogen separation and clarify the mechanism behind the thermal treatment. Argon is inert with vanadium and displayed permeability recovery after 43 h thermal treatment, but the permeability declined under certain conditions. In contrast, nitrogen is known to interact with vanadium and the hydrogen permeability was maintained at a level lower than the test with argon. Given that nitrogen can compete with hydrogen for the active sites on vanadium, nitrogen might hinder hydrogen adsorption and hydride formation, whereas argon reduced the partial pressure of hydrogen during the thermal treatment, enhancing the driving force of hydrogen desorption. In the X-ray diffraction spectrum, vanadium hydrides and oxides were confirmed after hydrogen permeation and thermal treatment. In the X-ray photoelectron spectroscopy data, oxygen was a dominant element due to vanadium oxides and adsorbed nitrogen was also observed. According to binding energy shifts of nitrogen, nitrogen used for thermal treatment might substitute or compete for active sites with adsorbed nitrogen and hydrogen, existing in vanadium lattice. Although thermal treatment can be used to recover hydrogen permeability, the alloy cannot be recovered as hydrogen-free. However, results demonstrate the potential of thermal treatment to complement an uncoated vanadium alloy for a hydrogen separation membrane.

Study on Deuterium Permeation Behavior of Palladium Films Prepared by Magnetron Sputtering Method

Pre-depositing a Pd film is crucial for accurately acquiring the hydrogen permeability of metal materials, as it permits the production of ultra-pure hydrogen. However, the microstructure of Pd film and its effect on the hydrogen isotope permeation behavior of substrate materials have been neglected. In this study, Pd films were deposited on China Low-activation Ferritic (CLF−1) steel by magnetron sputtering. The effect of sputtering pressure on the microstructure and deuterium permeation behavior of Pd films at temperatures of 550−650 °C is presented. SEM results demonstrated that the films had a columnar crystal structure with a thickness of 0.6 ± 0.2 μm. The gas-driven permeation results revealed that the deuterium ion current intensity of the coated CLF−1 sample was at least three times lower than that of uncoated CLF−1 steel, which was influenced by the combined effect of oxygen and surface cracks. Oxygen could not be excluded from the films at a sputtering pressure of 10−3 Pa order of magnitude. It was also found that the films cracked during deuterium permeation experiments, which affected the deuterium permeation behavior. Films with large surface coverage and small grain sizes exhibited better cracking resistance. Our study provides promising insights into the hydrogen permeability of Pd films.

Experimental Determination of Hydrogen Isotope Transport Parameters in Vanadium

Deuterium permeation through vanadium membranes in a wide range of pressures and the temperature range ~250–550 °C was experimentally investigated. Measurements on the same material were carried out in three laboratories with different features for an extended characterization and for cross-check validation. A unified equation for deuterium permeability in pure vanadium (99%) was provided as Φ=1.27×10−4·e−8667/T mol m⁻¹ s⁻¹ Pa^−0.5, which represents a significant progress for the characterization of the transport properties in this material, given the spread of data, which can currently be found in the literature. Adsorption and recombination rate constants were also measured for hydrogen and deuterium at low pressure for the same range of temperatures. Finally, the influence of the surface roughness was examined by measuring samples with different surface finish.

Assessment of Sieverts Law Assumptions and 'n' Values in Palladium Membranes: Experimental and Theoretical Analyses

Palladium and palladium alloy membranes are superior materials for hydrogen purification, removal, or reaction processes. Sieverts’ Law suggests that the flux of hydrogen through such membranes is proportional to the difference between the feed and permeate side partial pressures, each raised to the 0.5 power (n = 0.5). Sieverts’ Law is widely applied in analyzing the steady state hydrogen permeation through Pd-based membranes, even in some cases where the assumptions made in deriving Sieverts’ Law do not apply. Often permeation data are fit to the model allowing the pressure exponent (n) to vary. This study experimentally assessed the validity of Sieverts’ Law as hydrogen was separated from other gases and theoretically modelled the effects of pressure and temperature on the assumptions and hence the accuracy of the 0.5-power law even with pure hydrogen feed. Hydrogen fluxes through Pd and Pd-Ag alloy foils from feed mixtures (5–83% helium in hydrogen; 473–573 K; with and without a sweep gas) were measured to study the effect of concentration polarization (CP) on hydrogen permeance and the applicability of Sieverts’ Law under such conditions. Concentration polarization was found to dominate hydrogen transport under some experimental conditions, particularly when feed concentrations of hydrogen were low. All mixture feed experiments showed deviation from Sieverts’ Law. For example, the hydrogen flux through Pd foil was found to be proportional to the partial pressure difference (n ≈ 1) rather than being proportional to the difference in the square root of the partial pressures (n = 0.5), as suggested by Sieverts’ Law, indicating the high degree of concentration polarization. A theoretical model accounting for Langmuir adsorption with temperature dependent adsorption equilibrium coefficient was made and used to assess the effect of varying feed pressure from 1–136 atm at fixed temperature, and of varying temperature from 298 to 1273 K at fixed pressure. Adsorption effects, which dominate at high pressure and at low temperature, result in pressure exponents (n) values less than 0.5. With better understanding of the transport steps, a qualitative analysis of literature (n) values of 0.5, 0.5 < n < 1, and n > 1, was conducted suggesting the role of each condition or step on the hydrogen transport based on the empirically fit exponent value.