Electrospun PVA/TiC Nanofibers for High Performance Capacitive Humidity Sensing

Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) Electrospun Nanofibers Containing Natural Deep Eutectic Solvents Exhibiting a 3D Rugose Morphology and Charge Retention Properties

In the present study, electrospun nanofibers of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV), a biodegradable polyester, containing natural deep eutectic solvents (NADES) were obtained and reported for the first time, exhibiting an unreported 3D morphology and enhanced charge retention properties. Choline chloride (ChCl)/urea/water in a molar ratio of 1:2:1 was used as the NADES model system. Electrospun nanofibers were produced from a 10 wt % solution of PHBV containing 26 wt % NADES with respect to the polymer and were deposited on different substrates, that is, aluminum foil and non-woven spunbond polypropylene (PP). The morphology and charge retention ability were characterized under different conditions and on different substrates. The attained fiber morphology for the NADES-containing mats showed an average fiber diameter of around 300 nm, whereas the pure PHBV polymer under the same conditions produced electrospun fibers of around 880 nm. However, the deposition of PHBV/ChCl/urea/water fibers resulted in a surprising macroscopic rugose 3D surface morphology made of aligned nanofibers when processed at 50% relative humidity (RH). The nanofiber grammages above which this 3D morphology, associated with NADES-induced charge retention, formed was found to be dependent on the substrate used and RH. This morphology was not seen at 20% RH nor when pure PHBV was produced. Charge stability studies revealed that PHBV/ChCl/urea/water nanofibers exhibited lasting charge retention, especially when sandwiched between spunbond polypropylene textiles. Finally, such multilayer structures containing a very thin double layer of PHBV/ChCl/urea/water fibers after corona treatment exhibited improved paraffin aerosol penetration, which was ascribed to the combination of thinner fibers and their charge retention capacity. The here-developed electrospun PHBV fibers containing NADES demonstrated for the first time a new potential application as electret filter media.

Azobenzene/Acid Binary Systems for Colorimetric Humidity Sensing with Reversibility, High Sensitivity, and Tunable Colors

Humidity sensors are important for humidity detection in many storage and manufacturing processes. Issues like sensibility, response rate, controllability, and material and preparation process costs need to be taken into consideration for practical applications. Herein, we report an investigation on a series of azobenzene/acid binary systems using easily accessible compounds, whose thin films display reversible and widely tunable color changes in response to humidity stimulation, with high sensitivity, fast color change, and recovery speed. The interesting properties for colorimetric humidity sensing are showcased with potential applications in dynamic art painting, smart windows, and respiration monitoring.

Design and Fabrication of a Fast Response Resistive-Type Humidity Sensor Using Polypyrrole (Ppy) Polymer Thin Film Structures

In this research article, an organic polymer based polypyrrole (Ppy) composite material has been synthesized and analyzed for the design and fabrication purposes of a fast-responsive, highly sensitive, and an economical resistive-type novel humidity detection sensor. This humidity sensor most suitably serves the purpose for industrial humidity (i.e., values ranging from low to high) detection applications. First, a polypyrrole composite material (a mixture of polypyrrole, polypyrrole-NiO, polypyrrole-CeO₂, and polypyrrole-Nb₂O₅) has been synthesized by chemical oxidative polymerization method, and then is treated at various temperatures, i.e., 100, 150 and 200 °C, respectively. After this treatment, the synthesized samples were then characterized by using FTIR, SEM, and DTA/TGA techniques for analyzing humidity sensing properties. The polypyrrole samples with the best morphological structure and properties were then incorporated on interdigitated electrodes. For the fabrication purposes of this thin film structure, at first a few drops of polyvinyl alcohol (PVA) were placed over interdigitated electrodes (IDE) and then the synthesized polypyrrole composite was uniformly deposited in the form of a thin film over it. The plots show that this is a good resistive-type humidity detection device for the relative humidity range of 30% to 90%. The response and recovery times of this newly fabricated humidity sensor were reported to be the same as 128 s at room temperature. Additionally, the stability and the repeatability response behavior of this Ppy sensor were verified up to five cycles of multiple repetitions. This presents an excellent stability and repeatability performance of the sensor. Furthermore, the capacitances versus humidity response and recovery properties of the designed sensor were studied too. This illustrates an excellent capacitive verses humidity response and shows a linear and an active behavior. Lastly, the experimental result proves that polypyrrole composite thin film shows a reasonable best performance up to a temperature of 100 °C.

Highly Sensitive Humidity Sensors Based on Polyethylene Oxide/CuO/Multi Walled Carbon Nanotubes Composite Nanofibers

Polymer composites are favorite materials for sensing applications due to their low cost and easy fabrication. In the current study, composite nanofibers consisting of polyethylene oxide (PEO), oxidized multi-walled carbon nanotubes (MWCNT) and copper oxide (CuO) nanoparticles with 1% and 3% of fillers (i.e., PEO–CuO–MWCNT: 1%, and PEO–CuO–MWCNT: 3%) were successfully developed through electrospinning for humidity sensing applications. The composite nanofibers were characterized by FTIR, XRD, SEM and EDX analysis. Firstly, they were loaded on an interdigitated electrode (IDE), and then the humidity sensing efficiency was investigated through a digital LCR meter (E4980) at different frequencies (100 Hz–1 MHz), as well as the percentage of relative humidity (RH). The results indicated that the composite nanofibers containing 1% and 3% MWCNT, combined with CuO in PEO polymer matrix, showed potent resistive and capacitive response along with high sensitivity to humidity at room temperature in an RH range of 30–90%. More specifically, the PEO–CuO–MWCNT: 1% nanocomposite displayed a resistive rapid response time within 3 s and a long recovery time of 22 s, while the PEO–CuO–MWCNT: 3% one exhibited 20 s and 11 s between the same RH range, respectively.