In vitro assessment of 3-T MRI issues for a bioabsorbable, coronary artery scaffold with metallic markers

Assessment of MRI safety issues for stainless steel sutures used for microtia reconstruction

INTRODUCTION

Potential magnetic resonance imaging issues for stainless steel sutures used for microtia reconstruction could be clinically significant for safety and diagnostic yield considerations. Therefore, the purpose of this investigation was to assess magnetic resonance issues (magnetic field interactions, heating, and artifacts) for different types of stainless steel sutures used for microtia reconstruction.

METHODS

Small gauge, commonly used stainless steel sutures from four different manufacturers (5/0 Steelex, Aesculap/B, Braun Medical, Inc.; Nagata 38 Gauge Microtia Wire, Bear Medical Corporation; Auricular Reco Wire, Medicon Surgical Inc.; and 5-0 B&S 35 Surgical Steel Suture, Ethicon, Inc.) were tested using standardized ex vivo techniques to assess magnetic field interactions, heating, and artifacts at 3 Tesla. Before testing, the stainless steel sutures were configured in a manner same as that for cartilage reconstruction used to treat microtia.

RESULTS

Each stainless steel suture exhibited minor magnetic field interactions at 3 Tesla (translational attraction, deflection angle <10°, and no torque). Heating associated with a whole-body averaged specific absorption rate of 2.9 W/kg was not excessive (highest temperature changes, ≤1.8 °C). Artifacts were relatively minor in relation to the size and shape of each stainless steel suture (artifact size in relation to the size and shape of each stainless steel suture extending ≤5 mm).

CONCLUSIONS

The stainless steel sutures that underwent testing do not present additional risks to patients in a 3-Tesla or less magnetic field setting (i.e., magnetic resonance conditional). Artifacts for these sutures may only be an issue within close proximity to the reconstructed ear.

In Vitro Magnetic Resonance Imaging Evaluation of Fragmented, Open-Coil, Percutaneous Peripheral Nerve Stimulation Leads

OBJECTIVE

Percutaneous peripheral nerve stimulation (PNS) is an FDA-cleared pain treatment. Occasionally, fragments of the lead (MicroLead, SPR Therapeutics, LLC, Cleveland, OH, USA) may be retained following lead removal. Since the lead is metallic, there are associated magnetic resonance imaging (MRI) risks. Therefore, the objective of this investigation was to evaluate MRI-related issues (i.e., magnetic field interactions, heating, and artifacts) for various lead fragments.

METHODS

Testing was conducted using standardized techniques on lead fragments of different lengths (i.e., 50, 75, and 100% of maximum possible fragment length of 12.7 cm) to determine MRI-related problems. Magnetic field interactions (i.e., translational attraction and torque) and artifacts were tested for the longest lead fragment at 3 Tesla. MRI-related heating was evaluated at 1.5 Tesla/64 MHz and 3 Tesla/128 MHz with each lead fragment placed in a gelled-saline filled phantom. Temperatures were recorded on the lead fragments while using relatively high RF power levels. Artifacts were evaluated using T1-weighted, spin echo, and gradient echo (GRE) pulse sequences.

RESULTS

The longest lead fragment produced only minor magnetic field interactions. For the lead fragments evaluated, physiologically inconsequential MRI-related heating occurred at 1.5 Tesla/64 MHz while under certain 3 Tesla/128 MHz conditions, excessive temperature elevations may occur. Artifacts extended approximately 7 mm from the lead fragment on the GRE pulse sequence, suggesting that anatomy located at a position greater than this distance may be visualized on MRI.

CONCLUSIONS

MRI may be performed safely in patients with retained lead fragments at 1.5 Tesla using the specific conditions of this study (i.e., MR Conditional). Due to possible excessive temperature rises at 3 Tesla, performing MRI at that field strength is currently inadvisable.

In vitro and in vivo degradation of microfiber bioresorbable coronary scaffold

The degradation of Mirage Bioresorbable Microfiber Scaffold was evaluated in vitro and in vivo. The degradation in polymer molecular weight (MW), strut morphology, and integrity was accessed using gel permeation chromatography (GPC), X‐ray micro‐computed tomography (micro‐CT) evaluation. To simulate the physiological degradation in vitro, scaffolds were deployed in silicone mock vessels connected to a peristaltic pumping system, which pumps 37°C phosphate‐buffered saline (PBS, pH 7.4) at a constant rate. At various time points (30D, 60D, 90D, 180D, 270D, and 360D), the MW of microfibers decreased to 57.3, 49.8, 36.9, 13.9, 6.4, and 5.1% against the baseline. The in vivo degradation study was performed by implanting scaffolds in internal thoracic arteries (ITAs) of mini‐swine. At the scheduled sacrifice time points (30D, 90D, 180D, 270D, 360D, and 540D), the implanted ITAs were excised for GPC analysis; the MW of the implanted scaffolds dropped to 58.5, 34.7, 24.8, 16.1, 12.9, and 7.1, respectively. Mass loss of scaffolds reached 72.4% at 540D of implantation. Two stages of hydrolysis were observed in in vitro and in vivo degradation kinetics, and the statistical analysis suggested a positive correlation between in vivo and in vitro degradation. After 6 months of incubation in animals, significant strut degradation was seen in the micro‐CT evaluation in all sections as strut fragments and separations. The micro‐CT results further confirmed that every sample at 720D had X‐ray transmission similar to surrounding tissue, thereby indicating full degradation within 2 years. © 2017 The Authors. Journal of Biomedical Materials Research Part B: Applied Biomaterials published by Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 1842–1850, 2018.

Assessment of MRI Issues at 3 Tesla for a New Metallic Tissue Marker

Purpose. To assess the MRI issues at 3 Tesla for a metallic tissue marker used to localize removal areas of tissue abnormalities. Materials and Methods. A newly designed, metallic tissue marker (Achieve Marker, CareFusion, Vernon Hills, IL) used to mark biopsy sites, particularly in breasts, was assessed for MRI issues which included standardized tests to determine magnetic field interactions (i.e., translational attraction and torque), MRI-related heating, and artifacts at 3 Tesla. Temperature changes were determined for the marker using a gelled-saline-filled phantom. MRI was performed at a relatively high specific absorption rate (whole body averaged SAR, 2.9-W/kg). MRI artifacts were evaluated using T1-weighted, spin echo and gradient echo pulse sequences. Results. The marker displayed minimal magnetic field interactions (2-degree deflection angle and no torque). MRI-related heating was only 0.1°C above background heating (i.e., the heating without the tissue marker present). Artifacts seen as localized signal loss were relatively small in relation to the size and shape of the marker. Conclusions. Based on the findings, the new metallic tissue marker is acceptable or “MR Conditional” (using current labeling terminology) for a patient undergoing an MRI procedure at 3 Tesla or less.