Preparation and in vitro bioactivity of zinc incorporating tricalium silicate

The in vivo dissolution of tricalcium silicate bone cement

This study aimed to investigate the in vivo dissolution of tricalcium silicate (Ca₃ SiO₅ , C₃ S) bone cement in the rabbit femoral defect. Results indicated that C₃ S paste directly integrated with the bone tissue without the protection of the bone-like apatite. Calcium silicate hydrate gel (C-S-H gel) and Ca(OH)₂ were the main components of C₃ S paste. The dissolution model of C₃ S paste was a mass loss rather than a decrease in volume. The initial dissolution of C₃ S paste (0 ~ 6 weeks) was greatly attributed to the release of Ca(OH)₂ , and the later dissolution (>6 weeks) was attributed to the decalcification of C-S-H gel. Although the mass of C₃ S paste could decrease by more than 19 wt % after 6 weeks of implantation, the created pores (<1 μm) were not large enough for the bone tissue to migrate into C₃ S paste. The loss of Ca ions also resulted in the transformation of SiO₄ tetrahedrons from Q¹ and Q² to Q⁰ , Q³ , and Q⁴ in C-S-H gel. Because only isolated SiO₄ tetrahedrons (Q⁰ ) and Ca ions could be absorbed by the bone tissue, C₃ S paste gradually transformed into a silica-rich gel. The fundamental reason for no decrease in volume of C₃ S paste was that the SiO₄ tetrahedron network still maintained the frame structure of C₃ S paste during the implantation.

Metal doped calcium silicate biomaterial for skin tissue regeneration in vitro

This study spots light on combined Wound healing process conjoining blood coagulation, inflammation reduction, proliferation and remodeling of the cells. The objective is to overcome the drawbacks of conventional clinically applied wound dressings such as poor rigidity, porosity, mechanical potency and bactericidal activity. As nosocomial infection is a very common condition at the wound site, bio-adhesive materials with intrinsic antibacterial properties are used in clinical applications. Considering the provenability of Wollastonite [Calcium silicate (CaSiO3)] to regenerate the soft tissues by inducing vascularization and regeneration of fibroblast cells And the antibacterial potentiality of zinc in clinical applications, the present study focuses on synthesis of Zn-Ws particles and evaluation of its antimicrobial and wound healing potentialities towards skin tissue engineering applications. The compositional characterization by EDAS and FT-IR spectral analysis have substantiated the presence of major elements and corresponding band stretching associated with the synthesized particles whereas the particles morphology by SEM images have shown the size of the Ws and Zn-Ws to be 370 nm and 530 nm respectively. From the in vitro studies, skin regenerative potential of Zn-Ws was determined on promoting fibroblast cell (NIH3T3) proliferation by providing better adhesiveness, biocompatibility and cytocompatibility. The antibacterial property of Zn-Ws evaluation by minimum inhibitory concentration (MIC) and zone of inhibition (ZOI) methods against clinical isolates of Gram +Ve and Gram -Ve bacterial strains have confirmed that the addition of Zn has diminished the bacterial growth and also helped in degrading the bacterial biofilms. Thus it is summed up that the process of wound healing is expected to occur with reduced risk of post-injury infections by the presence of zinc-doping on wollastonite for skin tissue application.