Evaluation of passive oxide layer formation–biocompatibility relationship in NiTi shape memory alloys: Geometry and body location dependency

Improving the Bioactivity and Antibiofilm Properties of Metallic Implant Materials via Controlled Surface Microdeformation

Although metallic implants provide most of the required properties for bone-related applications, especially orthopedic implants, insufficient osseointegration, which may lead to loosening of the implant or prolonged healing time, is still an issue to be resolved. Osseointegration can be improved via application of various surface treatments on the metal surface. The current study focuses on a novel surface microdeformation method, which enables the formation of controlled surface patterns of various parameters. With this purpose, a surface microdeformation procedure was applied on 316L stainless steel surfaces, forming four different patterns which affected various surface parameters such as roughness, surface energy, dislocation activities close to the surface, and wettability. Static immersion tests in a simulated body fluid (SBF) environment showed that modifying the surface parameters via controlled surface patterning promoted the formation of a stable oxide layer and calcium-phosphate (CaP) deposition on the metal surfaces, improving bioactivity. Moreover, the higher amount of CaP deposition and oxide layer formation on the modified surfaces led to reduced ion release, which contributed to improved corrosion resistance. Finally, the effect of the formed surface patterns on antibiofilm formation was investigated via incubation with C. albicans for 24 h, which exhibited that microdeformation patterns remarkably inhibited the biofilm formation. Throughout the experiments, certain patterns yielded outstanding results among the four patterns formed. Overall, it was concluded that forming controlled patterns on stainless steel surfaces via surface microdeformation significantly contributed to the metal's biocompatibility via improving bioactivity, corrosion resistance, and antibiofilm formation properties. Especially, the specific surface properties such as increased surface energy, high surface roughness, and dislocation density close to the metal surface as well as increased hydrophilicity obtained via forming the pattern with relatively deeper and narrowly spaced indents yielded the most promising outcomes. These methodologies constitute novel approaches to be used while designing new methodologies for the surface modification of metallic implant materials for improved osseointegration.

Microstructure, Mechanical Properties and Corrosion Performance of Laser-Welded NiTi Shape Memory Alloy in Simulated Body Fluid

Laser-welding is a promising technique for welding NiTi shape memory alloys with acceptable tensile strength and comparable corrosion performance for biomedical applications. The microstructural characteristics and localized corrosion behavior of NiTi alloys in a simulated body fluid (SBF) environment are evaluated. A microstructural examination indicated the presence of fine and equiaxed grains with a B2 austenite phase in the base metal (BM), while the weld metal (WM) had a coarse dendritic microstructure with intermetallic precipitates including Ti2Ni and Ni4Ti3. The hardness decreased from the BM to the WM, and the average hardness for the BM was 352 ± 5 HV, while it ranged between 275 and 307 HV and 265 and 287 HV for the HAZ and WM, respectively. Uni-axial tensile tests revealed a substantial decrease in the tensile strength of NiTi WM (481 ± 19 MPa), with a reduced joint efficiency of 34%. The localized corrosion performance of NiTi BM was superior to the WM, with electrochemical test responses indicating a pitting potential and low corrosion rate in SBF environments. The corrosion rate of the NiTi BM and WM was 0.048 ± 0.0018 mils per year (mpy) and 0.41 ± 0.019 mpy, respectively. During welding, NiTi's strength and biocompatibility properties changed due to the alteration in microstructure and formation of intermetallic phases as a result of Ti enrichment. The performance and safety of welded medical devices may be impacted during welding, and it is essential to preserve the biocompatibility of NiTi components for biomedical applications.

Effect of phytic acid on chemical, structural, and mechanical characteristics of nickel-titanium endodontic files

This study investigated phytic acid (IP6) effect on chemical, structural, and mechanical characteristics of nickel-titanium (NiTi) files. The tested files were equally divided into groups according to the immersion protocol: sodium hypochlorite (NaOCl), ethylenediaminetetraacetic acid (EDTA), IP6, EDTA followed by NaOCl, and IP6 followed by NaOCl. These groups were then compared in terms of Ni, Ti, and chromium (Cr) ions release from the files. Microstructural changes using field emission scanning electron microscope (Fe-SEM) and energy dispersive X-ray spectroscopy (EDX) and surface roughness were analyzed. The mechanical characterization was conducted using cyclic fatigue resistance test. Fractured segments were scanned under SEM. Statistical analysis was performed using one-way ANOVA, Tukey test, Kruskal-Wallis test and Mann-Whitney U test. Results showed that NaOCl caused significant release of Cr, followed by IP6 and EDTA (P < 0.05). When files were pre-immersed in EDTA, NaOCl tended to induce less release of Ti and Cr. EDX evaluation revealed that the main surface elements were Ni, Ti, carbon, and oxygen. EDTA group contained the highest amount of carbon, while the control group showed the lowest. Surface roughness evaluation revealed no significant differences between groups despite the minor increases after immersion in certain groups. Black areas were observed in the NaOCl group which indicated corrosion. However, the cyclic fatigue test showed no significant differences between the groups.

Magnetism-enhanced biomaterial Mg guide wire by MAP process for development of catheter insertion

The surface topography of implant tools has indicated an interfacial contact in degradation still being discovered; however, the glossy texture of a tiny magnesium wire is important for absorbable medical devices. This paper investigated the alterations of surface quality by a magnetic abrasive polishing method using a rotational magnetic field-assisted system with input parameters of revolution, abrasive media, magnetic pole, flux density, vibration, and amplitude that could noticeably enhance asperities along a sample. Furthermore, the blood flow simulation is used to analyze flow within blood vessels while maintaining the surface roughness conditions of the guide wire. The results are compared and discussed. Magnetic field simulation is employed to investigate the magnetic field strength in the polishing zone. Scanning Electron Microscopy (SEM) provides visual aids for recognizing the differences between pre-and post-workpieces of magnesium wire. The experimental results reveal that a wire diameter of 0.50 mm predominantly achieves surface morphology from the initial roughness of 0.22 μm to 0.05 μm. The results corroborate that the distribution of blood in the circulatory system was relatively stable. Hence, this study establishes a crucial benchmark for the precision polishing of ultra-thin magnesium wires, which is vital for their use as high-precision biodegradable medical devices.

Nickel ion release and surface analyses on instrument fragments fractured beyond the apex: a laboratory investigation

BACKGROUND

To analyse the changes in surface and nickel ion release characteristics of fractured root canal shaping instruments in a simulated body fluid environment.

METHODS

A total of 54 new instruments were studied. The instrument groups consisted of five different NiTi alloys and a stainless-steel alloy. To standardize instrument fracture, a torsional type of failure was created on each instrument. The fractured specimens of each instrument group were randomly divided into three static immersion subgroups of 1 h, 7-day, and 30-day (n = 3). Simulated body fluid (SBF) was prepared to mimic human blood plasma by Kokubo&Takadama protocol for ex situ static immersions at 37ºC. The surfaces were examined via scanning electron microscopy coupled with energy-dispersive X-ray spectroscopy. To determine the quantitative ion release, the retrieved SBFs were analyzed using inductively coupled plasma mass spectrometry. Two-way ANOVA and Tukey post hoc tests sought the statistical significance of the nickel ion values(p < 0.05).

RESULTS

In 1 h of immersion, the newly formed structures, exhibiting mostly oxygen signals, were widespread and evident on NiTi surfaces. In contrast, fewer structures were detected on the SS surface in that subgroup. In 7 days of immersion, a tendency for a decrease in the density of the new structures was revealed in NiTi groups. The oxygen signals on NiTi group surfaces significantly increased, contrary to their decrease in SS. Signals of sodium, chlorine, and calcium were detected, indicating salt precipitates in groups. In 30 days of immersion, salt precipitates continued to form. The Ni-ion release values in all instrument groups presented significant differences in comparison to the SBF control in all immersion periods(p < 0.001). No significant differences were observed in immersion time periods or instrument groups(p > 0.05).

CONCLUSIONS

Within the limitations of the presented study, it was concluded that the fractured SS and NiTi root canal instruments release Ni ions in contact with body fluid. However, the Ni ion release values determined during the observation periods are lower than the critical toxic or allergic thresholds defined for the human body. This was due to the ionic dissolution cycle reaching a stable state from 1-hour to 30-day exposure to the body fluid of fractured instruments.

Influence of Low Temperature Plasma Oxidizing on the Bioactivity of NiTi Shape Memory Alloy for Medical Applications

The present study elucidates the impact of glow discharge oxidation within a low-temperature plasma environment on the bioactivity characteristics of an NiTi shape memory alloy. The properties of the produced surface layers, such as structure (TEM observations), surface morphology (SEM observations), chemical and phase composition (EDS and XRD measurements), wettability (optical gonimeter), and the biological response of osteoblasts and platelets to the oxidized surface compared with the NiTi alloy without a surface layer are presented. The presented surface modification of the NiTi shape memory alloy, achieved through oxidizing in a low-temperature plasma environment, led to the creation of a continuous surface layer composed of nanocrystalline titanium oxide TiO2 (rutile). The findings obtained from this study provide evidence that the oxidized layer augments the bioactivity of the shape memory alloy. This augmentation was substantiated through the spontaneous biomimetic deposition of apatite from a simulated body fluid (SBF) solution. Furthermore, the modified surface exhibited improved osteoblast proliferation, and enhanced platelet adhesion and activation. This proposed surface modification strategy holds promise as a prospective solution to enhance the biocompatibility and bioactivity of NiTi shape memory alloy intended for prolonged use in bone implant applications.

In Vivo Safety of New Coating for Biodegradable Magnesium Implants

Biodegradable Magnesium (Mg) implants are promising alternatives to permanent metallic prosthesis. To improve the biocompatibility and with the aim of degradation control, we provided Plasma Electrolytic Oxidation (PEO) of pure Mg implant in silicate-based solution with NaOH (S1 250 V) and Ca(OH)2 (S2 300 V). Despite the well-structured surface, S1 250 V implants induced enormous innate immunity reaction with the prevalence of neutrophils (MPO+) and M1-macrophages (CD68+), causing secondary alteration and massive necrosis in the peri-implant area in a week. This reaction was also accompanied by systemic changes in visceral organs affecting animals' survival after seven days of the experiment. In contrast, S2 300 V implantation was associated with focal lymphohistiocytic infiltration and granulation tissue formation, defining a more favorable outcome. This reaction was associated with the prevalence of M2-macrophages (CD163+) and high density of αSMA+ myofibroblasts, implying a resolution of inflammation and effective tissue repair at the site of the implantation. At 30 days, no remnants of S2 300 V implants were found, suggesting complete resorption with minor histological changes in peri-implant tissues. In conclusion, Ca(OH)2-contained silicate-based solution allows generating biocompatible coating reducing toxicity and immunogenicity with appropriate degradation properties that make it a promising candidate for medical applications.

Self-Expandable Electrode Based on Chemically Polished Nickel-Titanium Alloy Wire for Treating Endoluminal Tumors Using Bipolar Irreversible Electroporation

The application of irreversible electroporation (IRE) to endoluminal organs is being investigated; however, the current preclinical evidence and optimized electrodes are insufficient for clinical translation. Here, a novel self-expandable electrode (SE) made of chemically polished nickel-titanium (Ni-Ti) alloy wire for endoluminal IRE is developed in this study. Chemically polished heat-treated Ni-Ti alloy wires demonstrate increased electrical conductivity, reduced carbon and oxygen levels, and good mechanical and self-expanding properties. Bipolar IRE using chemically polished Ni-Ti wires successfully induces cancer cell death. IRE-treated potato tissue shows irreversibly and reversibly electroporated areas containing dead cells in an electrical strength-dependent manner. In vivo study using an optimized electric field strength demonstrates that endobiliary IRE using the SE evenly induces well-distributed mucosal injuries in the common bile duct (CBD) with the overexpression of the TUNEL, HSP70, and inflammatory cells without ductal perforation or stricture formation. This study demonstrates the basic concept of the endobiliary IRE procedure, which is technically feasible and safe in a porcine CBD as a novel therapeutic strategy for malignant biliary obstruction. The SE is a promising electrical energy delivery platform for effectively treating endoluminal organs.

Biomaterials for bone regeneration: an orthopedic and dentistry overview

Because bone-associated diseases are increasing, a variety of tissue engineering approaches with bone regeneration purposes have been proposed over the last years. Bone tissue provides a number of important physiological and structural functions in the human body, being essential for hematopoietic maintenance and for providing support and protection of vital organs. Therefore, efforts to develop the ideal scaffold which is able to guide the bone regeneration processes is a relevant target for tissue engineering researchers. Several techniques have been used for scaffolding approaches, such as diverse types of biomaterials. On the other hand, metallic biomaterials are widely used as support devices in dentistry and orthopedics, constituting an important complement for the scaffolds. Hence, the aim of this review is to provide an overview of the degradable biomaterials and metal biomaterials proposed for bone regeneration in the orthopedic and dentistry fields in the last years.

Hybrid a-CNH+TiO2+TiN-type surface layers produced on NiTi shape memory alloy for cardiovascular applications

AIM

The goal was to improve the properties of NiTi shape memory alloy to make it suitable for cardiac applications. For this purpose, a hybrid a-CNH+TiO₂+TiN-type surface layer was produced on NiTi alloy and characterized.

MATERIALS & METHODS

The NiTi alloy subjected to hybrid process combining low-temperature oxynitriding under glow discharge conditions and radio frequency chemical vapor deposition process was examined for microstructure, surface topography, corrosion resistance, wettability and surface-free energy, Ni ion release and platelets adhesion, aggregation and activation.

RESULTS

The hybrid surface layers showed slightly increased surface roughness, better corrosion resistance, a more hydrophobic nature, decreased surface free energy, smaller release of nickel ions and reduced platelets activation.

CONCLUSION

The produced layers could expand the range of NiTi medical applications.

Differences in cytocompatibility, dynamics of the oxide layers' formation, and nickel release between superelastic and thermo-activated nickel-titanium archwires

Superelastic (SE) and thermo-activated (TA) nickel-titanium (NiTi) archwires are used in everyday orthodontic practice, based on their acceptable biocompatibility and well-defined shape memory properties. However, the differences in their surface microstructure and cytotoxicity have not been clearly defined, and the standard cytotoxicity tests are too robust to detect small differences in the cytotoxicity of these alloys, all of which can lead to unexpected adverse reactions in some patients. Therefore, we tested the hypothesis that the differences in manufacture and microstructure of commercially available SE and TA archwires may influence their biocompatibility. The archwires were studied as-received and after conditioning for 24 h or 35 days in a cell culture medium under static conditions. All of the tested archwires, including their conditioned medium (CM), were non-cytotoxic for L929 cells, but Rematitan SE (both as received and conditioned) induced the apoptosis of rat thymocytes in a direct contact. In contrast, TruFlex SE and Equire TA increased the proliferation of thymocytes. The cytotoxic effect of Rematitan SE correlated with the higher release of Ni ions in CM, higher concentration of surface Ni and an increased oxygen layer thickness after the conditioning. In conclusion, the apoptosis assay on rat thymocytes, in contrast to the less sensitive standard assay on L929 cells, revealed that Rematitan SE was less cytocompatible compared to other archwires and the effect was most probably associated with a higher exposition of the cells to Ni on the surface of the archwire, due to the formation of unstable oxide layer.

An exploration of plastic deformation dependence of cell viability and adhesion in metallic implant materials

The relationship between cell viability and adhesion behavior, and micro-deformation mechanisms was investigated on austenitic 316L stainless steel samples, which were subjected to different amounts of plastic strains (5%, 15%, 25%, 35% and 60%) to promote a variety in the slip and twin activities in the microstructure. Confocal laser scanning microscopy (CLSM) and field emission scanning electron microscopy (FESEM) revealed that cells most favored the samples with the largest plastic deformation, such that they spread more and formed significant filopodial extensions. Specifically, brain tumor cells seeded on the 35% deformed samples exhibited the best adhesion performance, where a significant slip activity was prevalent, accompanied by considerable slip-twin interactions. Furthermore, maximum viability was exhibited by the cells seeded on the 60% deformed samples, which were particularly designed in a specific geometry that could endure greater strain values. Overall, the current findings open a new venue for the production of metallic implants with enhanced biocompatibility, such that the adhesion and viability of the cells surrounding an implant can be optimized by tailoring the surface relief of the material, which is dictated by the micro-deformation mechanism activities facilitated by plastic deformation imposed by machining.

Evaluation of the biocompatibility of NiTi dental wires: a comparison of laboratory experiments and clinical conditions

Effects of intraoral environment on the surface degradation of nickel-titanium (NiTi) shape memory alloy orthodontic wires was simulated through ex situ static immersion experiments in artificial saliva. The tested wires were compared to companion wires retrieved from patients in terms of chemical changes and formation of new structures on the surface. Results of the ex situ experiments revealed that the acidic erosion effective at the earlier stages of immersion led to the formation of new structures as the immersion period approached 30 days. Moreover, comparison of these results with the analysis of wires utilized in clinical treatment evidenced that ex situ experiments are reliable in terms predicting C-rich structure formation on the wire surfaces. However, the formation of C pileups at the contact sites of arch wires and brackets could not be simulated with the aid of static immersion experiments, warranting the simulation of the intraoral environment in terms of both chemical and physical conditions, including mechanical loading, when evaluating the biocompatibility of NiTi orthodontic arch wires.