Annealing of drawn monofilaments of liquid crystalline polymer vectra/vapor grown carbon fiber nanocomposites

Mechanical Properties of 3D-Printed Liquid Crystalline Polymers with Low and High Melting Temperatures

Additive manufacturing allows for the production of complex components using various types of materials such as plastics, metals and ceramics without the need for molding tools. In the field of high-performance polymers, semi-crystalline polymers such as polyetheretherketone (PEEK) or amorphous polymers such as polyetherimide (PEI) are already successfully applied. Contrary to semi-crystalline and amorphous polymers, thermotropic liquid crystalline polymers (LCPs) do not change into an isotropic liquid during melting. Instead, they possess anisotropic properties in their liquid phase. Within the scope of this work, this special group of polymers was investigated with regard to its suitability for processing by means of fused filament fabrication. Using an LCP with a low melting temperature of around 280 °C is compared to processing an LCP that exhibits a high melting temperature around 330 °C. In doing so, it was revealed that the achievable mechanical properties strongly depend on the process parameters such as the direction of deposition, printing temperature, printing speed and layer height. At a layer height of 0.10 mm, a Young's modulus of 27.3 GPa was achieved. Moreover, by employing an annealing step after the printing process, the tensile strength could be increased up to 406 MPa at a layer height of 0.15 mm. Regarding the general suitability for FFF as well as the achieved uniaxial mechanical properties, the LCP with a low melting temperature was advantageous compared to the LCP with a high melting temperature.

Enhanced Thermal Conductivities of Liquid Crystal Polyesters from Controlled Structure of Molecular Chains by Introducing Different Dicarboxylic Acid Monomers

Enhancing thermal conductivity coefficient (λ) of liquid crystal polyesters would further widen their application in electronics and electricals. In this work, a kind of biphenyl-based dihydroxy monomer is synthesized using 4, 4'-biphenyl (BP) and triethylene glycol (TEG) as raw material, which further reacts with three different dicarboxylic acids (succinic acid, p-phenylenediacetic acid, and terephthalic acid, respectively) by melt polycondensation to prepare intrinsically highly thermally conductive poly 4', 4”'-[1, 2-ethanediyl-bis(oxy-2, 1-ethanediyloxy)]-bis(p-hydroxybiphenyl) succinate (PEOS), poly 4', 4”'-[1, 2-ethanediyl-bis(oxy-2, 1-ethanediyloxy)]-bis(p-hydroxybiphenyl) p-phenyldiacetate (PEOP) and poly 4', 4”'-[1, 2-ethanediyl-bis(oxy-2, 1-ethanediyloxy)]-bis(p-hydroxybiphenyl) terephthalate (PEOT), collectively called biphenyl-based liquid crystal polyesters (B-LCPE). The results show that B-LCPE possess the desired molecular structure, exhibit smectic phase in liquid crystal range and semicrystalline polymers at room temperature, and possess excellent intrinsic thermal conductivities, thermal stabilities, and mechanical properties. λ of PEOT is 0.51 W/(m·K), significantly exceeds that of polyethylene terephthalate (0.15 W/(m·K)) which has similar molecular structure with PEOT, and also higher than that of PEOS (0.32 W/(m·K)) and PEOP (0.38 W/(m·K)). The corresponding heat resistance index (T_HRI), elasticity modulus, and hardness of PEOT are 174.6°C, 3.6 GPa, and 154.5 MPa, respectively, and also higher than those of PEOS (162.2°C, 1.8 GPa, and 83.4 MPa) and PEOP (171.8°C, 2.3 GPa, and 149.6 MPa).