Design of trimodal Fe micro-nanopowder feedstock for micro powder injection molding

Debinding of Yttria-Stabilised Zirconia/Bimodal Stainless Steel 316L Bi-Materials Produced through Two-Component Micro-Powder Injection Moulding

The fabrication of bi-material micro-components via two-component micro-powder injection moulding (2C-µPIM) from 3 mol% yttria-stabilised zirconia (3YSZ) and micro/nano bimodal stainless steel 316L (SS 316L) powders has received insufficient attention. Apart from this, retaining the bonding between ceramic and metal at different processing stages of 2C-µPIM is challenging. This study investigated the solvent and thermal debinding mechanisms of green bi-material micro-parts of 3YSZ and bimodal SS 316L without collapsing the ceramic/metal joining. In this research, feedstocks were prepared by integrating the powders individually with palm stearin and low-density polyethylene binders. The results demonstrated that during the solvent debinding process, the palm stearin removal rate in the bi-materials composed of 3YSZ and bimodally configured SS 316L feedstocks intensified with an increase in temperature. The establishment of interconnected pores in the solvent-debound components facilitated the thermal debinding process, which removed 99% of the binder system. Following sintering, the debound bi-materials exhibited a relative density of 95.3%. According to a study of the microstructures using field emission scanning electron microscopy, an adequate bond between 3YSZ and bimodal SS 316L was established in the micro-part after sintering. The bi-material sintered at 1350 °C had the highest hardness of 1017.4 HV along the joining region.

Study of solid loading of feedstock using trimodal iron powders for extrusion based additive manufacturing

Volume loading of feedstock using trimodal iron (Fe) powders was investigated for the application of extrusion-based additive manufacturing (AM). Fe trimodal powder composed of nano, sub-nano, and micro particles was manufactured via the powder metallurgy process where small particles behave as rolling bearings among large particles, and thereby improving the flow characteristics of feedstock by minimizing friction among the particles. The flow behavior and microstructures of the monomodal feedstock were compared with those of the trimodal feedstock. We have confirmed that the critical powder loading of monomodal powder was measured to be 70 vol.% while trimodal powder showed up to 74 vol.%. Furthermore, trimodal feedstocks of 60, 65, 70, 75, and 80 vol.% Fe powder were prepared to determine the optimal powder content for sintering. As a result, the feedstock with powder content of 70 vol.% gave the highest sintered density of 92.32%, the highest Vickers hardness of 80.67 HV, with the smallest dimensional variation in shrinkage, proposing 70 vol.% of trimodal feedstock to be the suitable powder content for AM. Finally, its microstructural and mechanical comparison with 70 vol.% sintered part using monomodal Fe powder, showed that the sintered part using trimodal feedstock displayed higher hardness, uniform shrinkage as well as smaller grain size, confirming trimodal feedstock to be favorable for the application of extrusion-based AM.