Flame Retardant Properties of Polyurethane/Expandable Praphite Composites

Enhancing Char Formation and Flame Retardancy of Ethylene-Vinyl Acetate Copolymer (EVA)/Aluminum Hydroxide (ATH) Composites by Grafting Ladder Phenyl/Vinyl Polysilsesquioxane (PhVPOSS)

The ladder phenyl/vinyl polysilsesquioxane (PhVPOSS) was used to improve the flame-retardancy performances of ethylene-vinyl acetate copolymer (EVA)/aluminum hydroxide (ATH) composites due to the reactivity of its vinyl groups. FTIR, XPS, 1H NMR, and SEM-EDS data demonstrated the PhVPOSS grafting onto EVA molecular chains. The PhVPOSS improved the thermal stability of EVA/ATH composites, as shown by the thermogravimetric analysis (TGA). Furthermore, with the cone calorimeter (CONE) experiments, EVA/ATH/PhVPOSS showed better fire safety than the EVA/ATH composites, with the PHRR, PSPR, and PCOP reduced by 7.89%, 57.4%, and 90.9%, respectively. The mechanism investigations of flame retardancy revealed that the charring behaviors of the EVA/ATH/PhVPOSS composites were improved by the formation of Si-C bonds and Si-O bonds, and a more compact and denser char layer can contribute more to the barrier effect.

Influence of the Characteristics of Expandable Graphite on the Morphology, Thermal Properties, Fire Behaviour and Compression Performance of a Rigid Polyurethane Foam

Three types of expandable graphite (EG) differing in particle size and expansion volume, are compared as flame retardant additives to rigid polyurethane foams (RPUFs). In this paper we discuss microstructure, thermal stability, fire behavior, and compression performance. We find that ell size distributions were less homogeneous and cell size was reduced. Furthermore, thermal conductivity increased along with EG loading. Thermogravimetric analysis (TGA) showed that EG only increased residue yield differently. The results indicate that a higher expansion of EG increased the limiting oxygen index (LOI) value, whereas a bigger particle size EG improved the rating of the vertical burning test (UL94). Results from the cone calorimeter test showed that a bigger particle size EG effectively reduced peak of heat release rate (pHRR). Furthermore, a higher expansion, led to a decrease in smoke production (TSP). The combination of both characteristics gives extraordinary results. The physical–mechanical characterization of the EG/RPUF foams revealed that their compression performance decreased slightly, mostly due to the effect of a bigger size EG.

Preparation and Flame Retardance of Polyurethane Composites Containing Microencapsulated Melamine Polyphosphate

A new microencapsulated flame retardant containing melamine polyphosphate (MPP) and 4,4'-oxydianiline-formaldehyde (OF) resin as the core and shell materials, respectively, was synthesized by in situ polymerization. ²⁹Si NMR was used to measure the condensation density of polyurethane containing silicon compound (Si-PU). The structures and properties of the microencapsulated melamine polyphosphate (OFMPP) were characterized using X-ray photoelectron spectroscopy, scanning electron microscopy and water solubility. Thermal behavior of the OFMPP was systematically analyzed through thermogravimetric analysis. Flame retardance tests such as the limiting oxygen index and UL-94 were employed to evaluate the effect of composition variation on the MPP and OFMPP in polyurethane composites. The results indicated that the microencapsulation of MPP with the OF resin improved hydrophobicity and that the flame retardance of the Si-PU/OFMPP composite (limiting oxygen index, LOI = 32%) was higher than that of the Si-PU/MPP composite (LOI = 27%) at the same additive loading (30 wt %).

The synergism between melamine and expandable graphite on improving the flame retardancy of polyamide 11

Expandable graphite (EG) has attracted more and more attention in fire science society due to its excellent char-forming ability, however, it cannot meet commercial flame-retardant requirements because of the low intensity of the char. This work reported our very recent efforts on improving the char quality of EG by introducing melamine (MEL) in order to enhance the fire resistance and thermal stability of polyamide 11 (PA 11) composite. The flammability characterized by limiting oxygen index, UL-94 vertical burning, and cone calorimeter (cone) tests shows that the presence of both EG and MEL can significantly improve the flame retardancy and thermal stability of PA 11 composites. The scanning electron microscopic analysis shows that EG and MEL are beneficial to form compact char layers that can isolate the matrix from heat and oxygen. It is proposed that the formation of hydrogen bonds between MEL and PA 11 are crucial for improving the flame retardancy of the composites.

Recent studies on the decomposition and strategies of smoke and toxicity suppression for polyurethane based materials

This review provides insight into recent studies related to thermal degradation, smoke and toxicity production and their reduction strategies for polyurethane-based materials.