The effect of chemical surface treatments of different denture base resins on the shear bond strength of denture repair

Effect of mechanical and chemical surface treatments on the repairing of milled and 3D-printed denture bases

Ensuring a strong bond between chairside autopolymerized acrylic resin to denture base is essential for denture repair and reline procedures. However, there is no established protocol to enhance bond strength between autopolymerizing resin and computer-aided design and computer-aided manufacturing (CAD-CAM) denture base materials. The purpose of this study was to determine shear bond strength of CAD-CAM denture bases and autopolymerizing acrylic resin after mechanical and chemical surface treatments compared with heat-polymerized acrylic resin. Heat-polymerized, milled, and 3-dimensional (3D) printed denture bases were divided into 4 surface treatment protocols: none (control), airborne-particle abrasion (APA), tetrahydrofuran, and Vitacoll application. Autopolymerizing acrylic resin cylinders were bonded to denture surface. Shear bond strength and failure modes were determined after thermocycling. Denture base surfaces were assessed for surface roughness, surface morphology, and microhardness before and after surface treatment. Data was analyzed using two-way ANOVA and multiple comparison tests. The results showed that APA significantly increased shear bond strength and surface roughness of all denture base materials. Tetrahydrofuran and Vitacoll application improved shear bond strength of heat-polymerized acrylic resin, but did not reach the level achieved by APA. Conversely, tetrahydrofuran application improved bond strength of 3D-printed denture to the level of APA. Tetrahydrofuran and Vitacoll application significantly reduced denture base hardness, compared with control and APA. In conclusion, mechanical surface treatment using APA enhances the adhesion of autopolymerizing acrylic resin to heat-polymerized and CAD-CAM denture bases. Tetrahydrofuran and Vitacoll chemical surface treatment improved adhesion to heat-polymerized acrylic resin, with only tetrahydrofuran enhancing bond strength of 3D-printed denture to the level of APA. Without surface treatment, the highest bond strength was shown in 3D-printed denture base material.

Efficient Digital Workflow to Replace a Missing Denture Tooth for Complete Denture Repair

Debonded denture teeth is a common complication on a fixed or removable dental prosthesis when denture teeth are fabricated separately from the denture base and bonded together. Missing denture teeth can alter a person's appearance, speech, or ability to eat. Traditionally, denture teeth repair can be a challenge for clinicians or dental laboratory technicians to find the identical tooth mould to meet esthetic and functional demands. This case report describes a digital workflow to scan, design, and mill a well-fitting and esthetic denture tooth to expedite treatment, improve patient satisfaction, and increase troop readiness when traditional methods may not be feasible.

Effect of Different Surface Treatments as Methods of Improving the Mechanical Properties after Repairs of PMMA for Dentures

Denture fractures are a common problem in dental practice, and their repair is considered a first option to restore their functional properties. However, the inter-material resistance may become compromised. Typically, the bond between these materials weakens. Therefore, various surface treatment methods may be considered to enhance their mechanical properties. Poly(methyl methacrylate) (PMMA) heat-polymerized resin (HPR) was used as the repaired material, cold-polymerized material (CPR) for the repairs, and different variants of alumina abrasive blasting (AB), methyl methacrylate (M), ethyl acetate (EA), methylene chloride (CH), and isopropyl alcohol (IA) treatments were applied. Finally, combined surface treatments were chosen and analyzed. Surface morphologies after treatments were observed by scanning electron microscopy and the flexural, shear, and impact strengths were tested. AB and chemical treatment with CH, M, and EA was used to improve all mechanical properties, and further improvement of the properties could be achieved by combining both types of treatments. Varied changes in surface morphologies were observed. Treatment with IA yielded less favorable results due to the low impact strength. The best results were achieved for the combination of AB and CH, but during the application of CH it was necessary to strictly control the exposure time.

Effect of various surface treatment methods on shear bond strength between acrylic denture teeth and thermoplastic nylon denture base

PURPOSE

To evaluate the effect of mechanical, chemical, and mechanical-chemical surface treatment methods on shear bond strength between acrylic denture teeth and thermoplastic nylon denture base.

MATERIALS AND METHODS

Maxillary central incisor teeth were treated with five different surface treatment methods: mechanical (sandblasting, T-shape diatoric holes), chemical (5% acetic acid solution, bonding agent), and mechanical-chemical (sandblasting + bonding agent) were embedded in thermoplastic nylon denture base (n = 10). A universal testing machine with a crosshead speed of 0.5 mm per minute was used to test the shear bond strength. Data obtained were statistically evaluated using one-way ANOVA and followed with Tukey post hoc test (α = 0.05) RESULTS: T-shaped diatoric holes exhibited significantly higher shear bond strength among the surface treatment groups, followed by sandblasting + bonding agent, sandblasting, bonding agent, and the acetic acid group (p < 0.001) CONCLUSION: T-shaped diatoric holes as a mechanical surface treatment showed higher shear bond strength than other methods.

Evaluation of the Bond Strength of Acrylic Teeth to Denture Base after Various Chemical Surface Treatments: An In Vitro Study

AIM

The purpose of the present study was to assess the bonding capacity and efficacy of acrylic teeth to denture bases following two different chemical surface treatments.

MATERIALS AND METHODS

A two-metal mold measuring 35 mm in length and 12 mm in diameter was created specifically for the investigation in order to standardize the wax pattern-based tooth attachment at 45°. Following standard protocol, 75 wax cylinder specimens were flasked, dewaxed, and surface treatment of teeth was done as follows with 25 samples in each group-group I: control group, group II: monomethyl methacrylate monomer group, group III: acetone group. The curing process was completed following the packing of the denture base material. The samples' shear bond strength was assessed using a universal testing machine. Every sample was taken out when it fractured, and the shear load (Newton, N) was noted. The significance of the variation in applied shear load was assessed using one-way analysis of variance (ANOVA) and post hoc ANOVA Tukey's honestly significant difference (HSD) test at the 5% level of significance.

RESULTS

The maximum shear bond strength was found in the samples treated with acetone (183.21 ± 0.06) followed by samples treated with monomethyl methacrylate monomer (171.64 ± 0.12) and the control group (149.32 ± 0.04). A statistically significant difference was found between the different groups (p < 0.001).

CONCLUSION

In conclusion, according to the current study's findings, acetone chemical surface treatment of acrylic teeth produced the strongest bond when compared with the control group and monomethyl methacrylate monomer.

CLINICAL SIGNIFICANCE

In prosthodontic practice, artificial teeth regularly de-bond and separate from the denture base. A weak interface is produced when certain clinical conditions, such as ridge prominence, cause excessive cutting of the acrylic teeth and base. Where the denture base polymer meets the teeth's highly cross-linked matrix, it de-bonds adhesively. Therefore, the bonding between the acrylic teeth and the denture base material can be improved by the chemical surface treatment. How to cite this article: Chaudhuri NG, Lahiri B, Francis NT, et al. Evaluation of the Bond Strength of Acrylic Teeth to Denture Base after Various Chemical Surface Treatments: An In Vitro Study. J Contemp Dent Pract 2024;25(6):514-517.

Effect of various surface treatments on relining bond strength of CAD-CAM denture base materials

PURPOSE

The aim of this study was to analyze the impact of various surface treatments and production methods on the shear bond strength (SBS) between reline material and denture base resins.

MATERIALS AND METHODS

One-hundred-twenty specimens were produced using conventional heat-polymerization, subtractive, and additive techniques. Each group consisted of 40 specimens. The specimens were divided into four subgroups, each with 10 samples, for surface treatments. These subgroups were: (1) Control-only monomer application, (2) 50 μm airborne-particle abrasion, (3) 110 μm airborne-particle abrasion, and (4) Roughening with tungsten carbide bur. Representative specimens from each subgroup were examined under SEM. Then, auto-polymerized resin was condensed in the center of the specimens. Specimens were subjected to thermal aging (5000 cycles at 5-55°C). The SBS test was conducted and failure loads were recorded. The data were evaluated by two-way ANOVA and Tukey pairwise multiple comparisons method (p < 0.05).

RESULTS

The additively produced group showed significantly lower SBS than conventional and subtractive groups (p < 0.001), with no significant differences between the subtractive and conventional groups. Specimens that underwent monomer application only showed the lowest SBS among surface treatments, while 50 μm airborne-particle abrasion showed the highest SBS. Based on the partial eta-squared analysis results, the surface treatment mainly impacted SBS.

CONCLUSIONS

Among the surface treatment methods, treating denture bases with 50 μm airborne-particle abrasion is more effective for maintaining adhesion, especially in the additive technique.

Effect of repair and surface treatments on the strength of digitally fabricated resin-based dental prostheses: A systematic review of in vitro studies

OBJECTIVE

This review investigated the current literature pertaining to the repairability of computer-aided design-computer-aided manufacturing (CAD-CAM) milled and three-dimensional (3D) printed resin-based dental prostheses (RBDPs) as well as the appropriate surface treatment for each repair material that will produce adequate repair bond strength.

DATA/SOURCES

PubMed, Web of Science, and Scopus databases were searched for published articles involving repair of CAD-CAM RBDPs between January 2010 and June 2023. Data were collected and analyzed to reveal the surface treatment effects, suggested repair materials, and strength of repaired RBDPs.

STUDY SELECTION

Out of 164 retrieved titles, 11 studies were included, of which five investigated the repair of 3D-printed RBDPs, three investigated the repair of CAD-CAM milled resins, and three investigated both materials. Additionally, of the included studies, seven investigated denture base resins, three studied provisional restoration resins, and one evaluated 3D-printed intraoral splints. Various surface treatments were suggested, with air-abrasive methods being the most commonly used. Different materials for resin repair were proposed and used, including auto-polymerized, reline, and composite resins. For 3D-printed resins, repair with Bis-acrylic/Bis-GMA composites improved repair strength.

CONCLUSION

Surface treatments positively affected the repair strength of conventional and milled RBDPs. However, challenges remain relevant to the repair of 3D-printed resins owing to composition mismatches and fabrication techniques. Therefore, further investigation is required to develop new 3D-printed resins.

CLINICAL SIGNIFICANCE

CAD-CAM milled resins have satisfactory repair strength, which increases with surface treatment. The repair of 3D-printed resins has proven challenging even with surface treatments. However, composite resins are the materials of choice.

Influence of hydrothermal aging on the shear bond strength of 3D printed denture-base resin to different relining materials

OBJECTIVES

This study evaluated the repairability of three-dimensional printed (3DP) denture bases based on different conventional relining materials and aging.

MATERIAL AND METHODS

The groups for surface characterization (surface-roughness and contact-angle measurements) were divided based on the denture base and surface treatment. Shear bond strength test and failure-mode analysis were conducted by a combination of three variables: denture base, relining materials, and hydrothermal aging (HA). The initial characterization involved quantifying the surface roughness (n = 10) and contact angle (n = 10) of denture base specimens with and without sandblasting (SB) treatment. Four relining materials (Kooliner [K], Vertex Self-Curing [V], Tokuyama Rebase II (Normal) [T], and Ufi Gel Hard [U]) were applied to 3DP, heat-cured (HC), and self-cured (SC) denture-base resin specimens. Shear bond strength (n = 15) and failure-mode analyses (n = 15) were performed before and after HA, along with evaluations of the fractured surfaces (n = 4). Statistical analyses were performed using a two-way analysis of variance (ANOVA) for surface characterization, and a three-way ANOVA was conducted for shear bond strength.

RESULTS

The surface roughness peaked in HC groups and increased after SB. The 3DP group displayed significantly lower contact angles, which increased after treatment, similar to the surface roughness. The shear bond strength was significantly lower for 3DP and HC denture bases than for SC denture bases, and peaked for U at 10.65 ± 1.88 MPa (mean ± SD). HA decreased the shear bond strength relative to untreated samples. Furthermore, 3DP, HC, and SC mainly showed mixed or cohesive failures with V, T, and U. K, on the other hand, trended toward adhesive failures when bonded with HC and SC.

CONCLUSION

This study has validated the repairability of 3DP dentures through relining them with common materials used in clinical practice. The repairability of the 3DP denture base was on par with that of conventional materials, but it decreased after aging. Notably, U, which had a postadhesive application, proved to be the most effective material for repairing 3DP dentures.

Bond strength between denture lining material and CAD-CAM denture base resin: A systematic review and meta-analysis

STATEMENT OF PROBLEM

An effective bond between a denture lining material and the denture base resin is necessary for proper function. Regarding the new technologies for manufacturing denture bases, a systematic search of the literature on this topic is lacking.

PURPOSE

The purpose of this systematic review and meta-analysis was to evaluate the bond strength between denture lining material and computer-aided design and computer-aided manufacturing (CAD-CAM) denture base resin (milled and 3-dimensionally printed) versus conventional denture base resin.

MATERIAL AND METHODS

Electronic databases (PubMed/MEDLINE, Scopus, and Web of Science) were independently searched by 4 researchers for relevant studies published up to April 2023. The population, intervention, comparison, and outcome (PICO) question was: "Comparing conventional and CAD-CAM (milled and 3-dimensionally printed) denture base materials, which promote greater bond strength when associated with denture lining material?" A meta-analysis was performed based on mean ±standard deviation bond strength values between denture base resins and denture lining material with 95% confidence intervals.

RESULTS

Five in vitro studies were included. For bond strength, no difference was noted between conventional and milled denture base resin (confidence interval: -0.99 [-2.17 to 0.20]; heterogeneity: t2=0.57; Chi2:4.57; I2=78%; P=.10), and conventional resin had better values compared with those of 3-dimensionally (3D) printed (confidence interval: 3.03 [2.40-3.66]; heterogeneity: t2=0.00; Chi2:0.56; I2=0%; P<.001) when relined with soft materials. The milled denture base resin was better than the conventional (confidence interval: -0.85 [-1.33 to -0.38]; heterogeneity: Chi2:28.87; I2=93%; P<.001), with no difference between 3D printed and conventional (confidence interval: 0.18 [-4.23 to 4.59]; heterogeneity: t2=16.51; Chi2:130.99; I2=98%; P=.94) for hard liners.

CONCLUSIONS

The bond strength between resins for milled CAD-CAM denture bases and denture lining material was similar to that of conventional denture base resin, regardless of the consistency of the denture lining material. The bond strength to 3D printed CAD-CAM resin was lower than that of the milled version.

The effects of different surface treatments applied to milled PMMA denture base material on repair bond strength

The high cost of CAD/CAM systems and materials is a severe economic burden. Therefore, repair of CAD/CAM PMMA, selecting appropriate repair materials, and surface modifications are clinically important. This study aims to evaluate the shear bond strength of PMMA repair materials after various surface treatments on CAD/CAM PMMA denture base material. For this purpose, a total of 480 CAD/CAM PMMA denture base test specimens were manufactured. Then all test specimens were divided into 6 groups, and different surface treatments were applied. Group A: sandblasting, Group B: 4% hydro fluoric acid, Group C: tungsten carbide bur, Group D: dichloromethane + methyl methacrylate mixture, Group E: dichloromethane and methyl methacrylate, Group F: no surface treatment. Each group is then divided into 4 different subcategories; repair processes were performed using; heat-cured acrylic resin (n:20), auto-polymerized acrylic resin (n:20), gingiva composite (n:20), and CAD/CAM PMMA tooth material (n:20). After repairs, thermal aging was applied to half of the test specimens in each subcategory. The shear bond strength value was measured with a universal test device. Sandblasting group showed the highest surface roughness value in all test specimens (p < 0.001). Heat-cured acrylic resin with sandblasting exhibited the highest bond strength, while the untreated gingiva composite resin exhibited the lowest value. Thermal aging decreased bond strength in all repair materials (p < 0.001). Among the surface treatment groups, sandblasting with Al2O3 particles exhibited the highest surface roughness value and repair bond strength. The application of organic solvents to the surface increased the surface roughness and repair bond strength. Applying dichloromethane and methyl methacrylate monomer separately is more effective than applying it as a mixture. The ideal bonding among repair materials was obtained with heat-cured acrylic resin.

CAD-CAM complete denture resins: Effect of relining on the shear bond strength

OBJECTIVES

The aim of this study was to compare the shear bond strength of relined CAD-CAM complete removable dental prosthesis (CRDP) resins with conventional heat-polymerized polymethylmethacrylate (PMMA) resin.

METHODS

A total of 96 resin specimens in identical dimensions of 10 mm × 10 mm × 11 mm were fabricated for four study groups [#1- Conventional heat-polymerized group: n=24 (ProBase); #2- Milled#1: n=24 (Ivobase); #3- Milled#2: n=24 (Ivotion); #4- 3D-printed: n=24, (NextDent Denture 3D+)]. Twelve specimens in each group were sectioned in the middle to produce a 3 mm defect and then were relined using a conventional denture relining material. All specimens underwent thermocycling (5-55°C) for 10,000 cycles. The shear bond tests were carried out in a universal testing machine. One-way ANOVA and Tukey's test were used for statistical analysis (p<0.05). The two-parameter Weibull distribution values were calculated.

RESULTS

Relined 3D-printed specimens had a significantly lower shear bond strength when compared with conventional (p=0.0003) and milled groups (Milled#1: p=0.0004; Milled#2: p<0.0001). There were no differences in the shear bond strengths between the milled and conventional groups. Weibull distribution presented the highest shape value for the non-relined Milled#1 (22.83) group and the lowest values for the 3D-printed relined group (4.001).

CONCLUSION

The findings of this study conclude that the shear bond strength of the conventionally-relined 3D-printed resins used for fabricating CRDPs was inferior to the shear bond strength of conventionally-relined resins employed for manufacturing CRDPs using CAD-CAM milling and conventional heat-polymerization techniques.

CLINICAL SIGNIFICANCE

When considering 3D-printing for the fabrication of CRDPs, it is recommended to employ it in clinical situations where a frequent need for denture relining is not expected.

Repair Bond Strength of Conventionally and Digitally Fabricated Denture Base Resins to Auto-Polymerized Acrylic Resin: Surface Treatment Effects In Vitro

Denture base fracture is one of the most annoying problems for both prosthodontists and patients. Denture repair is considered to be an appropriate solution rather than fabricating a new denture. Digital denture fabrication is widely spreading nowadays. However, the repair strength of CAD-CAM milled and 3D-printed resins is lacking. This study aimed to evaluate the effect of surface treatment on the shear bond strength (SBS) of conventionally and digitally fabricated denture base resins. One l heat-polymerized (Major base20), two milled (IvoCad, AvaDent), and three 3D-printed (ASIGA, NextDent, FormLabs) denture base resins were used to fabricate 10 × 10 × 3.3 acrylic specimens (N = 180, 30/resin, n = 10). Specimens were divided into three groups according to surface treatment; no treatment (control), monomer application (MMA), or sandblasting (SB) surface treatments were performed. Repair resin was bonded to the resin surface followed by thermocycling (5000 cycles). SBS was tested using a universal testing machine where a load was applied at the resin interface (0.5 mm/min). Data were collected and analyzed using ANOVA and a post hoc Tukey test (α = 0.05). SEM was used for failure type and topography of fractured surfaces analysis. The heat-polymerized and CAD-CAM milled groups showed close SBS values without significance (p > 0.05), while the 3D-printed resin groups showed a significant decrease in SBS (p < 0.0001). SBS increased significantly with monomer application (p < 0.0001) except for the ASIGA and NextDent groups, which showed no significant difference compared to the control groups (p > 0.05). All materials with SB surface treatment showed a significant increase in SBS when compared with the controls and MMA application (p < 0.0001). Adhesive failure type was observed in the control groups, which dramatically changed to cohesive or mixed in groups with surface treatment. The SBS of 3D-printed resin was decreased when compared with the conventional and CAD-CAM milled resin. Regardless of the material type, SB and MMA applications increased the SBS of the repaired resin and SB showed high performance.

Mechanical Properties Evaluation of Three Different Materials for Implant Supported Overdenture: An In-Vitro Study

Aim: the aim of this study was to compare the flexural strength and elastic modulus of three-dimensionally (3D) printed, conventional heat-cured, and high-impact implant-supported overdenture materials specimens. Materials and Methods: Thirty implant-supported overdenture materials specimens (bar-shaped, 65.0 × 10.2 × 5.1 ± 0.2 mm3) with one central hole were fabricated using 3D-printed, heat-cured conventional, and high-impact denture base resins (n = 10/group). Autopolymerizing acrylic resin was used to attach titanium matrix housings to the central holes of the specimens. A three-point bending test was conducted using a universal testing machine and a model analog with a crosshead speed of 5 mm/min. The indicative flexural strength and elastic modulus were recorded. Data were statistically analyzed using analysis of variance (ANOVA) and the Tukey tests at α = 0.05. Results: One-way ANOVA revealed a significant effect of denture base material on the flexural strength (p < 0.001) but not on the elastic modulus (p = 0.451) of the evaluated materials. The flexural strength of the 3D-printed specimens (95.99 ± 9.87 MPa) was significantly higher than the conventional (77.18 ± 9.69 MPa; p < 0.001) and high-impact ones (82.74 ± 7.73 MPa; p = 0.002). Conclusions: The maximum flexural strength was observed in the 3D-printed implant-supported overdenture material specimens, which might indicate their suitability as an alternative to the conventionally fabricated ones. Flexural strength and elastic modulus of conventional and high-impact heat-cured implant-supported overdenture materials specimens were comparable.

Effect of surface treatment on shear bond strength of relining material and 3D-printed denture base

PURPOSE

This study aimed to analyze the shear bond strength between the 3D-printed denture base and the chairside relining material, according to the surface treatment.

MATERIALS AND METHODS

Cylindrical specimens were prepared using DENTCA Denture Base II. The experimental groups were divided into 6 (n = 10): no surface treatment (C), Tokuyama Rebase II Normal adhesive (A), sandblasting (P), sandblasting and adhesive (PA), sandblasting and silane (PS), and the Rocatec system (PPS). After bonding the chairside relining material to the center of the specimens in a cylindrical shape, they were stored in distilled water for 24 hours. Shear bond strength was measured using a universal testing machine, and failure mode was analyzed with a scanning electron microscope. Shear bond strength values were analyzed using one-way analysis of variance, and Tukey’s honest significant difference test was used for post-hoc analysis (P < .05).

RESULTS

Group PPS exhibited significantly higher shear bond strength than all other groups. Groups P and PA displayed significantly higher bond strengths than the control group. There were no significant differences between groups PS and A compared to the control group. Regarding the failure mode, adhesive failure occurred primarily in groups C and A, and mixed failure mainly in groups P, PA, PS, and PPS.

CONCLUSION

The shear bond strength between the 3D-printed denture base and the chairside relining material exhibited significant differences according to the surface treatment methods. It is believed that excellent adhesive strength will be obtained when the Rocatec system is applied to 3D-printed dentures in clinical practice.

Comparative Effect of Different Surface Treatments on the Shear Bond Strength of Two Types of Artificial Teeth Bonded To Two Types of Denture Base Resins

PURPOSE

This in vitro study aims to assess the impact of various surface treatments on the shear bond strength (SBS) of two types of artificial teeth and denture base resins (DBRs).

MATERIALS AND METHODS

Two types of DBRs (CAD/CAM-milled and heat-polymerized) and two types of denture teeth (acrylic and composite) were investigated. Teeth were cut into slices (5 × 5 × 2 mm) and divided according to surface treatment into four subgroups (n = 10): no treatment (control), air abrasion (Alumina-blasting; AB), bur roughening, and dichloromethane (DCM) subgroups. According to manufacturer recommendations, the treated tooth slices were bonded to the acrylic disk of DBRs. The SBS test was performed using a universal testing machine. ANOVA was used for results analysis followed by Tukey's post hoc tests (α = 0.05).

RESULTS

DCM and AB increased the SBS of acrylic teeth to heat-polymerized DBR compared with other groups (p < 0.001). All surface treatments showed no significant difference in CAD/CAM DBR with acrylic teeth (p = 0.059; AB, p = 0.319; bur roughening, p = 0.895; DCM), while there was a significant decrease in SBS with composite teeth (p ˂ 0.001). Between teeth, acrylic teeth showed a statistically significant increase in SBS compared to composite teeth (p < 0.001).

CONCLUSION

AB and DCM application improved the SBS for acrylic teeth with the heat-polymerized DBR when compared with the untreated group, but none of the surface treatment agents showed significant improvement with CAD/CAM DBR. All surface treatment agents reduced the SBS for composite teeth with CAD/CAM DBR while AB only increased the SBS with heat-polymerized DBR.

Closed Repair Technique: Innovative Surface Design for Polymethylmethacrylate Denture Base Repair

PURPOSE

This study aimed to evaluate the repair strength of a newly introduced repair technique involving zero-gap repair width.

MATERIALS AND METHODS

A total of 36 rectangular prism specimens with dimensions of 64 × 10 × 3.3 mm were prepared from heat-polymerized acrylic resin. Nine specimens were kept intact. The other specimens were sectioned into halves and modified to create repair gaps of 2.5-mm beveled (2.5B) as control, 0-mm beveled (ZB), and 0-mm inverse bi-beveled (ZIBB). The ZIBB group was prepared with a V-shaped internal groove on both halves (repair tunnel), while the intaglio and cameo surfaces were kept intact except for two small holes at the cameo surface for repair resin injection. The 2.5B and ZB groups were repaired conventionally while the ZIBB group was repaired by injecting repair resin into the tunnel through one of the holes until excess material oozed from the other hole. Repaired specimens were thermally cycled at 5 and 55°C for 10,000 cycles with 1 min dwell time. A 3-point bending test was conducted using a universal testing machine for flexural strength and elastic modulus measurement. Kruskal-Wallis/Mann-Whitney tests and ANOVA/post hoc Tukey tests were applied for data analysis (α = 0.05).

RESULTS

The flexural strength of repaired specimens was substantially lower than that of intact specimens, and significant differences were present between repaired groups (p ˂ 0.05). ZB and ZIBB had higher flexural strength (p ˂ 0.001) and elastic modulus (p ˂ 0.05) than 2.5B. Among the ZB and ZIBB groups, ZB showed the highest flexural strength, and ZIBB had the highest elastic modulus.

CONCLUSION

The closed repair technique improved the flexural strength and elastic modulus of repaired acrylic denture base.

Bonding Interface and Repairability of 3D-Printed Intraoral Splints: Shear Bond Strength to Current Polymers, with and without Ageing

This in-vitro study investigates the bonding interfaces reached by the conditioning of a splint material additively manufactured by digital light processing (AM base) as well as the shear bond strength (SBS) of resins bonded to these surfaces (repair material). Therefore, the AM base was either stored in dry for 12 h or wet environment for 14 days to simulate ageing by intraoral wear. The dry and wet group was bonded after physical and/or chemical conditioning to cylinders made from polymethylmethacrylate or four novel polymers allowing splint modifications. Blasted and methylmethacrylate (MMA)-conditioned Polymethylmethacrylate (PMMA) bonded to PMMA acted as the gold standard. The surface profiles revealed highest differences of Ra towards the gold standard in AM base conditioned with other than MMA after sandblasting. The adhesively bonded repair materials of the wet AM base were further aged in wet environment for 14 days. The SBS of the gold standard (25.2 MPa and 25.6 MPa) was only reached by PMMA bonded to blasted and MMA-conditioned AM base after dry (22.7 MPa) and non-conditioned after wet storage (23 MPa). Four repair materials failed to reach the threshold of 5 MPa after dry storage and three after wet storage, respectively. Non-conditioned AM base revealed the highest risk for adhesive fractures when using other resins than PMMA.

Bond strength of three chairside crown reline materials to milled polymethyl methacrylate resin

STATEMENT OF PROBLEM

Information on the bond strength of milled polymethyl methacrylate interim restorations when relined with chairside reline materials is lacking.

PURPOSE

The purpose of this in vitro study was to measure the shear bond strength of various combinations of 3 different chairside reline materials bonded to milled polymethyl methacrylate blocks with 3 different types of surface treatments.

MATERIALS AND METHODS

Uniform blocks (10×10×22 mm) were milled from tooth-colored polymethyl methacrylate disks (Vivid PMMA; Pearson Dental Supply Co). The surface treatments tested were airborne-particle abrasion with 50-μm particle size aluminosilicate, application of acrylic resin monomer (Jet Liquid; Lang Dental Manufacturing Co) for 180 seconds, and airborne-particle abrasion with monomer application. The control groups were blocks with no surface treatment. The chairside reline materials tested were Jet acrylic resin (Jet Powder; Lang Dental Manufacturing Co), bis-acryl resin (Integrity; Dentsply Sirona), and flowable composite resin (Reveal; Bisco). All materials were applied through a Ø1.5×3-mm bonding ring. Ten specimens for each of the 12 groups were tested in a universal testing machine. Load was applied at a crosshead speed of 1 mm/min. Fracture surfaces were then analyzed for cohesive versus adhesive or mixed failure. Data were analyzed using 2-way ANOVA and Tukey-Kramer post hoc analysis (α=.05).

RESULTS

The mean shear bond strength values ranged from 1.77 ±0.79 MPa to 28.49 ±5.75 MPa. ANOVA revealed that reline material (P<.05), surface treatment (P<.05), and their interactions (P<.05) significantly affected the shear bond strength among the experimental groups. The strongest combination was Jet acrylic resin applied on specimens treated with airborne-particle abrasion and monomer. All 3 failure modalities (adhesive, cohesive, and mixed modes) were observed.

CONCLUSIONS

Of the materials tested, the most reliable material to bond to milled polymethyl methacrylate was Jet acrylic resin, and the bond strength values were increased substantially when the milled polymethyl methacrylate surface was airborne-particle abraded and monomer was applied.

Repairability of a 3D printed denture base polymer: Effects of surface treatment and artificial aging on the shear bond strength

OBJECTIVES

The present study aimed to evaluate the repairability of a 3D printed denture base material. The effects of surface treatments and artificial aging on the shear bond strength (SBS) were investigated.

METHODS

A total of 224 specimens were printed by digital light processing technology (Rapid Shape D30II) using a 3D printing denture base material (FREEPRINT denture). To evaluate the repairability, the SBS and failure modes were measured after surface treatment and artificial aging. Specifically, half of the specimens were further performed with thermocycling (5-55 °C, 5000 cycles) for artificial aging. The aged and non-aged specimens were further divided into four subgroups (n = 28) to simulate a denture base repair with one of the following treatments: control (without surface treatment), monomer (applying methylmethacrylate for 120 s), P600 (grinding with P600 silicon carbide paper) and sandblasting (blasted with 125 μm aluminum oxide with 2 bar), respectively. Surface roughness was measured (n = 6) and surface topography was observed by scanning electron microscopy (n = 2). A test rod was built on the sample surface using the same 3D printing material. Afterward, all specimens further underwent thermocycling (5-55 °C, 10,000 cycles).

RESULTS

For non-aged groups, no significant differences in SBS could be found (p < 0.05), and bondings failed cohesively in the denture base material. Regarding the aged control and monomer group, adhesive failures at the interface were primarily observed, and SBS values were statistically lower than those of the other groups (p < 0.05).

CONCLUSIONS

The 3D printed denture base material exhibited favorable repairability. For the realignment surface, the SBS at the bonding interface is satisfying and additional surface treatments could be not necessary. In contrast, the aged surface could significantly decrease the SBS; hence subtractive surface treatments are highly recommended.

Influence of artificial aging and ZrO2 nanoparticle-reinforced repair resin on the denture repair strength

Background

The purpose of this study was to evaluate the effect of aging process on the tensile strength (TS) of repaired acrylic denture base using ZrO2 nanoparticles (nano-ZrO2)-reinforced autopolymerized resin.

Material and Methods

A total of 240 heat-polymerized acrylic resin specimens (n=10) were prepared and sectioned creating 2 mm-repair-gap. Autopolymerized acrylic resin, pure and modified with 2.5, 5, and 7.5wt% nano-ZrO2 were used for specimens repair. TS of repaired specimens were measured using the universal testing machine after water immersion at 37oC for 2, 7 and 30 days. At each time interval, half the immersed specimens underwent thermo-cycling aging process (5000 cycles at 5/55°C) before TS testing. One-way ANOVA and Tukey-Kramer multiple-comparison tests were used for data analysis at α=0.05.

Results

Aging process for all groups showed significant differences in TS between unreinforced and nano-ZrO2 reinforced groups (p<0.05). Within immersed nano-ZrO2-reinforced specimens, 5% group immersed for 30-days showed the highest significant TS value (p<0.05). With regards to thermocycling, 5% group showed the highest TS values after 2-days and 30-days groups while after 7-days, significant differences were found between 2.5% group and 5% and 7.5% groups (p<0.05). SEM images analysis displayed the ductile fracture type for nano-ZrO2 reinforced groups.

Conclusions

In summary, 5.0%-nano-ZrO2 addition to repair resin showed an improvement in tensile strength of repaired acrylic resin with different aging processes. Key words:Acrylic resins, denture repair, tensile strength, thermocycling, water storage, zirconium oxide nanoparticle.

Impact of different surface treatments and repair material reinforcement on the flexural strength of repaired PMMA denture base material

This study assessed the impact of surface treatments and repair resin reinforcement with zirconium oxide nano-particles (nano-ZrO₂) on flexural strength (FS) of repaired denture base. A total of 320 heat-polymerized acrylic resin specimens were prepared and sectioned creating 2-mm gap. According to repair surface treatment, specimens were distributed into four groups: I) methyl methacrylate (M); II) alumina-blasted (AB); III) AB+silane coupling agent (SC); and IV) AB+methacrylate based composite bonding agent (MA). Groups were subdivided into 4 (n=20) according to nano-ZrO₂ concentration (0, 2.5, 5, 7.5 wt%). Half the specimens were thermo-cycled before testing. FS was determined by three-point bending test. Statistical analysis was done using ANOVA and Tukey-Kramer multiple comparison tests, with α=0.05. Alumina-blasting+(SC) or (MA) significantly increased FS of repaired specimens compared to control (p<0.05). All surface-treated specimens combined with nano-ZrO₂ reinforced repair resin significantly increased FS.

Influence of Different Repair Acrylic Resin and Thermocycling on the Flexural Strength of Denture Base Resin

Background and Objectives: Fractured acrylic denture base is a common occurrence in clinical practice. The effective denture repair procedure is cost-effective, time conserving, and results in lesser time without denture for the patient. Along with various reinforcements and surface modifications; different acrylic resins are investigated in improving the flexural strength of the fractured site. The aim of this study was to evaluate the flexural strength of a polymethyl methacrylate (PMMA) denture base repaired with heat-polymerized (HPA), auto-polymerized (APA) and light-polymerized acrylic (LPA) resins after thermocycling. Materials and Methods: Forty rectangular shaped (50 mm × 25 mm × 3 mm) PMMA specimens were fabricated. Group 1 specimens (n = 10) were kept as controls and the remaining 30 samples were sectioned at the center with a repair site dimension of 3 mm. The samples from three groups (n = 10) were repaired with HPA, APA, and LPA resins, respectively. The specimens were thermocycled for 5000 cycles and subjected to a three-point flexural test. The maximum load required to fracture the specimens was recorded, and further analyzed with ANOVA and the Games-Howell Post hoc test at the significance level p = 0.05. Results: The average maximum load and flexural strength of the control group was 173.60 N and 13.02 Mpa and corresponding values for denture repaired with HPA was 87.36 N and 6.55 Mpa. The corresponding values for APA resin and LPA resins were 62.94 N, 57.51 N, and 4.72 Mpa, 4.06 Mpa, respectively. Conclusions: The PMMA specimens repaired with HPA resins resulted in a significantly higher load to fracture compared to APA resin and LPA resin.

Effect of SiO2 Nanoparticles Addition on the Flexural Strength of Repaired Acrylic Denture Base

Objective  The objective of this study was to evaluate the effect of nano-SiO ₂ addition on the flexural strength (FS) of repaired acrylic denture base.

Materials and Methods  Heat-polymerized acrylic resin specimens were fabricated in dimensions of (65 × 10 × 2.5 ± 0.1 mm ³ ) and then sectioned and prepared, creating repair gap with butt (90 degrees) and bevel (45 degrees) repair surface designs forming two main groups according to joint design. Further subdivision was done into four groups ( n = 10) according to nano-SiO ₂ concentration: one unmodified group and three modified groups (0.25, 0.5, and 0.75 wt %) in the autopolymerized repair resin. Each pair of a specimen was assembled in a mold and repaired according to manufacturer’s recommendations.

Statistical Analysis  Three-point bending test was done to measure FS, followed by scanning electron microscope (SEM) examination for fracture surface analysis. Data were analyzed using ANOVA and Tukey’s post hoc test (α = 0.05).

Results  The addition of nano-SiO ₂ significantly improved FS of repaired acrylic resin in comparison to the unmodified group ( p ˂ 0.05). For butt joint, significant differences between nano-SiO ₂ reinforced groups were noticed ( p ˂ 0.05), while reinforced beveled groups did not differ significantly ( p ˃ 0.05). Bevel design remarkably increased FS compared with butt design per respective filler concentration. From the SEM images, improved FS was presented with a homogeneous distribution of nano-SiO ₂ within polymethyl methacrylate.

Conclusion  Nano-SiO ₂ addition to repair resin and 45 degree-beveled repair surface increased FS of repaired acrylic resin.

Comparative Effect of Glass Fiber and Nano-Filler Addition on Denture Repair Strength

PURPOSE

To evaluate and compare the effects of glass fiber (GF), Zirconium oxide nanoparticles (nano-ZrO₂ ), and silicon dioxide nanoparticles (nano-SiO₂ ) addition on the flexural strength and impact strength of repaired denture base material.

MATERIALS AND METHODS

Heat-polymerized acrylic resin specimens were fabricated. All specimens were sectioned centrally and beveled creating 2.5 mm repair gap except for 10 controls. Specimen grouping (n = 10/group) was done according to filler concentration of 0%, 0.25%, 0.5%, and 0.75% of auto-polymerized acrylic powder. Modified resin was mixed, packed in the repair gap, polymerized, finished and polished. Three-point bending test and Charpy type impact testing were done. Data were analyzed using one-way-ANOVA and Post-Hoc Tukey test (α = 0.05).

RESULTS

All additives significantly increased flexural strength and impact strength (p < 0.05). Within the modified subgroups, no significant differences were found for GF. Significant increase for nano-ZrO₂ and significant decrease for nano-SiO₂ as the concentration of additive increased were noted for both flexural strength and impact strength. Highest flexural strength was found with 0.75%-nano-ZrO₂ (69.59 ± 2.52MPa) and the lowest was found with 0.75%-nano-SiO₂ (53.82 ± 3.10MPa). The 0.25%-nano-SiO₂ showed the highest impact strength value (2.54 ± 0.21 kJ/m² ) while the lowest impact strength value was seen with 0.75%-nano-SiO₂ (1.54 ± 0.17 kJ/m² ).

CONCLUSION

Nano-filler effect was concentration dependent and its addition to repair resin increased the flexural and impact strengths. The incorporation of 0.75%-ZrO₂ or 0.25%-SiO₂ into repair resin proved to be a promising technique to enhance repair strength and avoid repeated fractures.

Effect of different surface treatment methods on the shear bond strength of orthodontic brackets to temporary crowns

INTRODUCTION

The number of adult patients seeking orthodontic treatment has been consistently increasing. Since the placing of the final restoration must be postponed until the completion of the orthodontic treatment, provisional restoration is recommended for the duration of the orthodontic treatment. These surfaces have special chemical properties, which necessitate the orthodontists to prepare the bonding area with special measures.

METHODS

Polycarbonate and polymethylmethacrylate (PMMA) crowns (n=80) were randomly subdivided into 4 groups. Conditioning methods were grinding, sandblasting, CO₂ laser and methyl methacrylate application. Samples underwent SBS testing. A scanning electron microscope (SEM) analysis was carried out. The data was analysed with ANOVA, Student t-test and Post-hoc test. Adhesive remnant index (ARI) was analysed with Chi² test.

RESULTS

In all surface treatments, the mean Shear Bond Strength (SBS) of PMMA was significantly higher than that of polycarbonate (P<0.001). In the polycarbonate groups, there was a significant difference between the mean SBS of the four treatment methods (P<0.001). However, there were no significant differences in PMMA group (P=0.076). In both crown materials, the mode of the failure was adhesive type, regardless of the conditioning method (P>0.05).

CONCLUSIONS

PMMAs rendered higher bond strength than polycarbonates. In PMMA, all the surface treatment methods resulted in acceptable bond strength. However, if bonding the brackets to polycarbonate crown is needed, other conditioning methods are preferred over CO₂ laser.

Flexural Strength of Surface-Treated Heat-Polymerized Acrylic Resin after Repair with Aluminum Oxide-Reinforced Autopolymerizing Acrylic Resin

Background:

A fracture of denture base in situ often occurs through a fatigue mechanism, which over a period of time leads to the formation of small cracks, resulting in fracture.

Aim and Objective:

To evaluate the flexural strength of repaired heat-polymerized acrylic resin, with different percentage of aluminum oxide (Al₂O₃) added to the repair resin and effect of two different surface treatments on the flexural strength of repaired heat-polymerized acrylic resin and also to evaluate quantification of filler particles using scanning electron microscopy.

Materials and Methodology:

Fifty specimens of heat-polymerized acrylic resin were prepared according to the American Dental Association specification no. 12 (65 mm × 10 mm × 2.5 mm). Al₂O₃<50 nm particle size was silanized using metal alloy primer before incorporation in polymer. Two different percentages of Al₂O₃ nanoparticles, that is, 1% and 1.5% were added to autopolymerizing acrylic resin which was used as repairing material.

Results:

The study showed that repair resin incorporated with 1.5% Al₂O₃ in the group surface treated with silicon carbide paper improved the flexural strength of denture base resin. A proper filler distribution and deep penetration within the polymer matrix were observed by scanning electron microscope in the same group.

Effect of surface treatment methods on the shear bond strength of auto-polymerized resin to thermoplastic denture base polymer

PURPOSE

Polyamide polymers do not provide sufficient bond strength to auto-polymerized resins for repairing fractured denture or replacing dislodged denture teeth. Limited treatment methods have been developed to improve the bond strength between auto-polymerized reline resins and polyamide denture base materials. The objective of the present study was to evaluate the effect of surface modification by acetic acid on surface characteristics and bond strength of reline resin to polyamide denture base.

MATERIALS AND METHODS

84 polyamide specimens were divided into three surface treatment groups (n=28): control (N), silica-coated (S), and acid-treated (A). Two different auto-polymerized reline resins GC and Triplex resins were bonded to the samples (subgroups T and G, respectively, n=14). The specimens were subjected to shear bond strength test after they were stored in distilled water for 1 week and thermo-cycled for 5000 cycles. Data were analyzed with independent t-test, two-way analysis of variance (ANOVA), and Tukey's post hoc multiple comparison test (α=.05).

RESULTS

The bond strength values of A and S were significantly higher than those of N (P<.001 for both). However, statistically significant difference was not observed between group A and group S. According to the independent Student's t-test, the shear bond strength values of AT were significantly higher than those of AG (P<.001).

CONCLUSION

The surface treatment of polyamide denture base materials with acetic acid may be an efficient and cost-effective method for increasing the shear bond strength to auto-polymerized reline resin.

Influence of incorporation of ZrO2 nanoparticles on the repair strength of polymethyl methacrylate denture bases

BACKGROUND

Repeated fracture of the denture base is a common problem in prosthodontics, and it represents a nuisance and a time sink for the clinician. Therefore, the possibility of increasing repair strength using new reinforcement materials is of great interest to prosthodontists.

AIM OF THE STUDY

This study aimed to evaluate the effects of incorporation of zirconia nanoparticles (nano-ZrO₂) on the flexural strength and impact strength of repaired polymethyl methacrylate (PMMA) denture bases.

MATERIALS AND METHODS

One hundred eighty specimens of heat-polymerized acrylic resin were fabricated (90 for each test) and divided into three main groups: one control group (intact specimens) and two groups divided according to surface design (45° bevels and butt joints), in which specimens were prepared in pairs to create 2.5 mm gaps. Nano-ZrO₂ was added to repair resin in 2.5 wt%, 5 wt%, and 7.5 wt% concentrations of acrylic powder. A three-point bending test was used to measure flexural strength, and a Charpy-type test was used to measure impact strength. Scanning electron microscopy was used to analyze the fracture surfaces and nano-ZrO₂ distribution. The results were analyzed with a paired sample t-test and an unpaired t-test, with a P-value of ≤0.05 being significant.

RESULTS

Incorporation of nano-ZrO₂ into the repair resin significantly increased flexural strength (P<0.05). The highest value was found in the bevel group reinforced with 7.5% nano-ZrO₂, whereas the lowest value was found in the butt group reinforced with 2.5% nano-ZrO₂. The impact strength values of all repaired groups were significantly lower than those of the control group (P<0.05). Among repaired groups, the higher impact strength value was seen in the butt group reinforced with 2.5% nano-ZrO₂. The bevel joint demonstrated mainly cohesive failure, whereas the butt joint demonstrated mainly adhesive failure.

CONCLUSION

Incorporation of nano-ZrO₂ into the repair resin improved the flexural strength of repaired denture bases, whereas it decreased impact strength, especially with high nano-ZrO₂ concentrations.

The effect of different chemical surface treatments of denture teeth on shear bond strength: a comparative study

BACKGROUND

The development of better cross linked acrylic resin teeth has solved the problems related to wearing and discoloration of acrylic teeth. The same cross linking at ridge lap region acts as a double edge sword as it weakens the bond between denture base and tooth.

AIM OF STUDY

The purpose of study was to evaluate the effect of surface treatment on the bond strength of resin teeth to denture base resin using monomethyl methacrylate monomer and dichloromethane with no surface treatment acting as control.

SETTINGS AND DESIGN

Denture base cylinder samples in wax (n=180) were made with maxillary central incisor attached at 450 (JIST 6506). These samples were randomly and equally divided into three groups of 60 each. These specimens were then flasked, dewaxed as per the standard protocol.

MATERIALS AND METHODS

Before acrylization, ridge lap area was treated as follows: Group A- no surface treatment act as control, Group B treated with monomethyl methacrylate monomer, Group C treated with dichloromethane. Digitally controlled acryliser was used for acrylization as per manufacturer's instructions and shear bond strength was tested on Universal Testing Machine (Servo Hydraulic, 50kN High Strain, BISS Research).

STATISTICAL ANALYSIS USED

Result was statistically analyzed with One-way analysis of variance (ANOVA) and Post-hoc ANOVA Tukey's HSD test at 5% level of significance.

RESULTS

The application of dichloromethane showed increased bond strength between cross linked acrylic resin teeth and heat cure denture base resin followed by monomethyl methacrylate monomer and control group.

CONCLUSION

The application of dichloromethane on the ridge lap surface of the resin teeth before packing of the dough into the mold significantly increased the bond strength between cross linked acrylic resin teeth and heat cure denture base resin.

Surface treatment with methyl formate-methyl acetate increased the shear bond strength between reline resins and denture base resin

BACKGROUND

Chemical surface treatment increases the shear bond strength (SBS) between hard reline resins (HRRs) and denture base resin.

OBJECTIVE

To evaluate the effect of methyl formate-methyl acetate (MF-MA), when used as a surface treatment agent, on the SBS between denture base resin and different HRRs.

MATERIALS AND METHODS

One hundred and twenty specimens of heat-polymerised acrylic resin denture base (Meliodent(®) ) were divided into 12 groups. These groups comprised denture base relined with three self-polymerised HRRs [Unifast trad(®) (UT), Tokuyama(®) RebaseII Fast (TR), Ufi gel hard(®) (UG)], and treated with their respective Bonding Agent (BA) or by MF:MA solutions at ratios of 35:65, 25:75, and 15:85 for 15 s. The SBS was measured using a Universal Testing Machine. The data were analysed using two-way anova and post hoc Tukey's analysis at p < 0.05.

RESULTS

The highest SBS was in the UT treated with MF:MA at a ratio of 25:75 group, followed by UT treated with MF:MA at ratios of 15:85, 35:65, UT treated with BA, and all UG treated with MF:MA groups. The SBS of the UT treated with MF:MA at a ratio of 25:75 group was significantly higher than those of the groups treated with BA. The SBS of the UG treated with MF:MA groups was significantly higher than control. The TR groups treated with BA or MF:MA groups showed no significant difference in SBS.

CONCLUSION

Surface treatment with MF-MA significantly enhanced the SBS of denture base resin and UT and UG compared to that of the groups treated with BA.

Comparative Evaluation of Tensile Bond Strength between Silicon Soft Liners and Processed Denture Base Resin Conditioned by Three Modes of Surface Treatment: An Invitro Study

Soft denture liners act as a cushion for the denture bearing mucosa through even distribution of functional load, avoiding local stress concentrations and improving retention of dentures there by providing comfort to the patient. The objective of the present study was to compare and evaluate the tensile bond strengths of silicone-based soft lining materials (Ufi Gel P and GC Reline soft) with different surface pre treatments of heat cure PMMA denture base acrylic resin. Stainless steel dies measuring 40 mm in length; 10 mm in width and 10 mm in height (40 × 10 × 10) were machined to prepare standardized for the polymethyl methacrylate resin blocks. Stainless steel dies (spacer for resilient liner) measuring 3 mm thick; 10 mm long and 10 mm wide were prepared as spacers to ensure uniformity of the soft liner being tested. Two types of Addition silicone-based soft lining materials (room temperature polymerised soft lining materials (RTPSLM): Ufi Gel P and GC Reline soft) were selected. Ufi Gel P (VOCO, Germany), GC Reline soft (GC America) are resilient, chairside vinyl polysiloxane denture reliners of two different manufacturers. A total of 80 test samples were prepared of which 40 specimens were prepared for Group A (Ufi Gel P) and 40 specimens for Group B (GC Reline soft). In these groups, based on Pre-treatment of acrylic resin specimens each group was subdivided into four sub groups of 10 samples each. Sub-group I-without any surface treatment. Sub-group II-sand blasted Sub-group III-treated with Methyl Methacrylate monomer Sub-group IV-treated with chemical etchant Acetone. The results were statistically analysed by Kruscal Wallis test, Mann-Whitney U test, and Independent t test. The specimens treated with MMA monomer wetting showed superior and significant bond strength than those obtained by other surface treatments. The samples belonging to subgroups of GC Reline soft exhibit superior tensile bond strength than subgroups of Ufi Gel P. The modes of failure of all specimens were mostly adhesive in nature. Surface pre treatments by chemical means improved the bond strength between the silicone liners and denture base.

Effect of adherend temperature on bond strengths of resin bonding systems to denture base resin and a semi-precious alloy

This study investigated the effect of adherend temperature on shear bond strengths of auto-polymerizing resin to denture base resin and 4-META/MMA-TBBO resin to silver-palladium-copper-gold (Ag-Pd-Cu-Au) alloy. Bonding procedure was carried out when adherend temperature was 10, 23, 37, or 55°C, and shear bond strengths (SBSs) were measured before and after thermocycling. Before thermocycling, there were no significant differences in bond strength among the four adherend temperatures for each adhesive resin: 31.59±6.11-32.89±2.12 MPa for auto-polymerizing resin; 35.43±2.2-38.38±0.61 MPa for 4-META/MMA-TBBO resin. After thermocycling, optimal adherend temperature to achieve the highest bond strength was 37°C for auto-polymerizing resin to denture base resin (30.02±2.29 MPa) and 10ºC for 4-META/MMA-TBBO resin to Ag-Pd-Cu-Au alloy (37.14±2.17 MPa).

Effects of different surface pre-treatments on the bond strength of adhesive resin cement to quartz fiber post

OBJECTIVE

The purpose of this study was to evaluate the effect of mechanical and chemical surface treatment methods on the bond strength of resin cement to fiber post.

MATERIALS AND METHODS

The roots of 36 maxillary central incisor teeth were mounted in auto polymerized acrylic resin blocks (10 × 15 mm) and the root canals were enlarged with the drills of post system (2.1 mm width, 12 mm length). Thirty-six fiber posts were randomly assigned to one of the following surface conditioning methods: silane coupling agent, methylene chloride etching, 24% hydrogen peroxide etching, air abrasion with 50 µm Al(2)O(3), 1-3 µm synthetic diamond particles and silica coating with 30 µm SiO(x). Fiber posts were cemented to the root canals with adhesive resin cement (Panavia F 2.0). Three slices of 1.5 mm thick were obtained from each root. Push-out tests were performed with a universal testing machine. The data were analyzed with one-way analysis of variance (ANOVA) and Tukey HSD tests (α = 0.05). The effect of the surface treatments were examined under a scanning electron microscope (SEM) and surface roughness were evaluated with a profilometer.

RESULTS

Surface pre-treatment methods affected the bond strength (p < 0.05). The highest bond strengths were obtained by air abrasion with synthetic diamond particles, the lowest bond strength were obtained by etching with methylene chloride (p < 0.05).

CONCLUSION

Mechanical surface pre-treatment methods showed higher bond strength values than chemical methods. Synthetic diamond particles may be an alternative method to increase resin cement bonding on the quartz fiber post surfaces.

Review of adhesive techniques used in removable prosthodontic practice

There are several benefits in using adhesive technique in removable prosthodontics as well as fixed prosthodontics. Previous studies have examined denture-base surface treatments that improve bond strength between a denture base resin and autopolymerizing repair resin. Dichloromethane and ethyl acetate are organic solvents that swell the denture base surface, thereby permitting diffusion of the acrylic resin. The optimal treatment duration is 5-10 s for dichloromethane and 120 s for ethyl acetate. It was reported that the bond durability of dichloromethane was superiorto that of ethyl acetate. Bonding between metal components and the denture base resin has an important role in the longevity of removable prostheses. The combination of metal conditioners and alumina air-abrasion is effective in fabricating and repairing removable dentures. Acidic monomers (4-META and MDP) are appropriate for base metal alloys, including Co-Cr alloy and titanium alloy, while thione monomers (MTU-6 and VBATDT) are suitable for noble metal alloys such as gold alloy and silver-palladium-copper-gold (Ag-Pd-Cu-Au) alloy. As an alternative to conventional restorations, resin-bonded restorations can provide precisely parallel guide planes with well-made rest seats. Careful consideration should be paid to stabilizing loosened teeth by fixing them with resin-bonded splints or fixed partial dentures.

A study to evaluate and compare the shear bond strength of resilient liners with heat cure denture base resins, with and without the effect of saliva: an in vitro study

AIM

To evaluate and compare the shear bond strength of resilient liners with heat cure denture base resins in the presence or absence of saliva.

MATERIALS AND METHODS

Two commercially available heat polymerized acrylics and three commercially available denture liners were immersed in artificial saliva for 7 days and 14 days, respectively. A total of 180 (Acralyn-H, No.90 and Lucitone - 199, No.90) specimens were prepared. Total of 90 overlapping joint specimens were prepared, 45 of them using Acralyn H (AGroup) and rest 45 using Lucitone-199 (L-Group). The specimens were tested for flexural strength with a 3-point bending test on an Instron universal testing machine. The results were analyzed with a one-way analysis of variance (ANOVA).

RESULTS

The mean difference in shear bond strength (SBS) at different time intervals was found to be statistically significant (p < 0.001). Lucitone-199 recorded a significantly higher mean SBS compared to Acralyn H (p < 0.001). Further, significant differences between GC and Densply, GC and Aswin liners, and between Dentsply and Aswin were noted (p < 0.001). Difference between baseline and 7 days time interval, as well as, between baseline and 14 days time interval with respect to the mean SBS of these materials were significant (p < 0.001). Also, the mean difference in SBS between 7 days time interval and 14 days time interval was statistically significant (p < 0.001). Among the three different liners, GC yielded a higher mean SBS compared to Aswin and Dentsply at all the three time intervals. The mean SBS recorded in Dentsply and Aswin was almost same at 14 days time interval, but at baseline and 7 days, it was higher in Aswin compared to Dentsply.

CONCLUSION

Lucitone-199 recorded a higher mean SBS compared to Acralyn H. As the time interval increases, the mean SBS recorded in both the denture base materials decrease. Among the three different liners, GC yields a higher mean SBS compared to Aswin and Dentsply at all the three time intervals.

CLINICAL SIGNIFICANCE

The most common reason for failures of resilient linings in removable dentures is the separation of these linings from the denture base. Therefore, poor adhesive bond properties are one of the serious defects of the material in clinical practice.

Effect of surface treatments and cyclic loading on the bond strength of acrylic resin denture teeth with autopolymerized repair acrylic resin

STATEMENT OF PROBLEM

Fracture of denture teeth from the denture base is a common problem associated with dental prostheses. Fractured tooth surfaces treated with chemical agents and mechanical features have the potential for improved repair strength.

PURPOSE

The purpose of this study was to compare bond strengths of denture teeth to autopolymerized repair acrylic resin after various surface treatments, before and after cyclic loading.

MATERIAL AND METHODS

Mandibular lateral incisor denture teeth were selected and ground on the ridge-lap portion using a standardized jig. Specimens with a ground surface were used as controls. The experimental groups included: ground plus airborne-particle abraded, ground plus diatoric recess, and ground plus an experimental bonding agent. The teeth were affixed by an autopolymerized repair acrylic resin to denture bases. Specimens (n=10) were subjected to compression testing (5 mm/min) at a 135-degree angle, before and after 14,400 loading cycles at 2 Hz and 22 N. Peak load to dislodgement was recorded and statistically analyzed (2-way ANOVA, Tukey HSD, alpha=.05). The specimens were then examined using x10 magnification, and fractures were categorized as adhesive, cohesive, or mixed.

RESULTS

The mean bond strengths ranged from 26.3 N to 44.2 N. There were no significant differences in fatigue versus nonfatigue strength values within each group (P=.244). Significant strength differences were found (P<.001) between the ground control, diatoric recess, and bonding agent groups. Microscopic examination revealed that the bonding agent group obtained the highest percentage of mixed-type fractures.

CONCLUSIONS

The use of a bonding agent and the placement of a diatoric recess in the denture tooth resulted in higher bond strengths than grinding alone. Cyclic loading had no significant impact on the bond strength of denture teeth to the autopolymerized repair acrylic resin.